Studies on ultrafine particle catalyst have attracted many researchers' attention by its large surface area,higher activity and selectivity.Based on the mechanism of α-Fe and Fe_xC_y as the catalytical active spe...Studies on ultrafine particle catalyst have attracted many researchers' attention by its large surface area,higher activity and selectivity.Based on the mechanism of α-Fe and Fe_xC_y as the catalytical active species this paper reports for the first time the preparation method of Fe_3C ultrafine parti- cle catalyst,from highly dispersed amorphous Fe powder and free carbon.The Fe powder and free car- bon,prepared by laser pyrolysis technique,was then treated by washing and heating at high tempera- ture protected with N_2.The catalyst prepared under different experimental conditions was characterazed by means of XRD,electronic diffraction and TEM.It shows that the crystlline grain size is in a range of 1-4nm and composed of Fe_3C and α-Fe.It has been found that the ultrafine particle iron-carbonide catalyst exhibited much higher activity and selectivity to light olefins.At the standard atmosphere and 380℃ reaction temperature,the conversion of CO reached a maximum of 80%.展开更多
A series of x （Fe,Ni）/Al2O3 catalysts （x = 2-12 wt%） were prepared using incipient wetness method and studied for the conversion of synthesis gas to light olefins.6 wt%（Fe,Ni）/Al2O3 catalyst was found to be the ...A series of x （Fe,Ni）/Al2O3 catalysts （x = 2-12 wt%） were prepared using incipient wetness method and studied for the conversion of synthesis gas to light olefins.6 wt%（Fe,Ni）/Al2O3 catalyst was found to be the optimal catalyst for the production of C2-C4 olefins.The effects of calcination behaviors and operational conditions on the catalytic performance of the optimal catalyst were investigated.The best operational conditions were molar feed ratio H2/CO = 2/1,T = 260 ℃,gas hourly space velocity （GHSV） = 2600 h^-1 and the pressure of 3 bar.Character-izations of both precursors and catalysts were carried out using X-ray diffraction （XRD）,temperature-programmed reduction （TPR）,scanning electron microscopy （SEM）,N2-adsorption-desorption measurement,thermal gravimetric analysis （TGA） and differential scanning calorimetry （DSC）.展开更多
The three-parameter Petal-Teja equation of state coupled with a characterization proceduref0r C<sub>7+</sub>-fraction based on gamma distribution function was employed to predict the phase behaviorof eight...The three-parameter Petal-Teja equation of state coupled with a characterization proceduref0r C<sub>7+</sub>-fraction based on gamma distribution function was employed to predict the phase behaviorof eight gas condensates.The lumping of the subdivided single carbon number（SCN）hydrocarbons inthe plus-fraction and the choice of empirical correlations for calculating the critical properties andacentric factor of SCN hydrocarbons were discussed.展开更多
Size effects make traditional bending theories infeasible in analyzing the springback behavior of H80 foils in the similarity bending experiment. It is observed that there is a certain critical thickness value, which ...Size effects make traditional bending theories infeasible in analyzing the springback behavior of H80 foils in the similarity bending experiment. It is observed that there is a certain critical thickness value, which divides the change trend of springback amount of foils into two opposite parts. In order to reveal the reason for size effects on the springback behavior of H80 foils, the method of hardness increment characterization was applied to describe the deformation distribution of foils. The competition between strengthening effect of geometrically necessary dislocations and weakening effect of surface grains determines the change trend of springback amount with foil thickness. When the thickness of foils is large, the weakening effects dominate the material behavior, resulting in that the springback amount decreases with the decrease in foil thickness. However, when the foil thickness is small, the strengthening effects dominate the springback tendency, leading to a sharp increase in the springback amount. Furthermore, the deformation distribution is disturbed due to the enhanced effects of individual grain heterogeneity with the decrease in the thickness of foils, leading to the large scatter of springback angle after unloading.展开更多
By introducing a vibrating force field into the extrusion process of polymer melt, an experimental equipment of constant velocity type dynamic rheometer of capillary (CVDRC) was designed. A set of experimental procedu...By introducing a vibrating force field into the extrusion process of polymer melt, an experimental equipment of constant velocity type dynamic rheometer of capillary (CVDRC) was designed. A set of experimental procedures was established, by which the dynamic rheological parameters of polymer can be acquired, and a set of data management methods to undergo time-domain or frequency-domain analysis was set up for dynamic rheological data of polymer melt. Meantime, the characterization formula of polymer melt's rheological behavior in a vibrating force field was set up. The instantaneous value of capillary entry pressure, capillary volume flow rate and their phase difference were measured and analyzed, and the melt apparent viscosity, which describes the rheological behavior of polymer melt in a vibrating force field, was obtained.展开更多
