Stable and well-dispersed poly(N-vinyl-2-pyrrolidone) (PVP)-stabilized ruthenium colloidal clusters wereprepaxed via the reduction of ruthenium(III) chloride by refluxing with low boiling point alcohols. Investigation...Stable and well-dispersed poly(N-vinyl-2-pyrrolidone) (PVP)-stabilized ruthenium colloidal clusters wereprepaxed via the reduction of ruthenium(III) chloride by refluxing with low boiling point alcohols. Investigation of the size ofRu colloids by transmission electron microscopy (TEM) indicated that the average diametes could be controlled in the rangeof 1.2-1.6 nm with relative standard deviations of less than 0.33 by changing the molar ratio of PVP to Ru. The X-rayphotoelectron spectroscopy (XPS) characterization verified the formation of elemental ruthenium colloids.展开更多
基金This work was supported by the National Natural Science Foundation of China (No. 29873058).
文摘Stable and well-dispersed poly(N-vinyl-2-pyrrolidone) (PVP)-stabilized ruthenium colloidal clusters wereprepaxed via the reduction of ruthenium(III) chloride by refluxing with low boiling point alcohols. Investigation of the size ofRu colloids by transmission electron microscopy (TEM) indicated that the average diametes could be controlled in the rangeof 1.2-1.6 nm with relative standard deviations of less than 0.33 by changing the molar ratio of PVP to Ru. The X-rayphotoelectron spectroscopy (XPS) characterization verified the formation of elemental ruthenium colloids.