CeO2-TiO2 films and CeO2-TiO/SnO2：Sb （6 mol%） double films were deposited on glass substrates by radio-frequency magnetron sputtering （R.F. Sputtering）, using SnO2：Sb（6 mol%） target, and CeO2- TiO2 targets wit...CeO2-TiO2 films and CeO2-TiO/SnO2：Sb （6 mol%） double films were deposited on glass substrates by radio-frequency magnetron sputtering （R.F. Sputtering）, using SnO2：Sb（6 mol%） target, and CeO2- TiO2 targets with different molar ratio of CeO2 to TiO2 （CeO2：TiO2-0：1.0; 0.1：0.9; 0.2：0.8; 0.3：0.7; 0.4：0.6; 0.5：0.5; 0.6：0.4; 0.7：0.3; 0.8：0.2; 0.9：0.1; 1.0：0）. The films are characterized by UV-visible transmission and infrared reflection spectra, scanning electron microscopy （SEM）, Raman spectroscopy, X-ray photoelectron spectroscopy （XPS） and X-ray diffraction （XRD）, respectively. The obtained results show that the amorphous phases composed of CeO2-TiO2 play an important role in absorbing UV, there are Ce^3-, Ce^4- and Ti^4- on the surface of the films; the glass substrates coated with CeO2-TiO2 （Ce/Ti=0.5：0.5; 0.6：0.4）/SnO2：Sb（6 mol%） double films show high absorbing UV（〉99）, high visible light transmission （75%） and good infrared reflection （〉70%）. The sheet resistance of the films is 30-50 Ω/□. The glass substrates coated with the double functional films can be used as window glass of buildings, automobile and so on.展开更多
Sb-doped SnO2(ATO)-(CeO2-TiO2) thin Films were deposited on glass substrates using the mixed solution including CeO2-TiO2 precursor and ATO particles by sol-gel dip coating process.ATO particles were prepared using lo...Sb-doped SnO2(ATO)-(CeO2-TiO2) thin Films were deposited on glass substrates using the mixed solution including CeO2-TiO2 precursor and ATO particles by sol-gel dip coating process.ATO particles were prepared using low-temperature hydrothermal process.The mixed molar ratio of ATO to(CeO2-TiO2) vs the properties of CeO2-TiO2 thin film was investigated.The optical properties of the films were characterized by UV-visible transmission and infrared reflection spectra,the sheet resistance of ATO particles and films were measured by rubber sheeter(MYI-50) and four-point probe(HisuperGroup Inc,SDY-5),the surface morphology and structure of the films were analyzed using 3D Digitale Mikroskop and X-ray diffraction(XRD),respectively.The results showed that the ATO precursor solution lost weight completely at about 500 oC,and the ATO particles was obtained,which indicated the same rutile lattice structure as SnO2.The glass substrates coated with ATO-(CeO2-TiO2) thin films showed better properties in antistatic electricity(104-106 Ω/),shielding UV(almost 100%),visible light transmission(70%) and infrared reflection(】30%).展开更多
The structure and catalytic desulfurization characteristics of CeO2-TiO2 mixed oxides were investigated by means ofX-ray diffraction （XRD）, X-ray photoelectron spectroscopy （XPS） and catalytic activity tests. Acco...The structure and catalytic desulfurization characteristics of CeO2-TiO2 mixed oxides were investigated by means ofX-ray diffraction （XRD）, X-ray photoelectron spectroscopy （XPS） and catalytic activity tests. According to the results, a CeO2-TiO2solid solution is formed when the mole ratio of cerium to titanium n（Ce）：n（Ti） is 5：5 or greater, and the most suitable n（Ce）：n（Ti） isdetermined as 7：3, over which the conversion rate of SO2 and the yield of sulfur at 500℃ reach 93% and 99%, respectively.According to the activity testing curve, Ce0.7Ti0.3O2 （n（Ce）：n（Ti）=7：3） without any pretreatment can be gradually activated by reagentgas after about 10 min, and reaches a steady activation status 60 min later. The XPS results of Ce0.7Ti0.3O2 after different time ofSO2＋CO reaction show that CeO2 is the active component that offers the redox couple Ce4＋/Ce3＋ and the labile oxygen vacancies, andTiO2 only functions as a catalyst structure stabilizer during the catalytic reaction process. After 48 h of catalytic reaction at 500℃,Ce0.7Ti0.3O2 still maintains a stable structure without being vulcanized, demonstrating its good anti-sulfur poisoning performance.展开更多
