CaO-SiO2-Al2O3-MgO-Fex O slag occurs in the production process of Corex ironmaking technology. Most of its metallurgical properties, especially the phosphorus property, are different from the slag produced from blast ...CaO-SiO2-Al2O3-MgO-Fex O slag occurs in the production process of Corex ironmaking technology. Most of its metallurgical properties, especially the phosphorus property, are different from the slag produced from blast furnace or converter. In order to explore the dephosphorization ability of CaO-SiO2-Al2O3-MgO-Fex O slag, its phosphorus capacity was measured at 1673 K by gas-slag-metal equilibrium technique. An iron crucible was used as the reaction vessel, Ag alloy with 0.2 % P was used as the metal phase which equilibrated with CaO-SiO2-Al2O3-MgO-Fex O slag, and a constant flow of CO-CO2-N2 gas was used to provide oxygen partial pressure in the experi- ment. The effects of MgO, Fex O and basicity on slag phosphorus capacity were investigated by single factor test. The results show that the phosphorus capacity rises firstly and then decreases with increasing MgO content under the condition of basicity 1.3, Fe2 O content of 20% and A12 03 content of 12%. The phosphorus value reaches maximum as the MgO content is 8%. When the basicity of slag is 1.1, MgO content is 10%, and Al2O3 is 12%, the phos- phorus capacity increases with the increase of Fe, O content. The phosphorus capacity rises linearly when the basicity is increased from 1.1 to 1. 5.展开更多
Activities of FeO in CaO-SiO2-Al2O3-MgO-FeO slags were determined at 1673 K by electrochemical of the solid electrolyte cell： Mo [Mo＋MoOu[ZrO2（MgO）[Fe＋（CaO-SiO2-Al2O3-MgO-FeO）＋Ag[Fe. The influences of slag com...Activities of FeO in CaO-SiO2-Al2O3-MgO-FeO slags were determined at 1673 K by electrochemical of the solid electrolyte cell： Mo [Mo＋MoOu[ZrO2（MgO）[Fe＋（CaO-SiO2-Al2O3-MgO-FeO）＋Ag[Fe. The influences of slag compositions and basicity on FeO activities were analyzed. The results reveal that, for slags of fixed （%CaO）/（%SiO2） ratio, MgO and Al2O3 content, there was an increase of FeO activities with increase of FeO content. For slags with constant {（%CaO）＋ （%MgO）}/（%SiO2） ratio, fixed FeO and A1203 content, FeO activities decreased when MgO content increased from 5% to 10%, and increased with the increase of MgO content when it was over 10%. The FeO activities increased when （%CaO）/（%SiO2） ratio changed from 1.03 to 1.30 in the slags of constant MgO, FeO and Al2O3 content.展开更多
基金Item Sponsored by the State Key Program of National Natural Science Foundation of China(U1360205)National Natural Science Foundation of China(51174074)
文摘CaO-SiO2-Al2O3-MgO-Fex O slag occurs in the production process of Corex ironmaking technology. Most of its metallurgical properties, especially the phosphorus property, are different from the slag produced from blast furnace or converter. In order to explore the dephosphorization ability of CaO-SiO2-Al2O3-MgO-Fex O slag, its phosphorus capacity was measured at 1673 K by gas-slag-metal equilibrium technique. An iron crucible was used as the reaction vessel, Ag alloy with 0.2 % P was used as the metal phase which equilibrated with CaO-SiO2-Al2O3-MgO-Fex O slag, and a constant flow of CO-CO2-N2 gas was used to provide oxygen partial pressure in the experi- ment. The effects of MgO, Fex O and basicity on slag phosphorus capacity were investigated by single factor test. The results show that the phosphorus capacity rises firstly and then decreases with increasing MgO content under the condition of basicity 1.3, Fe2 O content of 20% and A12 03 content of 12%. The phosphorus value reaches maximum as the MgO content is 8%. When the basicity of slag is 1.1, MgO content is 10%, and Al2O3 is 12%, the phos- phorus capacity increases with the increase of Fe, O content. The phosphorus capacity rises linearly when the basicity is increased from 1.1 to 1. 5.
基金Project supported by the National Natural Science Foundation of China （Grant No.50574036）
文摘Activities of FeO in CaO-SiO2-Al2O3-MgO-FeO slags were determined at 1673 K by electrochemical of the solid electrolyte cell： Mo [Mo＋MoOu[ZrO2（MgO）[Fe＋（CaO-SiO2-Al2O3-MgO-FeO）＋Ag[Fe. The influences of slag compositions and basicity on FeO activities were analyzed. The results reveal that, for slags of fixed （%CaO）/（%SiO2） ratio, MgO and Al2O3 content, there was an increase of FeO activities with increase of FeO content. For slags with constant {（%CaO）＋ （%MgO）}/（%SiO2） ratio, fixed FeO and A1203 content, FeO activities decreased when MgO content increased from 5% to 10%, and increased with the increase of MgO content when it was over 10%. The FeO activities increased when （%CaO）/（%SiO2） ratio changed from 1.03 to 1.30 in the slags of constant MgO, FeO and Al2O3 content.