A comprehensive study on the microstructural evolution of a new type Al-Zn-Mg-Cu-Er-Zr alloy duringhomogenization was conducted by optical microscope,scanning electron microscope,transmission electron microscopy and X...A comprehensive study on the microstructural evolution of a new type Al-Zn-Mg-Cu-Er-Zr alloy duringhomogenization was conducted by optical microscope,scanning electron microscope,transmission electron microscopy and X-raydiffraction analysis.The results show that serious segregation exists in as-cast alloy,and the primary phases are T(AlZnMgCu),S(Al2CuMg)and Al8Cu4Er,which preferentially locate in the grain boundary regions.The soluble T(AlZnMgCu)and S(Al2CuMg)phases dissolve into the matrix gradually during single-stage homogenized at465°C with prolonging holding time,but the residualAl8Cu4Er phase cannot dissolve completely.Compared with the single-stage homogenization,both a finer particle size and a highervolume fraction of L12-structured Al3(Er,Zr)dispersoids can be obtained in the two-stage homogenization process.A suitablehomogenization scheme for the present alloy is(400°C,10h)+(465°C,24h),which is consistent with the results of homogenizationkinetic analysis.展开更多
基金Project(2012CB619503) supported by the National Basic Research Program of ChinaProject(51201003) supported by the National Natural Science Foundation of ChinaProject(2142007) supported by Natural Science Foundation of Beijing,China
文摘A comprehensive study on the microstructural evolution of a new type Al-Zn-Mg-Cu-Er-Zr alloy duringhomogenization was conducted by optical microscope,scanning electron microscope,transmission electron microscopy and X-raydiffraction analysis.The results show that serious segregation exists in as-cast alloy,and the primary phases are T(AlZnMgCu),S(Al2CuMg)and Al8Cu4Er,which preferentially locate in the grain boundary regions.The soluble T(AlZnMgCu)and S(Al2CuMg)phases dissolve into the matrix gradually during single-stage homogenized at465°C with prolonging holding time,but the residualAl8Cu4Er phase cannot dissolve completely.Compared with the single-stage homogenization,both a finer particle size and a highervolume fraction of L12-structured Al3(Er,Zr)dispersoids can be obtained in the two-stage homogenization process.A suitablehomogenization scheme for the present alloy is(400°C,10h)+(465°C,24h),which is consistent with the results of homogenizationkinetic analysis.