The ineluctable introduction of lithium salt to polymer solid-state electrolytes incurs a compromise between strength,ionic conductivity,and thickness.Here,we propose Al_(2)O_(3)-coated polyimide(AO/PI)porous film as ...The ineluctable introduction of lithium salt to polymer solid-state electrolytes incurs a compromise between strength,ionic conductivity,and thickness.Here,we propose Al_(2)O_(3)-coated polyimide(AO/PI)porous film as a high-strength substrate to support fast-ion-conducting polymer-in-salt(PIS)solid-state electrolytes,aiming to suppress lithium dendrite growth and improve full-cell performance.The Al_(2)O_(3)coating layer not only refines the wettability of polyimide porous film to PIS,but also performs as a high modulus protective layer to suppress the growth of lithium dendrites.The resulting PI/AO@PIS exhibits a small thickness of only 35μm with an outstanding tensile strength of 11.3 MPa and Young's modulus of 537.6 MPa.In addition,the PI/AO@PIS delivers a high ionic conductivity of 0.1 m S/cm at 25°C.As a result,the PI/AO@PIS enables symmetric Li cells to achieve exceptional cyclability for over 1000 h at 0.1 m A/cm2without noticeable lithium dendrite formation.Moreover,the PI/AO@PIS-based LiFePO4||Li full cells demonstrate outstanding rate performance(125.7 m Ah/g at 5 C)and impressive cycling stability(96.1%capacity retention at 1 C after 200 cycles).This work highlights the efficacy of enhancing the mechanical properties of polymer matrices and extending cell performance through the incorporation of a dense inorganic interface layer.展开更多
β-Sialon has emerged as a promising material for enhancing the service life of Al_(2)O_(3)-C refractories due to its excellent physicochemical properties.The impact of varying concentrations of nanometer Al/Si alloy ...β-Sialon has emerged as a promising material for enhancing the service life of Al_(2)O_(3)-C refractories due to its excellent physicochemical properties.The impact of varying concentrations of nanometer Al/Si alloy on the in-situ synthesis of β-Sialon within Al_(2)O_(3)-C refractory materials,as well as its oxidation behavior,was investigated.The findings indicate that the presence of Al/Si alloy promotes the formation of AlN and SiC whiskers at 1300℃,which subsequently facilitate the production of plate-like β-Sialon at 1500℃.Density functional theory analysis reveals that the(020)crystal plane of β-Sialon exhibits the lowest adsorption energy for Al2O and AlO molecules under the influence of iron atoms,suggesting a solid-liquid-vapor growth mechanism for β-Sialon formation.The introduction of these ceramic phases significantly enhances the mechanical properties of Al_(2)O_(3)-C refractories.Specifically,the addition of 6 wt.%Al/Si alloy yielded specimens with the highest cold modulus of rupture and cold crushing strength at 1500℃,achieving values of 35.2 and 127.5 MPa,respectively--representing increases of 40.1%and 37.4%.Furthermore,during high-temperature oxidation,the formation of plate-like β-Sialon leads to the development of a dense protective layer on the surface.This impedes the diffusion pathways of oxygen and consequently enhances the oxidation resistance of the refractory.展开更多
Effects of particle size （A：d50 = 336. 9 μm, B：d50 =123.5μm, C： d50=19.5 μm, D： dso=2.21μm） and content （1 wt% , 3 wt% , 5 wt% , 7 wt% ） of silicon powder on cold crushing strength （CCS） , pore size dis...Effects of particle size （A：d50 = 336. 9 μm, B：d50 =123.5μm, C： d50=19.5 μm, D： dso=2.21μm） and content （1 wt% , 3 wt% , 5 wt% , 7 wt% ） of silicon powder on cold crushing strength （CCS） , pore size distribution and microstructure of Al2O3 - ZrO2 - C refractories coked at high temperature had been investigated by means of mercury porosimeter, SEM, EDS, tic. The results indicated that particle size and content of silicon powder affected the cold crushing strength of coked specimens. It increased with the addition of silicon powder and its finer particle size. However, it decreased greatly when using too fine silicon powder. The particle size and content of silicon powder also impacted the phase evolution and microstructure of coked specimens, much more β-SiC whiskers constituted network structure and well distributed in specimens with reduction of their slenderness ratios when finer silicon powder was added, corresponding to that, the specimens＇ pore size distribution range became narrower with smaller pore diameter, but β-SiC whiskers were distributed sparsely and the specific pore volume of small pores increased when much finer powder was added. It was worthly mentioned that some nitride could form in specimens with addition of appropriate particle size and content of silicon powder.展开更多
