Sulfated zirconia-lanthana （SO4^2-/ZrO2-La2O3） precursors were prepared by ultrasonic coprecipitation method and followed by aging at different temperature. The precursors were treated by 0.5 mol/L H2SO4. Samples of...Sulfated zirconia-lanthana （SO4^2-/ZrO2-La2O3） precursors were prepared by ultrasonic coprecipitation method and followed by aging at different temperature. The precursors were treated by 0.5 mol/L H2SO4. Samples of SO4^2-/ZrO2-La2O3 nano-crystalline catalysts were obtained by baking the treated precursors at different temperatures. The acidic properties of SO4^2-/ZrO2-La2O3 were tested by the Hammett indicator method. The phase composition, specific area, particle structure, and surface state were characterized by X-ray diffraction, BET, transmission electron microscopy, infrared spectrum, and X-ray photoelectron spec- troscopy. The catalytic activities were estimated by esterification of acetic acid with glycerin. It was shown that the catalyst prepared by ultrasonic stirring and low temperature （-15 ℃） exhibited highly active sites and high catalytic property.展开更多
A Y2O3 particle enhanced Ni/TiC composite coating was fabricated in-situ on a TC4 Ti alloy by laser surface cladding.The phase component,microstructure,composition distribution and properties of the composite layer we...A Y2O3 particle enhanced Ni/TiC composite coating was fabricated in-situ on a TC4 Ti alloy by laser surface cladding.The phase component,microstructure,composition distribution and properties of the composite layer were investigated.The composite layer has graded microstructures and compositions,due to the fast melting followed by rapid solidification and cooling during laser cladding.The TiC powders are completely dissolved into the melted layer during melting and segregated as fine dendrites when solidified.The size of TiC dendrites decreases with increasing depth.Y2O3 fine particles distribute in the whole clad layer.The Y2O3 particle enhanced Ni/TiC composite layer has a quite uniform hardness along depth with a maximum value of HV1380,which is 4 times higher than the initial hardness.The wear resistance of the Ti alloy is significantly improved after laser cladding due to the high hardness of the composite coating.展开更多
文摘Sulfated zirconia-lanthana （SO4^2-/ZrO2-La2O3） precursors were prepared by ultrasonic coprecipitation method and followed by aging at different temperature. The precursors were treated by 0.5 mol/L H2SO4. Samples of SO4^2-/ZrO2-La2O3 nano-crystalline catalysts were obtained by baking the treated precursors at different temperatures. The acidic properties of SO4^2-/ZrO2-La2O3 were tested by the Hammett indicator method. The phase composition, specific area, particle structure, and surface state were characterized by X-ray diffraction, BET, transmission electron microscopy, infrared spectrum, and X-ray photoelectron spec- troscopy. The catalytic activities were estimated by esterification of acetic acid with glycerin. It was shown that the catalyst prepared by ultrasonic stirring and low temperature （-15 ℃） exhibited highly active sites and high catalytic property.
基金Projects(51101096,51002093)supported by the National Natural Science Foundation of ChinaProject(1052nm05000)supported by Special Foundation of the Shanghai Science and Technology Commission for Nano-Materials ResearchProject(J51042)supported by Leading Academic Discipline Project of the Shanghai Education Commission,China
文摘A Y2O3 particle enhanced Ni/TiC composite coating was fabricated in-situ on a TC4 Ti alloy by laser surface cladding.The phase component,microstructure,composition distribution and properties of the composite layer were investigated.The composite layer has graded microstructures and compositions,due to the fast melting followed by rapid solidification and cooling during laser cladding.The TiC powders are completely dissolved into the melted layer during melting and segregated as fine dendrites when solidified.The size of TiC dendrites decreases with increasing depth.Y2O3 fine particles distribute in the whole clad layer.The Y2O3 particle enhanced Ni/TiC composite layer has a quite uniform hardness along depth with a maximum value of HV1380,which is 4 times higher than the initial hardness.The wear resistance of the Ti alloy is significantly improved after laser cladding due to the high hardness of the composite coating.