A new method was proposed for preparing AZ31/1060 composite plates with a corrugated interface,which involved cold-pressing a corrugated surface on the Al plate and then hot-pressing the assembled Mg/Al plate.The resu...A new method was proposed for preparing AZ31/1060 composite plates with a corrugated interface,which involved cold-pressing a corrugated surface on the Al plate and then hot-pressing the assembled Mg/Al plate.The results show that cold-pressing produces intense plastic deformation near the corrugated surface of the Al plate,which promotes dynamic recrystallization of the Al substrate near the interface during the subsequent hot-pressing.In addition,the initial corrugation on the surface of the Al plate also changes the local stress state near the interface during hot pressing,which has a large effect on the texture components of the substrates near the corrugated interface.The construction of the corrugated interface can greatly enhance the shear strength by 2−4 times due to the increased contact area and the strong“mechanical gearing”effect.Moreover,the mechanical properties are largely depended on the orientation relationship between corrugated direction and loading direction.展开更多
The Mg−Al composite rods of aluminum core-reinforced magnesium alloy were prepared by the extrusion−shear(ES)process,and the microstructure,deformation mechanism,and mechanical properties of the Mg−Al composite rods w...The Mg−Al composite rods of aluminum core-reinforced magnesium alloy were prepared by the extrusion−shear(ES)process,and the microstructure,deformation mechanism,and mechanical properties of the Mg−Al composite rods were investigated at different extrusion temperatures and shear stresses.The experimental results show that the proportion of dynamic recrystallization(DRX)and texture for Al and Mg alloys are controlled by the combination of temperature and shear stress.The texture type of the Al alloys exhibits slight variations at different temperatures.With the increase of temperature,the DRX behavior of Mg alloy shifts from discontinuous DRX(DDRX),continuous DRX(CDRX),and twin-induced DRX(TDRX)dominant to CDRX,the dislocation density in Mg alloy grains decreases significantly,and the average value of Schmid factor(SF)of the basalslip system increases.In particular,partial grains exhibit a distinct dominant slip system at 390℃.The hardness and thickness of the bonding layer,as well as the yield strength and elongation of the Mg alloy,reach their maximum at 360℃as a result of the intricate influence of the combined temperature and shear stress.展开更多
Cu/Al composite plates were fabricated using rolling and underwater explosive welding techniques,separately,to compare their interfacial microstructures and mechanical performance.Interface morphology,grain orientatio...Cu/Al composite plates were fabricated using rolling and underwater explosive welding techniques,separately,to compare their interfacial microstructures and mechanical performance.Interface morphology,grain orientation,grain boundary characteristics,and phase distribution were analyzed through optical microscope,scanning electron microscope,and electron backscattered diffractometer.Mechanical properties were assessed using tensile shear tests,90°bending tests,and hardness measurements.Vickers hardness and nanoindentation test results further provided information on the hardness distributions.Results indicate that the diffusion layer in rolled Cu/Al composites is relatively fragile,while that produced by underwater explosive welding features a diffusion layer of approximately 18μm in thickness,which is metallurgically bonded through atomic diffusion.The tensile shear strength of these composites ranges from 64.45 MPa to 70.84 MPa,and in the 90°three-point bending test,the underwater-explosive-welded samples exhibit superior flexural performance.This study elucidates the effects of different manufacturing methods on the interfacial properties and mechanical performance of Cu/Al composites,offering essential insights for the selection of manufacturing methods and applications.展开更多
In this study,microstructure and mechanical behavior of Mg/Al composite plates with Ti foil interlayer were systematically studied,with a great emphasis on the effect of different thicknesses of Ti foil interlayer.The...In this study,microstructure and mechanical behavior of Mg/Al composite plates with Ti foil interlayer were systematically studied,with a great emphasis on the effect of different thicknesses of Ti foil interlayer.The results show that compared to 100μm thick Ti foil,10μm thick Ti foil is more prone to fracture and is evenly distributed in fragments at the interface.The introduction of Ti foil can effectively refine the grain size of Mg layers of as-rolled Mg/Al composite plates,10μm thick Ti foil has a better refining effect than 100μm thick Ti foil.Ti foil can effectively increase the yield strength(YS)and ultimate strength(UTS)of as-rolled Mg/Al composite plates,10μm thick Ti foil significantly improves the elongation(El)of Mg/Al composite plate,while 100μm thick Ti foil slightly weakens the El.After annealing at 420℃ for 0.5 h and 4 h,Ti foil can inhibit the formation of intermetallic compounds(IMCs)at the interface of Mg/Al composite plates,which effectively improves the YS,UTS and El of Mg/Al composite plates.In addition,Ti foil can also significantly enhance the interfacial shear strength(SS)of Mg/Al composite plates before and after annealing.展开更多
High-volume fraction silicon particle-reinforced aluminium matrix composites(Si/Al)are increasingly applied in aerospace,radar communications,and large-scale integrated circuits because of their superior thermal condu...High-volume fraction silicon particle-reinforced aluminium matrix composites(Si/Al)are increasingly applied in aerospace,radar communications,and large-scale integrated circuits because of their superior thermal conductivity,wear resistance,and low thermal expansion coefficient.However,the abrasive and adhesive wear caused by the hard silicon reinforcement and the ductile aluminium matrix leads to significant tool wear,decreased machining efficiency,and compromised surface quality.This study combines theoretical analysis and cutting experiments to investigate polycrystalline diamond(PCD)tool wear during milling of 70 vol%Si/Al composite.A key contribution of this work is the development of a tool wear model that incorporates reinforcement particle characteristics,treating them as ellipsoidal structures,which enhances the accuracy of predicting abrasive and adhesive wear mechanisms.The model is based on abrasive and adhesive wear mechanisms,and can analyze the interaction between silicon particles,aluminium matrix,and tool components,thus providing deeper insights into PCD tool wear processes.Experimental validation of the model shows a good agreement with the results,with a mean deviation of approximately 10%.The findings on the tool wear mechanism reveal that,as tool wear progresses,the proportion of abrasive wear increases from 40%in the running-in stage to 75%in the rapid wear stage,while adhesive wear decreases.The optimal machining parameters of 120 m·min^(–1) cutting speed(v_(c))and 0.04 mm·z^(–1) feed rate(f_(z)),result in tool life of 33 min and surface roughness(S_(a))of 2.2μm.The study uncovers the variation patterns of abrasive and adhesive wear during the tool wear process,and the proposed model offers a robust framework for predicting tool wear during the machining of high-volume fraction Si/Al composites.The research findings also offer key insights for optimizing tool selection and machining parameters,advancing both the theoretical understanding and practical application of PCD tool wear.展开更多
