A series of Ce, H3PW12O40 co-doped TiO2 hollow fibers photocatalysts have been prepared by sol-gel method using ammonium ceric nitrate, H3PW12O40 and tetrabutyltitanate as precursors and cotton fibers as template, fol...A series of Ce, H3PW12O40 co-doped TiO2 hollow fibers photocatalysts have been prepared by sol-gel method using ammonium ceric nitrate, H3PW12O40 and tetrabutyltitanate as precursors and cotton fibers as template, followed by calcination at 500 ℃ in N2 atmosphere for 2 h. Scanning electron microscopy, X-ray diffraction, nitrogen adsorption-desorption mea- surements, and UV-Vis spectroscopy are employed to characterize the morphology, crystal structure, surface structure, and optical absorption properties of the samples. The photo- catalytic performance of the samples has been studied by photodegradation phenol in water under UV and visible light irradiation. The results show that the TiO2 fiber materials have hollow structures, and the co-doped TiO2 hollow fibers exhibit higher photocatalytic activities for the degradation of phenol than un-doped, single-doped TiO2 hollow fibers under UV and visible light. In addition, the recyclability of co-doped TiO2 fibers is also confirmed that the TiO2 fiber retains ca. 90% of its activity after being used four times. It is shown that the co-doped TiO2 fibers can be activated by visible light and may be potentially applied to the treatment of water contaminated by organic pollutants. The synergistic effect of Ce and H3PW12O40 co-doping plays an important role in improving the photocatalytic activity.展开更多
TiO2 powder and TiO2 thin film on the surface of glazed ceramic tile were prepared by sol-gel method.The influences of different doping Cr3+ concentration on the photocatalytic activity of TiO2 were discussed, UV-visi...TiO2 powder and TiO2 thin film on the surface of glazed ceramic tile were prepared by sol-gel method.The influences of different doping Cr3+ concentration on the photocatalytic activity of TiO2 were discussed, UV-visible and X-ray diffraction analysis were used to test the performance of TiO2 powder and film. The results indicate that photocatalytic activity of doping Cr3+-TiO2 thin film is higher than that of powder, and the interaction between Cr3+-doped and substrate can greatly enhance the photocatalytic activity. The results of X-ray diffraction and photoabsorption show that the Cr3+ -doped energy level in TiO2 is 0. 62 eV high from the top of valence band, which belongs to the type of deep energy level doping. On the basis of the semiconductor energy level theory and Cr3+ dopant energy level, the semiconductor energy level model of Cr3+ in TiO2 powder and thin film were established, and the doping mechanisms of Cr3+-doped in TiO2 powder and thin film were analyzed.展开更多
In this work, the effectiveness of V2O5-WO3/TiO2 catalysts modified with different CeO2 contents by impregnation and co-precipitation methods on the selective catalytic reduction of NOxby NH3 have been studied compara...In this work, the effectiveness of V2O5-WO3/TiO2 catalysts modified with different CeO2 contents by impregnation and co-precipitation methods on the selective catalytic reduction of NOxby NH3 have been studied comparatively by various experimental techniques. The results showed that the NO conversion of V2O5-WO3/CeO2-TiO2 catalysts modified by co-precipitation method obviously increased with the Ce doping contents in the studied range below 20%（All Ce contents are in mass fractions）, but the NO conversion of V2O5-WO3/CeO2/TiO2 catalysts modified by impregnation methods was lower than V2O5-WO3/CeO2-TiO2 catalysts especially beyond 2.5% Ce doping contents. The V2O5-WO3/CeO2-TiO2 catalysts showed better SCR activity, wider reaction window, and higher sulfur and water resistance. The characterization results elucidated that the modified catalysts by co-precipitation method exhibited higher specific surface area, much better dispersity of Ce component, more Ce^（3＋）species and more Br？nsted acid sites than that by impregnation. The vacancies caused by more Ce^（3＋）species were favorable for more NO oxidation to NO2, and the interaction between Ce species and WOxspecies generated more Br？nsted acid sites. It could be supposed that dispersed Ce Oxspecies and WOxspecies offered more second active centers respectively to adsorb oxygen and activate ammonia as co-catalysis to the primary active center of V ions, thus facilitated the better SCR activity of modified V2O5-WO3/CeO2-TiO2 catalysts by coprecipitation methods. The co-precipitation methods with Ce component were more suitable for production of modified commercial V2O5-WO3/TiO2 catalysts.展开更多
