In this work,flexible photothermal PVA/Ti_(2)O_(3) composite films with different amount(0 wt%,5 wt%,10 wt%,15 wt%)of Ti_(2)O_(3) particles modified by steric acid were prepared by a simple solution casting method.The...In this work,flexible photothermal PVA/Ti_(2)O_(3) composite films with different amount(0 wt%,5 wt%,10 wt%,15 wt%)of Ti_(2)O_(3) particles modified by steric acid were prepared by a simple solution casting method.The microstructures,XRD patterns,FTIR spectra,UV-Vis-NIR spectra thermo-conductivity,thermo-stability and photothermal effects of these composite films were all characterized.These results indicated that Ti_(2)O_(3) particles were well dispersed throughout the polyvinyl alcohol(PVA)matrix in the PVA/Ti_(2)O_(3) composite films.And Ti_(2)O_(3) particles could also effectively improve the photothermal properties of the composite films which exhibited high light absorption and generated a high temperature(about 57.4℃for film with 15 wt%Ti_(2)O_(3) amount)on the surface when it was irradiated by a simulated sunlight source(1 kW/m^(2)).展开更多
Cu2O/TiOa/Pt three-layer films were deposited on glass substrates using magnetron sputtering method. The surface morphology and the optical properties of the composite film were characterized by X-ray diffraction （XR...Cu2O/TiOa/Pt three-layer films were deposited on glass substrates using magnetron sputtering method. The surface morphology and the optical properties of the composite film were characterized by X-ray diffraction （XRD）, scanning electron microscopy （SEM）, ultraviolet- visible spectroscopy （UV-Vis） and photoluminescence spectroscopy （PL）. The photocatalytic activity of the samples was evaluated by the photocatalytic degradation of methyl orange （MO） aqueous solution under visible light irradiation. The results indicate that the Cu2O/TiO2/Pt composite films are made up of three layers which are Pt layer, anatase-TiO2 layer and Cu2O layer from bottom to top. The surface of the films is even and composed of regular-shaped spherical particles. The photocatalytic activity of the Cu2O/TiO2/Pt three-layer film is much higher than that of the Cu2O/TiO2 double-layer film. Such enhancement is ascribed to the presence of Pt layer, which further inhibits the photogenerated electron-hole recombination, prolongs the lifetime of the photogenerated carriers, increases the quantum efficiency and hence improves the photocatalytic activity of the film effectively.展开更多
Bi_(2)WO_(6) nanoplate/TiO_(2) nanowire and Bi_(2)WO_(6) nanoflower/TiO_(2) nanowire composite films were successfully prepared using a hydrothermal method.The results show that the light absorption for Bi_(2)WO_(6)/T...Bi_(2)WO_(6) nanoplate/TiO_(2) nanowire and Bi_(2)WO_(6) nanoflower/TiO_(2) nanowire composite films were successfully prepared using a hydrothermal method.The results show that the light absorption for Bi_(2)WO_(6)/TiO_(2) composite films is extended to the visible region after Bi_(2)WO_(6) nanoplates and nanoflowers are assembled onto TiO_(2) nanowires.Furthermore,Bi_(2)WO_(6) nanoflower/TiO_(2) nano wire composite film exhibits a better absorption property compared to Bi_(2)WO_(6) nanoplate/TiO_(2) nanowire film,which is mainly ascribed to the narrower bandgap of Bi_(2)WO_(6) nanoflower compared to that of Bi_(2)WO_(6) nanoplate.The photocurrent density for Bi_(2)WO_(6) nanoflower/TiO_(2) nanowire and Bi_(2)WO_(6) nanoplate/TiO_(2) nanowire composite films can reach 95 and 62.5 μA cm-2,respectively,which are much higher than that obtained for a pure TiO_(2) nanowire film(25 μA cm-2).Meanwhile,under illumination,the pure TiO_(2) nanowire,Bi_(2)WO_(6) nanoplate/TiO_(2) nanowire and Bi_(2)WO_(6) nanoflower/TiO_(2) nanowire films can reduce the potential of the coupled 304 stainless steel in 3.5 wt.%NaCl solution by 299,719 and 739 mV,respectively.Thus,Bi_(2)WO_(6) nanoflower/TiO_(2) nanowire film is found to provide the best effective photocathodic protection for 304 stainless steel.This work not only provides an example of shape-dependent photocathodic protection based on Bi_(2)WO_(6) but also opens up new possibilities to design an ideal microstructure on the basis of semiconductor materials for future applications of photocathodic protection.展开更多