Edge defects significantly impact the forming quality of Mg/Al composite plates during the rolling process.This study aims to develop an effective rolling technique to suppress these defects.First,an enhanced Lemaitre...Edge defects significantly impact the forming quality of Mg/Al composite plates during the rolling process.This study aims to develop an effective rolling technique to suppress these defects.First,an enhanced Lemaitre damage model with a generalized stress state damage prediction mechanism was used to evaluate the key mechanical factors contributing to defect formation.Based on this evaluation,an embedded composite rolling technique was proposed.Subsequently,comparative validation was conducted at 350℃ with a 50% reduction ratio.Results showed that the plates rolled using the embedded composite rolling technique had smooth surfaces and edges,with no macroscopic cracks observed.Numerical simulation indicated that,compared to conventional processes,the proposed technique reduced the maximum edge stress triaxiality of the plates from-0.02 to-1.56,significantly enhancing the triaxial compressive stress effect at the edges,which suppressed void nucleation and growth,leading to a 96%reduction in damage values.Mechanical property evaluations demonstrated that,compared to the conventional rolling process,the proposed technique improved edge bonding strength and tensile strength by approximately 67.7%and 118%,respectively.Further microstructural characterization revealed that the proposed technique,influenced by the restriction of deformation along the transverse direction(TD),weakened the plastic flow in the TD and enhanced plastic flow along the rolling direction(RD),resulting in higher grain boundary density and stronger basal texture.This,in turn,improved the toughness and transverse homogeneity of the plates.In summary,the embedded composite rolling technique provides crucial technical guidance for the preparation of Mg-based composite plates.展开更多
Non-isothermal aging(NIA)treatments have presented significant advantages in improving the comprehensive performance and aging hardening efficiency of the 7000 series aluminum alloys,but there is no attention paid to ...Non-isothermal aging(NIA)treatments have presented significant advantages in improving the comprehensive performance and aging hardening efficiency of the 7000 series aluminum alloys,but there is no attention paid to their composites.This study takes a linear heating aging process as an example to reveal the precipitation behaviors of a 15 vol.%SiC/7085Al composite as well as its impact on mechanical properties using differential scanning calorimetry,transmission electron microscopy,small-angle neutron scattering,hardness measurements,and tensile testing.The results indicated the formation of GP(Ⅰ,Ⅱ)zones,η’andηprecipitates in sequence,leading to the hardness and strength initially increasing and then decreasing with rising NIA temperatures.The maximums were reached at 183℃,corresponding to the appearance ofη’precipitates in large quantities.Owing to the rapid temperature rise during the NIA process,the precipitates entered the coarsening and redissolution stage before they were entirely formed,resulting in reduced peak strength compared to the T6 treatment.The composite exhibited a more significant reduction in strength than the 7085Al alloy because:(i)the annihilation of vacancies suppressed the formation of GPII zones,thereby weakening their transition toη’precipitates;(ii)quenching dislocations promoted the coarsening of precipitates.An improved NIA process,incorporating both heating and cooling aging treatments,was effectively designed with the assistance of in-situ SANS technology to address this issue,which allows for achieving strength comparable to that after the T6 treatment with only 15%of the aging time consumption.This research fills the gap in investigating the NIA precipitation behaviors of aluminum matrix composites,providing guidance for the formulation of NIA schedules.展开更多
SiC-reinforced aluminum matrix(SiCp/Al)composite is widely utilized in the aerospace,automotive,and electronics industries due to the combination of ceramic hardness and metal toughness.However,the significant dispari...SiC-reinforced aluminum matrix(SiCp/Al)composite is widely utilized in the aerospace,automotive,and electronics industries due to the combination of ceramic hardness and metal toughness.However,the significant disparity in properties between SiC particles and the aluminum matrix results in severe tool wear and diminished surface quality during conventional machining.This study proposes an environmentally friendly and clean dry electrical discharge assisted grinding process as an efficient and low-damage machining method for SiCp/Al.An experimental platform was set up to study the impact of grinding and discharge process parameters on surface quality.The study compared the chip formation mechanism and surface quality between dry electrical discharge assisted grinding and conventional grinding,revealing relationships between surface roughness,grinding force,grinding temperature,and related parameters.The results indicate that the proposed grinding method leads to smaller chip sizes,lower grinding forces and temperatures,and an average reduction of 19.2%in surface roughness compared to conventional grinding.The axial,tangential,and normal grinding forces were reduced by roughly 10.5%,37.8%,and 23.0%,respectively.The optimized process parameters were determined to be N=2500 r/min,vf=30 mm/min,a=10μm,E=15 V,f=5000 Hz,dc=80%,resulting in a surface roughness of 0.161μm.展开更多
Improving the thermal conductivity(TC)of diamond–metal composites has always been a significant challenge in the field of thermal management.In this paper,diamond/Al composites are systematically studied,and the infl...Improving the thermal conductivity(TC)of diamond–metal composites has always been a significant challenge in the field of thermal management.In this paper,diamond/Al composites are systematically studied,and the influence of the holding time(10–120 min)on interface structure and TC is discussed.The results of this research show that longterm thermal diffusion sintering can achieve dense interfacial bonding in diamond/Al composites,enhancing their TC.Diamond/Al composites with 50 vol%of 900μm diamond attain the highest TC value of 888.73 W·m^(-1)·K^(-1)under sintering conditions of 650?C,50 MPa,and 120 min—nearly 92%of the theoretical value predicted by the Maxwell model.This study establishes that high TC can be achieved through long-term thermal diffusion alone,without the need for complex diamond surface coating or substrate alloying.展开更多
