V2O5/WO3‐TiO2 and V2O5/WO3‐TiO2‐SiO2 catalysts were prepared by a wetness impregnation method, and both the catalysts were hydrothermally aged at 750℃ in 10 vol%H2O/air for 24 h. The catalysts were evaluated for N...V2O5/WO3‐TiO2 and V2O5/WO3‐TiO2‐SiO2 catalysts were prepared by a wetness impregnation method, and both the catalysts were hydrothermally aged at 750℃ in 10 vol%H2O/air for 24 h. The catalysts were evaluated for NOx conversion using NH3 as the reductant. Hydrothermal ageing decreased the NOx conversion of V2O5/WO3‐TiO2 catalyst severely over the entire measured tem‐perature range. Interestingly, the NH3‐SCR activity of the silica‐modified catalyst at 220–480℃ is enhanced after ageing. The catalysts were characterized by X‐ray diffraction, nitrogen adsorption, X‐ray fluorescence, Raman spectroscopy, H2 temperature‐programmed reduction, and NH3 temper‐ature‐programmed desorption. The addition of silica inhibited the phase transition from anatase to rutile titania, growth of TiO2 crystallite size and shrinkage of catalyst surface area. Consequently, the vanadia species remained highly dispersed and the hydrothermal stability of the V2O5/WO3‐TiO2 catalyst was significantly improved.展开更多
The selective catalytic reduction of NOV with NH3 (NH3-SCR) is a very effective technology to control the emission of NOA, and the thermal stability of NH3-SCR catalyst is very important for removal of NOV from diesel...The selective catalytic reduction of NOV with NH3 (NH3-SCR) is a very effective technology to control the emission of NOA, and the thermal stability of NH3-SCR catalyst is very important for removal of NOV from diesel engines. In this work, V2O5/WO3-TiO2 (VWT) and SiO2- doped V2O5/WO3-TiO2 (VWTSi10)) catalysts were prepared by impregnation method and characterized by Brunauer- Emmett-Teller (BET), X-ray diffraction (XRD), Raman, temperature programmed reduction by hydrogen (H2-TPR), X-ray photoelectron spectroscopy (XPS) and temperature programmed desorption by ammonia (NH3- TPD). The doping of SiO2 promotes the thermal stability of V2O5/WO3-TiO? for NH3-SCR significantly. After calcination at 650 °C for 50 h, the operation window of 10% SiO2-doped V2O5/WO3-TiO2 is 220-480 °C, while the maximum NOV conversion on V2O5/WO3-TiO2 is about 77%. The presenee of SiO2 obviously blocks the transformation of TiO2 from anatase to rutile and stabilizes the dispersion of VOv and WO3 on the surface. It is available for the existence of V44 and the amount of surface acid sites increases, which inhabits the NH3 oxidation at the high temperature range and promotes NH3-SCR activity.展开更多
The lack of thermodynamic information,such as primary phase fields and liquidus temperatures,in the CaO-SiO2-Nb2O5-La2O3 quaternary system phase diagram has restricted the comprehensive utilization of the niobium(Nb) ...The lack of thermodynamic information,such as primary phase fields and liquidus temperatures,in the CaO-SiO2-Nb2O5-La2O3 quaternary system phase diagram has restricted the comprehensive utilization of the niobium(Nb) and rare earth(RE) resources.In this work,the phase equilibria in low basicity region(w(CaO)/w(SiO2)<1) of CaO-SiO2-Nb2O5-(0-15 wt%)La2O3 system at 1373-1873 K were experimentally studied by thermodynamic equilibrium experiment,and then,the results were analyzed by X-ray diffraction(XRD),scanning electron microscopy(SEM),and energy dispersive spectrometry(EDS).Additionally,an optimized method was proposed to process the compositions of equilibrium liquid phases at different temperatures.According to the experimental results,the univariate line between CaNb2O6,SiO2 and LaNbO4 primary phase fields,interface between CaNb2O6 and SiO2 primary phase fields and isothermal liquidus surfaces in SiO2 primary phase field were determined.Finally,the spatial phase diagram of CaO-SiO2-Nb2O5-La2O3 within specific region was constructed,and furthermore,the phase diagram was also presented in CaO-SiO2-Nb2O5 pseudo-ternary system with w(La2O3)=5 wt%,10 wt% and 15 wt%.The research results have guiding significance for the improvement of related phase diagram and the comprehensive utilization of Nb and RE resources.展开更多
