Novel TiO2/BiVO4 microfiber heterojunctions were constructed using cotton as biomorphic templates. The as-synthesized samples were characterized by scanning electron microscope, X-ray diffraction, X-ray photoelectron ...Novel TiO2/BiVO4 microfiber heterojunctions were constructed using cotton as biomorphic templates. The as-synthesized samples were characterized by scanning electron microscope, X-ray diffraction, X-ray photoelectron spectroscopy, UV-Vis diffuse reflectance spectra and photocatalytic experiment. The morphology of the as-synthesized TiO2/BiVO4 composites was consisted of a large quantity of microfiber structures with diameter from 2.5 gm to 5 μm, and the surface of samples became more coarse and compact with the increase of weight ratio of TiO2. The TiO2/BiVO4 samples with proper content （10.00wt%） showed the highest pho- tocatalytic degradation activity for methylene blue （MB） degradation among all the samples under visible light, and 88.58%MB could be degraded within 150 min. The enhancement of photocatalytic activity was mainly attributed to the formation of n-n heterojunction at the contact interface of TiO2 and BiVO4, which not only narrowed the band gap of BiVO4 for extending the absorption range of visible light, but also promoted the transfer of charge carriers across interface. A possible photodegradation mechanism of MB in the presence of TiO2/BiVO4 microfibrous photocatalyst was proposed.展开更多
Monoclinic BiVO4 hollow nanospheres were successfully prepared via template-free method using citric acid （C6H8O7） as chelating agent and characterized by X-ray diffraction patterns, transmission electron microscope...Monoclinic BiVO4 hollow nanospheres were successfully prepared via template-free method using citric acid （C6H8O7） as chelating agent and characterized by X-ray diffraction patterns, transmission electron microscope, UV-Vis DRS, and TG-DTA technique. C6H8O7 played an important role in the formation of hollow spheres. Morphology observations revealed that when appropriate amount of C6H8O7 was introduced, the cavity with the diameter of 40 nm was obtained in BiVO4 nanospheres. UV-Vis diffuse reflectance spectra indicated that the samples had absorption in both UV and visible light region. The photocatalytic activities were evaluated by the degradation of methylene blue under Xe lamp irradiation. Hollow spheres endow BiVO4 samples with greatly improved photocatalytic activity. A possible formation mechanism of hollow spheres was proposed.展开更多
基金This work was supported by Program Funded by Sha.anxi Department （No.2013JK0690）, the Scientific Research Provincial Education Fundamental Research Funds of Xianyang Normal University （No. 14XSYK011, No.12XSYK025）, Shaanxi Province Natural Science Foundation （No.2015JQ5188）.
文摘Novel TiO2/BiVO4 microfiber heterojunctions were constructed using cotton as biomorphic templates. The as-synthesized samples were characterized by scanning electron microscope, X-ray diffraction, X-ray photoelectron spectroscopy, UV-Vis diffuse reflectance spectra and photocatalytic experiment. The morphology of the as-synthesized TiO2/BiVO4 composites was consisted of a large quantity of microfiber structures with diameter from 2.5 gm to 5 μm, and the surface of samples became more coarse and compact with the increase of weight ratio of TiO2. The TiO2/BiVO4 samples with proper content （10.00wt%） showed the highest pho- tocatalytic degradation activity for methylene blue （MB） degradation among all the samples under visible light, and 88.58%MB could be degraded within 150 min. The enhancement of photocatalytic activity was mainly attributed to the formation of n-n heterojunction at the contact interface of TiO2 and BiVO4, which not only narrowed the band gap of BiVO4 for extending the absorption range of visible light, but also promoted the transfer of charge carriers across interface. A possible photodegradation mechanism of MB in the presence of TiO2/BiVO4 microfibrous photocatalyst was proposed.
基金National Natural Science Foundation of China(51172135)The Program of Shaanxi Natural Science(2010JM6013)+1 种基金National Youth Science Foundation(51002092)the Graduate Innovation Found of Shaanxi University of Science and Technology(SUST-A04)
文摘Monoclinic BiVO4 hollow nanospheres were successfully prepared via template-free method using citric acid （C6H8O7） as chelating agent and characterized by X-ray diffraction patterns, transmission electron microscope, UV-Vis DRS, and TG-DTA technique. C6H8O7 played an important role in the formation of hollow spheres. Morphology observations revealed that when appropriate amount of C6H8O7 was introduced, the cavity with the diameter of 40 nm was obtained in BiVO4 nanospheres. UV-Vis diffuse reflectance spectra indicated that the samples had absorption in both UV and visible light region. The photocatalytic activities were evaluated by the degradation of methylene blue under Xe lamp irradiation. Hollow spheres endow BiVO4 samples with greatly improved photocatalytic activity. A possible formation mechanism of hollow spheres was proposed.