Total dose effects and single event effects on radiation-hardened power vertical double-diffusion metal oxide semiconductor（VDMOS） devices with composite SiO2-Si3N4 film gates are investigated.The relationships amon...Total dose effects and single event effects on radiation-hardened power vertical double-diffusion metal oxide semiconductor（VDMOS） devices with composite SiO2-Si3N4 film gates are investigated.The relationships among the important electrical parameters of the samples with different thickness SiO2-Si3N4 films,such as threshold voltage,breakdown voltage,and on-state resistance in accumulated dose,are discussed.The total dose experiment results show that the breakdown voltage and the on-state resistance barely change with the accumulated dose.However,the relationships between the threshold voltages of the samples and the accumulated dose are more complex,and not only positively drift,but also negatively drift.At the end of the total dose experiment,we select the group of samples which have the smaller threshold voltage shift to carry out the single event effect studies.We find that the samples with appropriate thickness ratio SiO2-Si3N4 films have a good radiation-hardening ability.This method may be useful in solving both the SEGR and the total dose problems with the composite SiO2-Si3N4 films.展开更多
In this work, TiO2/Ti composite films were fabricated by 2-setp MCT and the following high temperature oxidation. Antibacterial activity of the composite films treated by ultrasonic cleaning to increase the performanc...In this work, TiO2/Ti composite films were fabricated by 2-setp MCT and the following high temperature oxidation. Antibacterial activity of the composite films treated by ultrasonic cleaning to increase the performance reliability was examined. The prepared TiO2/Ti composite films showed high photocatalytic activity in the degradation of methylene blue solution. It is obvious that? TiO2/Ti composite films have antibacterial activity under UV irradiation.展开更多
MoS2/Zr composite films were deposited on the cemented carbide YT14 （WC＋14%TiC＋6%Co） by medium-frequency magnetron sputtered and coupled with multi-arc ion plated techniques.The influence of negative bias voltage ...MoS2/Zr composite films were deposited on the cemented carbide YT14 （WC＋14%TiC＋6%Co） by medium-frequency magnetron sputtered and coupled with multi-arc ion plated techniques.The influence of negative bias voltage on the composite film properties,including adhesion strength,micro-hardness,thickness and tribological properties were investigated.The results showed that proper negative bias voltage could significantly improve the mechanical and tribological properties of composite films.The effects of negative bias voltage on film properties were also put forward.The optimal negative bias voltage was -200 V under this experiment conditions.The obtained composite films were dense,the adhesion strength was about 60 N,the thickness was about 2.4 μm,and the micro-hardness was about 9.0 GPa.The friction coefficient and wear rate was 0.12 and 2.1×10-7 cm3/N·m respectively after 60 m sliding operation against hardened steel under a load of 20 N and a sliding speed of 200 rev·min-1.展开更多
ZrO2/TiO2 composite photocatalytic film was produced on the pure titanium substrate using in-situ Zr（OH）4 colloidal particle by the micro-arc oxidation technique and characterized by scanning electron microscope （...ZrO2/TiO2 composite photocatalytic film was produced on the pure titanium substrate using in-situ Zr（OH）4 colloidal particle by the micro-arc oxidation technique and characterized by scanning electron microscope （SEM）, energy dispersive X-ray （EDX）, X-ray diffraction （XRD） and ultraviolet-visible （UV-Vis） spectrophotometer. The composite film shows a lamellar and porous structure which consists of anatase, futile and ZrO2 phases. The optical absorption edge of film is shifted to longer wavelength when ZrO2 is introduced to TiO2. Furthermore, the photocatalytic reaction rate constants of degradation of rhodamine B solution with ZrO2/TiO2 composite film and pure TiO2 film under ultraviolet irradiation are measured as 0.0442 and 0.0186 h 1, respectively.展开更多