1060/7050 Al/Al laminated metal composites(LMCs)with heterogeneous lamellar structures were prepared by accumulative roll bonding(ARB),cold rolling and subsequent annealing treatment.The strengthening mechanism was in...1060/7050 Al/Al laminated metal composites(LMCs)with heterogeneous lamellar structures were prepared by accumulative roll bonding(ARB),cold rolling and subsequent annealing treatment.The strengthening mechanism was investigated by microstructural characterization,mechanical property tests and in-situ fracture morphology observations.The results show that microstructural differences between the constituent layers are present in the Al/Al LMCs after various numbers of ARB cycles.Compared with rolled 2560-layered Al/Al LMCs with 37.5%and 50.0%rolling reductions,those with 62.5%rolling reductions allow for more effective improvements in the mechanical properties after annealing treatment due to their relatively high mechanical incompatibility across the interface.During tensile deformation,with the increased magnitude of incompatibility in the 2560-layered Al/Al LMC with a heterogeneous lamellar structure,the densities of the geometrically necessary dislocations(GNDs)increase to accommodate the relatively large strain gradient,resulting in considerable back stress strengthening and improved mechanical properties.展开更多
Titanium/magnesium alloy bimetal composites show promising prospects for lightweight applications.The Ti/Mg bimetal composite was fabricated in Ti−6Al−4V pyramidal lattice structure via AZ91D melt infiltration.Compara...Titanium/magnesium alloy bimetal composites show promising prospects for lightweight applications.The Ti/Mg bimetal composite was fabricated in Ti−6Al−4V pyramidal lattice structure via AZ91D melt infiltration.Comparative analysis of the tensile and compressive properties was conducted between the composite and its constituent materials(Ti−6Al−4V lattice structure and AZ91D matrix).The tensile strength of the composite(95.9 MPa)was comparable to that of the Ti−6Al−4V lattice structure(94.4 MPa)but lower than that of the AZ91D alloy(120.8 MPa)due to gaps at the bimetal interfaces hindering load transfer during tension.The composite exhibited greater elongation(1.7%)compared to AZ91D(1.4%)alloy but less than the Ti−6Al−4V lattice structure(2.6%).The compressive performance of the composite outperformed that of the Ti−6Al−4V lattice structure,underscoring the significance of the AZ91D alloy in compressive deformation.Fracture analysis indicated that the predominant failure reasons in both the composite and lattice structures were attributed to the breakage of lattice struts at nodes caused by the stress concentration.展开更多
Carbon fiber reinforced aluminum matrix （Cf/Al） composite has many excellent properties, and it has received more and more attention. Two-dimensional （2D） Cf/Al composites were fabricated by vacuum and pressure in...Carbon fiber reinforced aluminum matrix （Cf/Al） composite has many excellent properties, and it has received more and more attention. Two-dimensional （2D） Cf/Al composites were fabricated by vacuum and pressure infiltration, which was an integrated technique and could provide high vacuum and high infiltration pressure. The effect of specific pressure on the infiltration quality of the obtained composites was comparatively evaluated through microstructure observation. The experimental results show that satisfied Cf/Al composites could be fabricated at the specific pressure of 75 MPa. In this case, the preform was infiltrated much more completely by aluminum alloy liquid, and the residual porosity was seldom found. It is found that the ultimate tensile strength of the obtained Cf/Al composite reached maximum at the specific pressure of 75 MPa, which was improved by 138.9% compared with that of matrix alloy.展开更多
The thermophysical properties of the SiC /Al composites mixed with diamond（SiC-Dia/Al） were studied through theoretical calculation and experiments. The thermal conductivity and the thermal expansion coefficient of ...The thermophysical properties of the SiC /Al composites mixed with diamond（SiC-Dia/Al） were studied through theoretical calculation and experiments. The thermal conductivity and the thermal expansion coefficient of the SiC-Dia/Al were calculated by differential effective medium（DEM） theoretical model and extended Turner model, respectively. The microstructure of the SiC-Dia/Al shows that the combination between SiC particles and Al is close, while that between diamond particles and Al is not close. The experimental results of the thermophysical properties of the SiC-Dia/Al are consistent with the calculated ones. The calculation results show that when the volume ratio of the diamond particles to the SiC particles is 3：7, the thermal conductivity and the thermal expansion coefficient can be improved by 39% and 30% compared to SiC/Al composites, respectively. In other words, by adding a small amount of diamond particles, the thermophysical properties of the composites can be improved effectively, while the cost increases little.展开更多
35% SiCp/2024 Al（volume fraction） composite was prepared by powder metallurgy method. The microstructures of Si Cp/Al interfaces and precipitate phase/Al interfaces were characterized by HRTEM, and the interface con...35% SiCp/2024 Al（volume fraction） composite was prepared by powder metallurgy method. The microstructures of Si Cp/Al interfaces and precipitate phase/Al interfaces were characterized by HRTEM, and the interface conditions were evaluated by tensile modules of elasticity and Brinell hardness measurement. The results show that the overall Si Cp/Al interface condition in this experiment is good and three kinds of Si Cp/Al interfaces are present in the composites, which include vast majority of clean planer interfaces, few slight reaction interfaces and tiny amorphous interfaces. The combination mechanism of Si C and Al in the clean planer interface is the formation of a semi-coherent interface by closely matching of atoms and there are no fixed or preferential crystallographic orientation relationships between Si C and Al. MgAl2O4 spinel particles act as an intermediate to form semi-coherent interface with SiC and Al respectively at the slight reaction interfaces. When the composite is aged at 190 °C for 9 h after being solution-treated at 510 °C for 2 h, numerous discoid-shaped and needle-shaped nanosized precipitates dispersively exist in the composite and are semi-coherent of low mismatch with Al matrix. The Brinell hardness of composites arrives peak value at this time.展开更多
The deformation behaviors of Al2O3/Al composites were investigated by compressive tests conducted at temperature of 300-450 °C and strain rates of 0.001-1.0 s-1 with Gleeble-1500 D thermal simulator system. The r...The deformation behaviors of Al2O3/Al composites were investigated by compressive tests conducted at temperature of 300-450 °C and strain rates of 0.001-1.0 s-1 with Gleeble-1500 D thermal simulator system. The results show that the flow stress increases with increasing strain rate and decreasing temperature. The hyperbolic sine constitutive equation can describe the flow stress behavior of Al2O3/Al composites, and the deformation activation energy and constitutive equations were calculated. The processing maps of Al2O3/Al-2 μm and Al2O3/Al-1 μm composites at strain of 0.6 were obtained and the optimum processing domains are in ranges of 300-330 °C, 0.007-0.03 s-1 and 335-360 °C, 0.015-0.06 s-1 for hot working, respectively. The instability zones of flow behavior can also be recognized by the maps.展开更多
