A shaped binderless and two binder‐containing ZSM‐11 zeolite catalysts were prepared and characterized by powder X‐ray diffraction, N2 adsorption‐desorption, and pyridine adsorption‐infrared measurements. The bin...A shaped binderless and two binder‐containing ZSM‐11 zeolite catalysts were prepared and characterized by powder X‐ray diffraction, N2 adsorption‐desorption, and pyridine adsorption‐infrared measurements. The binderless catalyst was synthesized using a dry‐gel conversion technique, inwhich 1,6‐hexanediamine and tetrabutylammonium bromide were used as structure‐directingagents and no other alkaline materials were added. The catalytic performance of the zeolites in the direct amination of isobutene to tert‐butylamine was evaluated in a fixed‐bed reactor. By virtue of its high crystallinity as well as its good mechanical strength, the shaped binderless ZSM‐11 catalyst showed a higher rate of formation of tert‐butylamine than did the binder‐containing catalysts.展开更多
A series of para-substituted meso-tetra phenylporphinatomanganese(Ⅱ)com plexes, Mn (T(p-X ) PP )(L), where X=H. CH3, Cl, OCH3, cuntaining a new kind of axial ligand L=t- RuNH2 have been synthesized by the Na BH4 re...A series of para-substituted meso-tetra phenylporphinatomanganese(Ⅱ)com plexes, Mn (T(p-X ) PP )(L), where X=H. CH3, Cl, OCH3, cuntaining a new kind of axial ligand L=t- RuNH2 have been synthesized by the Na BH4 reduction method These compounds were characterized by electronic and infrared spectra.展开更多
Large-scale oriented ZnO nanocone arrays were directly grown on zinc substrate through a hydrothermal reaction of Zn foil with aqueous butylamine solution (3 mol/L) at 100–180 °C for 12 h. The synthesized produc...Large-scale oriented ZnO nanocone arrays were directly grown on zinc substrate through a hydrothermal reaction of Zn foil with aqueous butylamine solution (3 mol/L) at 100–180 °C for 12 h. The synthesized products were characterized with X-ray diffraction, Raman spectrum, scanning electron microscopy and transmission electron microscopy. The results showed that the ZnO nanocones were single crystalline with the wurtzite structure and grown along the [0001] direction. The diameter of nanocones is decreased with increasing the reaction temperature. A possible growth mechanism was also proposed to account for the formation of the ZnO nanocone arrays. The photoluminescence spectra of the ZnO nanocone arrays were studied at room temperature, two UV emission bands at 377 and 396 nm assigned to free exciton emission and exciton-exciton collision, respectively, and phonon replicas associated with 2-E2 phonon were observed in the PL spectra.展开更多
基金supported by K.C.Wong Education Foundation, Hong Kong (201611)Youth Innovation Promotion Association, CAS (20120155)~~
文摘A shaped binderless and two binder‐containing ZSM‐11 zeolite catalysts were prepared and characterized by powder X‐ray diffraction, N2 adsorption‐desorption, and pyridine adsorption‐infrared measurements. The binderless catalyst was synthesized using a dry‐gel conversion technique, inwhich 1,6‐hexanediamine and tetrabutylammonium bromide were used as structure‐directingagents and no other alkaline materials were added. The catalytic performance of the zeolites in the direct amination of isobutene to tert‐butylamine was evaluated in a fixed‐bed reactor. By virtue of its high crystallinity as well as its good mechanical strength, the shaped binderless ZSM‐11 catalyst showed a higher rate of formation of tert‐butylamine than did the binder‐containing catalysts.
文摘A series of para-substituted meso-tetra phenylporphinatomanganese(Ⅱ)com plexes, Mn (T(p-X ) PP )(L), where X=H. CH3, Cl, OCH3, cuntaining a new kind of axial ligand L=t- RuNH2 have been synthesized by the Na BH4 reduction method These compounds were characterized by electronic and infrared spectra.
基金Supported by the National Natural Science Foundation of China (Grant No. 20573072)Specialized Research Fund for the Doctoral Program of Higher Education of China (Grant No. 20060718010)
文摘Large-scale oriented ZnO nanocone arrays were directly grown on zinc substrate through a hydrothermal reaction of Zn foil with aqueous butylamine solution (3 mol/L) at 100–180 °C for 12 h. The synthesized products were characterized with X-ray diffraction, Raman spectrum, scanning electron microscopy and transmission electron microscopy. The results showed that the ZnO nanocones were single crystalline with the wurtzite structure and grown along the [0001] direction. The diameter of nanocones is decreased with increasing the reaction temperature. A possible growth mechanism was also proposed to account for the formation of the ZnO nanocone arrays. The photoluminescence spectra of the ZnO nanocone arrays were studied at room temperature, two UV emission bands at 377 and 396 nm assigned to free exciton emission and exciton-exciton collision, respectively, and phonon replicas associated with 2-E2 phonon were observed in the PL spectra.