β-Sialon has emerged as a promising material for enhancing the service life of Al_(2)O_(3)-C refractories due to its excellent physicochemical properties.The impact of varying concentrations of nanometer Al/Si alloy ...β-Sialon has emerged as a promising material for enhancing the service life of Al_(2)O_(3)-C refractories due to its excellent physicochemical properties.The impact of varying concentrations of nanometer Al/Si alloy on the in-situ synthesis of β-Sialon within Al_(2)O_(3)-C refractory materials,as well as its oxidation behavior,was investigated.The findings indicate that the presence of Al/Si alloy promotes the formation of AlN and SiC whiskers at 1300℃,which subsequently facilitate the production of plate-like β-Sialon at 1500℃.Density functional theory analysis reveals that the(020)crystal plane of β-Sialon exhibits the lowest adsorption energy for Al2O and AlO molecules under the influence of iron atoms,suggesting a solid-liquid-vapor growth mechanism for β-Sialon formation.The introduction of these ceramic phases significantly enhances the mechanical properties of Al_(2)O_(3)-C refractories.Specifically,the addition of 6 wt.%Al/Si alloy yielded specimens with the highest cold modulus of rupture and cold crushing strength at 1500℃,achieving values of 35.2 and 127.5 MPa,respectively--representing increases of 40.1%and 37.4%.Furthermore,during high-temperature oxidation,the formation of plate-like β-Sialon leads to the development of a dense protective layer on the surface.This impedes the diffusion pathways of oxygen and consequently enhances the oxidation resistance of the refractory.展开更多
基金supported by the Natural Science Foundation of Henan Province(No.232300420329)Key Scientific Research Project of Colleges and Universities in Henan Province(Nos.23B430012,22A430028,and 25B430022)+2 种基金Henan Provincial Science and Technology Research Project(No.242102231064)National Natural Science Foundation of China(No.52202064)Luoyang Major Science and Technology Innovation Project(No.2301009A).
文摘β-Sialon has emerged as a promising material for enhancing the service life of Al_(2)O_(3)-C refractories due to its excellent physicochemical properties.The impact of varying concentrations of nanometer Al/Si alloy on the in-situ synthesis of β-Sialon within Al_(2)O_(3)-C refractory materials,as well as its oxidation behavior,was investigated.The findings indicate that the presence of Al/Si alloy promotes the formation of AlN and SiC whiskers at 1300℃,which subsequently facilitate the production of plate-like β-Sialon at 1500℃.Density functional theory analysis reveals that the(020)crystal plane of β-Sialon exhibits the lowest adsorption energy for Al2O and AlO molecules under the influence of iron atoms,suggesting a solid-liquid-vapor growth mechanism for β-Sialon formation.The introduction of these ceramic phases significantly enhances the mechanical properties of Al_(2)O_(3)-C refractories.Specifically,the addition of 6 wt.%Al/Si alloy yielded specimens with the highest cold modulus of rupture and cold crushing strength at 1500℃,achieving values of 35.2 and 127.5 MPa,respectively--representing increases of 40.1%and 37.4%.Furthermore,during high-temperature oxidation,the formation of plate-like β-Sialon leads to the development of a dense protective layer on the surface.This impedes the diffusion pathways of oxygen and consequently enhances the oxidation resistance of the refractory.
基金National Natural Science Foundation of China (50402026)Science Technology Foundation of Zhejiang Province in China (2008C31002)National Science Foundation of Shanghai (09ZR1437700)
文摘研究了阻挡层 Al2O3对应变 SiGe 上 HfO2薄膜的热稳定性和电学可靠性的影响。高分辨透射电镜(HRTEM)像表明,阻挡层使HfO2在 700 ℃温度下退火后仍然是非晶的。散能 X 射线谱(EDS)分析表明,阻挡层抑制了 Si 原子在 HfO2薄膜中的扩散。X 射线光电子谱(XPS)测试表明,阻挡层抑制了界面处 HfSiO 和 GeOx的生长。电学测试分析说明,带有阻挡层的 MIS 电容的电学性能得到提高,包括60Co γ射线辐射后较高的电容密度、较低的缺陷密度、以及较小的平带电压漂移。