基金the financial support from the 261Project of MIIT and Natural Science Foundation of Jiangsu Province(No.BK20240179)。
文摘The ineluctable introduction of lithium salt to polymer solid-state electrolytes incurs a compromise between strength,ionic conductivity,and thickness.Here,we propose Al_(2)O_(3)-coated polyimide(AO/PI)porous film as a high-strength substrate to support fast-ion-conducting polymer-in-salt(PIS)solid-state electrolytes,aiming to suppress lithium dendrite growth and improve full-cell performance.The Al_(2)O_(3)coating layer not only refines the wettability of polyimide porous film to PIS,but also performs as a high modulus protective layer to suppress the growth of lithium dendrites.The resulting PI/AO@PIS exhibits a small thickness of only 35μm with an outstanding tensile strength of 11.3 MPa and Young's modulus of 537.6 MPa.In addition,the PI/AO@PIS delivers a high ionic conductivity of 0.1 m S/cm at 25°C.As a result,the PI/AO@PIS enables symmetric Li cells to achieve exceptional cyclability for over 1000 h at 0.1 m A/cm2without noticeable lithium dendrite formation.Moreover,the PI/AO@PIS-based LiFePO4||Li full cells demonstrate outstanding rate performance(125.7 m Ah/g at 5 C)and impressive cycling stability(96.1%capacity retention at 1 C after 200 cycles).This work highlights the efficacy of enhancing the mechanical properties of polymer matrices and extending cell performance through the incorporation of a dense inorganic interface layer.
基金supported by the Natural Science Foundation of Henan Province(No.232300420329)Key Scientific Research Project of Colleges and Universities in Henan Province(Nos.23B430012,22A430028,and 25B430022)+2 种基金Henan Provincial Science and Technology Research Project(No.242102231064)National Natural Science Foundation of China(No.52202064)Luoyang Major Science and Technology Innovation Project(No.2301009A).
文摘β-Sialon has emerged as a promising material for enhancing the service life of Al_(2)O_(3)-C refractories due to its excellent physicochemical properties.The impact of varying concentrations of nanometer Al/Si alloy on the in-situ synthesis of β-Sialon within Al_(2)O_(3)-C refractory materials,as well as its oxidation behavior,was investigated.The findings indicate that the presence of Al/Si alloy promotes the formation of AlN and SiC whiskers at 1300℃,which subsequently facilitate the production of plate-like β-Sialon at 1500℃.Density functional theory analysis reveals that the(020)crystal plane of β-Sialon exhibits the lowest adsorption energy for Al2O and AlO molecules under the influence of iron atoms,suggesting a solid-liquid-vapor growth mechanism for β-Sialon formation.The introduction of these ceramic phases significantly enhances the mechanical properties of Al_(2)O_(3)-C refractories.Specifically,the addition of 6 wt.%Al/Si alloy yielded specimens with the highest cold modulus of rupture and cold crushing strength at 1500℃,achieving values of 35.2 and 127.5 MPa,respectively--representing increases of 40.1%and 37.4%.Furthermore,during high-temperature oxidation,the formation of plate-like β-Sialon leads to the development of a dense protective layer on the surface.This impedes the diffusion pathways of oxygen and consequently enhances the oxidation resistance of the refractory.
文摘Effects of particle size （A：d50 = 336. 9 μm, B：d50 =123.5μm, C： d50=19.5 μm, D： dso=2.21μm） and content （1 wt% , 3 wt% , 5 wt% , 7 wt% ） of silicon powder on cold crushing strength （CCS） , pore size distribution and microstructure of Al2O3 - ZrO2 - C refractories coked at high temperature had been investigated by means of mercury porosimeter, SEM, EDS, tic. The results indicated that particle size and content of silicon powder affected the cold crushing strength of coked specimens. It increased with the addition of silicon powder and its finer particle size. However, it decreased greatly when using too fine silicon powder. The particle size and content of silicon powder also impacted the phase evolution and microstructure of coked specimens, much more β-SiC whiskers constituted network structure and well distributed in specimens with reduction of their slenderness ratios when finer silicon powder was added, corresponding to that, the specimens＇ pore size distribution range became narrower with smaller pore diameter, but β-SiC whiskers were distributed sparsely and the specific pore volume of small pores increased when much finer powder was added. It was worthly mentioned that some nitride could form in specimens with addition of appropriate particle size and content of silicon powder.