V2O5/WO3‐TiO2 and V2O5/WO3‐TiO2‐SiO2 catalysts were prepared by a wetness impregnation method, and both the catalysts were hydrothermally aged at 750℃ in 10 vol%H2O/air for 24 h. The catalysts were evaluated for N...V2O5/WO3‐TiO2 and V2O5/WO3‐TiO2‐SiO2 catalysts were prepared by a wetness impregnation method, and both the catalysts were hydrothermally aged at 750℃ in 10 vol%H2O/air for 24 h. The catalysts were evaluated for NOx conversion using NH3 as the reductant. Hydrothermal ageing decreased the NOx conversion of V2O5/WO3‐TiO2 catalyst severely over the entire measured tem‐perature range. Interestingly, the NH3‐SCR activity of the silica‐modified catalyst at 220–480℃ is enhanced after ageing. The catalysts were characterized by X‐ray diffraction, nitrogen adsorption, X‐ray fluorescence, Raman spectroscopy, H2 temperature‐programmed reduction, and NH3 temper‐ature‐programmed desorption. The addition of silica inhibited the phase transition from anatase to rutile titania, growth of TiO2 crystallite size and shrinkage of catalyst surface area. Consequently, the vanadia species remained highly dispersed and the hydrothermal stability of the V2O5/WO3‐TiO2 catalyst was significantly improved.展开更多
Doping modification is one of the most effective ways to optimize the thermoelectric properties of Bi_(2)Te_(3)-based alloys.P-type Bi_(2−x)Sb_(x)Te_(3) thermoelectric materials have been successfully prepared by dire...Doping modification is one of the most effective ways to optimize the thermoelectric properties of Bi_(2)Te_(3)-based alloys.P-type Bi_(2−x)Sb_(x)Te_(3) thermoelectric materials have been successfully prepared by direct Sb doping method.It can be found that doping Sb into Bi_(2)Te_(3) lattice array for Bi-site replacement facilitates the generation of Sb′Te anti-site defects.This anti-site defects can increase the hole concentration and optimize electrical transport properties of Bi_(2−x)Sb_(x)Te_(3) alloys.In addition,the point defects induced by mass and stress fluctuations and the Sb impurities produced during the sintering process can enhance the multi-scale phonon scattering and reduce the lattice thermal conductivity.As a result,the Bi_(0.47)Sb_(1.63)Te_(3) sample has a maximum thermoelectric figure of merit ZT of 1.04 at 350 K.It is worth noting that the bipolar effect of Bi_(2)Te_(3)-based alloys can be weakened with the increase of Sb content.The Bi_(0.44)Sb_(1.66)Te_(3) sample has a maximum average ZT value(0.93)in the temperature range of 300–500 K,indicating that direct doping of Sb can broaden the temperature range corresponding to the optimal ZT value.This work provides an idea for developing high-performance near room temperature thermoelectric materials with a wide temperature range.展开更多
The development of high-performance cathode materials is critical to the practical application of sodiumion batteries(SIBs).O3-type NaCrO_(2)(NCO)is one of the most competitive cathodes,but it suffers from rapid capac...The development of high-performance cathode materials is critical to the practical application of sodiumion batteries(SIBs).O3-type NaCrO_(2)(NCO)is one of the most competitive cathodes,but it suffers from rapid capacity decay caused by severe irreversible structural evolution.An Mg-Ti co-doped Na_(0.99)Cr_(0.95)Mg_(0.02)Ti_(0.03)O_(2)(NCO-MT)cathode material is designed and synthesized via a facile solid-state reaction to enhance the cyclability of NCO.A capacity retention of 71.6%after 2500 cycles with the capacity fade rate of 0.011%per cycle is achieved for NCO-MT at 5 C,which is attributed to the highly reversible crystal structure during cycling.Our findings offer a novel insight into the high-performance O3-type layered cathode materials for SIBs and are beneficial to promote the development of high-rate SIBs.展开更多
In this work,the TiO_(2)/Sb_(2)S_(3) nanorod arrays(NRAs)were synthesized through a two-stage hydrothermal route for photoelectrochemical(PEC)water splitting.The effect of annealing treatment in Ar ambience on the PEC...In this work,the TiO_(2)/Sb_(2)S_(3) nanorod arrays(NRAs)were synthesized through a two-stage hydrothermal route for photoelectrochemical(PEC)water splitting.The effect of annealing treatment in Ar ambience on the PEC activity of TiO_(2)/Sb_(2)S_(3) composite sample was investigated by electrochemical impedance analysis,including Nyquist and Mott-Schottky(M-S)plots.It was demonstrated that vacuum annealing could crystallize Sb_(2)S_(3) component and change its color from red to black,leading to an increment of photocurrent density from 1.9 A/m^(2) to 4.25 A/m^(2) at 0 V versus saturated calomel electrode(VSCE).The enhanced PEC performance was mainly attributed to the improved visible light absorption.Moreover,annealing treatment facilitated retarding the electron-hole recombination occurred at the solid/liquid interfaces.Our work might provide a novel strategy for enhancing the PEC performance of a semiconductor electrode.展开更多
