We studied the local structure and properties of six-fold coordinated silicon(Si[6]) in BaOSiO2-P2O5 glasses. Nuclear magnetic resonance(NMR) and Raman spectroscopy revealed the existence of sixfold coordinated silico...We studied the local structure and properties of six-fold coordinated silicon(Si[6]) in BaOSiO2-P2O5 glasses. Nuclear magnetic resonance(NMR) and Raman spectroscopy revealed the existence of sixfold coordinated silicon species and network former units(NFUs) in the BaO-SiO2-P2O5 glasses. The glass transition temperature(Tg), which was measured by differential scanning calorimetry, increased rapidly along with the increase of SiO2 from 0 to 10 mol%, then declined and finally increased again, which showed a "Z" trend along with the increase of SiO2 while the density of the glasses showed the opposite trend. When the addition of SiO2 is 16 mol%, Tg decreased to an extremely low value(807.9 K). Besides, the Vickers indentation hardness(Hv) had been significantly enhanced from 4.66 to 6.63 GPa by adding 16 mol% SiO2. Furthermore, the liquid fragility index(m) of the glasses declined slowly firstly and then increased rapidly when the amount of SiO2 is greater than 13 mol%.展开更多
基金Funded by National Natural Science Foundation of China(Nos.51772223,51372180)
文摘We studied the local structure and properties of six-fold coordinated silicon(Si[6]) in BaOSiO2-P2O5 glasses. Nuclear magnetic resonance(NMR) and Raman spectroscopy revealed the existence of sixfold coordinated silicon species and network former units(NFUs) in the BaO-SiO2-P2O5 glasses. The glass transition temperature(Tg), which was measured by differential scanning calorimetry, increased rapidly along with the increase of SiO2 from 0 to 10 mol%, then declined and finally increased again, which showed a "Z" trend along with the increase of SiO2 while the density of the glasses showed the opposite trend. When the addition of SiO2 is 16 mol%, Tg decreased to an extremely low value(807.9 K). Besides, the Vickers indentation hardness(Hv) had been significantly enhanced from 4.66 to 6.63 GPa by adding 16 mol% SiO2. Furthermore, the liquid fragility index(m) of the glasses declined slowly firstly and then increased rapidly when the amount of SiO2 is greater than 13 mol%.