Ti3＋-doped TiO2 nanosheets with tunable phase composition （doped TiO2 （A/R）） were synthesized via a hydrothermal method with high surface area anatase TiO2 nanosheets TiO2 （A） as a substrate, structure directin...Ti3＋-doped TiO2 nanosheets with tunable phase composition （doped TiO2 （A/R）） were synthesized via a hydrothermal method with high surface area anatase TiO2 nanosheets TiO2 （A） as a substrate, structure directing agent, and inhibitor; the activity was evaluated using a probe reaction-photocatalytic CO2 conversion to methane under visible light irradiation with H2 as an electron donor and hydrogen source. High-resolution transmission electron microscope （HRTEM）, field emission scanning electron microscope, UV-Vis diffuse reflectance spectra, and X-ray diffraction （XRD） etc., were used to characterize the photocatalysts. XRD and HRTEM measurements confirmed the existence of anatase-rutile phase junction, while Ti3-and single-electron-trapped oxygen vacancy in the doped TiO2 （A/R） photocatalyst were revealed byelectron paramagnetic resonance （EPR） measurements. Effects of hydrothermal synthesis temperature and the amount of added anatase TiO2 on the photocatalytic activity were elucidated. Significantly enhanced photo- catalytic activity of doped TiO2 （A/R） was observed; under the optimized synthesis conditions, CH4 generation rate of doped TiO2 （A/R） was 2.3 times that of Ti3＋-doped rutile TiO2.展开更多
La-doped TiO_2 thin films on titanium substrates were prepared by the sol–gel method with titanium tetrachloride as a precursor and La_2O_3 as a source of lanthanum. The heat-treatment temperature dependence of the p...La-doped TiO_2 thin films on titanium substrates were prepared by the sol–gel method with titanium tetrachloride as a precursor and La_2O_3 as a source of lanthanum. The heat-treatment temperature dependence of the photoelectrochemical performance of the La-doped TiO_2 film in 0.2 mol/L Na_2SO_4 was investigated by the MottSchottky equation, electrochemical impedance spectroscopy, and the open-circuit potential test. The results from the Mott-Schottky curves show that the obtained films all were n-type semiconductors, and the film at 300 °C had the highest conduction band position and the widest space charge layer. The electrochemical impendence spectroscopy（EIS） tests of the 300 °C film decreased most during the change from illuminated to dark. The potential of the La–TiO_2 thin film electrode was the lowest after the 300 °C heat treatment. The open-circuit potential indicated that the photoelectrical performance of the La-TiO_2 films was enhanced with the addition of the La element and the largest decline（837.8 mV） in the electrode potential was achieved with the 300 °C heat treatment.展开更多
基金ACKNOWLEDGMENTS This work was supported by the National Natural Science Foundation of China （No.41373127） and Liaon- ing Provincial Natural Science Foundation of China （No.2013020121）.
文摘A series of Ce, H3PW12O40 co-doped TiO2 hollow fibers photocatalysts have been prepared by sol-gel method using ammonium ceric nitrate, H3PW12O40 and tetrabutyltitanate as precursors and cotton fibers as template, followed by calcination at 500 ℃ in N2 atmosphere for 2 h. Scanning electron microscopy, X-ray diffraction, nitrogen adsorption-desorption mea- surements, and UV-Vis spectroscopy are employed to characterize the morphology, crystal structure, surface structure, and optical absorption properties of the samples. The photo- catalytic performance of the samples has been studied by photodegradation phenol in water under UV and visible light irradiation. The results show that the TiO2 fiber materials have hollow structures, and the co-doped TiO2 hollow fibers exhibit higher photocatalytic activities for the degradation of phenol than un-doped, single-doped TiO2 hollow fibers under UV and visible light. In addition, the recyclability of co-doped TiO2 fibers is also confirmed that the TiO2 fiber retains ca. 90% of its activity after being used four times. It is shown that the co-doped TiO2 fibers can be activated by visible light and may be potentially applied to the treatment of water contaminated by organic pollutants. The synergistic effect of Ce and H3PW12O40 co-doping plays an important role in improving the photocatalytic activity.
基金Project (20466001) supported by the National Natural Science Foundation of China
文摘TiO2 powder and TiO2 thin film on the surface of glazed ceramic tile were prepared by sol-gel method.The influences of different doping Cr3+ concentration on the photocatalytic activity of TiO2 were discussed, UV-visible and X-ray diffraction analysis were used to test the performance of TiO2 powder and film. The results indicate that photocatalytic activity of doping Cr3+-TiO2 thin film is higher than that of powder, and the interaction between Cr3+-doped and substrate can greatly enhance the photocatalytic activity. The results of X-ray diffraction and photoabsorption show that the Cr3+ -doped energy level in TiO2 is 0. 62 eV high from the top of valence band, which belongs to the type of deep energy level doping. On the basis of the semiconductor energy level theory and Cr3+ dopant energy level, the semiconductor energy level model of Cr3+ in TiO2 powder and thin film were established, and the doping mechanisms of Cr3+-doped in TiO2 powder and thin film were analyzed.
