Bleached softwood kraft pulp (BSKP) fibers were pretreated in a 5 mol/L NaOH aqueous solution at 35℃ for 90 min. The ZnCl2/H2O/ C2H5OH was used to treat the pretreated BSKP fibers, filter papers were then prepared. I...Bleached softwood kraft pulp (BSKP) fibers were pretreated in a 5 mol/L NaOH aqueous solution at 35℃ for 90 min. The ZnCl2/H2O/ C2H5OH was used to treat the pretreated BSKP fibers, filter papers were then prepared. In the course of processing, the effects of various molar ratios of ZnCl2/H2O/C2H5OH on the filter paper performance were evaluated. SEMEDX was conducted to analyze the physical configuration of the filter papers. Moreover, FT-IR and XPS were performed to further characterize the BSKP, the pretreated BSKP and the filter paper fibers. The results indicated that the fibers treated by ZnCl2/H2O/C2H5OH were swollen and exhibited slight fibrillation, leading to a looser fiber structure and therefore, enhanced filter paper performance. Air permeability increased from 161.7 L/(m2·s) to 1450.4 L/(m2·s) for the filter papers when the molar ratio of ZnCl2/H2O/C2H5OH was 1:14:1. The optimum molar ratio of ZnCl2/H2O/C2H5OH was found to be 1:14:1, and no significant effect of ZnCl2/H2O/C2H5OH on fibers’ functional groups was detected. These results showed that filtration performance of filter papers was improved when treated with the ZnCl2/H2O/C2H5OH solution.展开更多
The novel copper?complex with salicylaldehyde benzoylhydrazone and pyridine ligands, Cu(C14H10N2O2)(C5H5N), has been synthesized and characterized by elemental analysis, IR and thermal analysis. The crystal structure ...The novel copper?complex with salicylaldehyde benzoylhydrazone and pyridine ligands, Cu(C14H10N2O2)(C5H5N), has been synthesized and characterized by elemental analysis, IR and thermal analysis. The crystal structure of the title complex has been determined by single crystal X ray diffraction techniques. The crystal belongs to monoclinic with space group P21/c. The cell parameters are: a=1.6362(9)nm, b=1.7140(9)nm, c=1.2255(7)nm, β=105.168(9)°, V=3.317(3)nm3, Z=8, Dc=1.525g·cm-3, μ(MoKα)=1.334mm-1, F(000)=1560. The structure wasrefined to final R1=0.0376, wR2=0.0909. The copper?ion lies in a distorted square planar environment composed of two oxygen atoms, one nitrogen atom of tridentate acyhydrazone Schiff base ligand and one nitrogen atom of the pyridine ligand. CCDC: 193111.展开更多
基金the support of the Natural Science Foundation of Heilongjiang Province (Grant No. C2018007)
文摘Bleached softwood kraft pulp (BSKP) fibers were pretreated in a 5 mol/L NaOH aqueous solution at 35℃ for 90 min. The ZnCl2/H2O/ C2H5OH was used to treat the pretreated BSKP fibers, filter papers were then prepared. In the course of processing, the effects of various molar ratios of ZnCl2/H2O/C2H5OH on the filter paper performance were evaluated. SEMEDX was conducted to analyze the physical configuration of the filter papers. Moreover, FT-IR and XPS were performed to further characterize the BSKP, the pretreated BSKP and the filter paper fibers. The results indicated that the fibers treated by ZnCl2/H2O/C2H5OH were swollen and exhibited slight fibrillation, leading to a looser fiber structure and therefore, enhanced filter paper performance. Air permeability increased from 161.7 L/(m2·s) to 1450.4 L/(m2·s) for the filter papers when the molar ratio of ZnCl2/H2O/C2H5OH was 1:14:1. The optimum molar ratio of ZnCl2/H2O/C2H5OH was found to be 1:14:1, and no significant effect of ZnCl2/H2O/C2H5OH on fibers’ functional groups was detected. These results showed that filtration performance of filter papers was improved when treated with the ZnCl2/H2O/C2H5OH solution.
文摘The novel copper?complex with salicylaldehyde benzoylhydrazone and pyridine ligands, Cu(C14H10N2O2)(C5H5N), has been synthesized and characterized by elemental analysis, IR and thermal analysis. The crystal structure of the title complex has been determined by single crystal X ray diffraction techniques. The crystal belongs to monoclinic with space group P21/c. The cell parameters are: a=1.6362(9)nm, b=1.7140(9)nm, c=1.2255(7)nm, β=105.168(9)°, V=3.317(3)nm3, Z=8, Dc=1.525g·cm-3, μ(MoKα)=1.334mm-1, F(000)=1560. The structure wasrefined to final R1=0.0376, wR2=0.0909. The copper?ion lies in a distorted square planar environment composed of two oxygen atoms, one nitrogen atom of tridentate acyhydrazone Schiff base ligand and one nitrogen atom of the pyridine ligand. CCDC: 193111.
