Two Al2O3/Cu composites containing 0.24 wt.% Al2O3 and 0.60 wt.% Al2O3 separately are prepared by internal oxidation. Effects of sliding speed and pressure on the frictional characteristics of the composites and coppe...Two Al2O3/Cu composites containing 0.24 wt.% Al2O3 and 0.60 wt.% Al2O3 separately are prepared by internal oxidation. Effects of sliding speed and pressure on the frictional characteristics of the composites and copper against brass are investigated and compared. The changes in morphology of the sliding surface and subsurface are examined with scanning electron microscope （SEM） and energy dispersive X-ray spectrum （EDS）. The results show that the wear resistance of the Al2O3/Cu composites is superior to that of copper under the same conditions, Under a given electrical current, the wear rate of Al2O3/Cu composites decreases as the Al2O3-content increases, However, the wear rates of the Al2O3/Cu composites and copper increase as the sliding speed and pressure increase under dry sliding condition. The main wear mechanisms for Al2O3/Cu composites are of abrasion and adhesion; for copper, it is adhesion, although wear by oxidation and electrical erosion can also be observed as the speed and pressure rise.展开更多
（TiB2＋Al2O3）/NiAl composites were synthesized by self-propagation high-temperature synthesis, and their phase compositions, microstructures and evolution modes were studied. The microstructures and shapes vary with...（TiB2＋Al2O3）/NiAl composites were synthesized by self-propagation high-temperature synthesis, and their phase compositions, microstructures and evolution modes were studied. The microstructures and shapes vary with the TiB2＋Al2O3 content in the NiAl matrix. TiB2 particles take a great variety of elementary shapes such as white bars, plates, herringbones, regular cubes and cuboids. These results outline a strategy of self-assembly processes in real time to build diversified microstructures. Some TiB2 grains in sizes of 2-5μm are embeded in Al2O3 clusters, while a small number of TiB2 particles disperse in the NiAl matrix. It is believed that the higher the TiB2＋Al2O3 content is, the more the regular shapes and homogeneous distributions of TiB2 and Al2O3 will be present in the NiAl matrix.展开更多
The deformation behaviors of Al2O3/Al composites were investigated by compressive tests conducted at temperature of 300-450 °C and strain rates of 0.001-1.0 s-1 with Gleeble-1500 D thermal simulator system. The r...The deformation behaviors of Al2O3/Al composites were investigated by compressive tests conducted at temperature of 300-450 °C and strain rates of 0.001-1.0 s-1 with Gleeble-1500 D thermal simulator system. The results show that the flow stress increases with increasing strain rate and decreasing temperature. The hyperbolic sine constitutive equation can describe the flow stress behavior of Al2O3/Al composites, and the deformation activation energy and constitutive equations were calculated. The processing maps of Al2O3/Al-2 μm and Al2O3/Al-1 μm composites at strain of 0.6 were obtained and the optimum processing domains are in ranges of 300-330 °C, 0.007-0.03 s-1 and 335-360 °C, 0.015-0.06 s-1 for hot working, respectively. The instability zones of flow behavior can also be recognized by the maps.展开更多
Al2O3/Au nano-laminated composite coatings were prepared by means of magnetron sputtering. The coating was compact and comprised of nano-laminated Al2O3 and Au layers. High temperature cyclic oxidation test was employ...Al2O3/Au nano-laminated composite coatings were prepared by means of magnetron sputtering. The coating was compact and comprised of nano-laminated Al2O3 and Au layers. High temperature cyclic oxidation test was employed to investigate the oxidation resistance of the composite coatings. The results revealed that the applied Al2O3/Au nano-laminated composite coatings improved the oxidation and spallation resistance of the stainless steel substrate significantly. The mechanism accounting for oxidation resistance was related with the suppression of inward oxygen diffusion and selective oxidation of Cr in the substrate. The mechanism accounting for spallation resistance was attributed to the relaxation of thermal stress by the nano-laminated structure.展开更多
The distributions of traps and electron density in the interfaces between polyimide （PI） matrix and Al2O3 nanoparticles are researched using the isothermal decay current and the small-angle x-ray scattering （SAXS）...The distributions of traps and electron density in the interfaces between polyimide （PI） matrix and Al2O3 nanoparticles are researched using the isothermal decay current and the small-angle x-ray scattering （SAXS） tests. According to the electron density distribution for quasi two-phase mixture doped by spherical nanoparticles, the electron densities in the interfaces of PI/Al2O3 nanocomposite films are evaluated. The trap level density and carrier mobility in the interface are studied. The experimental results show that the distribution and the change rate of the electron density in the three layers of interface are different, indicating different trap distributions in the interface layers. There is a maximum trap level density in the second layer, where the maximum trap level density for the nanocomposite film doped by 25 wt% is 1.054 × 10^22 eV·m^-3 at 1.324eV, resulting in the carrier mobility reducing. In addition, both the thickness and the electron density of the nanocomposite film interface increase with the addition of the doped Al2O3 contents. Through the study on the trap level distribution in the interface, it is possible to further analyze the insulation mechanism and to improve the performance of nano-dielectric materials.展开更多