Al2O3p-Al composites were synthesized using an in-situ reaction in the 80%Al-20%CuO （mass fraction） system. The effects of the CuO particle size on the synthesis temperature and microstructure of the composites were...Al2O3p-Al composites were synthesized using an in-situ reaction in the 80%Al-20%CuO （mass fraction） system. The effects of the CuO particle size on the synthesis temperature and microstructure of the composites were investigated by various methods. The results indicate that the CuO particle size has a significant effect on the temperature at which the complete reaction in the Al-CuO system occurs：the temperature is 200 ℃ lower in the Al-CuO system containing CuO particles with sizes less than 6μm than that containing CuO particles with sizes less than 100μm. The interfacial bonding between Al2O3 particles and Al is not complete when the temperature is below a critical value. The morphology of the Al2O3 particles varies from ribbon-like shape to near spherical shape when the temperature is above a critical value. These two critical temperatures are affected by the particle size of CuO, and the critical temperature of the sample containing CuO particles with sizes less than 6μm is 100 ℃ lower than that of the sample containing CuO particles with sizes less than 100μm.展开更多
In this study,HEA/AI composite interlayer was used to fabricate Ti/Mg bimetal composites by solidliquid compound casting process.The Al layer was prepared on the surface of TC4 alloy by hot dipping,and the FeCoNiCr HE...In this study,HEA/AI composite interlayer was used to fabricate Ti/Mg bimetal composites by solidliquid compound casting process.The Al layer was prepared on the surface of TC4 alloy by hot dipping,and the FeCoNiCr HEA layer was prepared by magnetron sputtering onto the Al layer.The influence of the HEA layer thickness and pouring temperature on interface evolution was investigated based on SEM observation and thermodynamic analysis.Results indicate that the sluggish diffusion effect of HEA can effectively inhibit the interfacial diffusion between Al and Mg,which is conducive to the formation of solid solution,especially when the thickness of HEA is 800 nm.With the increase of casting temperature from 720 ℃ to 730 ℃,740℃,and 750 ℃,α-Al(Mg),α-Al(Mg)+Al3Mg2,Al3Mg2+Al12Mg17,and Al12Mg17+δ-Mg are formed at the interface of Ti/Mg bimetal,respectively.When the thickness of the HEA layer is 800 nm and the pouring temperature is 720 ℃,the bonding strength of the Ti/Mg bimetal can reach the maximum of 93.6 MPa.展开更多
（TiB2＋Al2O3）/NiAl composites were synthesized by self-propagation high-temperature synthesis, and their phase compositions, microstructures and evolution modes were studied. The microstructures and shapes vary with...（TiB2＋Al2O3）/NiAl composites were synthesized by self-propagation high-temperature synthesis, and their phase compositions, microstructures and evolution modes were studied. The microstructures and shapes vary with the TiB2＋Al2O3 content in the NiAl matrix. TiB2 particles take a great variety of elementary shapes such as white bars, plates, herringbones, regular cubes and cuboids. These results outline a strategy of self-assembly processes in real time to build diversified microstructures. Some TiB2 grains in sizes of 2-5μm are embeded in Al2O3 clusters, while a small number of TiB2 particles disperse in the NiAl matrix. It is believed that the higher the TiB2＋Al2O3 content is, the more the regular shapes and homogeneous distributions of TiB2 and Al2O3 will be present in the NiAl matrix.展开更多
After Sn/Pd activating, the SiCp/Al composite with 65% SiC (volume fraction) was coated by electroless Ni?P alloy plating. Surface morphology of the composite and its effect on the Ni?P alloy depositing process and bo...After Sn/Pd activating, the SiCp/Al composite with 65% SiC (volume fraction) was coated by electroless Ni?P alloy plating. Surface morphology of the composite and its effect on the Ni?P alloy depositing process and bonding action of Ni and P atoms in the Ni?P alloy were studied. The results show that inhomogeneous distribution of the Sn/Pd activating points results in preferential deposition of the Ni?P alloy particles on the Al alloy and rough SiC particle surfaces and in the etched caves. The Ni?P alloy film has an amorphous structure where chemical bonding between Ni and P atoms exists. After a continuous Ni?P alloy film formed, electroless Ni?P alloy plating is not affected by surface morphology and characteristics of the SiCp/Al composite any longer, but by the electroless plating process itself. The Ni?P alloy film follows linear growth kinetics with an activation energy of 68.44 kJ/mol.展开更多
The B4C/2024Al composites were successfully produced by pressureless infiltration method, and the effects of heat treatment on phase content and mechanical properties were investigated by X-ray diffraction （XRD）, sc...The B4C/2024Al composites were successfully produced by pressureless infiltration method, and the effects of heat treatment on phase content and mechanical properties were investigated by X-ray diffraction （XRD）, scanning electron microscopy （SEM） and mechanical properties testing. The results show that phases of BnC/2024Al composites include B4C, Al, Al3BC, AlB2 and Al2Cu. The phase species remain unchanged; however, the phase content of the composites changes significantly after heat treatment at the temperature of 660, 700, 800 or 900 ℃ for 12, 24 or 36 h. It is found that the heat treatment results in not only considerable enhancement in hardness, but also reduction in bending strength of the composites. Heat treatment at 800 ℃ for 36 h does best to hardness of the composites, while at 700 ℃ for 36 h it is the most beneficial to their comprehensive mechanical properties.展开更多
基金supported by Guangdong Major Project of Basic and Applied Basic Research, China (No. 2020B0301030006)Fundamental Research Funds for the Central Universities, China (No. SWU-XDJH202313)+1 种基金Chongqing Postdoctoral Science Foundation Funded Project, China (No. 2112012728014435)the Chongqing Postgraduate Research and Innovation Project, China (No. CYS23197)。
文摘A new method was proposed for preparing AZ31/1060 composite plates with a corrugated interface,which involved cold-pressing a corrugated surface on the Al plate and then hot-pressing the assembled Mg/Al plate.The results show that cold-pressing produces intense plastic deformation near the corrugated surface of the Al plate,which promotes dynamic recrystallization of the Al substrate near the interface during the subsequent hot-pressing.In addition,the initial corrugation on the surface of the Al plate also changes the local stress state near the interface during hot pressing,which has a large effect on the texture components of the substrates near the corrugated interface.The construction of the corrugated interface can greatly enhance the shear strength by 2−4 times due to the increased contact area and the strong“mechanical gearing”effect.Moreover,the mechanical properties are largely depended on the orientation relationship between corrugated direction and loading direction.