A lithium ion conductive solid electrolyte, L20-AI203-TiO2-SiO2-P20s glass with NASICON- type structure have been synthesized and transformed into glass-ceramic through thermal-treatment at various temperatures from 7...A lithium ion conductive solid electrolyte, L20-AI203-TiO2-SiO2-P20s glass with NASICON- type structure have been synthesized and transformed into glass-ceramic through thermal-treatment at various temperatures from 700 to 1 000 ~C for 12 h. The differential scanning calorimetry （DSC）, X-ray diffraction （XRD）, scanning electron microscopy （SEM） and complex impedance techniques were employed to characterize the samples. The experimental results indicated that the capability of glass forming in this system is superior to that of L20-A1203-TiO2-PzO~. The glass has an amorphous structure and resultant glass-ceramic mainly consisting of LiTi2（PO4）3 phases. Impurity phases AIPO4, TiO2, TiP207 and unidentified phase were observed. With the enhanced heat-treatment temperature, grain grew gradually and lithium ion conductivity of glass-ceramics increased accordingly, the related impedance semicircles were depressed gradually and even disappeared, which could be analytically explained by the coordinate action of the ＇Constant phase element＇ （CPE） model and the ＇Concept of Mismatch and Relaxation＇ model （CMR）. When the sample is devitrified at 1 000 ~C, the maximum room temperature lithium ion conductivity comes up to 4.1 x 10-4 S/cm, which is suitable for the application as an electrolyte of all-solid-state lithium batteries.展开更多
The present work aimed to explore a kind of microwave dielectric materials with middle-permittivity, high Qf, near-zero τf, and lower sintering temperature. A series of Y2Ti2O7 microwave dielectric ceramics were synt...The present work aimed to explore a kind of microwave dielectric materials with middle-permittivity, high Qf, near-zero τf, and lower sintering temperature. A series of Y2Ti2O7 microwave dielectric ceramics were synthesized by conventional solid-state method. For improving the dielectric properties of Y2Ti2O7 system, Bi2O3, Nd2O3 and Nb2O5 were added and their effects on phase composition, micro-structure, and dielectric properties at microwave frequencies were investigated by means of X-ray diffraction （XRD） and scanning electron microscopy （SEM）. The queuing score method for multi-target orthogonal design was used to obtain the optimum prescription. The results showed that the Y2Ti2O7 ceramics with 8 wt.% Bi2O3 and 1 mol.% Nd2O3-Nb2O5 were well sintered at 1350 ℃, exhibiting excellent dielectric characteristics, i.e. εr≈76, Qf≈18980 GHz, τf =＋25.5 ppm/℃.展开更多
A series of new microwave dielectric ceramics Ba3-nLa1+nTinNb3-nO12 (n=0,1,2) were prepared in the BaO-La2O3-TiO2-Nb2O5 system by high temperature solid-state reaction route. The phase and structure of the ceramics we...A series of new microwave dielectric ceramics Ba3-nLa1+nTinNb3-nO12 (n=0,1,2) were prepared in the BaO-La2O3-TiO2-Nb2O5 system by high temperature solid-state reaction route. The phase and structure of the ceramics were characterized by X-ray diffraction, scanning electron microscope, and microwave dielectric properties measurements. These samples were identified as single phase and adopted A4B3O12-type cation-deficient hexagonal perovskite structure, which can be described as consisting of identical perovskite-like blocks, three corner-sharing BO6 octahedra thick, separated by layers of vacant octahedral. These ceramics have high dielectric constants in the range of 48-42, high quality factors (Q×f) up to 38 000 GHz, and low temperature coefficient of resonant frequencies (τf) in the range of (-40-+6)×10-6℃-1. With increasing content of La and Ti, the dielectric constants slightly decrease butτf gradually increases.展开更多
基金supported by the National Natural Science Foundation of China (51372137)the National High Technology Research and Development Program of China (863 Program,2015AA034603)~~