Ti3AlC2/TiC-Al2O3 composite was synthesized by a combustion reaction in TiO2-Al-C system. The effect of the compositions in raw materials on the products was investigated. Ti3AlC2/TiC-Al2O3 composite was obtained at t...Ti3AlC2/TiC-Al2O3 composite was synthesized by a combustion reaction in TiO2-Al-C system. The effect of the compositions in raw materials on the products was investigated. Ti3AlC2/TiC-Al2O3 composite was obtained at the molar ratio of TiO2：Al：C=3.0：5.0～5.1：1.8～2.0. The reaction path for the 3TiO2-5Al- 2C system was proposed. Al3Ti, Ti203, TiO, and 6-Al2O3 are found to be transitional phases. Finally, Ti3AlC2/TiC-Al2O3 composite forms at～900℃ of furnace temperature. The measured Vickers hardness, fracture toughness, and flexural strength of the nearly dense sample from 3TiO2-5Al-2C are 13.3±1.1 GPa, 5.8±0.3 MPa.m^1/2, and 466±39 MPa, respectively.展开更多
In this paper,a novel Ce(Gd2 Y)Al5O12/Ce:Y3Al5O12(Ce:GYAG/Ce:YAG)composite scintillation ceramic was designed and fabricated by a solid-state reaction method.The phase,luminescence and scintillation properties were in...In this paper,a novel Ce(Gd2 Y)Al5O12/Ce:Y3Al5O12(Ce:GYAG/Ce:YAG)composite scintillation ceramic was designed and fabricated by a solid-state reaction method.The phase,luminescence and scintillation properties were investigated.The Ce:GYAG/Ce:YAG composite ceramic consisting of two-phase has a broad emission band ranging from 500 to 750 nm.The total mass attenuation coefficient of Ce:GYAG/Ce:YAG is 0.3864 cm^-1,in between those of Ce:YAG and Ce:GYAG ceramics.In addition,the composite ceramic had a high light yield of 20430 ph/MeV.By controlling the ratio of GYAG and YAG,the composite ceramic can realize a spectrum design and total mass attenuation coefficient control to meet the requirements for wide-X-ray-energy-range detectors.展开更多
Cu2O/TiOa/Pt three-layer films were deposited on glass substrates using magnetron sputtering method. The surface morphology and the optical properties of the composite film were characterized by X-ray diffraction （XR...Cu2O/TiOa/Pt three-layer films were deposited on glass substrates using magnetron sputtering method. The surface morphology and the optical properties of the composite film were characterized by X-ray diffraction （XRD）, scanning electron microscopy （SEM）, ultraviolet- visible spectroscopy （UV-Vis） and photoluminescence spectroscopy （PL）. The photocatalytic activity of the samples was evaluated by the photocatalytic degradation of methyl orange （MO） aqueous solution under visible light irradiation. The results indicate that the Cu2O/TiO2/Pt composite films are made up of three layers which are Pt layer, anatase-TiO2 layer and Cu2O layer from bottom to top. The surface of the films is even and composed of regular-shaped spherical particles. The photocatalytic activity of the Cu2O/TiO2/Pt three-layer film is much higher than that of the Cu2O/TiO2 double-layer film. Such enhancement is ascribed to the presence of Pt layer, which further inhibits the photogenerated electron-hole recombination, prolongs the lifetime of the photogenerated carriers, increases the quantum efficiency and hence improves the photocatalytic activity of the film effectively.展开更多
Non-isothermal kinetic research has been carried out on oxidation behavior of β-Sialon in diphaseβ-Sialon/Al_2O_3 composite at high temperatures. A kinetic formula is established for non-isothermal oxidation process...Non-isothermal kinetic research has been carried out on oxidation behavior of β-Sialon in diphaseβ-Sialon/Al_2O_3 composite at high temperatures. A kinetic formula is established for non-isothermal oxidation process of β-Sialon. The rate of oxidation process is controlled by chemicalreaction at the initial stage and then by diffusion. The apparent activation energies and appar-ent rate constants at different temperatures are determined by treating TG data of the overallprocess.展开更多
The preferred internal oxidation of aluminum in Cu Al alloy was used to obtain in situ Al 2O 3/Cu composites. The reinforcement particles were mainly γ Al 2O 3, some θ Al 2O 3 and a little α Al 2O 3. Thermodynamics...The preferred internal oxidation of aluminum in Cu Al alloy was used to obtain in situ Al 2O 3/Cu composites. The reinforcement particles were mainly γ Al 2O 3, some θ Al 2O 3 and a little α Al 2O 3. Thermodynamics analyses show that the chemical reactions are 3Cu 2O+2Al=6Cu+Al 2O 3 or 3CuO+2Al=3Cu+Al 2O 3. A related equilibrium diagram was drawn. The experiments and investigation show that the formation rate of Al 2O 3 was controlled by the diffusion of oxygen in matrix.展开更多