基金supported by the general project of the National Natural Science Foundation of China(No.52071042)Chongqing Natural Science Foundation Project,China(Nos.CSTB2023NSCQ-MSX0079,cstc2021ycjh-bgzxm0148)Graduate Student Innovation Program of Chongqing University of Technology,China(No.gzlcx20232008).
文摘The Mg−Al composite rods of aluminum core-reinforced magnesium alloy were prepared by the extrusion−shear(ES)process,and the microstructure,deformation mechanism,and mechanical properties of the Mg−Al composite rods were investigated at different extrusion temperatures and shear stresses.The experimental results show that the proportion of dynamic recrystallization(DRX)and texture for Al and Mg alloys are controlled by the combination of temperature and shear stress.The texture type of the Al alloys exhibits slight variations at different temperatures.With the increase of temperature,the DRX behavior of Mg alloy shifts from discontinuous DRX(DDRX),continuous DRX(CDRX),and twin-induced DRX(TDRX)dominant to CDRX,the dislocation density in Mg alloy grains decreases significantly,and the average value of Schmid factor(SF)of the basalslip system increases.In particular,partial grains exhibit a distinct dominant slip system at 390℃.The hardness and thickness of the bonding layer,as well as the yield strength and elongation of the Mg alloy,reach their maximum at 360℃as a result of the intricate influence of the combined temperature and shear stress.
基金Anhui Province Key Research and Development Plan(2022a05020021)China Coal Science and Industry Group Chongqing Research Institute Independent Research and Development Project(2023YBXM58)。
文摘Cu/Al composite plates were fabricated using rolling and underwater explosive welding techniques,separately,to compare their interfacial microstructures and mechanical performance.Interface morphology,grain orientation,grain boundary characteristics,and phase distribution were analyzed through optical microscope,scanning electron microscope,and electron backscattered diffractometer.Mechanical properties were assessed using tensile shear tests,90°bending tests,and hardness measurements.Vickers hardness and nanoindentation test results further provided information on the hardness distributions.Results indicate that the diffusion layer in rolled Cu/Al composites is relatively fragile,while that produced by underwater explosive welding features a diffusion layer of approximately 18μm in thickness,which is metallurgically bonded through atomic diffusion.The tensile shear strength of these composites ranges from 64.45 MPa to 70.84 MPa,and in the 90°three-point bending test,the underwater-explosive-welded samples exhibit superior flexural performance.This study elucidates the effects of different manufacturing methods on the interfacial properties and mechanical performance of Cu/Al composites,offering essential insights for the selection of manufacturing methods and applications.
基金supported by the National Key Research and Development Program of China(2022YFB3708400)the Guangdong Major Project of Basic and Applied Basic Research(2020B0301030006)+4 种基金the Youth Talent Support Programme of Guangdong Provincial Association for Science and Technology(SKXRC202301)the Guangdong Academy of Science Fund(2020GDASYL-20200101001,2023GDASQNRC-0210,2023GDASQNRC-0321)the Guangdong Science and Technology plan project(2023A0505030002)the GINM’Special Project of Science and Technology Development(2023GINMZX-202301020108)Evaluation Project of Guangdong Provincial Key Laboratory(2023B1212060043).
文摘In this study,microstructure and mechanical behavior of Mg/Al composite plates with Ti foil interlayer were systematically studied,with a great emphasis on the effect of different thicknesses of Ti foil interlayer.The results show that compared to 100μm thick Ti foil,10μm thick Ti foil is more prone to fracture and is evenly distributed in fragments at the interface.The introduction of Ti foil can effectively refine the grain size of Mg layers of as-rolled Mg/Al composite plates,10μm thick Ti foil has a better refining effect than 100μm thick Ti foil.Ti foil can effectively increase the yield strength(YS)and ultimate strength(UTS)of as-rolled Mg/Al composite plates,10μm thick Ti foil significantly improves the elongation(El)of Mg/Al composite plate,while 100μm thick Ti foil slightly weakens the El.After annealing at 420℃ for 0.5 h and 4 h,Ti foil can inhibit the formation of intermetallic compounds(IMCs)at the interface of Mg/Al composite plates,which effectively improves the YS,UTS and El of Mg/Al composite plates.In addition,Ti foil can also significantly enhance the interfacial shear strength(SS)of Mg/Al composite plates before and after annealing.
基金supported by the National Natural Science Foundation of China(Grant No.52075255)the Jiangsu Provincial Science and Technology Plan(Grant No.BZ2023005).
