In this work we prepared several CeO2-TiO2 catalysts for the NH3-SCR reactionusing co-precipitation with assistance of microwave irradiation.The catalytic NH3-SCR activities over CeO2-TiO2 catalysts at low temperature...In this work we prepared several CeO2-TiO2 catalysts for the NH3-SCR reactionusing co-precipitation with assistance of microwave irradiation.The catalytic NH3-SCR activities over CeO2-TiO2 catalysts at low temperatures are largely enhanced by the treatment of microwave irradiation,the operation temperature window is also broadened.For better understanding the promotion mechanism,the catalyst prepared by conventional co-precipitation with and without microwave irradiation treatment was characterized with H2-TPR,NH3-TPD,XPS,XRD and BET.Microwave irradiation treatment accelerates the crystallite rate of CeO2-TiO2 catalysts,and greatly enlarges their surface area by adjusting their microstructures.The resistance to SO2 and H2O is also improved via regulating the hierarchical pore structure by the microwave irradiation.Microwave irradiation treatment can also improve the redox property and increase the acid sites over the catalyst surfaces.The result of in situ DRIFTS suggests that the microwave irradiation treatment generates more Br?nsted acid sites on CeO2-TiO2-2 h catalyst,helpful in SCR reactions.XPS results show that after microwave irradiation on the CeO2-TiO2 catalysts,the surface demonstrates an elevated concentration of chemisorbed oxygen,consequently leading to better oxidation of NO to NO2.Additionally,the molar ratio of Ce3+/Ce4+has been elevated after being treated by microwave irradiation,a vital factor in enhancing the NH3-SCR activities.展开更多
V2O5/WO3‐TiO2 and V2O5/WO3‐TiO2‐SiO2 catalysts were prepared by a wetness impregnation method, and both the catalysts were hydrothermally aged at 750℃ in 10 vol%H2O/air for 24 h. The catalysts were evaluated for N...V2O5/WO3‐TiO2 and V2O5/WO3‐TiO2‐SiO2 catalysts were prepared by a wetness impregnation method, and both the catalysts were hydrothermally aged at 750℃ in 10 vol%H2O/air for 24 h. The catalysts were evaluated for NOx conversion using NH3 as the reductant. Hydrothermal ageing decreased the NOx conversion of V2O5/WO3‐TiO2 catalyst severely over the entire measured tem‐perature range. Interestingly, the NH3‐SCR activity of the silica‐modified catalyst at 220–480℃ is enhanced after ageing. The catalysts were characterized by X‐ray diffraction, nitrogen adsorption, X‐ray fluorescence, Raman spectroscopy, H2 temperature‐programmed reduction, and NH3 temper‐ature‐programmed desorption. The addition of silica inhibited the phase transition from anatase to rutile titania, growth of TiO2 crystallite size and shrinkage of catalyst surface area. Consequently, the vanadia species remained highly dispersed and the hydrothermal stability of the V2O5/WO3‐TiO2 catalyst was significantly improved.展开更多
Hairong Wang, Yaoqiang Chen, Qiulin Zhang, Qingchao Zhu, Maochu Gong, Ming Zhao（ Key Laboratory of Green Chemistry ＆ Technology of Ministry Education, College of Chemistry, Sichuan University, Chengdu 610064, Sichua...Hairong Wang, Yaoqiang Chen, Qiulin Zhang, Qingchao Zhu, Maochu Gong, Ming Zhao（ Key Laboratory of Green Chemistry ＆ Technology of Ministry Education, College of Chemistry, Sichuan University, Chengdu 610064, Sichuan, China展开更多
基金Project supported by the National Natural Science Foundation of China(21577005)the National Key Research and Development Program of China(2016YFB0600400)
文摘In this work we prepared several CeO2-TiO2 catalysts for the NH3-SCR reactionusing co-precipitation with assistance of microwave irradiation.The catalytic NH3-SCR activities over CeO2-TiO2 catalysts at low temperatures are largely enhanced by the treatment of microwave irradiation,the operation temperature window is also broadened.For better understanding the promotion mechanism,the catalyst prepared by conventional co-precipitation with and without microwave irradiation treatment was characterized with H2-TPR,NH3-TPD,XPS,XRD and BET.Microwave irradiation treatment accelerates the crystallite rate of CeO2-TiO2 catalysts,and greatly enlarges their surface area by adjusting their microstructures.The resistance to SO2 and H2O is also improved via regulating the hierarchical pore structure by the microwave irradiation.Microwave irradiation treatment can also improve the redox property and increase the acid sites over the catalyst surfaces.The result of in situ DRIFTS suggests that the microwave irradiation treatment generates more Br?nsted acid sites on CeO2-TiO2-2 h catalyst,helpful in SCR reactions.XPS results show that after microwave irradiation on the CeO2-TiO2 catalysts,the surface demonstrates an elevated concentration of chemisorbed oxygen,consequently leading to better oxidation of NO to NO2.Additionally,the molar ratio of Ce3+/Ce4+has been elevated after being treated by microwave irradiation,a vital factor in enhancing the NH3-SCR activities.
基金supported by the National Natural Science Foundation of China (51372137)the National High Technology Research and Development Program of China (863 Program,2015AA034603)~~
文摘V2O5/WO3‐TiO2 and V2O5/WO3‐TiO2‐SiO2 catalysts were prepared by a wetness impregnation method, and both the catalysts were hydrothermally aged at 750℃ in 10 vol%H2O/air for 24 h. The catalysts were evaluated for NOx conversion using NH3 as the reductant. Hydrothermal ageing decreased the NOx conversion of V2O5/WO3‐TiO2 catalyst severely over the entire measured tem‐perature range. Interestingly, the NH3‐SCR activity of the silica‐modified catalyst at 220–480℃ is enhanced after ageing. The catalysts were characterized by X‐ray diffraction, nitrogen adsorption, X‐ray fluorescence, Raman spectroscopy, H2 temperature‐programmed reduction, and NH3 temper‐ature‐programmed desorption. The addition of silica inhibited the phase transition from anatase to rutile titania, growth of TiO2 crystallite size and shrinkage of catalyst surface area. Consequently, the vanadia species remained highly dispersed and the hydrothermal stability of the V2O5/WO3‐TiO2 catalyst was significantly improved.
基金the National Natural Science Foundation of China (20773090)the Specialized Research Fund for the Doctoral Program of Higher Education of China (20070610026, 200806100009)
文摘Hairong Wang, Yaoqiang Chen, Qiulin Zhang, Qingchao Zhu, Maochu Gong, Ming Zhao（ Key Laboratory of Green Chemistry ＆ Technology of Ministry Education, College of Chemistry, Sichuan University, Chengdu 610064, Sichuan, China