Aluminum matrix composites reinforced by in situ Al2O3 and Al3Zr particles are fabricated from A356-Zr(CO3)2 system via magnetochemistry reaction,and the morphologies,sizes and distributions of the in situ particles a...Aluminum matrix composites reinforced by in situ Al2O3 and Al3Zr particles are fabricated from A356-Zr(CO3)2 system via magnetochemistry reaction,and the morphologies,sizes and distributions of the in situ particles as well as the microstructures,mechanical mechanisms of the composites are investigated by XRD,SEM,TEM and in situ tensile tests.The results indicate that with the pulsed magnetic field assistance,the morphologies of the in situ particles are mainly with ball-shape,the sizes are in nanometer scale and the distributions in the matrix are uniform.The interfaces between the in situ particles and the aluminum matrix are net and no interfacial outgrowth is observed.These are due to the strong vibration induced by the applied magnetic field in the aluminum melt,which in turn,accelerates the melt reactions.The effects of the magnetic field on the above contributions are discussed in detail.展开更多
Al2O3p-Al composites were synthesized using an in-situ reaction in the 80%Al-20%CuO （mass fraction） system. The effects of the CuO particle size on the synthesis temperature and microstructure of the composites were...Al2O3p-Al composites were synthesized using an in-situ reaction in the 80%Al-20%CuO （mass fraction） system. The effects of the CuO particle size on the synthesis temperature and microstructure of the composites were investigated by various methods. The results indicate that the CuO particle size has a significant effect on the temperature at which the complete reaction in the Al-CuO system occurs：the temperature is 200 ℃ lower in the Al-CuO system containing CuO particles with sizes less than 6μm than that containing CuO particles with sizes less than 100μm. The interfacial bonding between Al2O3 particles and Al is not complete when the temperature is below a critical value. The morphology of the Al2O3 particles varies from ribbon-like shape to near spherical shape when the temperature is above a critical value. These two critical temperatures are affected by the particle size of CuO, and the critical temperature of the sample containing CuO particles with sizes less than 6μm is 100 ℃ lower than that of the sample containing CuO particles with sizes less than 100μm.展开更多
Al2O3 particle-reinforced ZL109 composite was prepared by in situ reaction between CuO and Al2O3 . The microstructure was observed by means of OM, SEM and TEM. The Al2O3 particles in sub-micron sizes distribute unifo...Al2O3 particle-reinforced ZL109 composite was prepared by in situ reaction between CuO and Al2O3 . The microstructure was observed by means of OM, SEM and TEM. The Al2O3 particles in sub-micron sizes distribute uniformly in the matrix, and the Cu displaced from the in situ reaction forms net-like alloy phases with other alloy elements. The hardness and the tensile strength of the composites at room temperature have a slight increase as compared to that of the matrix. However, the tensile strength at 350℃ has reached 90.23 MPa, or 16.92 MPa higher than that of the matrix. The mechanism of the reaction in the CuO/AI system was studied by using of differential scanning calorimetry（DSC） and thermodynamic calculation. The reaction between CuO and Al involves two steps. First, CuO reacts with Al to form Cu20 and Al2O3 at the melting temperature of the matrix alloy, and second, Cu20 reacts with Al to form Cu and Al2O3 at a higher temperature. At ZL109 casting temperature of 750- 780 ℃, the second step can also take place because of the effect of exothermic reaction of the first step.展开更多
Studies the combustion synthesis of Al Ti TiO 2 system and concludes that, due to its low exothermic nature, a stable combustion wave can be maintained only when the system is ignited at a certain preheating temperatu...Studies the combustion synthesis of Al Ti TiO 2 system and concludes that, due to its low exothermic nature, a stable combustion wave can be maintained only when the system is ignited at a certain preheating temperature, and coupled with appropriate pseudo HIP process, dense TiAl/Al 2O 3 composites with density as high as 97% of the theoretical value can be produced, and points out. Microstructure observation shows in situ formed Al 2O 3 particles are of an average size smaller than one micron, and the hardness of TiAl matrix is enhanced by introduction of these particles.展开更多
The interaction between Zn-AI eutectic alloy and Al203p/6061AI composites in the vacuum furnace was investigated. Great attention has been paid to the elements diffusion, the microstructure and formation of the interf...The interaction between Zn-AI eutectic alloy and Al203p/6061AI composites in the vacuum furnace was investigated. Great attention has been paid to the elements diffusion, the microstructure and formation of the interface between Zn-AI eutectic alloy and Al2O3p/6061AI composites. Experimental results show that Zn-AI eutectic alloy has a good wetting ability to Al2O3p/6061 Al composites and the wetting angle decreases with increasing the temperature in vacuum. After the interaction, an interaction layer forms between Zn-AI alloy and Al2O3p/6061 Al composites. The phases in the interaction layer mainly consist of α-AI(Zn), Al2O3 and CuZn5 resulted from the diffusion of elements from the Zn-AI alloy. Several porosities distribute in the region near the interface of the Zn-AI alloy/interaction layer. The amount of shrinkage voids in the interacting layer is relevant to the penetration of Zn element into Al2O3p/6061Al composites which is a function of temperature. So it is necessary to lower heating temperature in order to limit the Zn penetration.展开更多
