In this work,a series of Ce-Ti composite oxides with different Ti/Ce molar ratios was prepared by coprecipitation method,and investigated for the catalytic degradation of toluene and selective catalytic reduction of N...In this work,a series of Ce-Ti composite oxides with different Ti/Ce molar ratios was prepared by coprecipitation method,and investigated for the catalytic degradation of toluene and selective catalytic reduction of NO.The phase transition process between Ce species and Ti species is limited by modulating the interaction between Ce4+and Ti4+,while a completely amorphous composite is generated with an appropriate molar ratio of Ti/Ce(1.5/1).The catalyst CeTi1.5Oxexhibits the best catalytic performance,where the values of T90and T50for deep degradation of toluene are 297 and 330℃respectively at high weight hours space velocity(WHSV=120000 mL/(g·h)).Compared with CeO_(2),T90and T50decrease by48 and 34℃respectively while declining by 67 and 70℃compared to TiO_(2).For the SCR reaction,CeTi1.5Oxreaches 100%NO conversion at 250℃with WHSV=60000 mL/(g·h),reduced by 50℃compared to pure CeO_(2).The amorphous nanostructure with highly dispersed Ce and Ti species was confirmed by transmission electron microscopy(TEM)and X-ray diffraction(XRD)characterizations.The X-ray photoelectron spectroscopy(XPS)and Raman analyses show that a large number of active Ce-O-Ti species and surface oxygen vacancies are generated due to the strong interaction between Ti^(4+)and Ce^(4+)in CeTi_(1.5)O_(x).Additionally,H_(2)-TPR and O_(2)-TPD further confirm that the interaction promotes the low-temperature reducibility and mobility of surface-active oxygen species.Meanwhile,in-situ DRIFTS study reveals that CeTi1.5Oxwith amorphous nanostructure can dramatically enhance the dissociative and complete oxidation capacity for toluene.展开更多
In this work,V/Ce-Ti catalysts were modified with different kinds of transition metals(Cu,Fe,Co,Mn) by sol-gel and impregnation methods.The NH_(3) oxidation performance of them was tested to select the most active cat...In this work,V/Ce-Ti catalysts were modified with different kinds of transition metals(Cu,Fe,Co,Mn) by sol-gel and impregnation methods.The NH_(3) oxidation performance of them was tested to select the most active catalyst in NH_(3)-selective catalytic oxidation(NH_(3)-SCO).The effect of NO,SO_(2) and H_(2)O was also investigated.The experimental results indicate that 1% Cu-V/Ce-Ti catalyst exhibits the most significant ability to remove slip ammonia discharged from coal-fired plants and its NH_(3) conversion efficiency reaches90% at 300℃.In additio n,97% NO_x can be removed when NO is introduced in the gas.Cu-V/Ce-Ti catalyst also obtains good resistance to H_(2)O and SO_(2).Based on the characterization experiment,the introduced Cu and V are highly dispersed on Ce-Ti catalyst and they can increase the redox properties and the number of acidic sites.Besides,the redox cycles among Cu,V and Ce species on Cu-V/Ce-Ti catalyst surface are conducive to generating more active oxygen and promoting the oxidation capacity of the catalyst.展开更多
Mn-based catalysts have exhibited promising performance in low-temperature selective catalytic reduction of NOx with NH_(3)(NH_(3)-SCR).However,challenges such as H_(2)O-or SO_(2)-induced poisoning to these catalysts ...Mn-based catalysts have exhibited promising performance in low-temperature selective catalytic reduction of NOx with NH_(3)(NH_(3)-SCR).However,challenges such as H_(2)O-or SO_(2)-induced poisoning to these catalysts still remain.Herein,we report an efficient strategy to prepare the dual single-atom Ce-Ti/MnO_(2)catalyst via ball-milling and calcination processes to address these issues.Ce-Ti/MnO_(2)showed better catalytic performance with a higher NO conversion and enhanced H_(2)O-and SO_(2)-resistance at a lowtemperature window(100−150°C)than the MnO_(2),single-atom Ce/MnO_(2),and Ti/MnO_(2)catalysts.The in situ infrared Fourier transform spectroscopy analysis confirmed there is no competitive adsorption between NOx and H_(2)O over the Ce-Ti/MnO_(2)catalyst.The calculation results showed that the synergistic interaction of the neighboring Ce-Ti dual atoms as sacrificial sites weakens the ability of the active Mn sites for binding SO_(2)and H_(2)O but enhances their binding to NH_(3).The insight obtained in this work deepens the understanding of catalysis for NH_(3)-SCR.The synthesis strategy developed in this work is easily scaled up to commercialization and applicable to preparing other MnO_(2)-based single-atom catalysts.展开更多
基金Project supported by the National Natural Science Foundation of China(22072096,22108184)。
文摘In this work,a series of Ce-Ti composite oxides with different Ti/Ce molar ratios was prepared by coprecipitation method,and investigated for the catalytic degradation of toluene and selective catalytic reduction of NO.The phase transition process between Ce species and Ti species is limited by modulating the interaction between Ce4+and Ti4+,while a completely amorphous composite is generated with an appropriate molar ratio of Ti/Ce(1.5/1).The catalyst CeTi1.5Oxexhibits the best catalytic performance,where the values of T90and T50for deep degradation of toluene are 297 and 330℃respectively at high weight hours space velocity(WHSV=120000 mL/(g·h)).Compared with CeO_(2),T90and T50decrease by48 and 34℃respectively while declining by 67 and 70℃compared to TiO_(2).For the SCR reaction,CeTi1.5Oxreaches 100%NO conversion at 250℃with WHSV=60000 mL/(g·h),reduced by 50℃compared to pure CeO_(2).The amorphous nanostructure with highly dispersed Ce and Ti species was confirmed by transmission electron microscopy(TEM)and X-ray diffraction(XRD)characterizations.The X-ray photoelectron spectroscopy(XPS)and Raman analyses show that a large number of active Ce-O-Ti species and surface oxygen vacancies are generated due to the strong interaction between Ti^(4+)and Ce^(4+)in CeTi_(1.5)O_(x).Additionally,H_(2)-TPR and O_(2)-TPD further confirm that the interaction promotes the low-temperature reducibility and mobility of surface-active oxygen species.Meanwhile,in-situ DRIFTS study reveals that CeTi1.5Oxwith amorphous nanostructure can dramatically enhance the dissociative and complete oxidation capacity for toluene.
