In this work we prepared several CeO2-TiO2 catalysts for the NH3-SCR reactionusing co-precipitation with assistance of microwave irradiation.The catalytic NH3-SCR activities over CeO2-TiO2 catalysts at low temperature...In this work we prepared several CeO2-TiO2 catalysts for the NH3-SCR reactionusing co-precipitation with assistance of microwave irradiation.The catalytic NH3-SCR activities over CeO2-TiO2 catalysts at low temperatures are largely enhanced by the treatment of microwave irradiation,the operation temperature window is also broadened.For better understanding the promotion mechanism,the catalyst prepared by conventional co-precipitation with and without microwave irradiation treatment was characterized with H2-TPR,NH3-TPD,XPS,XRD and BET.Microwave irradiation treatment accelerates the crystallite rate of CeO2-TiO2 catalysts,and greatly enlarges their surface area by adjusting their microstructures.The resistance to SO2 and H2O is also improved via regulating the hierarchical pore structure by the microwave irradiation.Microwave irradiation treatment can also improve the redox property and increase the acid sites over the catalyst surfaces.The result of in situ DRIFTS suggests that the microwave irradiation treatment generates more Br?nsted acid sites on CeO2-TiO2-2 h catalyst,helpful in SCR reactions.XPS results show that after microwave irradiation on the CeO2-TiO2 catalysts,the surface demonstrates an elevated concentration of chemisorbed oxygen,consequently leading to better oxidation of NO to NO2.Additionally,the molar ratio of Ce3+/Ce4+has been elevated after being treated by microwave irradiation,a vital factor in enhancing the NH3-SCR activities.展开更多
A series of praseodymium added CeO2（ZrO2）/TiO2 catalysts separately prepared by methods of sol-gel and impregnation were tested for selective catalytic reduction of NO, and characterized by X-ray diffraction （XRD）...A series of praseodymium added CeO2（ZrO2）/TiO2 catalysts separately prepared by methods of sol-gel and impregnation were tested for selective catalytic reduction of NO, and characterized by X-ray diffraction （XRD）, N2-brumauer-emmett-teller （N2-BET）, NH3-temperature programmed desorption （NH3-TPD）, H2-temperature programmed reduction （H2-TPR）, PL spectra, Ra-man spectra, electron paramagnetic resonance （EPR） and X-ray photoelectron spectroscopy （XPS）, respectively. Influence of prepara-tion method on catalytic performance was studied. Results showed that the influence of Pr addition on catalytic performance of the CeO2（ZrO2）/TiO2 catalysts was different between the sol-gel method and the impregnation method. The Pr addition tended to interact with TiO2 and formed the structure of Ti-O-Pr in the sol-gel method while it was more likely to interact with CeO2 forming the struc-ture of Ce-O-Pr in the impregnation method. The total acid amount and redox properties of the catalysts prepared by sol-gel method decreased with the addition of Pr element, which resulted in decrease of catalytic activity. In contrast, the Pr-added catalyst prepared by impregnation method was found to possess easier reducibility, more total acid amount and higher proportion of Ce3＋ species, which was favourable for higher catalytic activity.展开更多
A novel catalyst,TiO2 nanotubes(TiO2 NTs)composite decorated by CuO and CeO2 particles,was prepared by a simple and cost-effective method.The TiO2 NTs were fabricated by the hydrothermal method,and CuO and CeO2 partic...A novel catalyst,TiO2 nanotubes(TiO2 NTs)composite decorated by CuO and CeO2 particles,was prepared by a simple and cost-effective method.The TiO2 NTs were fabricated by the hydrothermal method,and CuO and CeO2 particles loaded onto TiO2 NTs(CuO/CeO2@TiO2 NTs)were prepared by the water bath heating method.The CuO/CeO2@TiO2 NTs were investigated and characterized by transmission electron microscope(TEM),energy dispersive spectrometer(EDS),photoluminescence(PL),X-ray diffractometer(XRD)and ultraviolet-visible light diffuse reflectance spectrum(UV-Vis DRS).Both the p-n heterojunction formed at the p-CuO and n-TiO2 interfaces and the highly induced electron transfer of CeO2 can greatly promote the separation of electrons-holes.Therefore,CuO/CeO2@TiO2 NTs show enhanced absorption and have potential applications in photocatalysis.展开更多
