B_2O_3-SiO_2-ZnO-BaO-Al_2O_3 glass with different Al_2O_3 contents（1mol%, 3mol%, 5mol%, and 7mol%） was prepared, and it was intended to be used as lead-free and low-melting glass sealants for solid oxide fuel cells....B_2O_3-SiO_2-ZnO-BaO-Al_2O_3 glass with different Al_2O_3 contents（1mol%, 3mol%, 5mol%, and 7mol%） was prepared, and it was intended to be used as lead-free and low-melting glass sealants for solid oxide fuel cells. The effects of Al_2O_3 content on the structures, thermal properties, and sintering behaviors of the B_2O_3-SiO_2-ZnO-BaO-Al_2O_3 glass were investigated in detail. The Al_2O_3 content largely influenced the structures and thermal properties of the glass. When the Al_2O_3 content 5mol%, the transition temperature of the glass decreased with the Al_2O_3 content, while the crystallization temperature increased with the Al_2O_3 content. However, higher Al_2O_3 content degraded the stability of the glass. The B_2O_3-SiO_2-ZnO-BaO-Al_2O_3 glass with 5 mol% Al_2O_3 content exhibits the optimal sintering densification characteristics and can be used as glass sealants for solid oxide fuel cells.展开更多
In this work,porous biochar(MN-TRB_(750))was fabricated via direct pyrolysis of tea residue(TR)and Mg(NO_(3))_(2)·6H_(2)O(MN).The as-synthesized MN-TRB_(750) reached a specific surface area of 839.54 m^(2)·g...In this work,porous biochar(MN-TRB_(750))was fabricated via direct pyrolysis of tea residue(TR)and Mg(NO_(3))_(2)·6H_(2)O(MN).The as-synthesized MN-TRB_(750) reached a specific surface area of 839.54 m^(2)·g^(-1)and an average pore size of 3.75 nm with multi-level pore architecture.MN decreased TR's carbonization temperature and promoted the aromatics extent,pore structure for the frizzly flake-like biochar.Rhodamine B(RhB)was chosen as the adsorbate to explore the removal performance of organic dyes in this study.The results indicated that the maximum adsorption capacity of RhB on MN-TRB_(750) at 20℃ is up to 809.0 mg·g^(-1)with isotherms fitted well to Freundlich and Dubinin-Radushkevic models.The adsorption kinetics followed pseudo-second-order and Elovich models with an equilibrium adsorption capacity of 757.6 mg·g^(-1)as the initial concentration of RhB is 260 mg·L^(-1).High pore filling,hydrogen bond,π-πinteraction determined the adsorption of RhB onto MN-TRB850 through a multi-active center and exothermic chemical sorption process.展开更多
基金Funded by the Jiangxi Provincial Department of Education(KJLD13008)the National Natural Science Foundation of China(number 51362020)the Research Fund for the Doctoral Program of Higher Education(20123601110006)
文摘B_2O_3-SiO_2-ZnO-BaO-Al_2O_3 glass with different Al_2O_3 contents（1mol%, 3mol%, 5mol%, and 7mol%） was prepared, and it was intended to be used as lead-free and low-melting glass sealants for solid oxide fuel cells. The effects of Al_2O_3 content on the structures, thermal properties, and sintering behaviors of the B_2O_3-SiO_2-ZnO-BaO-Al_2O_3 glass were investigated in detail. The Al_2O_3 content largely influenced the structures and thermal properties of the glass. When the Al_2O_3 content 5mol%, the transition temperature of the glass decreased with the Al_2O_3 content, while the crystallization temperature increased with the Al_2O_3 content. However, higher Al_2O_3 content degraded the stability of the glass. The B_2O_3-SiO_2-ZnO-BaO-Al_2O_3 glass with 5 mol% Al_2O_3 content exhibits the optimal sintering densification characteristics and can be used as glass sealants for solid oxide fuel cells.
基金Supported by the Innovation and Entrepreneurship Plan Project of Shaanxi Province and Shaanxi Xueqian Normal University for College Students(S202314390048,2023DC048)。
文摘In this work,porous biochar(MN-TRB_(750))was fabricated via direct pyrolysis of tea residue(TR)and Mg(NO_(3))_(2)·6H_(2)O(MN).The as-synthesized MN-TRB_(750) reached a specific surface area of 839.54 m^(2)·g^(-1)and an average pore size of 3.75 nm with multi-level pore architecture.MN decreased TR's carbonization temperature and promoted the aromatics extent,pore structure for the frizzly flake-like biochar.Rhodamine B(RhB)was chosen as the adsorbate to explore the removal performance of organic dyes in this study.The results indicated that the maximum adsorption capacity of RhB on MN-TRB_(750) at 20℃ is up to 809.0 mg·g^(-1)with isotherms fitted well to Freundlich and Dubinin-Radushkevic models.The adsorption kinetics followed pseudo-second-order and Elovich models with an equilibrium adsorption capacity of 757.6 mg·g^(-1)as the initial concentration of RhB is 260 mg·L^(-1).High pore filling,hydrogen bond,π-πinteraction determined the adsorption of RhB onto MN-TRB850 through a multi-active center and exothermic chemical sorption process.