Ag3PO4/Ag/Ag2Mo2O7 composite photocatalyst was successfully prepared via an in situ precipitation method. The as-prepared Ag3PO4/Ag/Ag2Mo2O7 nanocomposite included Ag3PO4 nanoparticles （NPs） as well as Ag NPs assemb...Ag3PO4/Ag/Ag2Mo2O7 composite photocatalyst was successfully prepared via an in situ precipitation method. The as-prepared Ag3PO4/Ag/Ag2Mo2O7 nanocomposite included Ag3PO4 nanoparticles （NPs） as well as Ag NPs assembling on the surface of Ag2Mo2O7 nanowires. Under visible light irradiation （λ〉420 nm）, the Ag3PO4/Ag/Ag2Mo2O7 com- posite degraded rhodamine B （Rh B） efficiently and showed much higher photocatalytic efficiency than pure AgaPO4, Ag2Mo2O7, or Ag3PO4/Ag2Mo2O7. It was elucidated that the excellent photocatalytic performance of Ag3PO4/Ag/Ag2Mo2O7 for the degradation of Rh B under visible light could be ascribed to the high specific surface area, the extended absorption in the visible light region resulting from the Ag3PO4/Ag loading, and the effi- cient separation of photogenerated electrons and holes through the ternary heterostrucure composed of Ag3PO4, Ag and Ag2Mo2O7.展开更多
基金supported by the National Natural Science Foundation of China(No.21407059,No.21576112,No.21407064,and No.21607051)the Science Development Project of Jiangsu Province(BK20140527)+1 种基金the Science and Technology Research Project of the Department of Education of Jilin Province(No.2015220)the Open Subject of the State Key Laboratory of Rare Earth Resource Utilization(RERU2017011)
文摘Ag3PO4/Ag/Ag2Mo2O7 composite photocatalyst was successfully prepared via an in situ precipitation method. The as-prepared Ag3PO4/Ag/Ag2Mo2O7 nanocomposite included Ag3PO4 nanoparticles （NPs） as well as Ag NPs assembling on the surface of Ag2Mo2O7 nanowires. Under visible light irradiation （λ〉420 nm）, the Ag3PO4/Ag/Ag2Mo2O7 com- posite degraded rhodamine B （Rh B） efficiently and showed much higher photocatalytic efficiency than pure AgaPO4, Ag2Mo2O7, or Ag3PO4/Ag2Mo2O7. It was elucidated that the excellent photocatalytic performance of Ag3PO4/Ag/Ag2Mo2O7 for the degradation of Rh B under visible light could be ascribed to the high specific surface area, the extended absorption in the visible light region resulting from the Ag3PO4/Ag loading, and the effi- cient separation of photogenerated electrons and holes through the ternary heterostrucure composed of Ag3PO4, Ag and Ag2Mo2O7.