The outermost coating with single phase Ni2Al3 was obtained on copper surface by electrodepositing nickel followed by slurry pack aluminizing at 800 °C for 12 h. The oxidation resistance and microstructure of the...The outermost coating with single phase Ni2Al3 was obtained on copper surface by electrodepositing nickel followed by slurry pack aluminizing at 800 °C for 12 h. The oxidation resistance and microstructure of the coating oxidized in ambient air at 1000 °C for 25-250 h were investigated using SEM, X-ray diffraction and optical microscope methods. The results show that the copper with single phase Ni2Al3 coating possesses the best high temperature oxidation resistance, and the mass gain of the coating is 1/15 that of pure copper and 1/2 that of nickel coating, respectively. The specimen surface after being oxidized for 25 h still comprises Ni2Al3 phase. However, when the time of oxidizing treatment increases to 50 h, the Ni Al phase is formed. It is also found that the Ni2Al3 phase completely turns into Ni Al phase after oxidizing treatment for 100 h and above. The Ni Al coating shows excellent high temperature oxidation resistance when oxidation time is 250 h.展开更多
Mg-Al-Ni alloys were prepared by powder metallurgy, and their microstructure and elevated temperature mechanical properties were investigated. Results indicate that, in addition to α-Mg matrix, both coarse Al;Ni;part...Mg-Al-Ni alloys were prepared by powder metallurgy, and their microstructure and elevated temperature mechanical properties were investigated. Results indicate that, in addition to α-Mg matrix, both coarse Al;Ni;particles and fine Al Ni nano-particles exist in the Mg-Al-Ni alloys. The strength at 150?C is improved with the increase in Ni content. Mg-18.3Al-8Ni alloy possesses a compressive strength of234.7 MPa and a yield strength of 146.5 MPa. Plasticity is also improved with a low concentration of Ni. Mg-11.3Al-2Ni alloy possesses a compression ratio of 17.3%. The phases of Al;Ni;and Al Ni in the alloys block the movements of grain boundaries and dislocations during the deformation at elevated temperature. The existence of Al Ni phase provides a non-basal slip system, leading to the improvement in plasticity. Finally, the formation mechanism of Al-Ni phases in the process is discussed with thermodynamics and kinetics.展开更多
The Ni/Al2O3 catalysts were prepared by two impregnation methods: common and promoted with support salt, for CH4/CO2 reforming and studied by using TPR, TPD, TPMC（Temperature programmed methane decomposition carbon d...The Ni/Al2O3 catalysts were prepared by two impregnation methods: common and promoted with support salt, for CH4/CO2 reforming and studied by using TPR, TPD, TPMC（Temperature programmed methane decomposition carbon deposition） and activity test techniques. The results showed that the coke formation of the catalysts promoted with support salt（aluminium nitrate） was reduced to one sixth and the dispersion increased by 72.7% in comparison with catalyst prepared by common impregnation method. The interactions between Ni and Al with O on the surface of the support salt promoted catalyst appeared stronger.展开更多
基金Projects(CKJB201205,QKJB201202,YJK201307)supported by the Nanjing Institute of Technology,China
文摘The outermost coating with single phase Ni2Al3 was obtained on copper surface by electrodepositing nickel followed by slurry pack aluminizing at 800 °C for 12 h. The oxidation resistance and microstructure of the coating oxidized in ambient air at 1000 °C for 25-250 h were investigated using SEM, X-ray diffraction and optical microscope methods. The results show that the copper with single phase Ni2Al3 coating possesses the best high temperature oxidation resistance, and the mass gain of the coating is 1/15 that of pure copper and 1/2 that of nickel coating, respectively. The specimen surface after being oxidized for 25 h still comprises Ni2Al3 phase. However, when the time of oxidizing treatment increases to 50 h, the Ni Al phase is formed. It is also found that the Ni2Al3 phase completely turns into Ni Al phase after oxidizing treatment for 100 h and above. The Ni Al coating shows excellent high temperature oxidation resistance when oxidation time is 250 h.
基金supported by the National Natural Science Foundation of China (No. 51671063)the Research Fund for the Doctoral Program of Higher Education (No. 20132304110006)+1 种基金the Fundamental Research Funds for the Central Universities (No. HEUCF20161016)the Harbin City Application Technology Research and Development Project (Nos. 2015AE4AE005, 2015RQXXJ001, 2016AB2AG013)
文摘Mg-Al-Ni alloys were prepared by powder metallurgy, and their microstructure and elevated temperature mechanical properties were investigated. Results indicate that, in addition to α-Mg matrix, both coarse Al;Ni;particles and fine Al Ni nano-particles exist in the Mg-Al-Ni alloys. The strength at 150?C is improved with the increase in Ni content. Mg-18.3Al-8Ni alloy possesses a compressive strength of234.7 MPa and a yield strength of 146.5 MPa. Plasticity is also improved with a low concentration of Ni. Mg-11.3Al-2Ni alloy possesses a compression ratio of 17.3%. The phases of Al;Ni;and Al Ni in the alloys block the movements of grain boundaries and dislocations during the deformation at elevated temperature. The existence of Al Ni phase provides a non-basal slip system, leading to the improvement in plasticity. Finally, the formation mechanism of Al-Ni phases in the process is discussed with thermodynamics and kinetics.
文摘The Ni/Al2O3 catalysts were prepared by two impregnation methods: common and promoted with support salt, for CH4/CO2 reforming and studied by using TPR, TPD, TPMC（Temperature programmed methane decomposition carbon deposition） and activity test techniques. The results showed that the coke formation of the catalysts promoted with support salt（aluminium nitrate） was reduced to one sixth and the dispersion increased by 72.7% in comparison with catalyst prepared by common impregnation method. The interactions between Ni and Al with O on the surface of the support salt promoted catalyst appeared stronger.