Pure SnO2 and Ce-doped(1%,4%,7%,10% in mass ratio) SnO2 powders were prepared by a simple sol-gel method.The as-prepared samples were characterized by X-ray diffraction(XRD),scanning electron microscopy(SEM),and Bruna...Pure SnO2 and Ce-doped(1%,4%,7%,10% in mass ratio) SnO2 powders were prepared by a simple sol-gel method.The as-prepared samples were characterized by X-ray diffraction(XRD),scanning electron microscopy(SEM),and Brunauer-Emmett-Teller(BET) specific surface area analyzers.Results showed that the 7% Ce-doped sample has a particle size of 0.1-0.3 μm with a narrow particle size distribution while the pure SnO2 was consisted of large agglomerated particles with a diameter up to several micrometers.When used as the catalyst to degrade methyl orange(MO),the 7% Ce-doped sample showed best photocatalytic property.These properties can be attributed to the large surface area and small particle size of the 7% Ce-doped sample.展开更多
A series of Ce-doped MnOx/TiO2 catalysts were prepared by impregnation method and used for catalytic oxidation of NO in the presence of excess O2. The sample with the Ce doping concentration of Ce/Mn=l/3 and calcined ...A series of Ce-doped MnOx/TiO2 catalysts were prepared by impregnation method and used for catalytic oxidation of NO in the presence of excess O2. The sample with the Ce doping concentration of Ce/Mn=l/3 and calcined at 300 ℃ shows a superior activity for NO oxidation to NO2. On Ce（1）Mn（3）Ti catalyst, 58% NO conversion was obtained at 200 ℃ and 85% NO conversion at 250 ℃ with a GHSV of 41000 h-1, which was much higher than that over MnOx/TiO2 catalyst （48% at 250 ℃）. Characterization results implied that the higher activity of Ce（1）Mn（3）Ti could be attributed to the enrichment of well-dispersed MnO2 on the surface and the abundance of Mn3＋ and Zi3＋ species. The addition of Ce into MnO2/TiO2 could improve oxygen storage capacity and facilitate oxygen mobility of the catalyst as shown by PL and ESR, so that its activity for NO oxidation could be enhanced. The effect of H2O and SO2 on the catalyst activity was also investigated.展开更多
Ce-doped titanium oxide nanoparticles were investigated in the paper. The surface structures of undoped and Ce-doped TiO2 nanoparticles were observed by scanning tunneling microscopy （STM）. The experimental results ...Ce-doped titanium oxide nanoparticles were investigated in the paper. The surface structures of undoped and Ce-doped TiO2 nanoparticles were observed by scanning tunneling microscopy （STM）. The experimental results of scanning tunneling spectroscopy （STS） show that the surface electronic structures of TiO2 nanoparticles are modified by introducing new electronic states in the surface band gap through cerium ion doping. The results are discussed in terms of the influence of doping concentration on the surface band gap of TiO2.展开更多
Ce-doped Bi2O3 nanopowders were prepared by reverse titration chemical coprecipitation from Bi^3＋and Ce^（4＋）containing aqueous solution.Techniques of X-ray diffraction（XRD）,transmission electron microscopic（TEM...Ce-doped Bi2O3 nanopowders were prepared by reverse titration chemical coprecipitation from Bi^3＋and Ce^（4＋）containing aqueous solution.Techniques of X-ray diffraction（XRD）,transmission electron microscopic（TEM）and Fourier transform infrared spectroscopy（FTIR）were employed to characterize the as-synthesized materials.The XRD patterns indicated that the peaks can be easily indexed toβ-Bi2O3 and no diffraction peaks of Ce or other impurity phases were detected in the prepared samples.The calculated average crystalline size decreased from 31.72 to 11.96 nm when the Ce content increased from 1 wt%to 10 wt%.The morphology changed from flake-like into the spherical-like with increase in Ce content.The electric conductivity of Ce-doped Bi2O3 electrolyte was also investigated by two probe DC method.Conductivity analysis exhibited that the rate of conductivity increased with increasing Ce^2＋ratio,when the Ce concentration was up to 5 wt%,the as-synthesized Ce-doped Bi2O3 electrolyte showed the maximum value of conductivity（0.295 S？cm^（–1））.展开更多
以 Sn Cl4· Ti( OBu) 4、氨水、乙醇为原料 ,采用活性层包覆法 ,制备出 Ti O2 / Sn O2 复合光催化剂 ,并用IR、XRD、TEM和 BET等手段对样品进行了表征 .研究其对有机磷农药敌敌畏的光催化降解效果 ,与单一半导体催化剂 Sn O2 、Ti ...以 Sn Cl4· Ti( OBu) 4、氨水、乙醇为原料 ,采用活性层包覆法 ,制备出 Ti O2 / Sn O2 复合光催化剂 ,并用IR、XRD、TEM和 BET等手段对样品进行了表征 .研究其对有机磷农药敌敌畏的光催化降解效果 ,与单一半导体催化剂 Sn O2 、Ti O2 做了简单对比 .结果表明 :所制 Ti O2 / Sn O2 样品为包覆型结构 ,由锐钛矿型 Ti O2 金红石型 Sn O2 组成 ,与 Sn O2 及 Ti O2 晶体粉末相比所制 Ti O2 / Sn O2 包覆粒子光催化活性得到明显提高 .展开更多
利用直流电弧等离子体蒸发 -凝聚法制备 Sn O2 纳米粒子 ,研究了 Sn O2 粒子在等离子体焰流中的形成和生长机理 ,探讨了等离子体发生器功率、气体配比和冷却介质对 Sn O2 纳米粒子粒度和纯度的影响 ,制备出了纯度大于98.8%、粒度可控的 ...利用直流电弧等离子体蒸发 -凝聚法制备 Sn O2 纳米粒子 ,研究了 Sn O2 粒子在等离子体焰流中的形成和生长机理 ,探讨了等离子体发生器功率、气体配比和冷却介质对 Sn O2 纳米粒子粒度和纯度的影响 ,制备出了纯度大于98.8%、粒度可控的 Sn O2 纳米粉末 ,为制造高性能 Sn O2 气敏传感器打下了良好的基础。展开更多
基金Project supported by the National Natural Science Foundation of China (20871107)He'nan Outstanding Youth Science Fund (0612002700)the Natural Science Foundation of the Education Department of Henan Province (2009A150031)
文摘Pure SnO2 and Ce-doped(1%,4%,7%,10% in mass ratio) SnO2 powders were prepared by a simple sol-gel method.The as-prepared samples were characterized by X-ray diffraction(XRD),scanning electron microscopy(SEM),and Brunauer-Emmett-Teller(BET) specific surface area analyzers.Results showed that the 7% Ce-doped sample has a particle size of 0.1-0.3 μm with a narrow particle size distribution while the pure SnO2 was consisted of large agglomerated particles with a diameter up to several micrometers.When used as the catalyst to degrade methyl orange(MO),the 7% Ce-doped sample showed best photocatalytic property.These properties can be attributed to the large surface area and small particle size of the 7% Ce-doped sample.