The stress–strain behavior and strain rate sensitivity of pre-strained Ni80Cr20（Ni20Cr） were studied at strain rates from 4.8×10^（–4）s^（–1） to 1.1×10^（–1）s^（–1）. Specimens were prepared throug...The stress–strain behavior and strain rate sensitivity of pre-strained Ni80Cr20（Ni20Cr） were studied at strain rates from 4.8×10^（–4）s^（–1） to 1.1×10^（–1）s^（–1）. Specimens were prepared through cold drawing with abnormal plastic deformation. The texture of the specimen was characterized using electron backscatter diffraction. Results revealed that the ultimate tensile strength and ductility of the pre-strained Ni20Cr microwires simultaneously increased with increasing strain rate. Twinning-induced negative strain rate sensitivity was discovered. Positive strain rate sensitivity was present in fracture flow stress, whereas negative strain rate sensitivity was detected in flow stress values of σ_（0.5%） and σ_（1%）. Tensile test of the pre-strained Ni20Cr showed that twinning deformation predominated, whereas dislocation slip deformation dominated when twinning deformation reached saturation. The trends observed in the fractions of 2°-5°, 5°-15°, and 15°-180° grain boundaries confirmed that twinning deformation dominated the first stage.展开更多
A novel method for controlled synthesis of crystalline molybdenum dioxides nanowhiskers （whisker-MoO2） by using moderate reductive and precursor ion under hydrothermal conditions is reported. The result shows that t...A novel method for controlled synthesis of crystalline molybdenum dioxides nanowhiskers （whisker-MoO2） by using moderate reductive and precursor ion under hydrothermal conditions is reported. The result shows that the as-obtained samples have a monoclinic structure, and the whisker-MoO2 is composed of nanowires with diameters of ca. 20 nm. Formation of whisker-MoO2 was through a typical precursor-reduction process, in which cetyltrimethylammonium bromide （CTAB） served as a cationic surfactant and acetone as a reductant. The electrochemical behavior of whisker-MoO2 was studied.展开更多
为明确大豆分离蛋白(soy protein isolate,SPI)和κ-卡拉胶(κ-carrageenan,κ-CG)在不同pH及共混比条件下的相互作用,本研究通过浊度、Zeta电位、多光谱法和荧光猝灭等方法对SPI/κ-CG复合体系相行为、结构特性及结合机制进行了表征。...为明确大豆分离蛋白(soy protein isolate,SPI)和κ-卡拉胶(κ-carrageenan,κ-CG)在不同pH及共混比条件下的相互作用,本研究通过浊度、Zeta电位、多光谱法和荧光猝灭等方法对SPI/κ-CG复合体系相行为、结构特性及结合机制进行了表征。结果表明:随着pH降低(从8.0降至1.5),SPI/κ-CG复合溶液出现澄清、浑浊和相分离等不同的相行为;蛋白质/多糖质量比减小使相变临界pH(pH_(c)、pH_(φ1)、pH_(opt)和pH_(φ2))降低;SPI/κ-CG复合溶液在pH4.0即两者相互作用最强时表观粘度最高;κ-CG的加入使SPI三级结构发生改变,并且二级结构中β-折叠含量随pH降低呈现先增加后减小的趋势,而β-转角呈现先减小后增加的趋势;此外,荧光猝灭证明κ-CG对SPI为静态猝灭,两者具有较强的结合能力;热力学分析阐明了SPI与κ-CG相互作用由疏水相互作用和静电相互作用主导,是焓变驱动的自发反应。本研究揭示了SPI与κ-CG相互作用机制,为SPI/κ-CG复合物在食品领域的开发和应用提供了参考依据。展开更多
基金The project was supported by the National Natural Science Foundation of China.
文摘Studies on ultrafine particle catalyst have attracted many researchers' attention by its large surface area,higher activity and selectivity.Based on the mechanism of α-Fe and Fe_xC_y as the catalytical active species this paper reports for the first time the preparation method of Fe_3C ultrafine parti- cle catalyst,from highly dispersed amorphous Fe powder and free carbon.The Fe powder and free car- bon,prepared by laser pyrolysis technique,was then treated by washing and heating at high tempera- ture protected with N_2.The catalyst prepared under different experimental conditions was characterazed by means of XRD,electronic diffraction and TEM.It shows that the crystlline grain size is in a range of 1-4nm and composed of Fe_3C and α-Fe.It has been found that the ultrafine particle iron-carbonide catalyst exhibited much higher activity and selectivity to light olefins.At the standard atmosphere and 380℃ reaction temperature,the conversion of CO reached a maximum of 80%.
文摘A series of x （Fe,Ni）/Al2O3 catalysts （x = 2-12 wt%） were prepared using incipient wetness method and studied for the conversion of synthesis gas to light olefins.6 wt%（Fe,Ni）/Al2O3 catalyst was found to be the optimal catalyst for the production of C2-C4 olefins.The effects of calcination behaviors and operational conditions on the catalytic performance of the optimal catalyst were investigated.The best operational conditions were molar feed ratio H2/CO = 2/1,T = 260 ℃,gas hourly space velocity （GHSV） = 2600 h^-1 and the pressure of 3 bar.Character-izations of both precursors and catalysts were carried out using X-ray diffraction （XRD）,temperature-programmed reduction （TPR）,scanning electron microscopy （SEM）,N2-adsorption-desorption measurement,thermal gravimetric analysis （TGA） and differential scanning calorimetry （DSC）.