文摘High-volume fraction silicon particle-reinforced aluminium matrix composites(Si/Al)are increasingly applied in aerospace,radar communications,and large-scale integrated circuits because of their superior thermal conductivity,wear resistance,and low thermal expansion coefficient.However,the abrasive and adhesive wear caused by the hard silicon reinforcement and the ductile aluminium matrix leads to significant tool wear,decreased machining efficiency,and compromised surface quality.This study combines theoretical analysis and cutting experiments to investigate polycrystalline diamond(PCD)tool wear during milling of 70 vol%Si/Al composite.A key contribution of this work is the development of a tool wear model that incorporates reinforcement particle characteristics,treating them as ellipsoidal structures,which enhances the accuracy of predicting abrasive and adhesive wear mechanisms.The model is based on abrasive and adhesive wear mechanisms,and can analyze the interaction between silicon particles,aluminium matrix,and tool components,thus providing deeper insights into PCD tool wear processes.Experimental validation of the model shows a good agreement with the results,with a mean deviation of approximately 10%.The findings on the tool wear mechanism reveal that,as tool wear progresses,the proportion of abrasive wear increases from 40%in the running-in stage to 75%in the rapid wear stage,while adhesive wear decreases.The optimal machining parameters of 120 m·min^(–1) cutting speed(v_(c))and 0.04 mm·z^(–1) feed rate(f_(z)),result in tool life of 33 min and surface roughness(S_(a))of 2.2μm.The study uncovers the variation patterns of abrasive and adhesive wear during the tool wear process,and the proposed model offers a robust framework for predicting tool wear during the machining of high-volume fraction Si/Al composites.The research findings also offer key insights for optimizing tool selection and machining parameters,advancing both the theoretical understanding and practical application of PCD tool wear.
基金supported by National Key Research and Development Program(2018YFA0707300)Major Program of National Natural Science Foundation of China(U22A20188).
文摘Edge defects significantly impact the forming quality of Mg/Al composite plates during the rolling process.This study aims to develop an effective rolling technique to suppress these defects.First,an enhanced Lemaitre damage model with a generalized stress state damage prediction mechanism was used to evaluate the key mechanical factors contributing to defect formation.Based on this evaluation,an embedded composite rolling technique was proposed.Subsequently,comparative validation was conducted at 350℃ with a 50% reduction ratio.Results showed that the plates rolled using the embedded composite rolling technique had smooth surfaces and edges,with no macroscopic cracks observed.Numerical simulation indicated that,compared to conventional processes,the proposed technique reduced the maximum edge stress triaxiality of the plates from-0.02 to-1.56,significantly enhancing the triaxial compressive stress effect at the edges,which suppressed void nucleation and growth,leading to a 96%reduction in damage values.Mechanical property evaluations demonstrated that,compared to the conventional rolling process,the proposed technique improved edge bonding strength and tensile strength by approximately 67.7%and 118%,respectively.Further microstructural characterization revealed that the proposed technique,influenced by the restriction of deformation along the transverse direction(TD),weakened the plastic flow in the TD and enhanced plastic flow along the rolling direction(RD),resulting in higher grain boundary density and stronger basal texture.This,in turn,improved the toughness and transverse homogeneity of the plates.In summary,the embedded composite rolling technique provides crucial technical guidance for the preparation of Mg-based composite plates.
基金support of the Na-tional Key R&D Program of China(No.2021YFA1600700)the Na-tional Natural Science Foundation of China(grant Nos.U22A20114,52322106,52192595,and 52301200)+2 种基金the Project funded by China Postdoctoral Science Foundation(No.2023M733573)CSNS Con-sortium on High-performance Materials of Chinese Academy of Sciences(No.JZHKYPT-2021-01)the Natural Science Foun-dation of Liaoning Province(No.2023-BS-020)。
文摘Non-isothermal aging(NIA)treatments have presented significant advantages in improving the comprehensive performance and aging hardening efficiency of the 7000 series aluminum alloys,but there is no attention paid to their composites.This study takes a linear heating aging process as an example to reveal the precipitation behaviors of a 15 vol.%SiC/7085Al composite as well as its impact on mechanical properties using differential scanning calorimetry,transmission electron microscopy,small-angle neutron scattering,hardness measurements,and tensile testing.The results indicated the formation of GP(Ⅰ,Ⅱ)zones,η’andηprecipitates in sequence,leading to the hardness and strength initially increasing and then decreasing with rising NIA temperatures.The maximums were reached at 183℃,corresponding to the appearance ofη’precipitates in large quantities.Owing to the rapid temperature rise during the NIA process,the precipitates entered the coarsening and redissolution stage before they were entirely formed,resulting in reduced peak strength compared to the T6 treatment.The composite exhibited a more significant reduction in strength than the 7085Al alloy because:(i)the annihilation of vacancies suppressed the formation of GPII zones,thereby weakening their transition toη’precipitates;(ii)quenching dislocations promoted the coarsening of precipitates.An improved NIA process,incorporating both heating and cooling aging treatments,was effectively designed with the assistance of in-situ SANS technology to address this issue,which allows for achieving strength comparable to that after the T6 treatment with only 15%of the aging time consumption.This research fills the gap in investigating the NIA precipitation behaviors of aluminum matrix composites,providing guidance for the formulation of NIA schedules.
基金Supported by National Natural Science Foundation of China(Grant Nos.52475480,51805334)Guangdong Basic and Applied Basic Research Foundation(Grant Nos.2023A1515030249,2023A1515110059)Shenzhen Science and Technology Program(Grant No.GJHZ20220913144212023).
文摘SiC-reinforced aluminum matrix(SiCp/Al)composite is widely utilized in the aerospace,automotive,and electronics industries due to the combination of ceramic hardness and metal toughness.However,the significant disparity in properties between SiC particles and the aluminum matrix results in severe tool wear and diminished surface quality during conventional machining.This study proposes an environmentally friendly and clean dry electrical discharge assisted grinding process as an efficient and low-damage machining method for SiCp/Al.An experimental platform was set up to study the impact of grinding and discharge process parameters on surface quality.The study compared the chip formation mechanism and surface quality between dry electrical discharge assisted grinding and conventional grinding,revealing relationships between surface roughness,grinding force,grinding temperature,and related parameters.The results indicate that the proposed grinding method leads to smaller chip sizes,lower grinding forces and temperatures,and an average reduction of 19.2%in surface roughness compared to conventional grinding.The axial,tangential,and normal grinding forces were reduced by roughly 10.5%,37.8%,and 23.0%,respectively.The optimized process parameters were determined to be N=2500 r/min,vf=30 mm/min,a=10μm,E=15 V,f=5000 Hz,dc=80%,resulting in a surface roughness of 0.161μm.
