The luminescent properties of glasses synthesized in air atmosphere by conventional high temperature process were studied. The emissions spectra of Eu2+ and Eu3+ were observed in BaO-La2O3-B2O3-Eu2O3 glasses. The resu...The luminescent properties of glasses synthesized in air atmosphere by conventional high temperature process were studied. The emissions spectra of Eu2+ and Eu3+ were observed in BaO-La2O3-B2O3-Eu2O3 glasses. The results show that the broad emission peaks at 430 nm correspond to 5d→4f emission transition of Eu2+, the sharp emission peaks at 592, 616, 650 and 750 nm correspond to 5D0→7Fj（j=1-4） emission transition of Eu3+, respectively, which indicates that the BaO-La2O3-B2O3-Eu2O3 glass can convert ultraviolet and green components of sunlight into blue and red light so as to increase the intensity of blue and red light, respectively. The luminescent intensity of Eu2+ increases with increasing the molar ratio of Tb3+ in BaO-La2O3-B2O3-Eu2O3-Tb4O7 glasses, whereas the luminescent intensity of Eu3+ decreases. So the luminescent intensity of Eu（III, II） is influenced by Tb3+. These phenomena can be explained by electron transfer mechanism: Eu3+（4f6）+Tb3+（4f8）→Eu2+（4f7）+Tb4+（4f7）. Taking advantage of the luminescent properties of BaO-La2O3-B2O3-Eu2O3 glasses, light-conversion glass for agriculture can be produced.展开更多
TiB_2 ceramics powder was synthesized from B_2O_3-TiO_2-Mg system. The effects of TiB_2 addition as diluent on the combustion synthesis process were investigated. The results of thermodynamic calculation and experimen...TiB_2 ceramics powder was synthesized from B_2O_3-TiO_2-Mg system. The effects of TiB_2 addition as diluent on the combustion synthesis process were investigated. The results of thermodynamic calculation and experiments show that the increase of TiB_2 content ranging from 0 to 20wt% can reduce the adiabatic temperature T_(ad) from 3100 K to 2896 K and combustion temperature T_c from 2139 K to 1621 K respectively. The particle size and half width of the particle distribution are also increased with the addition of TiB_2 increasing from 0 to 20wt%. The combustion product is a mixture of TiB_2, MgO, and other intermediate phases. The leached product contains mainly TiB_2, TiO_2 and TiN, and its oxygen content is 7.77wt%.展开更多
文摘The luminescent properties of glasses synthesized in air atmosphere by conventional high temperature process were studied. The emissions spectra of Eu2+ and Eu3+ were observed in BaO-La2O3-B2O3-Eu2O3 glasses. The results show that the broad emission peaks at 430 nm correspond to 5d→4f emission transition of Eu2+, the sharp emission peaks at 592, 616, 650 and 750 nm correspond to 5D0→7Fj（j=1-4） emission transition of Eu3+, respectively, which indicates that the BaO-La2O3-B2O3-Eu2O3 glass can convert ultraviolet and green components of sunlight into blue and red light so as to increase the intensity of blue and red light, respectively. The luminescent intensity of Eu2+ increases with increasing the molar ratio of Tb3+ in BaO-La2O3-B2O3-Eu2O3-Tb4O7 glasses, whereas the luminescent intensity of Eu3+ decreases. So the luminescent intensity of Eu（III, II） is influenced by Tb3+. These phenomena can be explained by electron transfer mechanism: Eu3+（4f6）+Tb3+（4f8）→Eu2+（4f7）+Tb4+（4f7）. Taking advantage of the luminescent properties of BaO-La2O3-B2O3-Eu2O3 glasses, light-conversion glass for agriculture can be produced.
文摘TiB_2 ceramics powder was synthesized from B_2O_3-TiO_2-Mg system. The effects of TiB_2 addition as diluent on the combustion synthesis process were investigated. The results of thermodynamic calculation and experiments show that the increase of TiB_2 content ranging from 0 to 20wt% can reduce the adiabatic temperature T_(ad) from 3100 K to 2896 K and combustion temperature T_c from 2139 K to 1621 K respectively. The particle size and half width of the particle distribution are also increased with the addition of TiB_2 increasing from 0 to 20wt%. The combustion product is a mixture of TiB_2, MgO, and other intermediate phases. The leached product contains mainly TiB_2, TiO_2 and TiN, and its oxygen content is 7.77wt%.