In this work, CaF_2:Ln^(3+)(Ln:Er,Er/Yb)/Nafion composite films were prepared using Nafion as modifications and matrices by dripping method. The composite films were characterized by Fourier transform infrared spectro...In this work, CaF_2:Ln^(3+)(Ln:Er,Er/Yb)/Nafion composite films were prepared using Nafion as modifications and matrices by dripping method. The composite films were characterized by Fourier transform infrared spectroscopy(FT-IR), X-ray diffraction(XRD) and scanning electron microscopy(SEM). Composite films are transparent and CaF_2:Ln^(3+)(Ln:Er,Er/Yb) nanoparticles are well dispersed in Nafion films.The thicknesses of CaF_2:Er^(3+)/Nafion and CaF_2:Er^(3+),Yb^(3+)/Nafion composite film are about 77 and 73 μm,respectively. The nanoparticles in composite film possess cubic phase. CaF_2:Er^(3+),Yb^(3+)/Nafion composite film has stronger characteristic emission of Er^(3+) around 1530 nm with full width at half-maximum(FWHM) of 73 nm and longer luminescence lifetimes of 22.04 μs(25.03%) and 100.77 μs(74.97%).展开更多
This paper reports that single-layer and graded Au-TiO2 granular composite films with Au atom content 15%- 66% were prepared by using reactive co-sputtering technique. The third-order optical nonlinearity of single-la...This paper reports that single-layer and graded Au-TiO2 granular composite films with Au atom content 15%- 66% were prepared by using reactive co-sputtering technique. The third-order optical nonlinearity of single-layer and graded composite films was investigated by using s- and p-polarized Z-scans in femtosecond time scale. The nonlinear absorption coefficient βeff of single-layer Au-TiO2 films is measured to be -2.3×10^3-0.76×10^3 cm/GW with Au atom content 15%-66%. The βeff value of the 10-layer Au-TiO2 graded film is enhanced to be -2.1×10^4cm/GW calculated from p-polarized Z-scans, which is about ten times the maximum βeff of single-layer films. Broadened response in the wavelength region 730-860 nm of the enhanced optical nonlinearity of graded Au-TiO2 composite films was also investigated.展开更多
Nano sized powders of TiO2 （titanium dioxide） and Nb2O5 （Niobium （V） oxide） were used to fabricate TiO2/Nb2O5 composites thin films by EPD （electrophoretic deposition） technique. The metal oxide powders, toget...Nano sized powders of TiO2 （titanium dioxide） and Nb2O5 （Niobium （V） oxide） were used to fabricate TiO2/Nb2O5 composites thin films by EPD （electrophoretic deposition） technique. The metal oxide powders, together with magnesium nitrate hexahydrate pellets, were suspended in propan-2-ol inside an EPD cell. The electrodes, placed 1.2 cm apart, were partially immersed in the suspension and a DC potential applied across them. Key EPD process parameters, which include applied DC electric field, deposition time and solid concentration in suspension, were optimized through visual inspection and from UV-Vis-NIR spectrophotometer spectra. The highest （55%） transmittance was obtained for films with deposition time of 90 s, powder concentration of 0.01 g/40 mL, and 35 V DC （direct current） voltage. XRD micrographs confirmed that TiO2 and Nb2O5 particles were presented in the composite film. SEM （scanning electron microscope） micrographs of the composite electrode thin films showed that porous films of high quality with well controlled morphology were deposited by using the EPD technique.展开更多
Titanium dioxide （TiO2） loaded tungsten trioxide （WO3） composite films are prepared by an E-beam vapor system. Associated with the existence of a heterojunction at the interface of TiO2 and WO3, the prepared TiO2-...Titanium dioxide （TiO2） loaded tungsten trioxide （WO3） composite films are prepared by an E-beam vapor system. Associated with the existence of a heterojunction at the interface of TiO2 and WO3, the prepared TiO2-WO3 composite film shows enhanced photocurrent density, four times than the pure WO3 film illuminated under xenon lamp, and higher incident-photon-to-current conversion e^ciency. By varying the initial TiO2 film thickness, such composite structures could be optimized to obtain the highest photocurrent density. We believe that thin TiO2 films improve the light response and increase the surface roughness of WO3 films. Furthermore, the existence of the heterojunction results in the e^cient charge carriers＇ separation, transfer process, and a lower recombination of electron-hole pairs, which is beneficial for the enhancement of photocurrent density.展开更多