基金the program for Changjiang Scholars and Innovative Research Team in University (No.IRT0547
文摘CeO2-TiO2 films and CeO2-TiO/SnO2：Sb （6 mol%） double films were deposited on glass substrates by radio-frequency magnetron sputtering （R.F. Sputtering）, using SnO2：Sb（6 mol%） target, and CeO2- TiO2 targets with different molar ratio of CeO2 to TiO2 （CeO2：TiO2-0：1.0; 0.1：0.9; 0.2：0.8; 0.3：0.7; 0.4：0.6; 0.5：0.5; 0.6：0.4; 0.7：0.3; 0.8：0.2; 0.9：0.1; 1.0：0）. The films are characterized by UV-visible transmission and infrared reflection spectra, scanning electron microscopy （SEM）, Raman spectroscopy, X-ray photoelectron spectroscopy （XPS） and X-ray diffraction （XRD）, respectively. The obtained results show that the amorphous phases composed of CeO2-TiO2 play an important role in absorbing UV, there are Ce^3-, Ce^4- and Ti^4- on the surface of the films; the glass substrates coated with CeO2-TiO2 （Ce/Ti=0.5：0.5; 0.6：0.4）/SnO2：Sb（6 mol%） double films show high absorbing UV（〉99）, high visible light transmission （75%） and good infrared reflection （〉70%）. The sheet resistance of the films is 30-50 Ω/□. The glass substrates coated with the double functional films can be used as window glass of buildings, automobile and so on.
基金Project supported by the Changjiang Scholars and Innovative Research Team in University
文摘Sb-doped SnO2(ATO)-(CeO2-TiO2) thin Films were deposited on glass substrates using the mixed solution including CeO2-TiO2 precursor and ATO particles by sol-gel dip coating process.ATO particles were prepared using low-temperature hydrothermal process.The mixed molar ratio of ATO to(CeO2-TiO2) vs the properties of CeO2-TiO2 thin film was investigated.The optical properties of the films were characterized by UV-visible transmission and infrared reflection spectra,the sheet resistance of ATO particles and films were measured by rubber sheeter(MYI-50) and four-point probe(HisuperGroup Inc,SDY-5),the surface morphology and structure of the films were analyzed using 3D Digitale Mikroskop and X-ray diffraction(XRD),respectively.The results showed that the ATO precursor solution lost weight completely at about 500 oC,and the ATO particles was obtained,which indicated the same rutile lattice structure as SnO2.The glass substrates coated with ATO-(CeO2-TiO2) thin films showed better properties in antistatic electricity(104-106 Ω/),shielding UV(almost 100%),visible light transmission(70%) and infrared reflection(】30%).
文摘The structure and catalytic desulfurization characteristics of CeO2-TiO2 mixed oxides were investigated by means ofX-ray diffraction （XRD）, X-ray photoelectron spectroscopy （XPS） and catalytic activity tests. According to the results, a CeO2-TiO2solid solution is formed when the mole ratio of cerium to titanium n（Ce）：n（Ti） is 5：5 or greater, and the most suitable n（Ce）：n（Ti） isdetermined as 7：3, over which the conversion rate of SO2 and the yield of sulfur at 500℃ reach 93% and 99%, respectively.According to the activity testing curve, Ce0.7Ti0.3O2 （n（Ce）：n（Ti）=7：3） without any pretreatment can be gradually activated by reagentgas after about 10 min, and reaches a steady activation status 60 min later. The XPS results of Ce0.7Ti0.3O2 after different time ofSO2＋CO reaction show that CeO2 is the active component that offers the redox couple Ce4＋/Ce3＋ and the labile oxygen vacancies, andTiO2 only functions as a catalyst structure stabilizer during the catalytic reaction process. After 48 h of catalytic reaction at 500℃,Ce0.7Ti0.3O2 still maintains a stable structure without being vulcanized, demonstrating its good anti-sulfur poisoning performance.