基金Project supported by the National Natural Science Foundation of China(Grant Nos.12274372 and 12274373)the Major Science and Technology Projects of Henan Province(Grant No.231100230300)。
文摘Improving the thermal conductivity(TC)of diamond–metal composites has always been a significant challenge in the field of thermal management.In this paper,diamond/Al composites are systematically studied,and the influence of the holding time(10–120 min)on interface structure and TC is discussed.The results of this research show that longterm thermal diffusion sintering can achieve dense interfacial bonding in diamond/Al composites,enhancing their TC.Diamond/Al composites with 50 vol%of 900μm diamond attain the highest TC value of 888.73 W·m^(-1)·K^(-1)under sintering conditions of 650?C,50 MPa,and 120 min—nearly 92%of the theoretical value predicted by the Maxwell model.This study establishes that high TC can be achieved through long-term thermal diffusion alone,without the need for complex diamond surface coating or substrate alloying.
基金financial support from the Special Fund for Special Posts of Guizhou University,China(No.[2022]06)the Guizhou Provincial Basic Research Program(Natural Science),China(No.ZK[2023]78)+1 种基金the National Natural Science Foundation of China(No.52365020)the Open Fund Project of Key Laboratory of Advanced Manufacturing Technology,China(No.GZUAMT2022KF[04]).
文摘1060/7050 Al/Al laminated metal composites(LMCs)with heterogeneous lamellar structures were prepared by accumulative roll bonding(ARB),cold rolling and subsequent annealing treatment.The strengthening mechanism was investigated by microstructural characterization,mechanical property tests and in-situ fracture morphology observations.The results show that microstructural differences between the constituent layers are present in the Al/Al LMCs after various numbers of ARB cycles.Compared with rolled 2560-layered Al/Al LMCs with 37.5%and 50.0%rolling reductions,those with 62.5%rolling reductions allow for more effective improvements in the mechanical properties after annealing treatment due to their relatively high mechanical incompatibility across the interface.During tensile deformation,with the increased magnitude of incompatibility in the 2560-layered Al/Al LMC with a heterogeneous lamellar structure,the densities of the geometrically necessary dislocations(GNDs)increase to accommodate the relatively large strain gradient,resulting in considerable back stress strengthening and improved mechanical properties.
基金the financial support from the National Natural Science Foundation of China(Nos.51875062,52205336)。
文摘Titanium/magnesium alloy bimetal composites show promising prospects for lightweight applications.The Ti/Mg bimetal composite was fabricated in Ti−6Al−4V pyramidal lattice structure via AZ91D melt infiltration.Comparative analysis of the tensile and compressive properties was conducted between the composite and its constituent materials(Ti−6Al−4V lattice structure and AZ91D matrix).The tensile strength of the composite(95.9 MPa)was comparable to that of the Ti−6Al−4V lattice structure(94.4 MPa)but lower than that of the AZ91D alloy(120.8 MPa)due to gaps at the bimetal interfaces hindering load transfer during tension.The composite exhibited greater elongation(1.7%)compared to AZ91D(1.4%)alloy but less than the Ti−6Al−4V lattice structure(2.6%).The compressive performance of the composite outperformed that of the Ti−6Al−4V lattice structure,underscoring the significance of the AZ91D alloy in compressive deformation.Fracture analysis indicated that the predominant failure reasons in both the composite and lattice structures were attributed to the breakage of lattice struts at nodes caused by the stress concentration.
基金Projects(51221001,51275417)supported by the National Natural Science Foundation of ChinaProject(SKLSP201103)supported by the Fund of the State Key Laboratory of Solidification ProcessingProject(B08040)supported by the Introducing Talents of Discipline toUniversities,China
文摘Carbon fiber reinforced aluminum matrix （Cf/Al） composite has many excellent properties, and it has received more and more attention. Two-dimensional （2D） Cf/Al composites were fabricated by vacuum and pressure infiltration, which was an integrated technique and could provide high vacuum and high infiltration pressure. The effect of specific pressure on the infiltration quality of the obtained composites was comparatively evaluated through microstructure observation. The experimental results show that satisfied Cf/Al composites could be fabricated at the specific pressure of 75 MPa. In this case, the preform was infiltrated much more completely by aluminum alloy liquid, and the residual porosity was seldom found. It is found that the ultimate tensile strength of the obtained Cf/Al composite reached maximum at the specific pressure of 75 MPa, which was improved by 138.9% compared with that of matrix alloy.
文摘The thermophysical properties of the SiC /Al composites mixed with diamond（SiC-Dia/Al） were studied through theoretical calculation and experiments. The thermal conductivity and the thermal expansion coefficient of the SiC-Dia/Al were calculated by differential effective medium（DEM） theoretical model and extended Turner model, respectively. The microstructure of the SiC-Dia/Al shows that the combination between SiC particles and Al is close, while that between diamond particles and Al is not close. The experimental results of the thermophysical properties of the SiC-Dia/Al are consistent with the calculated ones. The calculation results show that when the volume ratio of the diamond particles to the SiC particles is 3：7, the thermal conductivity and the thermal expansion coefficient can be improved by 39% and 30% compared to SiC/Al composites, respectively. In other words, by adding a small amount of diamond particles, the thermophysical properties of the composites can be improved effectively, while the cost increases little.
基金Project(51371077)supported by the National Natural Science Foundation of China
文摘35% SiCp/2024 Al（volume fraction） composite was prepared by powder metallurgy method. The microstructures of Si Cp/Al interfaces and precipitate phase/Al interfaces were characterized by HRTEM, and the interface conditions were evaluated by tensile modules of elasticity and Brinell hardness measurement. The results show that the overall Si Cp/Al interface condition in this experiment is good and three kinds of Si Cp/Al interfaces are present in the composites, which include vast majority of clean planer interfaces, few slight reaction interfaces and tiny amorphous interfaces. The combination mechanism of Si C and Al in the clean planer interface is the formation of a semi-coherent interface by closely matching of atoms and there are no fixed or preferential crystallographic orientation relationships between Si C and Al. MgAl2O4 spinel particles act as an intermediate to form semi-coherent interface with SiC and Al respectively at the slight reaction interfaces. When the composite is aged at 190 °C for 9 h after being solution-treated at 510 °C for 2 h, numerous discoid-shaped and needle-shaped nanosized precipitates dispersively exist in the composite and are semi-coherent of low mismatch with Al matrix. The Brinell hardness of composites arrives peak value at this time.