文摘V2O5/WO3‐TiO2 and V2O5/WO3‐TiO2‐SiO2 catalysts were prepared by a wetness impregnation method, and both the catalysts were hydrothermally aged at 750℃ in 10 vol%H2O/air for 24 h. The catalysts were evaluated for NOx conversion using NH3 as the reductant. Hydrothermal ageing decreased the NOx conversion of V2O5/WO3‐TiO2 catalyst severely over the entire measured tem‐perature range. Interestingly, the NH3‐SCR activity of the silica‐modified catalyst at 220–480℃ is enhanced after ageing. The catalysts were characterized by X‐ray diffraction, nitrogen adsorption, X‐ray fluorescence, Raman spectroscopy, H2 temperature‐programmed reduction, and NH3 temper‐ature‐programmed desorption. The addition of silica inhibited the phase transition from anatase to rutile titania, growth of TiO2 crystallite size and shrinkage of catalyst surface area. Consequently, the vanadia species remained highly dispersed and the hydrothermal stability of the V2O5/WO3‐TiO2 catalyst was significantly improved.
基金financially supported by the National Key Research and Development Program of China (No. 2016YFC0204300)the National High Technology Research and Development Program of China (No. 2015AA034603)+2 种基金the National Natural Science Foundation of China (Nos. 21333003 and 21571061)the "Shu Guang" Project of the Shanghai Municipal Education Commission (No. 12SG29)the Commission of Science and Technology of Shanghai Municipality (No. 15DZ1205305)
文摘The selective catalytic reduction of NOV with NH3 (NH3-SCR) is a very effective technology to control the emission of NOA, and the thermal stability of NH3-SCR catalyst is very important for removal of NOV from diesel engines. In this work, V2O5/WO3-TiO2 (VWT) and SiO2- doped V2O5/WO3-TiO2 (VWTSi10)) catalysts were prepared by impregnation method and characterized by Brunauer- Emmett-Teller (BET), X-ray diffraction (XRD), Raman, temperature programmed reduction by hydrogen (H2-TPR), X-ray photoelectron spectroscopy (XPS) and temperature programmed desorption by ammonia (NH3- TPD). The doping of SiO2 promotes the thermal stability of V2O5/WO3-TiO? for NH3-SCR significantly. After calcination at 650 °C for 50 h, the operation window of 10% SiO2-doped V2O5/WO3-TiO2 is 220-480 °C, while the maximum NOV conversion on V2O5/WO3-TiO2 is about 77%. The presenee of SiO2 obviously blocks the transformation of TiO2 from anatase to rutile and stabilizes the dispersion of VOv and WO3 on the surface. It is available for the existence of V44 and the amount of surface acid sites increases, which inhabits the NH3 oxidation at the high temperature range and promotes NH3-SCR activity.
基金Project supported by the National Key R&D Program of China(2017YFC0805100)the National Natural Science Foundation of China(51774087)the Fundamental Research Funds for the Central Universities China(N162506002)
文摘The lack of thermodynamic information,such as primary phase fields and liquidus temperatures,in the CaO-SiO2-Nb2O5-La2O3 quaternary system phase diagram has restricted the comprehensive utilization of the niobium(Nb) and rare earth(RE) resources.In this work,the phase equilibria in low basicity region(w(CaO)/w(SiO2)<1) of CaO-SiO2-Nb2O5-(0-15 wt%)La2O3 system at 1373-1873 K were experimentally studied by thermodynamic equilibrium experiment,and then,the results were analyzed by X-ray diffraction(XRD),scanning electron microscopy(SEM),and energy dispersive spectrometry(EDS).Additionally,an optimized method was proposed to process the compositions of equilibrium liquid phases at different temperatures.According to the experimental results,the univariate line between CaNb2O6,SiO2 and LaNbO4 primary phase fields,interface between CaNb2O6 and SiO2 primary phase fields and isothermal liquidus surfaces in SiO2 primary phase field were determined.Finally,the spatial phase diagram of CaO-SiO2-Nb2O5-La2O3 within specific region was constructed,and furthermore,the phase diagram was also presented in CaO-SiO2-Nb2O5 pseudo-ternary system with w(La2O3)=5 wt%,10 wt% and 15 wt%.The research results have guiding significance for the improvement of related phase diagram and the comprehensive utilization of Nb and RE resources.