In situ （Al2O3-Si）/Al composites with a reinforcement volume fraction of 10% were synthesized from the Al-SiO2 system using low energy ball milling and reaction hot pressing. Differential thermal analysis was used t...In situ （Al2O3-Si）/Al composites with a reinforcement volume fraction of 10% were synthesized from the Al-SiO2 system using low energy ball milling and reaction hot pressing. Differential thermal analysis was used to investigate the reaction mechanisms between SiO2 and Al. X-ray diffraction results revealed that the reaction between Al and SiO2 took place completely at 900 ℃ with a holding time of 2 h, thereby forming Al2O3 and Si. Scanning electron microscopic, energy dispersive X-ray spectroscopic, and transmission electron microscopic （TEM） results showed that the in situ synthesized A1203 and Si particles, whose sizes are less than 2 μm, were polygonal in shape and dispersed uniformly in the matrix. Moreover, Al2O3 particle size showed a tendency to increase from - 2 to - 6 μm when the synthesis temperature was increased. Furthermore, TEM observation showed that the interface between the reinforcements and Al matrix is clean. The yield strength, ultimate tensile strength, and Brinell hardness of the in situ （Al2O3-Si）/Al composite was significantly higher than the aluminum matrix. Mechanisms governing the tensile fracture process are discussed.展开更多
A tritium permeation barrier is required in fusion blankets for the reduction of fuel loss and radiological hazard.In this study,an Al2O3/Y2O3 composite coating was prepared on 316 L stainless steel by radiofrequency ...A tritium permeation barrier is required in fusion blankets for the reduction of fuel loss and radiological hazard.In this study,an Al2O3/Y2O3 composite coating was prepared on 316 L stainless steel by radiofrequency magnetron sputtering in order to improve the tritium permeation resistance.The microstructure and the phase composition of the Al2O3/Y2O3 composite coating are observed by scanning electron microscopy,transmission electron microscopy and grazing incidence X-ray diffraction.Moreover,Auger electron spectroscopy was used to characterize the depth profiles of Al,Y and O elements.The results clearly indicate that the Al2O3/Y2O3 composite coating is fully dense and the total thickness is approximately 340 nm.The Al2O3/Y2O3 coating consists of an amorphous Al2O3 and the cubic Y2O3,in which Al,Y and O elements are homogeneously distributed in the vertical base direction.Furthermore,the deuterium permeation property of the Al2O3/Y2O3 composite coating was measured by the gas phase permeation method.The results show that the introduction of an interface and the existence of a tiny amount of micro-defects improve the deuterium resistance of the Al2O3/Y2O3 coating,and its deuterium permeation reduction factor is 536-750 at 873-973 K.Therefore,it is concluded that the Al2O3/Y2O3 co mposite coating as deuterium permeation barrier can significa ntly enha nce the deuterium permeation resistance property.展开更多
Alumina dispersion strengthened copper composite （nano-Al2O3/Cu composite） was recently emerged as a kind of potentially viable and attractive engineering material for applications requiring high strength, high ther...Alumina dispersion strengthened copper composite （nano-Al2O3/Cu composite） was recently emerged as a kind of potentially viable and attractive engineering material for applications requiring high strength, high thermal and electrical conductivities and resistance to softening at elevated temperatures. The nano-Al2O3/Cu composite was produced by internal oxidation. The microstructures of the composite were analyzed by the TEM and its hot deformation behavior was investigated by means of continuous compression tests performed on a Gleeble 1500 thermo-simulator. Making use of the modified algorithm-Levenberg-Marquardt （L-M） algorithm BP neural network, a model for predicting the flow stresses during hot deformation was set up on the base of the experimental data. Results show that the microstructures of the composite are characterized by uniform distribution of nano-Al2O3 particles in Cu-matrix. The sliding of dislocations is the main deformation mechanism. The dynamic recovery is the main softening mode with the flow stress decreasing gently from 500℃ to 850 ~C. The recrystallization of Cu-matrix can be retarded late into as high as 850 ℃, when it happens only partially. The well-trained BP neural network model can accurately describe the influence of the temperature, strain rate, and true strain on the flow stresses, therefore, it can precisely predict the flow stresses of the composite under given deforming conditions and provide a new way to optimize hot deforming process parameters.展开更多
Al/Al203 composites of different ratios were hot-press sintered at 575~640℃ under a pressure of 30 MPa for 2 h in a vacuum furnace. It was found that the relative density of the Al/Al203 ...Al/Al203 composites of different ratios were hot-press sintered at 575~640℃ under a pressure of 30 MPa for 2 h in a vacuum furnace. It was found that the relative density of the Al/Al203 composites could be increased evidently with the rise of sinter temperature. No reaction occurred between At and Al203 at the sinter temperatures. Under 640℃-30 MPa-2 h experimental condition, Al/Al203 system FGM was successfully fabricated, and its density range changed quasi-continuously from 2.887×103 kg/m3 to 3.1909×103 kg/m3 within the middle 1.0 mm thickness range.展开更多