CuIn（S,Se）2 thin films were prepared by thermal crystallization of co-sputtered Cu-In alloy precursors in S/Se atmosphere. In-depth compositional uniformity is an important prereq- uisite for obtaining device-qualit...CuIn（S,Se）2 thin films were prepared by thermal crystallization of co-sputtered Cu-In alloy precursors in S/Se atmosphere. In-depth compositional uniformity is an important prereq- uisite for obtaining device-quality CuIn（S,Se）2 absorber thin films. In order to figure out the influence of heat treatments on in-depth composition uniformity of CuIn（S,Se）2 thin films, two kinds of reaction temperature profiles were investigated. One process is ＂one step profile＂, referring to formation of CuIn（S,Se）2 thin films just at elevated temperature （e.g. 500 ℃）. The other is ＂two step profile＂, which allows for slow diffusion of S and Se elements into the alloy precursors at a low temperature before the formation and re-crystallization of CuIn（S,Se）2 thin films at higher temperature （e.g. first 250 ℃ then 500 ℃）. X-ray diffrac- tion studies reveal that there is a discrepancy in the shape of （112） peak. Samples annealed with ＂one step profile＂ have splits on （112） peaks, while samples annealed with ＂two step profile＂ have relatively symmetrical （112） peaks. Grazing incident X-ray diffraction and en- ergy dispersive spectrum measurements of samples successively etched in bromine methanol show that CuIn（S,Se）2 thin films have better in-depth composition uniformity after ＂two step profile＂ annealing. The reaction mechanism during the two thermal processing was also investigated by X-ray diffraction and Raman spectra.展开更多
The Ni-P/TiO2 composite film on sintered NdFeB permanent magnet was investigated by X-ray diffraction （XRD）,environmental scanning electron microscopy （ESEM）,and energy dispersive X-ray spectrometer （EDX）. The c...The Ni-P/TiO2 composite film on sintered NdFeB permanent magnet was investigated by X-ray diffraction （XRD）,environmental scanning electron microscopy （ESEM）,and energy dispersive X-ray spectrometer （EDX）. The corrosion resistance of Ni-P/TiO2 film coated on NdFeB magnet,in 0.5 mol/L NaCl solution,was studied by potentiodynamic polarization,salt spray test and electrochemical impedance spectroscopy （EIS） techniques. The self-corrosion current density （icorr） and the polarization resistance （Rp） of Ni-P/TiO2 film are 0.22 μA/cm2 （about 14% of that of Ni-P coating）,and 120 kΩ·cm2 （about 2 times of that of Ni-P coating）,respectively. The anti-salt spray time of Ni-P/TiO2 film is about 2.5 times of that of the Ni-P coating. The results indicate that Ni-P/TiO2 film has a better corrosion resistance than Ni-P coating,and the composite film increases the corrosion resistance of NdFeB magnet markedly.展开更多
A novel fiber optic sensor based on optical composite oxygen-sensitive film was developed for determination of 2,4-dichlorophenol(DCP).The optical composite oxygen-sensitive film consists of tris(2,2’-bipyridyl)dichl...A novel fiber optic sensor based on optical composite oxygen-sensitive film was developed for determination of 2,4-dichlorophenol(DCP).The optical composite oxygen-sensitive film consists of tris(2,2’-bipyridyl)dichloro ruthenium(II)hexahydrate(Ru(bpy)3Cl2)as the fluorescence indicator and iron(III)tetrasulfophthalocyanine(Fe(III)PcTs)as bionic enzyme.A lock-in amplifier was used for detecting the lifetime of the composite oxygen-sensitive film by measuring the phase delay of the sensor head.The different variables affecting the sensor performance were evaluated and optimized.Under the optimal conditions(i e,pH 6.0,25℃,Fe(III)PcTs concentration of 5.0×10^-5 mol/L),the linear detection range,detection limit and response time of the fiber optic sensor are 3.0×10^-7-9.0×10^-5 mol/L,4.8×10^-8 mol/L(S/N=3),and 220 s,respectively.The sensor displays high selectivity,good repeatability and stability,which have good potentials in analyzing DCP concentration in practical water samples.展开更多
A NiP/TiO2 composite film on carbon steel was prepared by electroless plating and sol-gel composite process. An artificial neural network was applied to optimize the prepared condition of the composite film. Corrosion...A NiP/TiO2 composite film on carbon steel was prepared by electroless plating and sol-gel composite process. An artificial neural network was applied to optimize the prepared condition of the composite film. Corrosion behavior of the NiP/TiO2 composite film was investigated by polarization resistance measurement, anode polarization, ESEM （environmental scanning electron microscopy） and EIS （electrochemical impedance spectroscopy） measurements. Results showed that the NiP/ TiO2 composite film has a good corrosion resistance in 0.5mol/L H2SO4 solution. The element valence of the composite film was characterized by XPS （X-ray photoelectron spectroscopy） spectrum, and an anticorrosion mechanism of the composite film was discussed.展开更多