基金Project supported by the Guangxi Natural Science Foundation(2014GXNSFAA118057)Guangxi Science and Technology Planning Project(AB16380276)
文摘In this work, the effectiveness of V2O5-WO3/TiO2 catalysts modified with different CeO2 contents by impregnation and co-precipitation methods on the selective catalytic reduction of NOxby NH3 have been studied comparatively by various experimental techniques. The results showed that the NO conversion of V2O5-WO3/CeO2-TiO2 catalysts modified by co-precipitation method obviously increased with the Ce doping contents in the studied range below 20%（All Ce contents are in mass fractions）, but the NO conversion of V2O5-WO3/CeO2/TiO2 catalysts modified by impregnation methods was lower than V2O5-WO3/CeO2-TiO2 catalysts especially beyond 2.5% Ce doping contents. The V2O5-WO3/CeO2-TiO2 catalysts showed better SCR activity, wider reaction window, and higher sulfur and water resistance. The characterization results elucidated that the modified catalysts by co-precipitation method exhibited higher specific surface area, much better dispersity of Ce component, more Ce^（3＋）species and more Br？nsted acid sites than that by impregnation. The vacancies caused by more Ce^（3＋）species were favorable for more NO oxidation to NO2, and the interaction between Ce species and WOxspecies generated more Br？nsted acid sites. It could be supposed that dispersed Ce Oxspecies and WOxspecies offered more second active centers respectively to adsorb oxygen and activate ammonia as co-catalysis to the primary active center of V ions, thus facilitated the better SCR activity of modified V2O5-WO3/CeO2-TiO2 catalysts by coprecipitation methods. The co-precipitation methods with Ce component were more suitable for production of modified commercial V2O5-WO3/TiO2 catalysts.
文摘Ti3＋-doped TiO2 nanosheets with tunable phase composition （doped TiO2 （A/R）） were synthesized via a hydrothermal method with high surface area anatase TiO2 nanosheets TiO2 （A） as a substrate, structure directing agent, and inhibitor; the activity was evaluated using a probe reaction-photocatalytic CO2 conversion to methane under visible light irradiation with H2 as an electron donor and hydrogen source. High-resolution transmission electron microscope （HRTEM）, field emission scanning electron microscope, UV-Vis diffuse reflectance spectra, and X-ray diffraction （XRD） etc., were used to characterize the photocatalysts. XRD and HRTEM measurements confirmed the existence of anatase-rutile phase junction, while Ti3-and single-electron-trapped oxygen vacancy in the doped TiO2 （A/R） photocatalyst were revealed byelectron paramagnetic resonance （EPR） measurements. Effects of hydrothermal synthesis temperature and the amount of added anatase TiO2 on the photocatalytic activity were elucidated. Significantly enhanced photo- catalytic activity of doped TiO2 （A/R） was observed; under the optimized synthesis conditions, CH4 generation rate of doped TiO2 （A/R） was 2.3 times that of Ti3＋-doped rutile TiO2.
基金supported by the Education Department of Sichuan Province(No.14ZB0025)
文摘La-doped TiO_2 thin films on titanium substrates were prepared by the sol–gel method with titanium tetrachloride as a precursor and La_2O_3 as a source of lanthanum. The heat-treatment temperature dependence of the photoelectrochemical performance of the La-doped TiO_2 film in 0.2 mol/L Na_2SO_4 was investigated by the MottSchottky equation, electrochemical impedance spectroscopy, and the open-circuit potential test. The results from the Mott-Schottky curves show that the obtained films all were n-type semiconductors, and the film at 300 °C had the highest conduction band position and the widest space charge layer. The electrochemical impendence spectroscopy（EIS） tests of the 300 °C film decreased most during the change from illuminated to dark. The potential of the La–TiO_2 thin film electrode was the lowest after the 300 °C heat treatment. The open-circuit potential indicated that the photoelectrical performance of the La-TiO_2 films was enhanced with the addition of the La element and the largest decline（837.8 mV） in the electrode potential was achieved with the 300 °C heat treatment.