A series of CeO2–ZrO2–WO3（CZW）catalysts prepared by a hydrothermal synthesis method showed excellent catalytic activity for selective catalytic reduction（SCR）of NO with NH3 over a wide temperature of 150–550℃....A series of CeO2–ZrO2–WO3（CZW）catalysts prepared by a hydrothermal synthesis method showed excellent catalytic activity for selective catalytic reduction（SCR）of NO with NH3 over a wide temperature of 150–550℃.The effect of hydrothermal treatment of CZW catalysts on SCR activity was investigated in the presence of 10% H2O.The fresh catalyst showed above 90% NOx conversion at 201–459℃,which is applicable to diesel exhaust NOx purification（200–440℃）.The SCR activity results indicated that hydrothermal aging decreased the SCR activity of CZW at low temperatures（below 300℃）,while the activity was notably enhanced at high temperature（above 450℃）.The aged CZW catalyst（hydrothermal aging at 700℃ for 8 hr）showed almost 80% NOx conversion at 229–550℃,while the V2O5–WO3/TiO2 catalyst presented above 80% NOx conversion at 308–370℃.The effect of structural changes,acidity,and redox properties of CZW on the SCR activity was investigated.The results indicated that the excellent hydrothermal stability of CZW was mainly due to the CeO2–ZrO2 solid solution,amorphous WO3 phase and optimal acidity.In addition,the formation of WO3 clusters increased in size as the hydrothermal aging temperature increased,resulting in the collapse of structure,which could further affect the acidity and redox properties.展开更多
A series of CeO2-ZrO2-WO3 catalysts for the selective catalytic reduction （SCR） of NO with NH3 were prepared by hydrothermal method. The influence of calcination temperature on the catalytic activity, microstructure...A series of CeO2-ZrO2-WO3 catalysts for the selective catalytic reduction （SCR） of NO with NH3 were prepared by hydrothermal method. The influence of calcination temperature on the catalytic activity, microstructure, surface acidity and redox behavior of CeO2-ZrO2-WO3 catalyst was investigated using various characterization methods. It was found that the CeO2-ZrO2-WO3 catalyst calcined at 600 ℃ showed the best catalytic performance and excellent N2 selectivity, and yielded more than 90% NO conversion in a wide temperature range of 250-500 ℃ with a space velocity （GHSV） of 60000 131. As the calcination temperature was increased from 400 to 600 ℃, the NO conversion obviously increased, but decreased at higher calcination temperature. The results implied that the higher surface area, the strongest synergistic interaction, the superior redox property and the highly dispersed or amorphous WO3 species contributed to the excellent SCR activity of the CeO2-ZrO2-WO3 catalyst calcined at 600℃.展开更多
CeO2-based oxygen materials were prepared with co-precipitation method and characterized via Brunauer-Emmet Teller(BET)method,X-ray diffraction(XRD)and temperature-programmed reduction(H2-TPR).This paper revealed that...CeO2-based oxygen materials were prepared with co-precipitation method and characterized via Brunauer-Emmet Teller(BET)method,X-ray diffraction(XRD)and temperature-programmed reduction(H2-TPR).This paper revealed that three CeO2-based oxygen storage materials are all forming homogeneous solid solution.Among the samples,CeO2-ZrO2-Al2O3(CZA)has the best textural properties and excellent thermal stability.The specific surface area and pore volume of aged CZA are 90 m2/g and 0.29 mL/g.We proposed a viewpoint:Al3+ might insert among the interspace of fluorite structure or highly dispersal in solid solutions.展开更多
基金supported by the National Natural Science Foundation of China(Nos.U1137603,21307047)the Opening Project of Key Laboratory of Green Catalysis of Sichuan Institutes of High Education(No.LYJ1309)
文摘A series of CeO2–ZrO2–WO3（CZW）catalysts prepared by a hydrothermal synthesis method showed excellent catalytic activity for selective catalytic reduction（SCR）of NO with NH3 over a wide temperature of 150–550℃.The effect of hydrothermal treatment of CZW catalysts on SCR activity was investigated in the presence of 10% H2O.The fresh catalyst showed above 90% NOx conversion at 201–459℃,which is applicable to diesel exhaust NOx purification（200–440℃）.The SCR activity results indicated that hydrothermal aging decreased the SCR activity of CZW at low temperatures（below 300℃）,while the activity was notably enhanced at high temperature（above 450℃）.The aged CZW catalyst（hydrothermal aging at 700℃ for 8 hr）showed almost 80% NOx conversion at 229–550℃,while the V2O5–WO3/TiO2 catalyst presented above 80% NOx conversion at 308–370℃.The effect of structural changes,acidity,and redox properties of CZW on the SCR activity was investigated.The results indicated that the excellent hydrothermal stability of CZW was mainly due to the CeO2–ZrO2 solid solution,amorphous WO3 phase and optimal acidity.In addition,the formation of WO3 clusters increased in size as the hydrothermal aging temperature increased,resulting in the collapse of structure,which could further affect the acidity and redox properties.
基金supported by the National Natural Science Foundation of China(21273043,21077026)Science and Technology Commission of Shanghai Municipality,China(13DZ2275200)~~
基金Project supported by the National Natural Science Foundation of China(21377048,21307047)the Opening Project of Key Laboratory of Green Catalysis of Sichuan Institutes of High Education(LYJ1309)
文摘A series of CeO2-ZrO2-WO3 catalysts for the selective catalytic reduction （SCR） of NO with NH3 were prepared by hydrothermal method. The influence of calcination temperature on the catalytic activity, microstructure, surface acidity and redox behavior of CeO2-ZrO2-WO3 catalyst was investigated using various characterization methods. It was found that the CeO2-ZrO2-WO3 catalyst calcined at 600 ℃ showed the best catalytic performance and excellent N2 selectivity, and yielded more than 90% NO conversion in a wide temperature range of 250-500 ℃ with a space velocity （GHSV） of 60000 131. As the calcination temperature was increased from 400 to 600 ℃, the NO conversion obviously increased, but decreased at higher calcination temperature. The results implied that the higher surface area, the strongest synergistic interaction, the superior redox property and the highly dispersed or amorphous WO3 species contributed to the excellent SCR activity of the CeO2-ZrO2-WO3 catalyst calcined at 600℃.
文摘CeO2-based oxygen materials were prepared with co-precipitation method and characterized via Brunauer-Emmet Teller(BET)method,X-ray diffraction(XRD)and temperature-programmed reduction(H2-TPR).This paper revealed that three CeO2-based oxygen storage materials are all forming homogeneous solid solution.Among the samples,CeO2-ZrO2-Al2O3(CZA)has the best textural properties and excellent thermal stability.The specific surface area and pore volume of aged CZA are 90 m2/g and 0.29 mL/g.We proposed a viewpoint:Al3+ might insert among the interspace of fluorite structure or highly dispersal in solid solutions.