采用CeO2-TiO2复合物薄膜作为聚苯胺电致变色器件的对电极,选用聚合物固态电解质(PE:PMMA-PC-EC-L iC lO4),构筑了新型双层结构(Dual-type)聚苯胺(PANI)固态电致变色(EC)器件.用电化学现场紫外-可见光谱法表征了该EC器件(ITO|PANI||PE||...采用CeO2-TiO2复合物薄膜作为聚苯胺电致变色器件的对电极,选用聚合物固态电解质(PE:PMMA-PC-EC-L iC lO4),构筑了新型双层结构(Dual-type)聚苯胺(PANI)固态电致变色(EC)器件.用电化学现场紫外-可见光谱法表征了该EC器件(ITO|PANI||PE||CeO2-TiO2|ITO)的电致变色性能,并与单层结构(S ingle-type)EC器件(ITO|PANI||PE||ITO)进行了比较.研究结果表明,双层结构EC器件比单层结构EC器件的电致变色性能好,如响应速度快,循环寿命长.同时,考察了电解质组分对聚苯胺电致变色稳定性的影响.EC器件(ITO|PANI||PE||CeO2-TiO2|ITO)的颜色呈现由透明的黄色(-1.5 V,PANIvs.CeO2-TiO2)到蓝色(1.0 V)的可逆变化,在700 nm处的透射率由42.19%变到13.35%,经过150个循环,其透射率差仍保持不变,着色效率为152.1 cm2/C.展开更多
基金Project supported by the National Natural Science Foundation of China(21577005)the National Key Research and Development Program of China(2016YFB0600400)
文摘In this work we prepared several CeO2-TiO2 catalysts for the NH3-SCR reactionusing co-precipitation with assistance of microwave irradiation.The catalytic NH3-SCR activities over CeO2-TiO2 catalysts at low temperatures are largely enhanced by the treatment of microwave irradiation,the operation temperature window is also broadened.For better understanding the promotion mechanism,the catalyst prepared by conventional co-precipitation with and without microwave irradiation treatment was characterized with H2-TPR,NH3-TPD,XPS,XRD and BET.Microwave irradiation treatment accelerates the crystallite rate of CeO2-TiO2 catalysts,and greatly enlarges their surface area by adjusting their microstructures.The resistance to SO2 and H2O is also improved via regulating the hierarchical pore structure by the microwave irradiation.Microwave irradiation treatment can also improve the redox property and increase the acid sites over the catalyst surfaces.The result of in situ DRIFTS suggests that the microwave irradiation treatment generates more Br?nsted acid sites on CeO2-TiO2-2 h catalyst,helpful in SCR reactions.XPS results show that after microwave irradiation on the CeO2-TiO2 catalysts,the surface demonstrates an elevated concentration of chemisorbed oxygen,consequently leading to better oxidation of NO to NO2.Additionally,the molar ratio of Ce3+/Ce4+has been elevated after being treated by microwave irradiation,a vital factor in enhancing the NH3-SCR activities.
基金supported by National Key Research and Development Program of China(2016YFC0205500)National Natural Science Foundation of China(51272105)+1 种基金Jiangsu Provincial Science and Technology Supporting Program(BE2013718)the Priority Academic Program Development of Jiangsu Higher Education Institutions(PAPD)
文摘A series of praseodymium added CeO2（ZrO2）/TiO2 catalysts separately prepared by methods of sol-gel and impregnation were tested for selective catalytic reduction of NO, and characterized by X-ray diffraction （XRD）, N2-brumauer-emmett-teller （N2-BET）, NH3-temperature programmed desorption （NH3-TPD）, H2-temperature programmed reduction （H2-TPR）, PL spectra, Ra-man spectra, electron paramagnetic resonance （EPR） and X-ray photoelectron spectroscopy （XPS）, respectively. Influence of prepara-tion method on catalytic performance was studied. Results showed that the influence of Pr addition on catalytic performance of the CeO2（ZrO2）/TiO2 catalysts was different between the sol-gel method and the impregnation method. The Pr addition tended to interact with TiO2 and formed the structure of Ti-O-Pr in the sol-gel method while it was more likely to interact with CeO2 forming the struc-ture of Ce-O-Pr in the impregnation method. The total acid amount and redox properties of the catalysts prepared by sol-gel method decreased with the addition of Pr element, which resulted in decrease of catalytic activity. In contrast, the Pr-added catalyst prepared by impregnation method was found to possess easier reducibility, more total acid amount and higher proportion of Ce3＋ species, which was favourable for higher catalytic activity.
基金National Natural Science Foundation of China(No.11372205)
文摘A novel catalyst,TiO2 nanotubes(TiO2 NTs)composite decorated by CuO and CeO2 particles,was prepared by a simple and cost-effective method.The TiO2 NTs were fabricated by the hydrothermal method,and CuO and CeO2 particles loaded onto TiO2 NTs(CuO/CeO2@TiO2 NTs)were prepared by the water bath heating method.The CuO/CeO2@TiO2 NTs were investigated and characterized by transmission electron microscope(TEM),energy dispersive spectrometer(EDS),photoluminescence(PL),X-ray diffractometer(XRD)and ultraviolet-visible light diffuse reflectance spectrum(UV-Vis DRS).Both the p-n heterojunction formed at the p-CuO and n-TiO2 interfaces and the highly induced electron transfer of CeO2 can greatly promote the separation of electrons-holes.Therefore,CuO/CeO2@TiO2 NTs show enhanced absorption and have potential applications in photocatalysis.