Ferroelectric materials were widely applied for actuators and sensors. Barium zirconate titanate Ba(Zr0.25Ti0.75)O3 thin film was grown on Pt/Ti/SiO2/Si(100) substrates by pulsed laser deposition. Structure and surfac...Ferroelectric materials were widely applied for actuators and sensors. Barium zirconate titanate Ba(Zr0.25Ti0.75)O3 thin film was grown on Pt/Ti/SiO2/Si(100) substrates by pulsed laser deposition. Structure and surface morphology of the thin film were studied by X-ray diffractometry(XRD) and scan electronic microscopy(SEM). The composition and chemical state near the film surface were obtained by X-ray photoelectron spectroscopy(XPS). On the sample surface,O 1s spectra can be assigned to those from the lattice and surface adsorbed oxygen ions,while C1s only result from surface contamination. The result shows that only one chemical state is found for each spectrum of Ba 3d,Zr 3d and Ti 2p photoelectron in the BZT thin film.展开更多
基金Project(05001825) supported by Guangdong Provincial Natural Science Foundation of Chinaproject(KF0707) supported by the Opening Project Program of Key Laboratory of Low Dimensional Materials and Application Technology (Xiangtan University), Ministry ofEducation, China
文摘Ferroelectric materials were widely applied for actuators and sensors. Barium zirconate titanate Ba(Zr0.25Ti0.75)O3 thin film was grown on Pt/Ti/SiO2/Si(100) substrates by pulsed laser deposition. Structure and surface morphology of the thin film were studied by X-ray diffractometry(XRD) and scan electronic microscopy(SEM). The composition and chemical state near the film surface were obtained by X-ray photoelectron spectroscopy(XPS). On the sample surface,O 1s spectra can be assigned to those from the lattice and surface adsorbed oxygen ions,while C1s only result from surface contamination. The result shows that only one chemical state is found for each spectrum of Ba 3d,Zr 3d and Ti 2p photoelectron in the BZT thin film.