Activities of FeO in CaO-SiO2-Al2O3-MgO-FeO slags were determined at 1673 K by electrochemical of the solid electrolyte cell： Mo [Mo＋MoOu[ZrO2（MgO）[Fe＋（CaO-SiO2-Al2O3-MgO-FeO）＋Ag[Fe. The influences of slag com...Activities of FeO in CaO-SiO2-Al2O3-MgO-FeO slags were determined at 1673 K by electrochemical of the solid electrolyte cell： Mo [Mo＋MoOu[ZrO2（MgO）[Fe＋（CaO-SiO2-Al2O3-MgO-FeO）＋Ag[Fe. The influences of slag compositions and basicity on FeO activities were analyzed. The results reveal that, for slags of fixed （%CaO）/（%SiO2） ratio, MgO and Al2O3 content, there was an increase of FeO activities with increase of FeO content. For slags with constant {（%CaO）＋ （%MgO）}/（%SiO2） ratio, fixed FeO and A1203 content, FeO activities decreased when MgO content increased from 5% to 10%, and increased with the increase of MgO content when it was over 10%. The FeO activities increased when （%CaO）/（%SiO2） ratio changed from 1.03 to 1.30 in the slags of constant MgO, FeO and Al2O3 content.展开更多
The lack of thermodynamic information,such as primary phase fields and liquidus temperatures,in the CaO-SiO2-Nb2O5-La2O3 quaternary system phase diagram has restricted the comprehensive utilization of the niobium(Nb) ...The lack of thermodynamic information,such as primary phase fields and liquidus temperatures,in the CaO-SiO2-Nb2O5-La2O3 quaternary system phase diagram has restricted the comprehensive utilization of the niobium(Nb) and rare earth(RE) resources.In this work,the phase equilibria in low basicity region(w(CaO)/w(SiO2)<1) of CaO-SiO2-Nb2O5-(0-15 wt%)La2O3 system at 1373-1873 K were experimentally studied by thermodynamic equilibrium experiment,and then,the results were analyzed by X-ray diffraction(XRD),scanning electron microscopy(SEM),and energy dispersive spectrometry(EDS).Additionally,an optimized method was proposed to process the compositions of equilibrium liquid phases at different temperatures.According to the experimental results,the univariate line between CaNb2O6,SiO2 and LaNbO4 primary phase fields,interface between CaNb2O6 and SiO2 primary phase fields and isothermal liquidus surfaces in SiO2 primary phase field were determined.Finally,the spatial phase diagram of CaO-SiO2-Nb2O5-La2O3 within specific region was constructed,and furthermore,the phase diagram was also presented in CaO-SiO2-Nb2O5 pseudo-ternary system with w(La2O3)=5 wt%,10 wt% and 15 wt%.The research results have guiding significance for the improvement of related phase diagram and the comprehensive utilization of Nb and RE resources.展开更多
基金Project supported by the National Natural Science Foundation of China （Grant No.50574036）
文摘Activities of FeO in CaO-SiO2-Al2O3-MgO-FeO slags were determined at 1673 K by electrochemical of the solid electrolyte cell： Mo [Mo＋MoOu[ZrO2（MgO）[Fe＋（CaO-SiO2-Al2O3-MgO-FeO）＋Ag[Fe. The influences of slag compositions and basicity on FeO activities were analyzed. The results reveal that, for slags of fixed （%CaO）/（%SiO2） ratio, MgO and Al2O3 content, there was an increase of FeO activities with increase of FeO content. For slags with constant {（%CaO）＋ （%MgO）}/（%SiO2） ratio, fixed FeO and A1203 content, FeO activities decreased when MgO content increased from 5% to 10%, and increased with the increase of MgO content when it was over 10%. The FeO activities increased when （%CaO）/（%SiO2） ratio changed from 1.03 to 1.30 in the slags of constant MgO, FeO and Al2O3 content.
基金Project supported by the National Key R&D Program of China(2017YFC0805100)the National Natural Science Foundation of China(51774087)the Fundamental Research Funds for the Central Universities China(N162506002)
文摘The lack of thermodynamic information,such as primary phase fields and liquidus temperatures,in the CaO-SiO2-Nb2O5-La2O3 quaternary system phase diagram has restricted the comprehensive utilization of the niobium(Nb) and rare earth(RE) resources.In this work,the phase equilibria in low basicity region(w(CaO)/w(SiO2)<1) of CaO-SiO2-Nb2O5-(0-15 wt%)La2O3 system at 1373-1873 K were experimentally studied by thermodynamic equilibrium experiment,and then,the results were analyzed by X-ray diffraction(XRD),scanning electron microscopy(SEM),and energy dispersive spectrometry(EDS).Additionally,an optimized method was proposed to process the compositions of equilibrium liquid phases at different temperatures.According to the experimental results,the univariate line between CaNb2O6,SiO2 and LaNbO4 primary phase fields,interface between CaNb2O6 and SiO2 primary phase fields and isothermal liquidus surfaces in SiO2 primary phase field were determined.Finally,the spatial phase diagram of CaO-SiO2-Nb2O5-La2O3 within specific region was constructed,and furthermore,the phase diagram was also presented in CaO-SiO2-Nb2O5 pseudo-ternary system with w(La2O3)=5 wt%,10 wt% and 15 wt%.The research results have guiding significance for the improvement of related phase diagram and the comprehensive utilization of Nb and RE resources.
