Fluorite is widely employed as fluxing agent in metallurgy flux , which inevitably leads to serious fluorine pollution.B2O3 is employed as fluxing agent of CaO-SiO2-Fe2O3steelmaking fluxes to substitute for CaF2.The e...Fluorite is widely employed as fluxing agent in metallurgy flux , which inevitably leads to serious fluorine pollution.B2O3 is employed as fluxing agent of CaO-SiO2-Fe2O3steelmaking fluxes to substitute for CaF2.The effects of B2O3 and CaF2 on the melting properties of this system were investigated.The melting temperatures of fluxes including softening temperature （Ts）, hemispherical temperature （Th）, and flow temperature （Tf） were measured using the hemisphere method.The results indicate that the fluxing effect of B2O3is more significant than that of CaF2 .When the addition amount of B2O3 （mass percent） exceeds 6% , the melting temperatures of fluxes including Ts , Th and Tf are decreased lower than 1 300℃.The basicity of fluxes has a significant effect on the melting temperature , and the melting temperatures of the fluxes increase with the increase of fluxes basicity.However , when B2O3 is used as fluxing agent , the melting temperature changes little with the basicity increasing from 2.5 to 5.0. These characteristics are suitable for steelmaking process.Moreover , Fe2O3 has an important fluxing effect on this CaO-based steelmaking fluxes.This indicates that the fluxes system is suitable for steelmaking process.展开更多
Activities of FeO in CaO-SiO2-Al2O3-MgO-FeO slags were determined at 1673 K by electrochemical of the solid electrolyte cell： Mo [Mo＋MoOu[ZrO2（MgO）[Fe＋（CaO-SiO2-Al2O3-MgO-FeO）＋Ag[Fe. The influences of slag com...Activities of FeO in CaO-SiO2-Al2O3-MgO-FeO slags were determined at 1673 K by electrochemical of the solid electrolyte cell： Mo [Mo＋MoOu[ZrO2（MgO）[Fe＋（CaO-SiO2-Al2O3-MgO-FeO）＋Ag[Fe. The influences of slag compositions and basicity on FeO activities were analyzed. The results reveal that, for slags of fixed （%CaO）/（%SiO2） ratio, MgO and Al2O3 content, there was an increase of FeO activities with increase of FeO content. For slags with constant {（%CaO）＋ （%MgO）}/（%SiO2） ratio, fixed FeO and A1203 content, FeO activities decreased when MgO content increased from 5% to 10%, and increased with the increase of MgO content when it was over 10%. The FeO activities increased when （%CaO）/（%SiO2） ratio changed from 1.03 to 1.30 in the slags of constant MgO, FeO and Al2O3 content.展开更多
The sulphide capacity of CaO-SiO2-Al2O3-MgO-FetO slags was studied at 1773 K using gas-slag equilibrium techniques. Utilizing a Pt crucible, the slag was equilibrated with a mixture of gases, namely, CO, CO2, SO2 and ...The sulphide capacity of CaO-SiO2-Al2O3-MgO-FetO slags was studied at 1773 K using gas-slag equilibrium techniques. Utilizing a Pt crucible, the slag was equilibrated with a mixture of gases, namely, CO, CO2, SO2 and N2 to provide the partial pressure of oxygen and sulphur. It was shown that at fixed FetO and Al2O3 contents and a fixed { （%CaO）＋（%MgO）}/（%SIO2） ratio, the sulphide capacity decreases with increasing MgO content. At a constant （%CaO）/（%SiO2） ratio and constant MgO and Al2O3 contents, increasing the FetO content of the slags also results in an increase of the sulphide capacity. The rising basicity of （%CaO）/（%SiO2） from 1.0 to 1.4 at fixed MgO, FetO and Al2O3 contents significantly increases the sulphide capacity.展开更多
基金Item Sponsored by National Natural Science Foundation of China ( 51174099 )Natural Science Foundation of Jiangsu Province of China ( BK2010355 )National Science Foundation for Post-Doctoral Scientists of China ( 20100471382 )
文摘Fluorite is widely employed as fluxing agent in metallurgy flux , which inevitably leads to serious fluorine pollution.B2O3 is employed as fluxing agent of CaO-SiO2-Fe2O3steelmaking fluxes to substitute for CaF2.The effects of B2O3 and CaF2 on the melting properties of this system were investigated.The melting temperatures of fluxes including softening temperature （Ts）, hemispherical temperature （Th）, and flow temperature （Tf） were measured using the hemisphere method.The results indicate that the fluxing effect of B2O3is more significant than that of CaF2 .When the addition amount of B2O3 （mass percent） exceeds 6% , the melting temperatures of fluxes including Ts , Th and Tf are decreased lower than 1 300℃.The basicity of fluxes has a significant effect on the melting temperature , and the melting temperatures of the fluxes increase with the increase of fluxes basicity.However , when B2O3 is used as fluxing agent , the melting temperature changes little with the basicity increasing from 2.5 to 5.0. These characteristics are suitable for steelmaking process.Moreover , Fe2O3 has an important fluxing effect on this CaO-based steelmaking fluxes.This indicates that the fluxes system is suitable for steelmaking process.
基金Project supported by the National Natural Science Foundation of China （Grant No.50574036）
文摘Activities of FeO in CaO-SiO2-Al2O3-MgO-FeO slags were determined at 1673 K by electrochemical of the solid electrolyte cell： Mo [Mo＋MoOu[ZrO2（MgO）[Fe＋（CaO-SiO2-Al2O3-MgO-FeO）＋Ag[Fe. The influences of slag compositions and basicity on FeO activities were analyzed. The results reveal that, for slags of fixed （%CaO）/（%SiO2） ratio, MgO and Al2O3 content, there was an increase of FeO activities with increase of FeO content. For slags with constant {（%CaO）＋ （%MgO）}/（%SiO2） ratio, fixed FeO and A1203 content, FeO activities decreased when MgO content increased from 5% to 10%, and increased with the increase of MgO content when it was over 10%. The FeO activities increased when （%CaO）/（%SiO2） ratio changed from 1.03 to 1.30 in the slags of constant MgO, FeO and Al2O3 content.
基金This project was financially supported by the National Natural Science Foundation of China (No.50574036) and Natural Science Foun-dation of HeBei Province, China (No.502267).
文摘The sulphide capacity of CaO-SiO2-Al2O3-MgO-FetO slags was studied at 1773 K using gas-slag equilibrium techniques. Utilizing a Pt crucible, the slag was equilibrated with a mixture of gases, namely, CO, CO2, SO2 and N2 to provide the partial pressure of oxygen and sulphur. It was shown that at fixed FetO and Al2O3 contents and a fixed { （%CaO）＋（%MgO）}/（%SIO2） ratio, the sulphide capacity decreases with increasing MgO content. At a constant （%CaO）/（%SiO2） ratio and constant MgO and Al2O3 contents, increasing the FetO content of the slags also results in an increase of the sulphide capacity. The rising basicity of （%CaO）/（%SiO2） from 1.0 to 1.4 at fixed MgO, FetO and Al2O3 contents significantly increases the sulphide capacity.