Reduction smelting of the bismuth oxide residue from pressure leaching of bismuth sulfide was investigated in the FeO-SiO_2-CaO ternary slag system.The results show that all the recovery ratios of Bi,Ag,Cu and Pb incr...Reduction smelting of the bismuth oxide residue from pressure leaching of bismuth sulfide was investigated in the FeO-SiO_2-CaO ternary slag system.The results show that all the recovery ratios of Bi,Ag,Cu and Pb increase with the increase of reductive coal proportion,reaction temperature and time,while too much reductive coal would help Fe enter metal phase;CaO/SiO_2and Fe O/SiO_2 of the chosen slag system should be 0.5-0.75 and 1.25-1.75,respectively,for the reason that the slag system has the optimum mobility and is beneficial for the recovery of metals.The corresponding optimum conditions are determined as follows:the added coal proportion is 7%of the leaching residue,CaO/SiO_2 mass ratio in the chosen slag system is 0.5 and FeO-SiO_2 is 1.5,the reaction temperature is 1300°C and the reaction time is 40 min.Under the above conditions,the recovery ratios of Bi,Ag,Cu and Pb are 99.6%,99.8%,97.0%and 97.3%,respectively.展开更多
分析了9.5 t热作模钢H13重熔锭在380 kg 60CaF_2-30Al_2O_3-10CaO三元渣的重熔过程中渣头和渣皮的结构和成分。结果表明,电渣锭生产过程的渣皮呈现明显的分层结构,自外侧向内,依次为急冷层、氧化铝析出层和内部返熔层;渣头中CaF_2含量...分析了9.5 t热作模钢H13重熔锭在380 kg 60CaF_2-30Al_2O_3-10CaO三元渣的重熔过程中渣头和渣皮的结构和成分。结果表明,电渣锭生产过程的渣皮呈现明显的分层结构,自外侧向内,依次为急冷层、氧化铝析出层和内部返熔层;渣头中CaF_2含量普遍低于初渣值,而渣皮中CaF_2含量高于初渣值;铝氧化物在渣头外缘比重最高;重熔后渣的氧含量明显高于初渣。展开更多
The influence of CaF2 content on the formation behavior of spinel inclusions in the Ni-Cr-V-alloyed special steel was presented. The spinel was not formed at CaF2 content lower than 10 wt%. However, it was formed at e...The influence of CaF2 content on the formation behavior of spinel inclusions in the Ni-Cr-V-alloyed special steel was presented. The spinel was not formed at CaF2 content lower than 10 wt%. However, it was formed at early stage when the CaF2 content was greater than 30 wt%, followed by a modification to the aluminosilicate-type inclusions. Because the slag was saturated by MgO, the activity of MgO was unity irrespective of CaF2 content in the slag. Thus, Mg was transferred from slag to metal phase. Mg transferred to molten steel reacted with Al2O3-rich inclusions to form MgO.Al2O3 spinel. However, the spinel inclusion was modified to aluminosilicate-type inclusions by the reaction with Si and Ca transferred from slag to molten steel about 2-3 h later.展开更多
A sub-regular solution model SELF-SReM4 used to evaluate activity of the components in a homogeneous region of a quaternary system has been developed in Shanghai Enhanced Laboratory of Ferrometallurgy.The application ...A sub-regular solution model SELF-SReM4 used to evaluate activity of the components in a homogeneous region of a quaternary system has been developed in Shanghai Enhanced Laboratory of Ferrometallurgy.The application of SELF-SReM4 in C-Mn-Fe-Si system without the SiC formation has been introduced in previous paper.It’s application for molten slag of MnO-SiO2-Al2O3-CaO was introduced in this paper.They provide a basis for the prediction of the metal-slag equilibrium conditions.展开更多
The desulfurization experiment of an Al2O3-CaO base pre-molten refining slag containing SrO was carried out. Experimental samples were made from industrial materials. In order to predict the slag's desulfurization...The desulfurization experiment of an Al2O3-CaO base pre-molten refining slag containing SrO was carried out. Experimental samples were made from industrial materials. In order to predict the slag's desulfurization ability, sulphur capacity was calculated by means of optical basicity, and there is consistency between calculated results and experimental data. A mathematical model between components and sulphur partition ratio was established with the experimental data. Based on the regression equation, the effects of single and interactive components on sulphur partition ratio were discussed. The results show that the sulphur capacity and distribution ratio decrease with the increment of Al2O3/CaO. SrO and MgO can increase the sulphur partition ratio. The best content of SrO in the slag should not be more than 10%, and the MgO content should be about 8%. The effect of CaF2 on sulphur partition ratio is not obvious, therefore the addition should be limited for environmental protection.展开更多
Because of the addition of significant quantities of aluminum and manganese, the great challenge of casting 20Mn23Al nonmagnetic steel is to design a mold slag that is chemically compatible with this steel composition...Because of the addition of significant quantities of aluminum and manganese, the great challenge of casting 20Mn23Al nonmagnetic steel is to design a mold slag that is chemically compatible with this steel composition. A new mold slag with low melting point and low basicity was proposed. The initial slag （the base mold slag） and two corresponding mold slags sampled after 8 min and 15 min were investigated, and the changes of mold slag composition and properties of molten slag were discussed. The results showed that the slag quickly changed in chemical composition to a slag that contained a small quantity of silica and a larger quantity of alumina, and the basieity increased obviously; the heat flux density through the slag film decreased slightly compared with the slag film at 0 min, 8 min and 15 min; the mold slag used for nonmagnetic steel was precipitated as CaF2 crystals. The casting experi- ment shows that the slab has good surface quality without longitudinal face cracks and slag inclusions; the Al2O3 content in the molten slag pool increased with time at the beginning stage, and it can approach equilibrium state after about 600 s.展开更多
