The age-hardening response,mechanical,and corrosion-resistant properties of AA7085 alloys with and without the addition of 0.3 wt.%scandium(Sc)were compared.Using advanced techniques such as aberration-corrected trans...The age-hardening response,mechanical,and corrosion-resistant properties of AA7085 alloys with and without the addition of 0.3 wt.%scandium(Sc)were compared.Using advanced techniques such as aberration-corrected transmission electron microscopy and first-principles calculations,the underlying micromechanisms of Sc microalloying were revealed.Results show that the increase in strength of the AA7085-Sc alloy is mainly attributed to the decreased Al grain size and increased number density of both Al_(3)Sc@Al_(3)(Sc,Zr)core−shell nanoparticles and Sc-containingη_(p) and GP−η_(p) nanoprecipitates.Strong strain fields and evident electron transfer from Zr to the neighboring matrix Al atoms exist at the Al_(3)Sc@Al_(3)(Sc,Zr)/Al interface.The Sc doping in GP−η_(p) andη_(p) suppresses the GP−η_(p)→η_(p) transformation.Modified corrosion resistance of the AA7085-Sc alloy compared with AA7085 alloy is associated with the fine grain boundary precipitates ofη_(p)hases and narrow precipitation free zone.The reasons of property changes of AA7085 alloy after Sc microalloying are explored based on the multiscale microstructural characterization.展开更多
The densification characterization,phase constitution,precipitation evolution and mechanical performance of Al−Mg−Sc−Zr alloy processed by laser powder bed fusion(LPBF)were systematically investigated.Moreover,the evo...The densification characterization,phase constitution,precipitation evolution and mechanical performance of Al−Mg−Sc−Zr alloy processed by laser powder bed fusion(LPBF)were systematically investigated.Moreover,the evolution of phase constitution and precipitation behavior after heat treatment were characterized by using X-ray diffraction(XRD)and transmission electron microscope(TEM)analysis.The ultimate tensile strength(UTS)of as-built samples ranged from 396.8 to 414.6 MPa as the scanning speed decreased from 1600 to 1000 mm/s.After post heat treatment,the yield strength(YS)increased to(513.1±1.3)MPa,while the UTS increased from(414.6±5.1)to(539.2±1.5)MPa.The significant improvement of mechanical performance was ascribed to the formation of secondary Al3(Sc,Zr)precipitates.展开更多
基金the support from the National Natural Science Foundation of China (Nos. U20A20274, 52061003)the Natural Science Foundation of Yunnan Province, China (No. 202301AT070209)the Science and Technology Major Project of Yunnan Province, China (No. 202102AG050017)。
文摘The age-hardening response,mechanical,and corrosion-resistant properties of AA7085 alloys with and without the addition of 0.3 wt.%scandium(Sc)were compared.Using advanced techniques such as aberration-corrected transmission electron microscopy and first-principles calculations,the underlying micromechanisms of Sc microalloying were revealed.Results show that the increase in strength of the AA7085-Sc alloy is mainly attributed to the decreased Al grain size and increased number density of both Al_(3)Sc@Al_(3)(Sc,Zr)core−shell nanoparticles and Sc-containingη_(p) and GP−η_(p) nanoprecipitates.Strong strain fields and evident electron transfer from Zr to the neighboring matrix Al atoms exist at the Al_(3)Sc@Al_(3)(Sc,Zr)/Al interface.The Sc doping in GP−η_(p) andη_(p) suppresses the GP−η_(p)→η_(p) transformation.Modified corrosion resistance of the AA7085-Sc alloy compared with AA7085 alloy is associated with the fine grain boundary precipitates ofη_(p)hases and narrow precipitation free zone.The reasons of property changes of AA7085 alloy after Sc microalloying are explored based on the multiscale microstructural characterization.
基金support of the Research and Development Program in Key Areas of Guangdong Province,China(No.2019B090907001)the Science and Technology Program of Guangdong Province,China(No.2014B010129002)the National Key R&D Program of China(No.2017YFB0305800)。
文摘The densification characterization,phase constitution,precipitation evolution and mechanical performance of Al−Mg−Sc−Zr alloy processed by laser powder bed fusion(LPBF)were systematically investigated.Moreover,the evolution of phase constitution and precipitation behavior after heat treatment were characterized by using X-ray diffraction(XRD)and transmission electron microscope(TEM)analysis.The ultimate tensile strength(UTS)of as-built samples ranged from 396.8 to 414.6 MPa as the scanning speed decreased from 1600 to 1000 mm/s.After post heat treatment,the yield strength(YS)increased to(513.1±1.3)MPa,while the UTS increased from(414.6±5.1)to(539.2±1.5)MPa.The significant improvement of mechanical performance was ascribed to the formation of secondary Al3(Sc,Zr)precipitates.