Hot compression behavior of TiC–Al2O3/Al composites was studied using the Gleeble-1500 system at a temperature range of 300–550 °C and at strain rate range of 0.01–10.00 s-1. The associated structural changes ...Hot compression behavior of TiC–Al2O3/Al composites was studied using the Gleeble-1500 system at a temperature range of 300–550 °C and at strain rate range of 0.01–10.00 s-1. The associated structural changes were studied by TEM observations. The results show that stress level decreases with deformation temperature increasing and strain rate decreasing, which can be represented by a Zener–Hollomon parameter in an exponent-type equation with hot deformation activation energy Q of 172.56 kJ·mol-1.Dynamic recovery occurs easily when strain rates are less than 10.00 s-1. Dynamic recrystallization can occur at strain rate of 10.00 s-1.展开更多
基金National Natural Science Foundation of China (50432020)Henan Innovation Project for University Prominent Re- search Talents (2007KYCX008)+3 种基金Henan Education Department Science and Technology Project (2007430004)Henan Plan Project for College Youth Backbone TeacherHenan University of Science and Technology Major Pre-research Foundation (2005ZD003)Henan University of Science and Technology Personnel Scientific Research Foundation (of023)
文摘Two Al2O3/Cu composites containing 0.24 wt.% Al2O3 and 0.60 wt.% Al2O3 separately are prepared by internal oxidation. Effects of sliding speed and pressure on the frictional characteristics of the composites and copper against brass are investigated and compared. The changes in morphology of the sliding surface and subsurface are examined with scanning electron microscope （SEM） and energy dispersive X-ray spectrum （EDS）. The results show that the wear resistance of the Al2O3/Cu composites is superior to that of copper under the same conditions, Under a given electrical current, the wear rate of Al2O3/Cu composites decreases as the Al2O3-content increases, However, the wear rates of the Al2O3/Cu composites and copper increase as the sliding speed and pressure increase under dry sliding condition. The main wear mechanisms for Al2O3/Cu composites are of abrasion and adhesion; for copper, it is adhesion, although wear by oxidation and electrical erosion can also be observed as the speed and pressure rise.
基金Project(51272141)supported by the National Natural Science Foundation of ChinaProject(ts20110828)supported by the Taishan Scholars Project of Shandong Province,ChinaProject(2015AA034404)supported by the Ministry of Science and Technology of China
文摘（TiB2＋Al2O3）/NiAl composites were synthesized by self-propagation high-temperature synthesis, and their phase compositions, microstructures and evolution modes were studied. The microstructures and shapes vary with the TiB2＋Al2O3 content in the NiAl matrix. TiB2 particles take a great variety of elementary shapes such as white bars, plates, herringbones, regular cubes and cuboids. These results outline a strategy of self-assembly processes in real time to build diversified microstructures. Some TiB2 grains in sizes of 2-5μm are embeded in Al2O3 clusters, while a small number of TiB2 particles disperse in the NiAl matrix. It is believed that the higher the TiB2＋Al2O3 content is, the more the regular shapes and homogeneous distributions of TiB2 and Al2O3 will be present in the NiAl matrix.
基金Project(2012AA030311)supported by the National High-tech Research and Development Program of ChinaProject(2010BB4074)supported by the Natural Science Foundation of Chongqing Municipality,ChinaProject(2010ZD-02)supported by the State Key Laboratory for Advanced Metals and Materials,China
文摘The deformation behaviors of Al2O3/Al composites were investigated by compressive tests conducted at temperature of 300-450 °C and strain rates of 0.001-1.0 s-1 with Gleeble-1500 D thermal simulator system. The results show that the flow stress increases with increasing strain rate and decreasing temperature. The hyperbolic sine constitutive equation can describe the flow stress behavior of Al2O3/Al composites, and the deformation activation energy and constitutive equations were calculated. The processing maps of Al2O3/Al-2 μm and Al2O3/Al-1 μm composites at strain of 0.6 were obtained and the optimum processing domains are in ranges of 300-330 °C, 0.007-0.03 s-1 and 335-360 °C, 0.015-0.06 s-1 for hot working, respectively. The instability zones of flow behavior can also be recognized by the maps.
基金Project (50771021) supported by the National Natural Science Foundation of China
文摘Al2O3/Au nano-laminated composite coatings were prepared by means of magnetron sputtering. The coating was compact and comprised of nano-laminated Al2O3 and Au layers. High temperature cyclic oxidation test was employed to investigate the oxidation resistance of the composite coatings. The results revealed that the applied Al2O3/Au nano-laminated composite coatings improved the oxidation and spallation resistance of the stainless steel substrate significantly. The mechanism accounting for oxidation resistance was related with the suppression of inward oxygen diffusion and selective oxidation of Cr in the substrate. The mechanism accounting for spallation resistance was attributed to the relaxation of thermal stress by the nano-laminated structure.