基金Project(2012AA030311)supported by the National High-tech Research and Development Program of ChinaProject(2010BB4074)supported by the Natural Science Foundation of Chongqing Municipality,ChinaProject(2010ZD-02)supported by the State Key Laboratory for Advanced Metals and Materials,China
文摘The deformation behaviors of Al2O3/Al composites were investigated by compressive tests conducted at temperature of 300-450 °C and strain rates of 0.001-1.0 s-1 with Gleeble-1500 D thermal simulator system. The results show that the flow stress increases with increasing strain rate and decreasing temperature. The hyperbolic sine constitutive equation can describe the flow stress behavior of Al2O3/Al composites, and the deformation activation energy and constitutive equations were calculated. The processing maps of Al2O3/Al-2 μm and Al2O3/Al-1 μm composites at strain of 0.6 were obtained and the optimum processing domains are in ranges of 300-330 °C, 0.007-0.03 s-1 and 335-360 °C, 0.015-0.06 s-1 for hot working, respectively. The instability zones of flow behavior can also be recognized by the maps.
基金Project(2012MS0801)supported by the Natural Science Foundation of Inner Mongolia,China
文摘Al2O3p-Al composites were synthesized using an in-situ reaction in the 80%Al-20%CuO （mass fraction） system. The effects of the CuO particle size on the synthesis temperature and microstructure of the composites were investigated by various methods. The results indicate that the CuO particle size has a significant effect on the temperature at which the complete reaction in the Al-CuO system occurs：the temperature is 200 ℃ lower in the Al-CuO system containing CuO particles with sizes less than 6μm than that containing CuO particles with sizes less than 100μm. The interfacial bonding between Al2O3 particles and Al is not complete when the temperature is below a critical value. The morphology of the Al2O3 particles varies from ribbon-like shape to near spherical shape when the temperature is above a critical value. These two critical temperatures are affected by the particle size of CuO, and the critical temperature of the sample containing CuO particles with sizes less than 6μm is 100 ℃ lower than that of the sample containing CuO particles with sizes less than 100μm.
基金financial supports from the National Natural Science Foundation of China (No. 51875062)China Postdoctoral Science Foundation (No. 2021M700567)。
文摘In this study,HEA/AI composite interlayer was used to fabricate Ti/Mg bimetal composites by solidliquid compound casting process.The Al layer was prepared on the surface of TC4 alloy by hot dipping,and the FeCoNiCr HEA layer was prepared by magnetron sputtering onto the Al layer.The influence of the HEA layer thickness and pouring temperature on interface evolution was investigated based on SEM observation and thermodynamic analysis.Results indicate that the sluggish diffusion effect of HEA can effectively inhibit the interfacial diffusion between Al and Mg,which is conducive to the formation of solid solution,especially when the thickness of HEA is 800 nm.With the increase of casting temperature from 720 ℃ to 730 ℃,740℃,and 750 ℃,α-Al(Mg),α-Al(Mg)+Al3Mg2,Al3Mg2+Al12Mg17,and Al12Mg17+δ-Mg are formed at the interface of Ti/Mg bimetal,respectively.When the thickness of the HEA layer is 800 nm and the pouring temperature is 720 ℃,the bonding strength of the Ti/Mg bimetal can reach the maximum of 93.6 MPa.
基金Project(51272141)supported by the National Natural Science Foundation of ChinaProject(ts20110828)supported by the Taishan Scholars Project of Shandong Province,ChinaProject(2015AA034404)supported by the Ministry of Science and Technology of China
文摘（TiB2＋Al2O3）/NiAl composites were synthesized by self-propagation high-temperature synthesis, and their phase compositions, microstructures and evolution modes were studied. The microstructures and shapes vary with the TiB2＋Al2O3 content in the NiAl matrix. TiB2 particles take a great variety of elementary shapes such as white bars, plates, herringbones, regular cubes and cuboids. These results outline a strategy of self-assembly processes in real time to build diversified microstructures. Some TiB2 grains in sizes of 2-5μm are embeded in Al2O3 clusters, while a small number of TiB2 particles disperse in the NiAl matrix. It is believed that the higher the TiB2＋Al2O3 content is, the more the regular shapes and homogeneous distributions of TiB2 and Al2O3 will be present in the NiAl matrix.
基金Project(2014DFA50860)supported by International Science&Technology Cooperation Program of China
文摘After Sn/Pd activating, the SiCp/Al composite with 65% SiC (volume fraction) was coated by electroless Ni?P alloy plating. Surface morphology of the composite and its effect on the Ni?P alloy depositing process and bonding action of Ni and P atoms in the Ni?P alloy were studied. The results show that inhomogeneous distribution of the Sn/Pd activating points results in preferential deposition of the Ni?P alloy particles on the Al alloy and rough SiC particle surfaces and in the etched caves. The Ni?P alloy film has an amorphous structure where chemical bonding between Ni and P atoms exists. After a continuous Ni?P alloy film formed, electroless Ni?P alloy plating is not affected by surface morphology and characteristics of the SiCp/Al composite any longer, but by the electroless plating process itself. The Ni?P alloy film follows linear growth kinetics with an activation energy of 68.44 kJ/mol.
基金Project(2011CB605805)supported by the National Basic Research Program of China
文摘The B4C/2024Al composites were successfully produced by pressureless infiltration method, and the effects of heat treatment on phase content and mechanical properties were investigated by X-ray diffraction （XRD）, scanning electron microscopy （SEM） and mechanical properties testing. The results show that phases of BnC/2024Al composites include B4C, Al, Al3BC, AlB2 and Al2Cu. The phase species remain unchanged; however, the phase content of the composites changes significantly after heat treatment at the temperature of 660, 700, 800 or 900 ℃ for 12, 24 or 36 h. It is found that the heat treatment results in not only considerable enhancement in hardness, but also reduction in bending strength of the composites. Heat treatment at 800 ℃ for 36 h does best to hardness of the composites, while at 700 ℃ for 36 h it is the most beneficial to their comprehensive mechanical properties.