Thermodynamic assessment in the ternary systems ZrO2 -CeO2 -Y2 O3, ZrO2 -CeO2 -Ce2 03 and the limiting binaries ZrO2 -Y2 O3, ZrO2 -CeO2, CeO2 -Y2 03, ZrO2 -Ce2O3, CeO2 -Ce2O3 as well as the modeling for oxides are rev...Thermodynamic assessment in the ternary systems ZrO2 -CeO2 -Y2 O3, ZrO2 -CeO2 -Ce2 03 and the limiting binaries ZrO2 -Y2 O3, ZrO2 -CeO2, CeO2 -Y2 03, ZrO2 -Ce2O3, CeO2 -Ce2O3 as well as the modeling for oxides are reviewed comprehensively. Based on the recent estimations on the YO1.5-CeO2, ZrO2-CeO2 and ZrO2 -YO1.6 systems, isothermal sections at 1273 and 1 973 K of the ternary CeO2- ZrO2-YO1.5system are calculated. In the system of ZrO2-CeO2-Ce2O3, the complex relation between the nonstoichiometry （y） in CeO2-x, the composition of the ZrO2 -CeO2 solid solution and the oxygen partial pressure （Po2 ） for different ZrO2 containing solid solutions CexZr1-xO2-x. are evaluated from 1 473 to 1 773 K. The relation between the degree of Ce^＋4 reduction to Ce.3 under different Po2 in the fluorite CeO2-xy and CexZr1-xOz-x solid solutions at different temperatures can be used as a guide in the development of functional ceramics.展开更多
文摘Thermodynamic assessment in the ternary systems ZrO2 -CeO2 -Y2 O3, ZrO2 -CeO2 -Ce2 03 and the limiting binaries ZrO2 -Y2 O3, ZrO2 -CeO2, CeO2 -Y2 03, ZrO2 -Ce2O3, CeO2 -Ce2O3 as well as the modeling for oxides are reviewed comprehensively. Based on the recent estimations on the YO1.5-CeO2, ZrO2-CeO2 and ZrO2 -YO1.6 systems, isothermal sections at 1273 and 1 973 K of the ternary CeO2- ZrO2-YO1.5system are calculated. In the system of ZrO2-CeO2-Ce2O3, the complex relation between the nonstoichiometry （y） in CeO2-x, the composition of the ZrO2 -CeO2 solid solution and the oxygen partial pressure （Po2 ） for different ZrO2 containing solid solutions CexZr1-xO2-x. are evaluated from 1 473 to 1 773 K. The relation between the degree of Ce^＋4 reduction to Ce.3 under different Po2 in the fluorite CeO2-xy and CexZr1-xOz-x solid solutions at different temperatures can be used as a guide in the development of functional ceramics.