基金Supported by the National Natural Science Foundation of China under Grant Nos 51337002,51077028,51502063 and 51307046the Foundation of Harbin Science and Technology Bureau of Heilongjiang Province under Grant No RC2014QN017034
文摘The distributions of traps and electron density in the interfaces between polyimide （PI） matrix and Al2O3 nanoparticles are researched using the isothermal decay current and the small-angle x-ray scattering （SAXS） tests. According to the electron density distribution for quasi two-phase mixture doped by spherical nanoparticles, the electron densities in the interfaces of PI/Al2O3 nanocomposite films are evaluated. The trap level density and carrier mobility in the interface are studied. The experimental results show that the distribution and the change rate of the electron density in the three layers of interface are different, indicating different trap distributions in the interface layers. There is a maximum trap level density in the second layer, where the maximum trap level density for the nanocomposite film doped by 25 wt% is 1.054 × 10^22 eV·m^-3 at 1.324eV, resulting in the carrier mobility reducing. In addition, both the thickness and the electron density of the nanocomposite film interface increase with the addition of the doped Al2O3 contents. Through the study on the trap level distribution in the interface, it is possible to further analyze the insulation mechanism and to improve the performance of nano-dielectric materials.
文摘Ti3AlC2/TiC-Al2O3 composite was synthesized by a combustion reaction in TiO2-Al-C system. The effect of the compositions in raw materials on the products was investigated. Ti3AlC2/TiC-Al2O3 composite was obtained at the molar ratio of TiO2：Al：C=3.0：5.0～5.1：1.8～2.0. The reaction path for the 3TiO2-5Al- 2C system was proposed. Al3Ti, Ti203, TiO, and 6-Al2O3 are found to be transitional phases. Finally, Ti3AlC2/TiC-Al2O3 composite forms at～900℃ of furnace temperature. The measured Vickers hardness, fracture toughness, and flexural strength of the nearly dense sample from 3TiO2-5Al-2C are 13.3±1.1 GPa, 5.8±0.3 MPa.m^1/2, and 466±39 MPa, respectively.
基金financially supported by the National Natural Science Foundation of China(Nos.61378069,61405221,and 11535010)Youth Innovation Promotion Association of the Chinese Academy of Science(CAS)+2 种基金National Key Research and Development Program of China(SQ2017YFGX010025-03)Interdisciplinary Innovation Team of the CASGeneral Financial Grant from the China Postdoctoral Science Foundation(No.2016M601654)
文摘In this paper,a novel Ce(Gd2 Y)Al5O12/Ce:Y3Al5O12(Ce:GYAG/Ce:YAG)composite scintillation ceramic was designed and fabricated by a solid-state reaction method.The phase,luminescence and scintillation properties were investigated.The Ce:GYAG/Ce:YAG composite ceramic consisting of two-phase has a broad emission band ranging from 500 to 750 nm.The total mass attenuation coefficient of Ce:GYAG/Ce:YAG is 0.3864 cm^-1,in between those of Ce:YAG and Ce:GYAG ceramics.In addition,the composite ceramic had a high light yield of 20430 ph/MeV.By controlling the ratio of GYAG and YAG,the composite ceramic can realize a spectrum design and total mass attenuation coefficient control to meet the requirements for wide-X-ray-energy-range detectors.
基金financially supported by the National Natural Science Foundation of China (No.51301118)the Projects of International Cooperation in Shanxi (No.2014081002)the Scientific and Technological Innovation Programs of Higher Education Institutions in Shanxi (No.2013108)
文摘Cu2O/TiOa/Pt three-layer films were deposited on glass substrates using magnetron sputtering method. The surface morphology and the optical properties of the composite film were characterized by X-ray diffraction （XRD）, scanning electron microscopy （SEM）, ultraviolet- visible spectroscopy （UV-Vis） and photoluminescence spectroscopy （PL）. The photocatalytic activity of the samples was evaluated by the photocatalytic degradation of methyl orange （MO） aqueous solution under visible light irradiation. The results indicate that the Cu2O/TiO2/Pt composite films are made up of three layers which are Pt layer, anatase-TiO2 layer and Cu2O layer from bottom to top. The surface of the films is even and composed of regular-shaped spherical particles. The photocatalytic activity of the Cu2O/TiO2/Pt three-layer film is much higher than that of the Cu2O/TiO2 double-layer film. Such enhancement is ascribed to the presence of Pt layer, which further inhibits the photogenerated electron-hole recombination, prolongs the lifetime of the photogenerated carriers, increases the quantum efficiency and hence improves the photocatalytic activity of the film effectively.
文摘Non-isothermal kinetic research has been carried out on oxidation behavior of β-Sialon in diphaseβ-Sialon/Al_2O_3 composite at high temperatures. A kinetic formula is established for non-isothermal oxidation process of β-Sialon. The rate of oxidation process is controlled by chemicalreaction at the initial stage and then by diffusion. The apparent activation energies and appar-ent rate constants at different temperatures are determined by treating TG data of the overallprocess.
文摘The preferred internal oxidation of aluminum in Cu Al alloy was used to obtain in situ Al 2O 3/Cu composites. The reinforcement particles were mainly γ Al 2O 3, some θ Al 2O 3 and a little α Al 2O 3. Thermodynamics analyses show that the chemical reactions are 3Cu 2O+2Al=6Cu+Al 2O 3 or 3CuO+2Al=3Cu+Al 2O 3. A related equilibrium diagram was drawn. The experiments and investigation show that the formation rate of Al 2O 3 was controlled by the diffusion of oxygen in matrix.
