In this paper,a Sr^2+and Dy^3+co-doped γ-Ce2S3 red pigment was synthesized via a combination of coprecipitation and sulfurization processes.Mixed oxide was prepared by presintering the coprecipitates,(Ce,Sr,Dy)CO3,fo...In this paper,a Sr^2+and Dy^3+co-doped γ-Ce2S3 red pigment was synthesized via a combination of coprecipitation and sulfurization processes.Mixed oxide was prepared by presintering the coprecipitates,(Ce,Sr,Dy)CO3,followed by high-temperature sulfurization under a CS2 atmosphere.The effects of the sulfurization temperature,time,and doped proportion on the phase composition,color performance and temperature stability of γ-Ce2S3 were systematically studied.The results show that a stable γ-Ce2S3 red pigment can be obtained through Sr^2+and Dy^3+co-doping at 730℃ for 200 min.The diffraction peaks of all the samples shift to higher 2θ values with increasing doping proportion,indicating that part of the Dy^3+species enter the lattice and form a solid solution.The band gap of the samples remains practically constant at 2.01-2.04 eV,which causes their red color.The best red-color quality(L*=37.13,a*=34.77,b*=29.44) is achieved when the pigment has a Dy^3+/Ce^3+molar ratio of 0.15,and the material maintains its excellent red color(L*=31.49 a*=30.94 b*=25.33) after being heated at 410℃ for 30 min.展开更多
SiO2 coated Ce2S3 red pigment was prepared in ethanol/H2O system via sol-gel method and TEOS were used as silica sources. X-ray diffraction （XRD）, scanning electron microscopy （SEM）, energy dispersive spectroscopy...SiO2 coated Ce2S3 red pigment was prepared in ethanol/H2O system via sol-gel method and TEOS were used as silica sources. X-ray diffraction （XRD）, scanning electron microscopy （SEM）, energy dispersive spectroscopy （EDX）, UV-visible spectro-photometer and automatic colorimeter were used to investigate the properties of the samples. The results showed that the compact SiO2 film formed on the surface of Ce2S3 pigment at a cerium silicon molar ratio of 2. The thermal stability temperature of Ce2S3 pigment was improved to 450 oC after SiO2 coating. In addition, the color of Ce2S3 pigment was not affected significantly through coating colorless and transparent SiO2 and it could be used as safe red pigment in higher temperature fields.展开更多
Ceria spheres with different sizes and sulfurized products with corresponding morphology were prepared by hydro-thermal and gas-solid reaction method at 600-800℃ under CS2 atmosphere for a short time, respectively. D...Ceria spheres with different sizes and sulfurized products with corresponding morphology were prepared by hydro-thermal and gas-solid reaction method at 600-800℃ under CS2 atmosphere for a short time, respectively. Dimensional effect in preparation ofγ-Ce2S3 was firstly investigated by means of techniques such as scanning electron microscopy （SEM）, X-ray dif-fraction （XRD）, thermal gravimetric analysis （TGA） and spectrophotometer. The results showed that when ceria nanoparticles with small size were used as precursors, theγ-Ce2S3 could be prepared at the lower temperature and the badly sintered products were obtained; when ceria nanoparticles with large size were employed as precursors, pureγ-Ce2S3 was difficultly obtained even if the temperature was up to 800℃ and the products tended to keep their original size. The heat-resistance property of theγ-Ce2S3 with large size was better than the smaller one, and the pureγ-Ce2S3 prepared from precursor with small size had a good pigmen-tary performance.展开更多
A series of cerium sulfides were successfully prepared using commercially available nanoscale CeO_2 as precursor, anhydrous Na_2CO_3 as dopants, CS_2 as sulfur source, under 600–800 oC, respectively. Properties of sa...A series of cerium sulfides were successfully prepared using commercially available nanoscale CeO_2 as precursor, anhydrous Na_2CO_3 as dopants, CS_2 as sulfur source, under 600–800 oC, respectively. Properties of samples were investigated by means of X-ray diffraction（XRD）, scanning electron microscopy（SEM） and spectrophotometry. The results showed that corresponding γ-Ce_2S_3 with small size was obtained by using nanoscale CeO_2 as precursor; pure phase γ-Ce_2S_3 could be obtained under low temperature of 700 oC. Coloring properties of γ-Ce_2S_3 obtained under 800 oC were studied by researching γ-Ce_2S_3/PE and γ-Ce_2S_3/PVC composites, respectively. The results showed that satisfied coloring effects to PE and PVC were obtained by using 0.5 phr and 0.2 phr γ-Ce_2S_3, respectively.展开更多
The as-sintered sinter skin and the polished section of WC-11Co-0.4Cr 3 C 2-0.3VC-0.2RE（RE=mischmetal with La/Ce ratio of 0.65） alloy were analyzed.It was shown that the microstructures on the skin and in the inner ...The as-sintered sinter skin and the polished section of WC-11Co-0.4Cr 3 C 2-0.3VC-0.2RE（RE=mischmetal with La/Ce ratio of 0.65） alloy were analyzed.It was shown that the microstructures on the skin and in the inner part of the alloy were all characterized with a WC＋β＋M structure,where β was a cobalt-based binder phase and M represented a RE-containing phase.There existed an inward diffusion of S atoms,which caught and fixed the Ce atoms in the alloy and an outward diffusion of La atoms during the sintering process.Consequently,the M phase was characterized with the decreased La/Ce ratio（0.59） in the inner part and the increased La/Ce ratio（1.01） on the skin.The M phase on the skin was characterized with a γ-Ce 2 S 3 type structure.To suppress the long range migration of rare earth to the skin,S in the sintering atmosphere had to be eliminated.展开更多
基金supported by the National Natural Science Foundation of China(51462010)the Natural Science Foundation of Jiangxi Province(20161BAB206132,20171ACB20022)the Science and technology program Foundation of Jingdezhen(2017GYZD019-012).