The selective catalytic reduction of NOV with NH3 (NH3-SCR) is a very effective technology to control the emission of NOA, and the thermal stability of NH3-SCR catalyst is very important for removal of NOV from diesel...The selective catalytic reduction of NOV with NH3 (NH3-SCR) is a very effective technology to control the emission of NOA, and the thermal stability of NH3-SCR catalyst is very important for removal of NOV from diesel engines. In this work, V2O5/WO3-TiO2 (VWT) and SiO2- doped V2O5/WO3-TiO2 (VWTSi10)) catalysts were prepared by impregnation method and characterized by Brunauer- Emmett-Teller (BET), X-ray diffraction (XRD), Raman, temperature programmed reduction by hydrogen (H2-TPR), X-ray photoelectron spectroscopy (XPS) and temperature programmed desorption by ammonia (NH3- TPD). The doping of SiO2 promotes the thermal stability of V2O5/WO3-TiO? for NH3-SCR significantly. After calcination at 650 °C for 50 h, the operation window of 10% SiO2-doped V2O5/WO3-TiO2 is 220-480 °C, while the maximum NOV conversion on V2O5/WO3-TiO2 is about 77%. The presenee of SiO2 obviously blocks the transformation of TiO2 from anatase to rutile and stabilizes the dispersion of VOv and WO3 on the surface. It is available for the existence of V44 and the amount of surface acid sites increases, which inhabits the NH3 oxidation at the high temperature range and promotes NH3-SCR activity.展开更多
基金supported by the National Natural Science Foundation of China (51372137)the National High Technology Research and Development Program of China (863 Program,2015AA034603)~~
文摘V2O5/WO3‐TiO2 and V2O5/WO3‐TiO2‐SiO2 catalysts were prepared by a wetness impregnation method, and both the catalysts were hydrothermally aged at 750℃ in 10 vol%H2O/air for 24 h. The catalysts were evaluated for NOx conversion using NH3 as the reductant. Hydrothermal ageing decreased the NOx conversion of V2O5/WO3‐TiO2 catalyst severely over the entire measured tem‐perature range. Interestingly, the NH3‐SCR activity of the silica‐modified catalyst at 220–480℃ is enhanced after ageing. The catalysts were characterized by X‐ray diffraction, nitrogen adsorption, X‐ray fluorescence, Raman spectroscopy, H2 temperature‐programmed reduction, and NH3 temper‐ature‐programmed desorption. The addition of silica inhibited the phase transition from anatase to rutile titania, growth of TiO2 crystallite size and shrinkage of catalyst surface area. Consequently, the vanadia species remained highly dispersed and the hydrothermal stability of the V2O5/WO3‐TiO2 catalyst was significantly improved.
基金supported by the Anhui Province Natural Science Foundation for Excellent Youth Scholars(2208085Y17)the University Synergy Innovation Program of Anhui Province(GXXT-2022-008+1 种基金GXXT-2021-022)the Anhui Key Lab of Metal Material and Processing Open Project.
文摘Doping modification is one of the most effective ways to optimize the thermoelectric properties of Bi_(2)Te_(3)-based alloys.P-type Bi_(2−x)Sb_(x)Te_(3) thermoelectric materials have been successfully prepared by direct Sb doping method.It can be found that doping Sb into Bi_(2)Te_(3) lattice array for Bi-site replacement facilitates the generation of Sb′Te anti-site defects.This anti-site defects can increase the hole concentration and optimize electrical transport properties of Bi_(2−x)Sb_(x)Te_(3) alloys.In addition,the point defects induced by mass and stress fluctuations and the Sb impurities produced during the sintering process can enhance the multi-scale phonon scattering and reduce the lattice thermal conductivity.As a result,the Bi_(0.47)Sb_(1.63)Te_(3) sample has a maximum thermoelectric figure of merit ZT of 1.04 at 350 K.It is worth noting that the bipolar effect of Bi_(2)Te_(3)-based alloys can be weakened with the increase of Sb content.The Bi_(0.44)Sb_(1.66)Te_(3) sample has a maximum average ZT value(0.93)in the temperature range of 300–500 K,indicating that direct doping of Sb can broaden the temperature range corresponding to the optimal ZT value.This work provides an idea for developing high-performance near room temperature thermoelectric materials with a wide temperature range.