TiO2 films have received increasing attention for the removal of organic pollutants via photocatalysis. To develop a simple and effective method for improving the photodegradation efficiency of pollutants in surface w...TiO2 films have received increasing attention for the removal of organic pollutants via photocatalysis. To develop a simple and effective method for improving the photodegradation efficiency of pollutants in surface water, we herein examined the preparation of a P25-TiO2 composite film on a cement substrate via a sol–gel method. In this case, Rhodamine B（Rh B）was employed as the target organic pollutant. The self-generated TiO2 film and the P25-TiO2 composite film were characterized by X-ray diffraction（XRD）, N2 adsorption/desorption measurements, scanning electron microscopy（SEM）, transmission electron microscopy（TEM）, and diffuse reflectance spectroscopy（DRS）. The photodegradation efficiencies of the two films were studied by Rh B removal in water under UV（ultraviolet） irradiation. Over 4 day exposure, the P25-TiO2 composite film exhibited higher photocatalytic performance than the self-generated TiO2 film. The photodegradation rate indicated that the efficiency of the P25-TiO2 composite film was enhanced by the addition of the rutile phase Degussa P25 powder. As such, cooperation between the anatase TiO2 and rutile P25 nanoparticles was beneficial for separation of the photo-induced electrons and holes. In addition, the influence of P25 doping on the P25-TiO2 composite films was evaluated. We found that up to a certain saturation point, increased doping enhanced the photodegradation ability of the composite film. Thus, we herein demonstrated that the doping of P25 powders is a simple but effective strategy to prepare a P25-TiO2 composite film on a cement substrate, and the resulting film exhibits excellent removal efficiency in the degradation of organic pollutants.展开更多
The oxidation behaviors of Fe26Cr1Mo with and without the Ni La 2O 3 electrodeposited composite film have been investigated by thermogravimetric analysis (TGA) and a scanning electron microscope equipped with an en...The oxidation behaviors of Fe26Cr1Mo with and without the Ni La 2O 3 electrodeposited composite film have been investigated by thermogravimetric analysis (TGA) and a scanning electron microscope equipped with an energy dispersive analytical X ray system(SEM/EDAX). The experimental results show that the oxide scale growing on Fe26Cr1Mo exposed at 900 ℃ spalled severely during cooling, while after the stainless steel was coated with the Ni La 2O 3 electrodeposited composite film, its high temperature cyclic oxidation resistance was significantly improved. The reason is that a La 2O 3 modified NiO scale, which has a superior adhesion to the substrate, was formed on the Fe26Cr1Mo stainless steel coated with Ni La 2O 3 composite film.展开更多
基金Funded by the Youth Backbone Teacher Training Plan in University of Henan Province(No.21220028)Science and Technology Research Project of Henan Province(No.242102321066)+2 种基金Natural Science Foundation of Henan Province(No.232300420312)Henan University of Technology Young Backbone Teacher Training Plan(No.21421260)the Innovation Training Program for College Students in Henan Province(No.202310463046)。
文摘In this work,flexible photothermal PVA/Ti_(2)O_(3) composite films with different amount(0 wt%,5 wt%,10 wt%,15 wt%)of Ti_(2)O_(3) particles modified by steric acid were prepared by a simple solution casting method.The microstructures,XRD patterns,FTIR spectra,UV-Vis-NIR spectra thermo-conductivity,thermo-stability and photothermal effects of these composite films were all characterized.These results indicated that Ti_(2)O_(3) particles were well dispersed throughout the polyvinyl alcohol(PVA)matrix in the PVA/Ti_(2)O_(3) composite films.And Ti_(2)O_(3) particles could also effectively improve the photothermal properties of the composite films which exhibited high light absorption and generated a high temperature(about 57.4℃for film with 15 wt%Ti_(2)O_(3) amount)on the surface when it was irradiated by a simulated sunlight source(1 kW/m^(2)).