基金Project(2007AA03Z548) supported by High-Tech Research and Development Program of ChinaProject(50971066) supported by the National Natural Science Foundation of ChinaProject(1283000349) supported by the Jiangsu University Research Fund for Advanced Scholars,China
文摘Aluminum matrix composites reinforced by in situ Al2O3 and Al3Zr particles are fabricated from A356-Zr(CO3)2 system via magnetochemistry reaction,and the morphologies,sizes and distributions of the in situ particles as well as the microstructures,mechanical mechanisms of the composites are investigated by XRD,SEM,TEM and in situ tensile tests.The results indicate that with the pulsed magnetic field assistance,the morphologies of the in situ particles are mainly with ball-shape,the sizes are in nanometer scale and the distributions in the matrix are uniform.The interfaces between the in situ particles and the aluminum matrix are net and no interfacial outgrowth is observed.These are due to the strong vibration induced by the applied magnetic field in the aluminum melt,which in turn,accelerates the melt reactions.The effects of the magnetic field on the above contributions are discussed in detail.
基金Project(2012MS0801)supported by the Natural Science Foundation of Inner Mongolia,China
文摘Al2O3p-Al composites were synthesized using an in-situ reaction in the 80%Al-20%CuO （mass fraction） system. The effects of the CuO particle size on the synthesis temperature and microstructure of the composites were investigated by various methods. The results indicate that the CuO particle size has a significant effect on the temperature at which the complete reaction in the Al-CuO system occurs：the temperature is 200 ℃ lower in the Al-CuO system containing CuO particles with sizes less than 6μm than that containing CuO particles with sizes less than 100μm. The interfacial bonding between Al2O3 particles and Al is not complete when the temperature is below a critical value. The morphology of the Al2O3 particles varies from ribbon-like shape to near spherical shape when the temperature is above a critical value. These two critical temperatures are affected by the particle size of CuO, and the critical temperature of the sample containing CuO particles with sizes less than 6μm is 100 ℃ lower than that of the sample containing CuO particles with sizes less than 100μm.
文摘Al2O3 particle-reinforced ZL109 composite was prepared by in situ reaction between CuO and Al2O3 . The microstructure was observed by means of OM, SEM and TEM. The Al2O3 particles in sub-micron sizes distribute uniformly in the matrix, and the Cu displaced from the in situ reaction forms net-like alloy phases with other alloy elements. The hardness and the tensile strength of the composites at room temperature have a slight increase as compared to that of the matrix. However, the tensile strength at 350℃ has reached 90.23 MPa, or 16.92 MPa higher than that of the matrix. The mechanism of the reaction in the CuO/AI system was studied by using of differential scanning calorimetry（DSC） and thermodynamic calculation. The reaction between CuO and Al involves two steps. First, CuO reacts with Al to form Cu20 and Al2O3 at the melting temperature of the matrix alloy, and second, Cu20 reacts with Al to form Cu and Al2O3 at a higher temperature. At ZL109 casting temperature of 750- 780 ℃, the second step can also take place because of the effect of exothermic reaction of the first step.
文摘Studies the combustion synthesis of Al Ti TiO 2 system and concludes that, due to its low exothermic nature, a stable combustion wave can be maintained only when the system is ignited at a certain preheating temperature, and coupled with appropriate pseudo HIP process, dense TiAl/Al 2O 3 composites with density as high as 97% of the theoretical value can be produced, and points out. Microstructure observation shows in situ formed Al 2O 3 particles are of an average size smaller than one micron, and the hardness of TiAl matrix is enhanced by introduction of these particles.
文摘The interaction between Zn-AI eutectic alloy and Al203p/6061AI composites in the vacuum furnace was investigated. Great attention has been paid to the elements diffusion, the microstructure and formation of the interface between Zn-AI eutectic alloy and Al2O3p/6061AI composites. Experimental results show that Zn-AI eutectic alloy has a good wetting ability to Al2O3p/6061 Al composites and the wetting angle decreases with increasing the temperature in vacuum. After the interaction, an interaction layer forms between Zn-AI alloy and Al2O3p/6061 Al composites. The phases in the interaction layer mainly consist of α-AI(Zn), Al2O3 and CuZn5 resulted from the diffusion of elements from the Zn-AI alloy. Several porosities distribute in the region near the interface of the Zn-AI alloy/interaction layer. The amount of shrinkage voids in the interacting layer is relevant to the penetration of Zn element into Al2O3p/6061Al composites which is a function of temperature. So it is necessary to lower heating temperature in order to limit the Zn penetration.
基金financially supported by the National Natural Foundation of China (No.51201047)National Basic Research Program of China (No.2012CB619600)
文摘In situ （Al2O3-Si）/Al composites with a reinforcement volume fraction of 10% were synthesized from the Al-SiO2 system using low energy ball milling and reaction hot pressing. Differential thermal analysis was used to investigate the reaction mechanisms between SiO2 and Al. X-ray diffraction results revealed that the reaction between Al and SiO2 took place completely at 900 ℃ with a holding time of 2 h, thereby forming Al2O3 and Si. Scanning electron microscopic, energy dispersive X-ray spectroscopic, and transmission electron microscopic （TEM） results showed that the in situ synthesized A1203 and Si particles, whose sizes are less than 2 μm, were polygonal in shape and dispersed uniformly in the matrix. Moreover, Al2O3 particle size showed a tendency to increase from - 2 to - 6 μm when the synthesis temperature was increased. Furthermore, TEM observation showed that the interface between the reinforcements and Al matrix is clean. The yield strength, ultimate tensile strength, and Brinell hardness of the in situ （Al2O3-Si）/Al composite was significantly higher than the aluminum matrix. Mechanisms governing the tensile fracture process are discussed.
