A low rare-earth containing ZEK100-O magnesium alloy was welded to AA1230-clad high-strength AA2024-T3 aluminum alloy via solidstate ultrasonic spot welding(USW)to evaluate the microstructure,tensile lap shear strengt...A low rare-earth containing ZEK100-O magnesium alloy was welded to AA1230-clad high-strength AA2024-T3 aluminum alloy via solidstate ultrasonic spot welding(USW)to evaluate the microstructure,tensile lap shear strength,and fatigue properties.The tensile strength increased with increasing welding energy,peaked at a welding energy of 1000 J,and then decreased due to the formation of an increasingly thick diffusion layer mainly containing Al12Mg17intermetallic compound at higher energy levels.The peak tensile lap shear strength attained at 1000 J was attributed to the optimal inter-diffusion between the magnesium alloy and softer AA1230-clad Al layer along with the presence of‘fishhook'-like mechanical interlocks at the weld interface and the formation of an indistinguishable intermetallic layer.The dissimilar joints welded at 1000 J also exhibited a longer fatigue life than other Mg-Al dissimilar joints,suggesting the beneficial role of the softer clad layer with a better intermingling capacity during USW.While the transverse-through-thickness(TTT)failure mode prevailed at lower cyclic loading levels,interfacial failure was the predominant mode of fatigue failure at higher cyclic loads,where distinctive fatigue striations were also observed on the fracture surface of the softer clad Al layer.This was associated with the presence of opening stress and bending moment near the nugget edge despite the tension-tension lap shear cyclic loading applied.展开更多
Copper cladding aluminum(CCA)rods with the section dimensions of12mm in diameter and2mm in sheath thickness were fabricated by vertical core-filling continuous casting(VCFC)technology.The kinds and morphology of inter...Copper cladding aluminum(CCA)rods with the section dimensions of12mm in diameter and2mm in sheath thickness were fabricated by vertical core-filling continuous casting(VCFC)technology.The kinds and morphology of interfacial intermetallic compounds(IMCs)were investigated by SEM,XRD and TEM.The results showed that the interfacial structure of Cu/Al was mainly composed of layeredγ1(Cu9Al4),cellularθ(CuAl2),andα(Al)+θ(CuAl2)phases.Moreover,residual acicularε2(Cu3Al2+x)phase was observed at the Cu/Al interface.By comparing the driving force of formation forε2(Cu3Al2+x)andγ1(Cu9Al4)phases,the conclusion was drawn that theε2(Cu3Al2+x)formed firstly at the Cu/Al interface.In addition,the interfacial formation mechanism of copper cladding aluminum composites was revealed completely.展开更多
In this study the process of cladding steel wires with aluminum is investigated experimentally. It is studied how the cladding process and the quality of products are influenced by the aluminum deformation temperature...In this study the process of cladding steel wires with aluminum is investigated experimentally. It is studied how the cladding process and the quality of products are influenced by the aluminum deformation temperature, the wheel speed, the temperature of steel wire, the wire speed and the steel wire tensile force. The relation among the process parameters above is discussed, and the effect of the aluminum deformation temperature on the coating microstructure is analyzed. This paper suggested a reasonable range of process parameters for producing aluminum cladding steel wires.展开更多
The material used in this experiment was 3003 cladding aluminum alloy, the cladding metal was 4004 aluminum alloy. The aluminum plate was brazed by means of vacuum brazing. The microstructure in the brazing joint was ...The material used in this experiment was 3003 cladding aluminum alloy, the cladding metal was 4004 aluminum alloy. The aluminum plate was brazed by means of vacuum brazing. The microstructure in the brazing joint was studied by means of X-ray diffractometry （XRD） and transmission electron microscopy （TEM）. The test result indicates that the suitable brazing technique parameters are brazing temperature, 628℃; keeping time, 10 min; vacuum degree, 6.5×10^-4 Pa. XRD test indicates that there are new intermetallic compounds different from the base metal. TEM analysis indicates that Cu2Mg and CuaMn2Mg are formed in the brazing joint. The shape of Cu2Mg is irregular and the shape of Cu3Mn2Mg is circle, and there are tiny particles in it.展开更多
An aluminum/copper clad composite was fabricated by the casting-cold extrusion forming technology and the microstructures of the products were observed and analyzed.It is found that aluminum grains at the interface ar...An aluminum/copper clad composite was fabricated by the casting-cold extrusion forming technology and the microstructures of the products were observed and analyzed.It is found that aluminum grains at the interface are refined in the radial profiles of cone-shaped deformation zone,but the grains in the center maintain the original state and the grain size is non-uniform.A clear boundary presents between the refined area and center area.In contrast,the copper grains in the radial profiles have been significantly refined.In the center area of the copper,the grains are bigger than those at the boundary.On the surface of the deformable body,the grain size is the smallest,but with irregular grain morphology.After the product is entirely extruded,all the copper and aluminum grains are refined with small and uniform morphology.In the center area,the average diameter of aluminum grains is smaller than 5 μm,and the copper grain on the surface is about 10 μm.At the interface,the grain size is very small,with a good combination of copper and aluminum.The thickness of interface is in the range of 10-15 μm.Energy spectrum analysis shows that CuAl3 phase presents at the interface.展开更多