基金Project(134414) supported by the Postdoctoral Funded Program of Central South University,China
文摘Reduction smelting of the bismuth oxide residue from pressure leaching of bismuth sulfide was investigated in the FeO-SiO_2-CaO ternary slag system.The results show that all the recovery ratios of Bi,Ag,Cu and Pb increase with the increase of reductive coal proportion,reaction temperature and time,while too much reductive coal would help Fe enter metal phase;CaO/SiO_2and Fe O/SiO_2 of the chosen slag system should be 0.5-0.75 and 1.25-1.75,respectively,for the reason that the slag system has the optimum mobility and is beneficial for the recovery of metals.The corresponding optimum conditions are determined as follows:the added coal proportion is 7%of the leaching residue,CaO/SiO_2 mass ratio in the chosen slag system is 0.5 and FeO-SiO_2 is 1.5,the reaction temperature is 1300°C and the reaction time is 40 min.Under the above conditions,the recovery ratios of Bi,Ag,Cu and Pb are 99.6%,99.8%,97.0%and 97.3%,respectively.
文摘分析了9.5 t热作模钢H13重熔锭在380 kg 60CaF_2-30Al_2O_3-10CaO三元渣的重熔过程中渣头和渣皮的结构和成分。结果表明,电渣锭生产过程的渣皮呈现明显的分层结构,自外侧向内,依次为急冷层、氧化铝析出层和内部返熔层;渣头中CaF_2含量普遍低于初渣值,而渣皮中CaF_2含量高于初渣值;铝氧化物在渣头外缘比重最高;重熔后渣的氧含量明显高于初渣。
文摘The influence of CaF2 content on the formation behavior of spinel inclusions in the Ni-Cr-V-alloyed special steel was presented. The spinel was not formed at CaF2 content lower than 10 wt%. However, it was formed at early stage when the CaF2 content was greater than 30 wt%, followed by a modification to the aluminosilicate-type inclusions. Because the slag was saturated by MgO, the activity of MgO was unity irrespective of CaF2 content in the slag. Thus, Mg was transferred from slag to metal phase. Mg transferred to molten steel reacted with Al2O3-rich inclusions to form MgO.Al2O3 spinel. However, the spinel inclusion was modified to aluminosilicate-type inclusions by the reaction with Si and Ca transferred from slag to molten steel about 2-3 h later.
文摘A sub-regular solution model SELF-SReM4 used to evaluate activity of the components in a homogeneous region of a quaternary system has been developed in Shanghai Enhanced Laboratory of Ferrometallurgy.The application of SELF-SReM4 in C-Mn-Fe-Si system without the SiC formation has been introduced in previous paper.It’s application for molten slag of MnO-SiO2-Al2O3-CaO was introduced in this paper.They provide a basis for the prediction of the metal-slag equilibrium conditions.
文摘The desulfurization experiment of an Al2O3-CaO base pre-molten refining slag containing SrO was carried out. Experimental samples were made from industrial materials. In order to predict the slag's desulfurization ability, sulphur capacity was calculated by means of optical basicity, and there is consistency between calculated results and experimental data. A mathematical model between components and sulphur partition ratio was established with the experimental data. Based on the regression equation, the effects of single and interactive components on sulphur partition ratio were discussed. The results show that the sulphur capacity and distribution ratio decrease with the increment of Al2O3/CaO. SrO and MgO can increase the sulphur partition ratio. The best content of SrO in the slag should not be more than 10%, and the MgO content should be about 8%. The effect of CaF2 on sulphur partition ratio is not obvious, therefore the addition should be limited for environmental protection.
基金Item Sponsored by National Natural Science Foundation of China(50874125)
文摘Because of the addition of significant quantities of aluminum and manganese, the great challenge of casting 20Mn23Al nonmagnetic steel is to design a mold slag that is chemically compatible with this steel composition. A new mold slag with low melting point and low basicity was proposed. The initial slag （the base mold slag） and two corresponding mold slags sampled after 8 min and 15 min were investigated, and the changes of mold slag composition and properties of molten slag were discussed. The results showed that the slag quickly changed in chemical composition to a slag that contained a small quantity of silica and a larger quantity of alumina, and the basieity increased obviously; the heat flux density through the slag film decreased slightly compared with the slag film at 0 min, 8 min and 15 min; the mold slag used for nonmagnetic steel was precipitated as CaF2 crystals. The casting experi- ment shows that the slab has good surface quality without longitudinal face cracks and slag inclusions; the Al2O3 content in the molten slag pool increased with time at the beginning stage, and it can approach equilibrium state after about 600 s.