基金financially supported by National Key Research and Development Program of China(No.2022YFE0202400)the National Natural Science Foundation of China(No.22379103)+2 种基金Natural Science Foundation of Guangdong Province of China(No.2021A1515010388)the Science and Technology Projects of Suzhou City(No.SYC2022043)the Qing Lan Project of Jiangsu Province(2022)。
文摘The development of high-performance cathode materials is critical to the practical application of sodiumion batteries(SIBs).O3-type NaCrO_(2)(NCO)is one of the most competitive cathodes,but it suffers from rapid capacity decay caused by severe irreversible structural evolution.An Mg-Ti co-doped Na_(0.99)Cr_(0.95)Mg_(0.02)Ti_(0.03)O_(2)(NCO-MT)cathode material is designed and synthesized via a facile solid-state reaction to enhance the cyclability of NCO.A capacity retention of 71.6%after 2500 cycles with the capacity fade rate of 0.011%per cycle is achieved for NCO-MT at 5 C,which is attributed to the highly reversible crystal structure during cycling.Our findings offer a novel insight into the high-performance O3-type layered cathode materials for SIBs and are beneficial to promote the development of high-rate SIBs.
基金supported by the Fundamental Research Funds for the Central Universities(No.2019ZDPY04).
文摘In this work,the TiO_(2)/Sb_(2)S_(3) nanorod arrays(NRAs)were synthesized through a two-stage hydrothermal route for photoelectrochemical(PEC)water splitting.The effect of annealing treatment in Ar ambience on the PEC activity of TiO_(2)/Sb_(2)S_(3) composite sample was investigated by electrochemical impedance analysis,including Nyquist and Mott-Schottky(M-S)plots.It was demonstrated that vacuum annealing could crystallize Sb_(2)S_(3) component and change its color from red to black,leading to an increment of photocurrent density from 1.9 A/m^(2) to 4.25 A/m^(2) at 0 V versus saturated calomel electrode(VSCE).The enhanced PEC performance was mainly attributed to the improved visible light absorption.Moreover,annealing treatment facilitated retarding the electron-hole recombination occurred at the solid/liquid interfaces.Our work might provide a novel strategy for enhancing the PEC performance of a semiconductor electrode.
基金financially supported by the National Key Research and Development Program of China (No. 2016YFC0204300)the National High Technology Research and Development Program of China (No. 2015AA034603)+2 种基金the National Natural Science Foundation of China (Nos. 21333003 and 21571061)the "Shu Guang" Project of the Shanghai Municipal Education Commission (No. 12SG29)the Commission of Science and Technology of Shanghai Municipality (No. 15DZ1205305)
文摘The selective catalytic reduction of NOV with NH3 (NH3-SCR) is a very effective technology to control the emission of NOA, and the thermal stability of NH3-SCR catalyst is very important for removal of NOV from diesel engines. In this work, V2O5/WO3-TiO2 (VWT) and SiO2- doped V2O5/WO3-TiO2 (VWTSi10)) catalysts were prepared by impregnation method and characterized by Brunauer- Emmett-Teller (BET), X-ray diffraction (XRD), Raman, temperature programmed reduction by hydrogen (H2-TPR), X-ray photoelectron spectroscopy (XPS) and temperature programmed desorption by ammonia (NH3- TPD). The doping of SiO2 promotes the thermal stability of V2O5/WO3-TiO? for NH3-SCR significantly. After calcination at 650 °C for 50 h, the operation window of 10% SiO2-doped V2O5/WO3-TiO2 is 220-480 °C, while the maximum NOV conversion on V2O5/WO3-TiO2 is about 77%. The presenee of SiO2 obviously blocks the transformation of TiO2 from anatase to rutile and stabilizes the dispersion of VOv and WO3 on the surface. It is available for the existence of V44 and the amount of surface acid sites increases, which inhabits the NH3 oxidation at the high temperature range and promotes NH3-SCR activity.