文摘The three-parameter Petal-Teja equation of state coupled with a characterization proceduref0r C<sub>7+</sub>-fraction based on gamma distribution function was employed to predict the phase behaviorof eight gas condensates.The lumping of the subdivided single carbon number（SCN）hydrocarbons inthe plus-fraction and the choice of empirical correlations for calculating the critical properties andacentric factor of SCN hydrocarbons were discussed.
基金financially supported by the Foundation of Suzhou University of Science and Technology(No.XKQ2017005)
文摘Size effects make traditional bending theories infeasible in analyzing the springback behavior of H80 foils in the similarity bending experiment. It is observed that there is a certain critical thickness value, which divides the change trend of springback amount of foils into two opposite parts. In order to reveal the reason for size effects on the springback behavior of H80 foils, the method of hardness increment characterization was applied to describe the deformation distribution of foils. The competition between strengthening effect of geometrically necessary dislocations and weakening effect of surface grains determines the change trend of springback amount with foil thickness. When the thickness of foils is large, the weakening effects dominate the material behavior, resulting in that the springback amount decreases with the decrease in foil thickness. However, when the foil thickness is small, the strengthening effects dominate the springback tendency, leading to a sharp increase in the springback amount. Furthermore, the deformation distribution is disturbed due to the enhanced effects of individual grain heterogeneity with the decrease in the thickness of foils, leading to the large scatter of springback angle after unloading.
文摘By introducing a vibrating force field into the extrusion process of polymer melt, an experimental equipment of constant velocity type dynamic rheometer of capillary (CVDRC) was designed. A set of experimental procedures was established, by which the dynamic rheological parameters of polymer can be acquired, and a set of data management methods to undergo time-domain or frequency-domain analysis was set up for dynamic rheological data of polymer melt. Meantime, the characterization formula of polymer melt's rheological behavior in a vibrating force field was set up. The instantaneous value of capillary entry pressure, capillary volume flow rate and their phase difference were measured and analyzed, and the melt apparent viscosity, which describes the rheological behavior of polymer melt in a vibrating force field, was obtained.
基金Funded by the National Natural Science Foundation of China(No.11135007)
文摘The stress–strain behavior and strain rate sensitivity of pre-strained Ni80Cr20（Ni20Cr） were studied at strain rates from 4.8×10^（–4）s^（–1） to 1.1×10^（–1）s^（–1）. Specimens were prepared through cold drawing with abnormal plastic deformation. The texture of the specimen was characterized using electron backscatter diffraction. Results revealed that the ultimate tensile strength and ductility of the pre-strained Ni20Cr microwires simultaneously increased with increasing strain rate. Twinning-induced negative strain rate sensitivity was discovered. Positive strain rate sensitivity was present in fracture flow stress, whereas negative strain rate sensitivity was detected in flow stress values of σ_（0.5%） and σ_（1%）. Tensile test of the pre-strained Ni20Cr showed that twinning deformation predominated, whereas dislocation slip deformation dominated when twinning deformation reached saturation. The trends observed in the fractions of 2°-5°, 5°-15°, and 15°-180° grain boundaries confirmed that twinning deformation dominated the first stage.
基金This work was financially supported by the National Natural Science Foundation of China （No.20271001）.
文摘A novel method for controlled synthesis of crystalline molybdenum dioxides nanowhiskers （whisker-MoO2） by using moderate reductive and precursor ion under hydrothermal conditions is reported. The result shows that the as-obtained samples have a monoclinic structure, and the whisker-MoO2 is composed of nanowires with diameters of ca. 20 nm. Formation of whisker-MoO2 was through a typical precursor-reduction process, in which cetyltrimethylammonium bromide （CTAB） served as a cationic surfactant and acetone as a reductant. The electrochemical behavior of whisker-MoO2 was studied.
文摘为明确大豆分离蛋白(soy protein isolate,SPI)和κ-卡拉胶(κ-carrageenan,κ-CG)在不同pH及共混比条件下的相互作用,本研究通过浊度、Zeta电位、多光谱法和荧光猝灭等方法对SPI/κ-CG复合体系相行为、结构特性及结合机制进行了表征。结果表明:随着pH降低(从8.0降至1.5),SPI/κ-CG复合溶液出现澄清、浑浊和相分离等不同的相行为;蛋白质/多糖质量比减小使相变临界pH(pH_(c)、pH_(φ1)、pH_(opt)和pH_(φ2))降低;SPI/κ-CG复合溶液在pH4.0即两者相互作用最强时表观粘度最高;κ-CG的加入使SPI三级结构发生改变,并且二级结构中β-折叠含量随pH降低呈现先增加后减小的趋势,而β-转角呈现先减小后增加的趋势;此外,荧光猝灭证明κ-CG对SPI为静态猝灭,两者具有较强的结合能力;热力学分析阐明了SPI与κ-CG相互作用由疏水相互作用和静电相互作用主导,是焓变驱动的自发反应。本研究揭示了SPI与κ-CG相互作用机制,为SPI/κ-CG复合物在食品领域的开发和应用提供了参考依据。