文摘In this paper,a Sr^2+and Dy^3+co-doped γ-Ce2S3 red pigment was synthesized via a combination of coprecipitation and sulfurization processes.Mixed oxide was prepared by presintering the coprecipitates,(Ce,Sr,Dy)CO3,followed by high-temperature sulfurization under a CS2 atmosphere.The effects of the sulfurization temperature,time,and doped proportion on the phase composition,color performance and temperature stability of γ-Ce2S3 were systematically studied.The results show that a stable γ-Ce2S3 red pigment can be obtained through Sr^2+and Dy^3+co-doping at 730℃ for 200 min.The diffraction peaks of all the samples shift to higher 2θ values with increasing doping proportion,indicating that part of the Dy^3+species enter the lattice and form a solid solution.The band gap of the samples remains practically constant at 2.01-2.04 eV,which causes their red color.The best red-color quality(L*=37.13,a*=34.77,b*=29.44) is achieved when the pigment has a Dy^3+/Ce^3+molar ratio of 0.15,and the material maintains its excellent red color(L*=31.49 a*=30.94 b*=25.33) after being heated at 410℃ for 30 min.
基金Project supported by National Science and Technology Support Program(2011BAE30B03)Special Fund from Shaanxi Provincial Department of Education(12JK0467the Graduate Innovation Fund of Shaanxi Universityof Science and Technology for the financial support
文摘SiO2 coated Ce2S3 red pigment was prepared in ethanol/H2O system via sol-gel method and TEOS were used as silica sources. X-ray diffraction （XRD）, scanning electron microscopy （SEM）, energy dispersive spectroscopy （EDX）, UV-visible spectro-photometer and automatic colorimeter were used to investigate the properties of the samples. The results showed that the compact SiO2 film formed on the surface of Ce2S3 pigment at a cerium silicon molar ratio of 2. The thermal stability temperature of Ce2S3 pigment was improved to 450 oC after SiO2 coating. In addition, the color of Ce2S3 pigment was not affected significantly through coating colorless and transparent SiO2 and it could be used as safe red pigment in higher temperature fields.
基金Project supported by the National Natural Science Foundation of China(20961006)Inner Mongolia Natural Science Foundation(20080404MS0201)Inner Mongolia Technology Innovation and Guidance Funds
文摘Ceria spheres with different sizes and sulfurized products with corresponding morphology were prepared by hydro-thermal and gas-solid reaction method at 600-800℃ under CS2 atmosphere for a short time, respectively. Dimensional effect in preparation ofγ-Ce2S3 was firstly investigated by means of techniques such as scanning electron microscopy （SEM）, X-ray dif-fraction （XRD）, thermal gravimetric analysis （TGA） and spectrophotometer. The results showed that when ceria nanoparticles with small size were used as precursors, theγ-Ce2S3 could be prepared at the lower temperature and the badly sintered products were obtained; when ceria nanoparticles with large size were employed as precursors, pureγ-Ce2S3 was difficultly obtained even if the temperature was up to 800℃ and the products tended to keep their original size. The heat-resistance property of theγ-Ce2S3 with large size was better than the smaller one, and the pureγ-Ce2S3 prepared from precursor with small size had a good pigmen-tary performance.
基金supported by the National Natural Science Foundation of China(21661024)the Open Funds of the State Key Laboratory of Rare Earth Resource Utilization(RERU2017009)Inner Mongolia Scientific Research Projects(NJZZ14003)
文摘A series of cerium sulfides were successfully prepared using commercially available nanoscale CeO_2 as precursor, anhydrous Na_2CO_3 as dopants, CS_2 as sulfur source, under 600–800 oC, respectively. Properties of samples were investigated by means of X-ray diffraction（XRD）, scanning electron microscopy（SEM） and spectrophotometry. The results showed that corresponding γ-Ce_2S_3 with small size was obtained by using nanoscale CeO_2 as precursor; pure phase γ-Ce_2S_3 could be obtained under low temperature of 700 oC. Coloring properties of γ-Ce_2S_3 obtained under 800 oC were studied by researching γ-Ce_2S_3/PE and γ-Ce_2S_3/PVC composites, respectively. The results showed that satisfied coloring effects to PE and PVC were obtained by using 0.5 phr and 0.2 phr γ-Ce_2S_3, respectively.
基金supported by National Natural Science Foundation of China (51074189,50823006)Science and Technology Planning Project Founda-tion of Hunan Province,China (2010FJ2006)+1 种基金Research Foundation for the Doctoral Program of Higher Education of China (20100162110001)the National Science & Technology Special Foundation of China (2011BAE09B02,2012ZX04003021)
文摘The as-sintered sinter skin and the polished section of WC-11Co-0.4Cr 3 C 2-0.3VC-0.2RE（RE=mischmetal with La/Ce ratio of 0.65） alloy were analyzed.It was shown that the microstructures on the skin and in the inner part of the alloy were all characterized with a WC＋β＋M structure,where β was a cobalt-based binder phase and M represented a RE-containing phase.There existed an inward diffusion of S atoms,which caught and fixed the Ce atoms in the alloy and an outward diffusion of La atoms during the sintering process.Consequently,the M phase was characterized with the decreased La/Ce ratio（0.59） in the inner part and the increased La/Ce ratio（1.01） on the skin.The M phase on the skin was characterized with a γ-Ce 2 S 3 type structure.To suppress the long range migration of rare earth to the skin,S in the sintering atmosphere had to be eliminated.