基金National Basic Research Program of China (No.2009CB939704)National Natural Science Foundation of China (Nos.51032005, 60808024)the Fundamental Research Funds for the Central Universities (Wuhan University of Technology)
文摘A lithium ion conductive solid electrolyte, L20-AI203-TiO2-SiO2-P20s glass with NASICON- type structure have been synthesized and transformed into glass-ceramic through thermal-treatment at various temperatures from 700 to 1 000 ~C for 12 h. The differential scanning calorimetry （DSC）, X-ray diffraction （XRD）, scanning electron microscopy （SEM） and complex impedance techniques were employed to characterize the samples. The experimental results indicated that the capability of glass forming in this system is superior to that of L20-A1203-TiO2-PzO~. The glass has an amorphous structure and resultant glass-ceramic mainly consisting of LiTi2（PO4）3 phases. Impurity phases AIPO4, TiO2, TiP207 and unidentified phase were observed. With the enhanced heat-treatment temperature, grain grew gradually and lithium ion conductivity of glass-ceramics increased accordingly, the related impedance semicircles were depressed gradually and even disappeared, which could be analytically explained by the coordinate action of the ＇Constant phase element＇ （CPE） model and the ＇Concept of Mismatch and Relaxation＇ model （CMR）. When the sample is devitrified at 1 000 ~C, the maximum room temperature lithium ion conductivity comes up to 4.1 x 10-4 S/cm, which is suitable for the application as an electrolyte of all-solid-state lithium batteries.
基金supported by the Key University Science Research of Jiangsu Province (08KJA430002)the Priority Academic Program D velopment of Jiangsu Higher Education Institute
文摘The present work aimed to explore a kind of microwave dielectric materials with middle-permittivity, high Qf, near-zero τf, and lower sintering temperature. A series of Y2Ti2O7 microwave dielectric ceramics were synthesized by conventional solid-state method. For improving the dielectric properties of Y2Ti2O7 system, Bi2O3, Nd2O3 and Nb2O5 were added and their effects on phase composition, micro-structure, and dielectric properties at microwave frequencies were investigated by means of X-ray diffraction （XRD） and scanning electron microscopy （SEM）. The queuing score method for multi-target orthogonal design was used to obtain the optimum prescription. The results showed that the Y2Ti2O7 ceramics with 8 wt.% Bi2O3 and 1 mol.% Nd2O3-Nb2O5 were well sintered at 1350 ℃, exhibiting excellent dielectric characteristics, i.e. εr≈76, Qf≈18980 GHz, τf =＋25.5 ppm/℃.
基金Projects(50572078, 20571059) supported by the National Natural Science Foundation of China
文摘A series of new microwave dielectric ceramics Ba3-nLa1+nTinNb3-nO12 (n=0,1,2) were prepared in the BaO-La2O3-TiO2-Nb2O5 system by high temperature solid-state reaction route. The phase and structure of the ceramics were characterized by X-ray diffraction, scanning electron microscope, and microwave dielectric properties measurements. These samples were identified as single phase and adopted A4B3O12-type cation-deficient hexagonal perovskite structure, which can be described as consisting of identical perovskite-like blocks, three corner-sharing BO6 octahedra thick, separated by layers of vacant octahedral. These ceramics have high dielectric constants in the range of 48-42, high quality factors (Q×f) up to 38 000 GHz, and low temperature coefficient of resonant frequencies (τf) in the range of (-40-+6)×10-6℃-1. With increasing content of La and Ti, the dielectric constants slightly decrease butτf gradually increases.