The Cu?Al composite casts were prepared by the method of pouring molten aluminum. The solidification process and themicrostructure of the transition layer were investigated during the recombination process of the liqu...The Cu?Al composite casts were prepared by the method of pouring molten aluminum. The solidification process and themicrostructure of the transition layer were investigated during the recombination process of the liquid Al and the solid Cu. The results reveal that the microstructure of the transition layer in the Cu?Al composite cast consists of α(Al)+α(Al)?CuAl2 eutectic,α(Al)?CuAl2 eutectic, CuAl2+α(Al)?CuAl2 eutectic and Cu9Al4. Additionally, the pouring temperature, cooling mode of the Cu platesurface and start time of the forced cooling after pouring have no effect on the microstructure species. But the proportion of thevarious microstructures in the transition layer changes with the process parameters. The pure Al at the top of the transition layer startsto solidify first and then the α(Al) phase grows in a dendritic way, while the CuAl2 phase exhibits plane or cellular crystal growth from the two sides of the transition layer towards its interior. The stronger the cooling intensity of the Cu plate outer surface, the more developed the dendrite, and the easier it is for the CuAl2 phase to grow into a plane crystal.展开更多
A low-clad-ratio AA4045/AA3003 cladding billet was fabricated using a semi-continuous casting process and was subsequently extruded indirectly into a cladding pipe. The temperature distribution near the interface was ...A low-clad-ratio AA4045/AA3003 cladding billet was fabricated using a semi-continuous casting process and was subsequently extruded indirectly into a cladding pipe. The temperature distribution near the interface was measured. The microstructures, elemental distribution, Vickers hardness around the bonding interface, and the interfacial shear strength were examined. The results showed that the interface temperature rebounded when AA4045 melt contacted the supporting layer. The two alloys bonded well, with few defects, via the diffusion of Si and Mn in the temperature range from 569℃ to 632℃. The mean shear strength of the bonding interface was 82.3 MPa, which was greater than that of AA3003（75.8 MPa）, indicating that the two alloys bonded with each other metallurgically via elemental interdiffusion. Moreover, no relative slip occurred between the two alloys during the extrusion process.展开更多
The force feed lubrication method is used for drawing aluminum clad steel wire. It is studied how deformation of wire and aspect of the lubricant film are influenced by the die angle, the reduction, the drawing spee...The force feed lubrication method is used for drawing aluminum clad steel wire. It is studied how deformation of wire and aspect of the lubricant film are influenced by the die angle, the reduction, the drawing speed and the gap between pressure die and wire. It has been concluded that when the factors above mentioned promote to thicken lubricant film, the drawing force is reduced and this favors the homogenous deformation of aluminum coating and steel core.展开更多
基金the National Natural Science Foundation of China(Grant No.51971183)supported by OU(Osaka University,Japan)program for multilateral international collaboration research in joining and welding。
文摘A low rare-earth containing ZEK100-O magnesium alloy was welded to AA1230-clad high-strength AA2024-T3 aluminum alloy via solidstate ultrasonic spot welding(USW)to evaluate the microstructure,tensile lap shear strength,and fatigue properties.The tensile strength increased with increasing welding energy,peaked at a welding energy of 1000 J,and then decreased due to the formation of an increasingly thick diffusion layer mainly containing Al12Mg17intermetallic compound at higher energy levels.The peak tensile lap shear strength attained at 1000 J was attributed to the optimal inter-diffusion between the magnesium alloy and softer AA1230-clad Al layer along with the presence of‘fishhook'-like mechanical interlocks at the weld interface and the formation of an indistinguishable intermetallic layer.The dissimilar joints welded at 1000 J also exhibited a longer fatigue life than other Mg-Al dissimilar joints,suggesting the beneficial role of the softer clad layer with a better intermingling capacity during USW.While the transverse-through-thickness(TTT)failure mode prevailed at lower cyclic loading levels,interfacial failure was the predominant mode of fatigue failure at higher cyclic loads,where distinctive fatigue striations were also observed on the fracture surface of the softer clad Al layer.This was associated with the presence of opening stress and bending moment near the nugget edge despite the tension-tension lap shear cyclic loading applied.
基金Project(51274038)supported by the National Natural Science Foundation of China
文摘Copper cladding aluminum(CCA)rods with the section dimensions of12mm in diameter and2mm in sheath thickness were fabricated by vertical core-filling continuous casting(VCFC)technology.The kinds and morphology of interfacial intermetallic compounds(IMCs)were investigated by SEM,XRD and TEM.The results showed that the interfacial structure of Cu/Al was mainly composed of layeredγ1(Cu9Al4),cellularθ(CuAl2),andα(Al)+θ(CuAl2)phases.Moreover,residual acicularε2(Cu3Al2+x)phase was observed at the Cu/Al interface.By comparing the driving force of formation forε2(Cu3Al2+x)andγ1(Cu9Al4)phases,the conclusion was drawn that theε2(Cu3Al2+x)formed firstly at the Cu/Al interface.In addition,the interfacial formation mechanism of copper cladding aluminum composites was revealed completely.
