Activities of FeO in CaO-SiO2-Al2O3-MgO-FeO slags were determined at 1673 K by electrochemical of the solid electrolyte cell： Mo [Mo＋MoOu[ZrO2（MgO）[Fe＋（CaO-SiO2-Al2O3-MgO-FeO）＋Ag[Fe. The influences of slag com...Activities of FeO in CaO-SiO2-Al2O3-MgO-FeO slags were determined at 1673 K by electrochemical of the solid electrolyte cell： Mo [Mo＋MoOu[ZrO2（MgO）[Fe＋（CaO-SiO2-Al2O3-MgO-FeO）＋Ag[Fe. The influences of slag compositions and basicity on FeO activities were analyzed. The results reveal that, for slags of fixed （%CaO）/（%SiO2） ratio, MgO and Al2O3 content, there was an increase of FeO activities with increase of FeO content. For slags with constant {（%CaO）＋ （%MgO）}/（%SiO2） ratio, fixed FeO and A1203 content, FeO activities decreased when MgO content increased from 5% to 10%, and increased with the increase of MgO content when it was over 10%. The FeO activities increased when （%CaO）/（%SiO2） ratio changed from 1.03 to 1.30 in the slags of constant MgO, FeO and Al2O3 content.展开更多
基金Project supported by the National Natural Science Foundation of China （Grant No.50574036）
文摘Activities of FeO in CaO-SiO2-Al2O3-MgO-FeO slags were determined at 1673 K by electrochemical of the solid electrolyte cell： Mo [Mo＋MoOu[ZrO2（MgO）[Fe＋（CaO-SiO2-Al2O3-MgO-FeO）＋Ag[Fe. The influences of slag compositions and basicity on FeO activities were analyzed. The results reveal that, for slags of fixed （%CaO）/（%SiO2） ratio, MgO and Al2O3 content, there was an increase of FeO activities with increase of FeO content. For slags with constant {（%CaO）＋ （%MgO）}/（%SiO2） ratio, fixed FeO and A1203 content, FeO activities decreased when MgO content increased from 5% to 10%, and increased with the increase of MgO content when it was over 10%. The FeO activities increased when （%CaO）/（%SiO2） ratio changed from 1.03 to 1.30 in the slags of constant MgO, FeO and Al2O3 content.