基金Project supported by the National Natural Science Foundation of China(51671034)。
文摘A tritium permeation barrier is required in fusion blankets for the reduction of fuel loss and radiological hazard.In this study,an Al2O3/Y2O3 composite coating was prepared on 316 L stainless steel by radiofrequency magnetron sputtering in order to improve the tritium permeation resistance.The microstructure and the phase composition of the Al2O3/Y2O3 composite coating are observed by scanning electron microscopy,transmission electron microscopy and grazing incidence X-ray diffraction.Moreover,Auger electron spectroscopy was used to characterize the depth profiles of Al,Y and O elements.The results clearly indicate that the Al2O3/Y2O3 composite coating is fully dense and the total thickness is approximately 340 nm.The Al2O3/Y2O3 coating consists of an amorphous Al2O3 and the cubic Y2O3,in which Al,Y and O elements are homogeneously distributed in the vertical base direction.Furthermore,the deuterium permeation property of the Al2O3/Y2O3 composite coating was measured by the gas phase permeation method.The results show that the introduction of an interface and the existence of a tiny amount of micro-defects improve the deuterium resistance of the Al2O3/Y2O3 coating,and its deuterium permeation reduction factor is 536-750 at 873-973 K.Therefore,it is concluded that the Al2O3/Y2O3 co mposite coating as deuterium permeation barrier can significa ntly enha nce the deuterium permeation resistance property.
基金Henan Innovation Project for University Prominent Research Talents (2007KYCX008)Henan Major Science and Technol-ogy Project (0523021500)+1 种基金Henan University of Science and Technology Major Pre-research Foundation (2005ZD003)Henan University of Science and Technology Personnel Scientific Research Foundation
文摘Alumina dispersion strengthened copper composite （nano-Al2O3/Cu composite） was recently emerged as a kind of potentially viable and attractive engineering material for applications requiring high strength, high thermal and electrical conductivities and resistance to softening at elevated temperatures. The nano-Al2O3/Cu composite was produced by internal oxidation. The microstructures of the composite were analyzed by the TEM and its hot deformation behavior was investigated by means of continuous compression tests performed on a Gleeble 1500 thermo-simulator. Making use of the modified algorithm-Levenberg-Marquardt （L-M） algorithm BP neural network, a model for predicting the flow stresses during hot deformation was set up on the base of the experimental data. Results show that the microstructures of the composite are characterized by uniform distribution of nano-Al2O3 particles in Cu-matrix. The sliding of dislocations is the main deformation mechanism. The dynamic recovery is the main softening mode with the flow stress decreasing gently from 500℃ to 850 ~C. The recrystallization of Cu-matrix can be retarded late into as high as 850 ℃, when it happens only partially. The well-trained BP neural network model can accurately describe the influence of the temperature, strain rate, and true strain on the flow stresses, therefore, it can precisely predict the flow stresses of the composite under given deforming conditions and provide a new way to optimize hot deforming process parameters.
基金国家自然科学基金，Foundation of State Key Laboratory of Advanced Technology for Materials Synthesis and Processing，Wuhan University of Technology
文摘Al/Al203 composites of different ratios were hot-press sintered at 575~640℃ under a pressure of 30 MPa for 2 h in a vacuum furnace. It was found that the relative density of the Al/Al203 composites could be increased evidently with the rise of sinter temperature. No reaction occurred between At and Al203 at the sinter temperatures. Under 640℃-30 MPa-2 h experimental condition, Al/Al203 system FGM was successfully fabricated, and its density range changed quasi-continuously from 2.887×103 kg/m3 to 3.1909×103 kg/m3 within the middle 1.0 mm thickness range.
基金financially supported by the Inner Mongolia Science and Technology Reward Foundation(No.20101707)the Inner Mongolia Natural Science Foundation(No.2013MS0804)+1 种基金the Inner Mongolia High School Scientific Research Foundation(No.NJZZ14056)the Inner Mongolia University of Technology Foundation(No.ZD20120015)
文摘Hot compression behavior of TiC–Al2O3/Al composites was studied using the Gleeble-1500 system at a temperature range of 300–550 °C and at strain rate range of 0.01–10.00 s-1. The associated structural changes were studied by TEM observations. The results show that stress level decreases with deformation temperature increasing and strain rate decreasing, which can be represented by a Zener–Hollomon parameter in an exponent-type equation with hot deformation activation energy Q of 172.56 kJ·mol-1.Dynamic recovery occurs easily when strain rates are less than 10.00 s-1. Dynamic recrystallization can occur at strain rate of 10.00 s-1.