Pd/Ce0.67Zr0.33O2 catalyst was pretreated in different atmosphere respectively, and characterized by CO chemical adsorption, XPS, HR-TEM, H2-TPR, Raman, OSC and in situ DRIFTS to investigate the effect of the structur...Pd/Ce0.67Zr0.33O2 catalyst was pretreated in different atmosphere respectively, and characterized by CO chemical adsorption, XPS, HR-TEM, H2-TPR, Raman, OSC and in situ DRIFTS to investigate the effect of the structure properties of PdOx species on the catalytic performance for CO, HC and NOx elimination. The results show that Pd/CZ catalyst pretreated in air atmosphere has higher oxidation activity of HC due to having high Pd dispersion and strong interaction between PdOx and CZ support. Pd/CZ-H catalyst pretreated in reducing atmosphere exhibits better catalytic performance of NOx elimination because of having relatively big Pd particle size, more Pd species in metallic state and higher concentration of oxygen vacancies. While for the Pd/CZ-RG catalyst pretreated in reactant atmosphere, strong adsorption of HC species on the surface of catalysts would lead to a part of active sites being covered, which inhibits HC and NO conversions.展开更多
Ce0.65Zr0.35O2 solid solution was prepared by co-precipitation method and characterized by X-ray diffraction (XRD), Raman spectra, BET, oxygen storage capacity (OSC) and temperature-programmed reduction measurements (...Ce0.65Zr0.35O2 solid solution was prepared by co-precipitation method and characterized by X-ray diffraction (XRD), Raman spectra, BET, oxygen storage capacity (OSC) and temperature-programmed reduction measurements (H2-TPR) after calcination at 100 ℃, 300 ℃, 600 ℃, and 1 000 ℃. The results showed that the precipitation was a crystalline of fluorite structure, and in the process of the precipitation transformation into Ce0.65Zr0.35O2 solid solution, the fluorite structure of the precipitation kept unchanged. The samples had different BET surface areas and OSC at different temperatures, but they held the performance of stable structure. After 1 000 ℃, there didn′t appear the other crystalline phase. So the samples prepared by co-precipitation method had excellent texture and higher thermal stability.展开更多
Monolithic catalysts of Pt/La-Al2O3 and Pt/Ce0.67Zr0.3302 were prepared to investigate methane selective catalytic reduction （SCR） of NO. The results indicate that Pt/Ce0.67Zr0.33O2 shows high activity and both NO a...Monolithic catalysts of Pt/La-Al2O3 and Pt/Ce0.67Zr0.3302 were prepared to investigate methane selective catalytic reduction （SCR） of NO. The results indicate that Pt/Ce0.67Zr0.33O2 shows high activity and both NO and CH4 can be converted completely at 450℃. Meanwhile, NO and CH4 can be converted completely when there exists excess oxygen. The Pt/Ce0.67Zr0.33O2 catalyst were further investigated by using methane as reducing agent to SCR NO in a novel equipment which combined the CH4 selective catalytic reduction of NO with methane combustion. The result shows that the catalyst is high active and the novel equipment is very effective. The conversion of NO is above 92% under the conditions used in this work. The prepared burner and catalysts have great potential for application.展开更多
基金Project supported by the Key Program of Science Technology Department of Zhejiang Province(2018C03037)
文摘Pd/Ce0.67Zr0.33O2 catalyst was pretreated in different atmosphere respectively, and characterized by CO chemical adsorption, XPS, HR-TEM, H2-TPR, Raman, OSC and in situ DRIFTS to investigate the effect of the structure properties of PdOx species on the catalytic performance for CO, HC and NOx elimination. The results show that Pd/CZ catalyst pretreated in air atmosphere has higher oxidation activity of HC due to having high Pd dispersion and strong interaction between PdOx and CZ support. Pd/CZ-H catalyst pretreated in reducing atmosphere exhibits better catalytic performance of NOx elimination because of having relatively big Pd particle size, more Pd species in metallic state and higher concentration of oxygen vacancies. While for the Pd/CZ-RG catalyst pretreated in reactant atmosphere, strong adsorption of HC species on the surface of catalysts would lead to a part of active sites being covered, which inhibits HC and NO conversions.
文摘Ce0.65Zr0.35O2 solid solution was prepared by co-precipitation method and characterized by X-ray diffraction (XRD), Raman spectra, BET, oxygen storage capacity (OSC) and temperature-programmed reduction measurements (H2-TPR) after calcination at 100 ℃, 300 ℃, 600 ℃, and 1 000 ℃. The results showed that the precipitation was a crystalline of fluorite structure, and in the process of the precipitation transformation into Ce0.65Zr0.35O2 solid solution, the fluorite structure of the precipitation kept unchanged. The samples had different BET surface areas and OSC at different temperatures, but they held the performance of stable structure. After 1 000 ℃, there didn′t appear the other crystalline phase. So the samples prepared by co-precipitation method had excellent texture and higher thermal stability.
基金Supported by the National High Technology Research and Development Program of China (863 Program, 2006AA06Z347)the NationalNatural Science Foundation of China (20773090).
文摘Monolithic catalysts of Pt/La-Al2O3 and Pt/Ce0.67Zr0.3302 were prepared to investigate methane selective catalytic reduction （SCR） of NO. The results indicate that Pt/Ce0.67Zr0.33O2 shows high activity and both NO and CH4 can be converted completely at 450℃. Meanwhile, NO and CH4 can be converted completely when there exists excess oxygen. The Pt/Ce0.67Zr0.33O2 catalyst were further investigated by using methane as reducing agent to SCR NO in a novel equipment which combined the CH4 selective catalytic reduction of NO with methane combustion. The result shows that the catalyst is high active and the novel equipment is very effective. The conversion of NO is above 92% under the conditions used in this work. The prepared burner and catalysts have great potential for application.