With the aim to further improve the mechanical properties of Mg-A1-RE-based alloy, Mg-3.0Al-1.8Ce-0.3Y-0.2Mn alloy was prepared by high-pressure die-casting technique. The microstructure, thermal stability of intermet...With the aim to further improve the mechanical properties of Mg-A1-RE-based alloy, Mg-3.0Al-1.8Ce-0.3Y-0.2Mn alloy was prepared by high-pressure die-casting technique. The microstructure, thermal stability of intermetallic phases and mechanical properties were investigated. The results show that the alloy is composed of fine primary a-Mg dendrites and eutectic in the interdendritic regions. The intermetallic phases in eutectic are Aln（Ce,Y）3 and A12（Ce,Y） with the former being the dominant one. The thermal stability of Al11（ce,Y）3 is conditioned. It is basically stable at temperature up to 200℃ within 800 h, while most of the Al11（Ce,Y）3 intermetallics transform to A12（Ce,Y） at higher temperature of 450 ℃ for 800 h. The alloy exhibits remarkably improved strength both at room temperature and 200℃, which is mainly attributed to the reinforcement of dendrite boundaries with Alll（Ce,Y）3 intermetallics, small dendritic arm spacing effect as well as the solid solution strengthening with Y element.展开更多
In order to improve the hot corrosion resistance of DZ125 alloy,Ce-Y modified aluminum coatings were prepared on DZ125 alloy by pack cementation process at 950°C for 2 h.The microstructure,phase constitution and ...In order to improve the hot corrosion resistance of DZ125 alloy,Ce-Y modified aluminum coatings were prepared on DZ125 alloy by pack cementation process at 950°C for 2 h.The microstructure,phase constitution and formation mechanism of the coatings were investigated.The hot corrosion behaviors of DZ125 alloy and the coatings in molten salt environment of 25%K2SO4+75%Na2SO4(mass fraction)at 900°C were studied.Results show that the obtained Al-Ce-Y coatings were mainly composed of Al3Ni2,Al3Ni and Cr7Ni3,with a thickness of about 120μm.After hot corrosion test,DZ125 alloy suffered catastrophic hot corrosion and serious internal oxidation and internal sulfidation arose.Two layers of corrosion products formed on surfaces of DZ125 alloy,including the outer layer consisting of Cr2O3 and NiCr2O4,and the inner layer of Al2O3,Ni3S2 and Ni-base solid solution.After being coated with Al-Ce-Y coating,the hot corrosion resistance of DZ125 alloy is improved notably,due to the formation of a dense scale mainly consisting of Al-rich Al2O3 in the coating layer.展开更多
基金Project (HEUCFR1128) supported by the Fundamental Research Funds for the Central Universities,ChinaProject (2010AA4BE031)supported by the Key Project of Science and Technology of Harbin City,China+1 种基金Projects (20100471015,20100471046) supported by the China Postdoctoral Science FoundationProject (LBH-Z09217) supported by the Heilongjiang Postdoctorial Fund,China
文摘With the aim to further improve the mechanical properties of Mg-A1-RE-based alloy, Mg-3.0Al-1.8Ce-0.3Y-0.2Mn alloy was prepared by high-pressure die-casting technique. The microstructure, thermal stability of intermetallic phases and mechanical properties were investigated. The results show that the alloy is composed of fine primary a-Mg dendrites and eutectic in the interdendritic regions. The intermetallic phases in eutectic are Aln（Ce,Y）3 and A12（Ce,Y） with the former being the dominant one. The thermal stability of Al11（ce,Y）3 is conditioned. It is basically stable at temperature up to 200℃ within 800 h, while most of the Al11（Ce,Y）3 intermetallics transform to A12（Ce,Y） at higher temperature of 450 ℃ for 800 h. The alloy exhibits remarkably improved strength both at room temperature and 200℃, which is mainly attributed to the reinforcement of dendrite boundaries with Alll（Ce,Y）3 intermetallics, small dendritic arm spacing effect as well as the solid solution strengthening with Y element.
基金Project(51961003)supported by the National Natural Science Foundation of ChinaProject(NGY2018-148)supported by the Science and Technology Research of Ningxia Colleges,ChinaProject(NZ16083)supported by Key Program of Natural Science Foundation of Ningxia,China
文摘In order to improve the hot corrosion resistance of DZ125 alloy,Ce-Y modified aluminum coatings were prepared on DZ125 alloy by pack cementation process at 950°C for 2 h.The microstructure,phase constitution and formation mechanism of the coatings were investigated.The hot corrosion behaviors of DZ125 alloy and the coatings in molten salt environment of 25%K2SO4+75%Na2SO4(mass fraction)at 900°C were studied.Results show that the obtained Al-Ce-Y coatings were mainly composed of Al3Ni2,Al3Ni and Cr7Ni3,with a thickness of about 120μm.After hot corrosion test,DZ125 alloy suffered catastrophic hot corrosion and serious internal oxidation and internal sulfidation arose.Two layers of corrosion products formed on surfaces of DZ125 alloy,including the outer layer consisting of Cr2O3 and NiCr2O4,and the inner layer of Al2O3,Ni3S2 and Ni-base solid solution.After being coated with Al-Ce-Y coating,the hot corrosion resistance of DZ125 alloy is improved notably,due to the formation of a dense scale mainly consisting of Al-rich Al2O3 in the coating layer.