In order to improve dry sliding wear resistance of pure aluminum against steel, aluminum-based composites reinforced with different contents of SiC,MoS2 and SiC/MoS2 particles were synthesized by press and sintering o...In order to improve dry sliding wear resistance of pure aluminum against steel, aluminum-based composites reinforced with different contents of SiC,MoS2 and SiC/MoS2 particles were synthesized by press and sintering of the corresponding powder mixtures. The microstructural evaluations showed a dense microstructure which were in good agreement with the result of density and hardness measurements. The results of pin on disk wear tests performed against an AISI 52100 steel pin at a constant load and sliding velocity showed that there was a critical content for both types of the reinforcements at which the lowest wear rate was obtained, i.e. 10 vol.% and 2 vol.%, respectively,for Al/SiC and Al/MoS2 composites. However,the lowest wear rate and friction of coefficient were attained for Al/10 SiC/2 MoS2 hybrid composite. According to the scanning electron microscope observations, the predominant wear mechanism was changed from adhesion to abrasion mostly whenMoS2 particles were incorporated in the pure aluminum. Mild delamination was identified as the main wear mechanism for Al/SiC and Al/SiC/MoS2 composites. The frictional traces and worn surfaces of Al/SiC/MoS2 composites approached to those of Al/SiC composites,indicating the dominant role of SiC particles in tribological behavior of the hybrid composites.展开更多
The effects of dry O_(2)post oxidation annealing(POA)at different temperatures on SiC/SiO_(2)stacks are comparatively studied in this paper.The results show interface trap density(Dit)of SiC/SiO_(2)stacks,leakage curr...The effects of dry O_(2)post oxidation annealing(POA)at different temperatures on SiC/SiO_(2)stacks are comparatively studied in this paper.The results show interface trap density(Dit)of SiC/SiO_(2)stacks,leakage current density(Jg),and time-dependent dielectric breakdown(TDDB)characteristics of the oxide,are affected by POA temperature and are closely correlated.Specifically,Dit,Jg,and inverse median lifetime of TDDB have the same trend against POA temperature,which is instructive for SiC/SiO_(2)interface quality improvement.Moreover,area dependence of TDDB characteristics for gate oxide on SiC shows different electrode areas lead to same slope of TDDB Weibull curves.展开更多
文摘In order to improve dry sliding wear resistance of pure aluminum against steel, aluminum-based composites reinforced with different contents of SiC,MoS2 and SiC/MoS2 particles were synthesized by press and sintering of the corresponding powder mixtures. The microstructural evaluations showed a dense microstructure which were in good agreement with the result of density and hardness measurements. The results of pin on disk wear tests performed against an AISI 52100 steel pin at a constant load and sliding velocity showed that there was a critical content for both types of the reinforcements at which the lowest wear rate was obtained, i.e. 10 vol.% and 2 vol.%, respectively,for Al/SiC and Al/MoS2 composites. However,the lowest wear rate and friction of coefficient were attained for Al/10 SiC/2 MoS2 hybrid composite. According to the scanning electron microscope observations, the predominant wear mechanism was changed from adhesion to abrasion mostly whenMoS2 particles were incorporated in the pure aluminum. Mild delamination was identified as the main wear mechanism for Al/SiC and Al/SiC/MoS2 composites. The frictional traces and worn surfaces of Al/SiC/MoS2 composites approached to those of Al/SiC composites,indicating the dominant role of SiC particles in tribological behavior of the hybrid composites.
基金the General Program of the National Natural Science Foundation of China(Grant No.61974159)the Youth Innovation Promotion Association of the Chinese Academy of Sciences and Scientific Instrument Developing Project of the Chinese Academy of Sciences(Grant No.YJKYYQ20200039)。
文摘The effects of dry O_(2)post oxidation annealing(POA)at different temperatures on SiC/SiO_(2)stacks are comparatively studied in this paper.The results show interface trap density(Dit)of SiC/SiO_(2)stacks,leakage current density(Jg),and time-dependent dielectric breakdown(TDDB)characteristics of the oxide,are affected by POA temperature and are closely correlated.Specifically,Dit,Jg,and inverse median lifetime of TDDB have the same trend against POA temperature,which is instructive for SiC/SiO_(2)interface quality improvement.Moreover,area dependence of TDDB characteristics for gate oxide on SiC shows different electrode areas lead to same slope of TDDB Weibull curves.