基金supported by the National Natural Science Foundation of China (Grant No. 51078185)
文摘A series of Ce-doped MnOx/TiO2 catalysts were prepared by impregnation method and used for catalytic oxidation of NO in the presence of excess O2. The sample with the Ce doping concentration of Ce/Mn=l/3 and calcined at 300 ℃ shows a superior activity for NO oxidation to NO2. On Ce（1）Mn（3）Ti catalyst, 58% NO conversion was obtained at 200 ℃ and 85% NO conversion at 250 ℃ with a GHSV of 41000 h-1, which was much higher than that over MnOx/TiO2 catalyst （48% at 250 ℃）. Characterization results implied that the higher activity of Ce（1）Mn（3）Ti could be attributed to the enrichment of well-dispersed MnO2 on the surface and the abundance of Mn3＋ and Zi3＋ species. The addition of Ce into MnO2/TiO2 could improve oxygen storage capacity and facilitate oxygen mobility of the catalyst as shown by PL and ESR, so that its activity for NO oxidation could be enhanced. The effect of H2O and SO2 on the catalyst activity was also investigated.
文摘Ce-doped titanium oxide nanoparticles were investigated in the paper. The surface structures of undoped and Ce-doped TiO2 nanoparticles were observed by scanning tunneling microscopy （STM）. The experimental results of scanning tunneling spectroscopy （STS） show that the surface electronic structures of TiO2 nanoparticles are modified by introducing new electronic states in the surface band gap through cerium ion doping. The results are discussed in terms of the influence of doping concentration on the surface band gap of TiO2.
基金Funded by Changzhou Science and Technology Innovation Project(Nos.CC20140048,CC20130204)National Natural Science Foundation of China(No.51273027)2015 Research and Innovation Project for College Graduates of Jiangsu Province
文摘Ce-doped Bi2O3 nanopowders were prepared by reverse titration chemical coprecipitation from Bi^3＋and Ce^（4＋）containing aqueous solution.Techniques of X-ray diffraction（XRD）,transmission electron microscopic（TEM）and Fourier transform infrared spectroscopy（FTIR）were employed to characterize the as-synthesized materials.The XRD patterns indicated that the peaks can be easily indexed toβ-Bi2O3 and no diffraction peaks of Ce or other impurity phases were detected in the prepared samples.The calculated average crystalline size decreased from 31.72 to 11.96 nm when the Ce content increased from 1 wt%to 10 wt%.The morphology changed from flake-like into the spherical-like with increase in Ce content.The electric conductivity of Ce-doped Bi2O3 electrolyte was also investigated by two probe DC method.Conductivity analysis exhibited that the rate of conductivity increased with increasing Ce^2＋ratio,when the Ce concentration was up to 5 wt%,the as-synthesized Ce-doped Bi2O3 electrolyte showed the maximum value of conductivity（0.295 S？cm^（–1））.
文摘以 Sn Cl4· Ti( OBu) 4、氨水、乙醇为原料 ,采用活性层包覆法 ,制备出 Ti O2 / Sn O2 复合光催化剂 ,并用IR、XRD、TEM和 BET等手段对样品进行了表征 .研究其对有机磷农药敌敌畏的光催化降解效果 ,与单一半导体催化剂 Sn O2 、Ti O2 做了简单对比 .结果表明 :所制 Ti O2 / Sn O2 样品为包覆型结构 ,由锐钛矿型 Ti O2 金红石型 Sn O2 组成 ,与 Sn O2 及 Ti O2 晶体粉末相比所制 Ti O2 / Sn O2 包覆粒子光催化活性得到明显提高 .
文摘利用直流电弧等离子体蒸发 -凝聚法制备 Sn O2 纳米粒子 ,研究了 Sn O2 粒子在等离子体焰流中的形成和生长机理 ,探讨了等离子体发生器功率、气体配比和冷却介质对 Sn O2 纳米粒子粒度和纯度的影响 ,制备出了纯度大于98.8%、粒度可控的 Sn O2 纳米粉末 ,为制造高性能 Sn O2 气敏传感器打下了良好的基础。