文摘In this study the process of cladding steel wires with aluminum is investigated experimentally. It is studied how the cladding process and the quality of products are influenced by the aluminum deformation temperature, the wheel speed, the temperature of steel wire, the wire speed and the steel wire tensile force. The relation among the process parameters above is discussed, and the effect of the aluminum deformation temperature on the coating microstructure is analyzed. This paper suggested a reasonable range of process parameters for producing aluminum cladding steel wires.
文摘The material used in this experiment was 3003 cladding aluminum alloy, the cladding metal was 4004 aluminum alloy. The aluminum plate was brazed by means of vacuum brazing. The microstructure in the brazing joint was studied by means of X-ray diffractometry （XRD） and transmission electron microscopy （TEM）. The test result indicates that the suitable brazing technique parameters are brazing temperature, 628℃; keeping time, 10 min; vacuum degree, 6.5×10^-4 Pa. XRD test indicates that there are new intermetallic compounds different from the base metal. TEM analysis indicates that Cu2Mg and CuaMn2Mg are formed in the brazing joint. The shape of Cu2Mg is irregular and the shape of Cu3Mn2Mg is circle, and there are tiny particles in it.
基金Project(60806006) supported by the National Natural Science Foundation of China
文摘An aluminum/copper clad composite was fabricated by the casting-cold extrusion forming technology and the microstructures of the products were observed and analyzed.It is found that aluminum grains at the interface are refined in the radial profiles of cone-shaped deformation zone,but the grains in the center maintain the original state and the grain size is non-uniform.A clear boundary presents between the refined area and center area.In contrast,the copper grains in the radial profiles have been significantly refined.In the center area of the copper,the grains are bigger than those at the boundary.On the surface of the deformable body,the grain size is the smallest,but with irregular grain morphology.After the product is entirely extruded,all the copper and aluminum grains are refined with small and uniform morphology.In the center area,the average diameter of aluminum grains is smaller than 5 μm,and the copper grain on the surface is about 10 μm.At the interface,the grain size is very small,with a good combination of copper and aluminum.The thickness of interface is in the range of 10-15 μm.Energy spectrum analysis shows that CuAl3 phase presents at the interface.
基金Project(LJQ2014062)supported by the Outstanding Young Scholars in Colleges and Universities of Liaoning Province,China
文摘The Cu?Al composite casts were prepared by the method of pouring molten aluminum. The solidification process and themicrostructure of the transition layer were investigated during the recombination process of the liquid Al and the solid Cu. The results reveal that the microstructure of the transition layer in the Cu?Al composite cast consists of α(Al)+α(Al)?CuAl2 eutectic,α(Al)?CuAl2 eutectic, CuAl2+α(Al)?CuAl2 eutectic and Cu9Al4. Additionally, the pouring temperature, cooling mode of the Cu platesurface and start time of the forced cooling after pouring have no effect on the microstructure species. But the proportion of thevarious microstructures in the transition layer changes with the process parameters. The pure Al at the top of the transition layer startsto solidify first and then the α(Al) phase grows in a dendritic way, while the CuAl2 phase exhibits plane or cellular crystal growth from the two sides of the transition layer towards its interior. The stronger the cooling intensity of the Cu plate outer surface, the more developed the dendrite, and the easier it is for the CuAl2 phase to grow into a plane crystal.
基金the support of the Science and Technology Program of Guangzhou, China (No.2015B090926013)the doctoral foundation of the China Ministry of Education (No.20130042130001)
文摘A low-clad-ratio AA4045/AA3003 cladding billet was fabricated using a semi-continuous casting process and was subsequently extruded indirectly into a cladding pipe. The temperature distribution near the interface was measured. The microstructures, elemental distribution, Vickers hardness around the bonding interface, and the interfacial shear strength were examined. The results showed that the interface temperature rebounded when AA4045 melt contacted the supporting layer. The two alloys bonded well, with few defects, via the diffusion of Si and Mn in the temperature range from 569℃ to 632℃. The mean shear strength of the bonding interface was 82.3 MPa, which was greater than that of AA3003（75.8 MPa）, indicating that the two alloys bonded with each other metallurgically via elemental interdiffusion. Moreover, no relative slip occurred between the two alloys during the extrusion process.
文摘The force feed lubrication method is used for drawing aluminum clad steel wire. It is studied how deformation of wire and aspect of the lubricant film are influenced by the die angle, the reduction, the drawing speed and the gap between pressure die and wire. It has been concluded that when the factors above mentioned promote to thicken lubricant film, the drawing force is reduced and this favors the homogenous deformation of aluminum coating and steel core.