基金supported by the National Natural Science Foundation of China (21277060 and 21107030)the Development Program of the Science and Technology of Shandong Province (2011GSF11702)+3 种基金the Foundation for Outstanding Young Scientist in Shandong Province (BS2011HZ002)the Natural Science Foundation of Shandong Province (ZR2013BQ003)the Open Project from Jiangsu Key Laboratory of Atmospheric Environment Monitoring and Pollution Control of Nanjing University of Information Science and Technology (KHK1116)Jiangsu Province Innovation Platform for Superiority Subject of Environmental Science and Engineering~~
基金Project supported by the National Key R&D Program of China (2019YFD1101300)。
文摘In this work,V/Ce-Ti catalysts were modified with different kinds of transition metals(Cu,Fe,Co,Mn) by sol-gel and impregnation methods.The NH_(3) oxidation performance of them was tested to select the most active catalyst in NH_(3)-selective catalytic oxidation(NH_(3)-SCO).The effect of NO,SO_(2) and H_(2)O was also investigated.The experimental results indicate that 1% Cu-V/Ce-Ti catalyst exhibits the most significant ability to remove slip ammonia discharged from coal-fired plants and its NH_(3) conversion efficiency reaches90% at 300℃.In additio n,97% NO_x can be removed when NO is introduced in the gas.Cu-V/Ce-Ti catalyst also obtains good resistance to H_(2)O and SO_(2).Based on the characterization experiment,the introduced Cu and V are highly dispersed on Ce-Ti catalyst and they can increase the redox properties and the number of acidic sites.Besides,the redox cycles among Cu,V and Ce species on Cu-V/Ce-Ti catalyst surface are conducive to generating more active oxygen and promoting the oxidation capacity of the catalyst.
基金We gratefully acknowledge the financial supports from the National Natural Science Foundation of China(Nos.52070180,51938014,and 21802054)the Science Research Project of the Ministry of Education of the Heilongjiang Province of China(No.145109102)+2 种基金the Beijing Chenxi Environmental Engineering Co.,Ltd.Z.Z.thanks the financial support of Guangdong Key discipline fund for this collaborationY.J.thanks the financial supports from the Outstanding Youth cultivation program of Beijing Technology and Business University(No.19008021144)Research Foundation for Advanced Talents of Beijing Technology and Business University(No.19008020159).
文摘Mn-based catalysts have exhibited promising performance in low-temperature selective catalytic reduction of NOx with NH_(3)(NH_(3)-SCR).However,challenges such as H_(2)O-or SO_(2)-induced poisoning to these catalysts still remain.Herein,we report an efficient strategy to prepare the dual single-atom Ce-Ti/MnO_(2)catalyst via ball-milling and calcination processes to address these issues.Ce-Ti/MnO_(2)showed better catalytic performance with a higher NO conversion and enhanced H_(2)O-and SO_(2)-resistance at a lowtemperature window(100−150°C)than the MnO_(2),single-atom Ce/MnO_(2),and Ti/MnO_(2)catalysts.The in situ infrared Fourier transform spectroscopy analysis confirmed there is no competitive adsorption between NOx and H_(2)O over the Ce-Ti/MnO_(2)catalyst.The calculation results showed that the synergistic interaction of the neighboring Ce-Ti dual atoms as sacrificial sites weakens the ability of the active Mn sites for binding SO_(2)and H_(2)O but enhances their binding to NH_(3).The insight obtained in this work deepens the understanding of catalysis for NH_(3)-SCR.The synthesis strategy developed in this work is easily scaled up to commercialization and applicable to preparing other MnO_(2)-based single-atom catalysts.