The effects of Zn content on the microstxucture and the mechanical and corrosion properties of as-cast low-alloyed Mg-xZn~.2Ca alloys （x = 0.6wt%, 2.0wt%, 2.5wt%, hereafter denoted as 0.6Zn, 2.0Zn, and 2.5Zn alloys, ...The effects of Zn content on the microstxucture and the mechanical and corrosion properties of as-cast low-alloyed Mg-xZn~.2Ca alloys （x = 0.6wt%, 2.0wt%, 2.5wt%, hereafter denoted as 0.6Zn, 2.0Zn, and 2.5Zn alloys, respectively） axe investigated. The results show that the Zn content not only influences grain refinement but also induces different phase precipitation behaviors. The as-cast microstxucture of the 0.6Zn alloy is composed of ct-Mg, Mg2Ca, and Ca2Mg6Zn3 phases, whereas 2.0Zn and 2.5Zn alloys only contain ct-Mg and Ca2Mg6Zn3 phases, as revealed by X-ray diffraction （XRD） and txonsmission electron microscopy （TEM） analyses. Moreover, with in- creasing Zn content, both the ultimate tensile strength （UTS） and the elongation to fracture first increase and then decrease. Among the three investigated alloys, the largest UTS （178 MPa） and the highest elongation to fracture （6.5%） are obtained for the 2.0Zn alloy. In addition, the corrosion rate increases with increasing Zn content. This paper provides on updated investigation of the alloy composi- tion-microstxucture-property relationships of different Zn-containing Mg-Zn-Ca alloys.展开更多
The effect of fly ash on controlling alkail-silica rection （ASR） in simudated alkali solution was studied. The expausion of mortar bars and the content of Ca（ OH）2 in cement paste cured at 80 °G for 91 d were...The effect of fly ash on controlling alkail-silica rection （ASR） in simudated alkali solution was studied. The expausion of mortar bars and the content of Ca（ OH）2 in cement paste cured at 80 °G for 91 d were measured. Traasmission electron microscopy （TEM） and high-resolution transmission electron microscot9 （HRTEM） were employed to study the microstructure of C-S-H. TEM/ energy dispersive spectroscopy （EDS） leas then used to determine the composition of C-S-H. The pore structure of the paste was analyzed by mercury intntsion porosimetry （MIP）. The results show that the contents of fly ash of 30% and 45% can well inhibit ASR. And the content of Ca（OH） 2 decreases with the increase of fly ash. That fly ash reacted with Ca（OH）2 to produce C-S-H with a low Ca/Si molar ratio could bind more Na^＋ and K^＋ ious, and produce a reduction in the amount of soluble alkali available for ASR. At the same time, the C- S- H produced by pozzolanic reaction converted large pores to snudler ones （ gel pores smaller than 10 nm ） to deusify the pore structure. Perhaps that could inhibit alkali trausport to aggregate for ASR.展开更多
基金supported by the National Natural Science Foundation of China(No.51671017)Fundamental Research Funds for the Central Universities(No.FRF-GF-17-B3)+1 种基金Beijing Laboratory of Metallic Materials and Processing for Modern Transportation,the Opening Research Fund of State Key Laboratory for Advanced Metals and Materials(Nos.2016Z-11,2017Z-08)State's Key Project of Research and Development Plan(No.2016YFB0300801)
文摘The effects of Zn content on the microstxucture and the mechanical and corrosion properties of as-cast low-alloyed Mg-xZn~.2Ca alloys （x = 0.6wt%, 2.0wt%, 2.5wt%, hereafter denoted as 0.6Zn, 2.0Zn, and 2.5Zn alloys, respectively） axe investigated. The results show that the Zn content not only influences grain refinement but also induces different phase precipitation behaviors. The as-cast microstxucture of the 0.6Zn alloy is composed of ct-Mg, Mg2Ca, and Ca2Mg6Zn3 phases, whereas 2.0Zn and 2.5Zn alloys only contain ct-Mg and Ca2Mg6Zn3 phases, as revealed by X-ray diffraction （XRD） and txonsmission electron microscopy （TEM） analyses. Moreover, with in- creasing Zn content, both the ultimate tensile strength （UTS） and the elongation to fracture first increase and then decrease. Among the three investigated alloys, the largest UTS （178 MPa） and the highest elongation to fracture （6.5%） are obtained for the 2.0Zn alloy. In addition, the corrosion rate increases with increasing Zn content. This paper provides on updated investigation of the alloy composi- tion-microstxucture-property relationships of different Zn-containing Mg-Zn-Ca alloys.
基金Founded bythe National Basic Research Programof China"973"(No.2001CB610706)
文摘The effect of fly ash on controlling alkail-silica rection （ASR） in simudated alkali solution was studied. The expausion of mortar bars and the content of Ca（ OH）2 in cement paste cured at 80 °G for 91 d were measured. Traasmission electron microscopy （TEM） and high-resolution transmission electron microscot9 （HRTEM） were employed to study the microstructure of C-S-H. TEM/ energy dispersive spectroscopy （EDS） leas then used to determine the composition of C-S-H. The pore structure of the paste was analyzed by mercury intntsion porosimetry （MIP）. The results show that the contents of fly ash of 30% and 45% can well inhibit ASR. And the content of Ca（OH） 2 decreases with the increase of fly ash. That fly ash reacted with Ca（OH）2 to produce C-S-H with a low Ca/Si molar ratio could bind more Na^＋ and K^＋ ious, and produce a reduction in the amount of soluble alkali available for ASR. At the same time, the C- S- H produced by pozzolanic reaction converted large pores to snudler ones （ gel pores smaller than 10 nm ） to deusify the pore structure. Perhaps that could inhibit alkali trausport to aggregate for ASR.