The effect of the deposition temperature of the buffer layer In_2S_3 on the band alignment of CZTS/In_2S_3 heterostructures and the solar cell performance have been investigated.The In_2S_3 films are prepared by therm...The effect of the deposition temperature of the buffer layer In_2S_3 on the band alignment of CZTS/In_2S_3 heterostructures and the solar cell performance have been investigated.The In_2S_3 films are prepared by thermal evaporation method at temperatures of 30,100,150,and 200 ℃,respectively.By using x-ray photoelectron spectroscopy（XPS）,the valence band offsets（VBO） are determined to be-0.28 ±0.1,-0.28 ±0.1,-0.34 ±0.1,and-0.42 ±0.1 eV for the CZTS/In_2S_3heterostructures deposited at 30,100,150,and 200 ℃,respectively,and the corresponding conduction band offsets（CBO）are found to be 0.3 ±0.1,0.41 ±0.1,0.22±0.1,and 0.01 ±0.1 eV,respectively.The XPS study also reveals that interdiffusion of In and Cu occurs at the interface of the heterostructures,which is especially serious at 200 ℃ leading to large amount of interface defects or the formation of CuInS_2 phase at the interface.The CZTS solar cell with the buffer layer In_2S_3 deposited at 150 ℃ shows the best performance due to the proper CBO value at the heterostructure interface and the improved crystal quality of In_2S_3 film induced by the appropriate deposition temperature.The device prepared at 100 ℃presents the poorest performance owing to too high a value of CBO.It is demonstrated that the deposition temperature is a crucial parameter to control the quality of the solar cells.展开更多
基金Project supported by the National Natural Science Foundation of China(Grant Nos.61574038 and 61674038)the Natural Science Foundation of Fujian Province,China(Grant No.2014J05073)
文摘The effect of the deposition temperature of the buffer layer In_2S_3 on the band alignment of CZTS/In_2S_3 heterostructures and the solar cell performance have been investigated.The In_2S_3 films are prepared by thermal evaporation method at temperatures of 30,100,150,and 200 ℃,respectively.By using x-ray photoelectron spectroscopy（XPS）,the valence band offsets（VBO） are determined to be-0.28 ±0.1,-0.28 ±0.1,-0.34 ±0.1,and-0.42 ±0.1 eV for the CZTS/In_2S_3heterostructures deposited at 30,100,150,and 200 ℃,respectively,and the corresponding conduction band offsets（CBO）are found to be 0.3 ±0.1,0.41 ±0.1,0.22±0.1,and 0.01 ±0.1 eV,respectively.The XPS study also reveals that interdiffusion of In and Cu occurs at the interface of the heterostructures,which is especially serious at 200 ℃ leading to large amount of interface defects or the formation of CuInS_2 phase at the interface.The CZTS solar cell with the buffer layer In_2S_3 deposited at 150 ℃ shows the best performance due to the proper CBO value at the heterostructure interface and the improved crystal quality of In_2S_3 film induced by the appropriate deposition temperature.The device prepared at 100 ℃presents the poorest performance owing to too high a value of CBO.It is demonstrated that the deposition temperature is a crucial parameter to control the quality of the solar cells.