基金financially supported by the National Natural Science Foundation of China (No.51301118)the Projects of International Cooperation in Shanxi (No.2014081002)the Scientific and Technological Innovation Programs of Higher Education Institutions in Shanxi (No.2013108)
文摘Cu2O/TiOa/Pt three-layer films were deposited on glass substrates using magnetron sputtering method. The surface morphology and the optical properties of the composite film were characterized by X-ray diffraction （XRD）, scanning electron microscopy （SEM）, ultraviolet- visible spectroscopy （UV-Vis） and photoluminescence spectroscopy （PL）. The photocatalytic activity of the samples was evaluated by the photocatalytic degradation of methyl orange （MO） aqueous solution under visible light irradiation. The results indicate that the Cu2O/TiO2/Pt composite films are made up of three layers which are Pt layer, anatase-TiO2 layer and Cu2O layer from bottom to top. The surface of the films is even and composed of regular-shaped spherical particles. The photocatalytic activity of the Cu2O/TiO2/Pt three-layer film is much higher than that of the Cu2O/TiO2 double-layer film. Such enhancement is ascribed to the presence of Pt layer, which further inhibits the photogenerated electron-hole recombination, prolongs the lifetime of the photogenerated carriers, increases the quantum efficiency and hence improves the photocatalytic activity of the film effectively.
基金supported by the National Natural Science Foundation of China(Nos.51822402,51671044 and 52001051)the National Key Research and Development Program of China(Nos.2019YFA0209901 and 2018YFA0702901)+4 种基金the fund of the State Key Laboratory of Solidification Processing in NWPU(Grant No.SKLSP201902)the Liao Ning Revitalization Talents Program(XLYC1807047)the National MCF Energy R&D Program(No.2018YFE0312400)the Fund of Science and Technology on Reactor Fuel and Materials Laboratory(STRFML-2020-04)the China Postdoctoral Science Foundation(No.2020M670747).
文摘Bi_(2)WO_(6) nanoplate/TiO_(2) nanowire and Bi_(2)WO_(6) nanoflower/TiO_(2) nanowire composite films were successfully prepared using a hydrothermal method.The results show that the light absorption for Bi_(2)WO_(6)/TiO_(2) composite films is extended to the visible region after Bi_(2)WO_(6) nanoplates and nanoflowers are assembled onto TiO_(2) nanowires.Furthermore,Bi_(2)WO_(6) nanoflower/TiO_(2) nano wire composite film exhibits a better absorption property compared to Bi_(2)WO_(6) nanoplate/TiO_(2) nanowire film,which is mainly ascribed to the narrower bandgap of Bi_(2)WO_(6) nanoflower compared to that of Bi_(2)WO_(6) nanoplate.The photocurrent density for Bi_(2)WO_(6) nanoflower/TiO_(2) nanowire and Bi_(2)WO_(6) nanoplate/TiO_(2) nanowire composite films can reach 95 and 62.5 μA cm-2,respectively,which are much higher than that obtained for a pure TiO_(2) nanowire film(25 μA cm-2).Meanwhile,under illumination,the pure TiO_(2) nanowire,Bi_(2)WO_(6) nanoplate/TiO_(2) nanowire and Bi_(2)WO_(6) nanoflower/TiO_(2) nanowire films can reduce the potential of the coupled 304 stainless steel in 3.5 wt.%NaCl solution by 299,719 and 739 mV,respectively.Thus,Bi_(2)WO_(6) nanoflower/TiO_(2) nanowire film is found to provide the best effective photocathodic protection for 304 stainless steel.This work not only provides an example of shape-dependent photocathodic protection based on Bi_(2)WO_(6) but also opens up new possibilities to design an ideal microstructure on the basis of semiconductor materials for future applications of photocathodic protection.
文摘Total dose effects and single event effects on radiation-hardened power vertical double-diffusion metal oxide semiconductor（VDMOS） devices with composite SiO2-Si3N4 film gates are investigated.The relationships among the important electrical parameters of the samples with different thickness SiO2-Si3N4 films,such as threshold voltage,breakdown voltage,and on-state resistance in accumulated dose,are discussed.The total dose experiment results show that the breakdown voltage and the on-state resistance barely change with the accumulated dose.However,the relationships between the threshold voltages of the samples and the accumulated dose are more complex,and not only positively drift,but also negatively drift.At the end of the total dose experiment,we select the group of samples which have the smaller threshold voltage shift to carry out the single event effect studies.We find that the samples with appropriate thickness ratio SiO2-Si3N4 films have a good radiation-hardening ability.This method may be useful in solving both the SEGR and the total dose problems with the composite SiO2-Si3N4 films.
文摘In this work, TiO2/Ti composite films were fabricated by 2-setp MCT and the following high temperature oxidation. Antibacterial activity of the composite films treated by ultrasonic cleaning to increase the performance reliability was examined. The prepared TiO2/Ti composite films showed high photocatalytic activity in the degradation of methylene blue solution. It is obvious that? TiO2/Ti composite films have antibacterial activity under UV irradiation.
基金Funded by the National Natural Science Foundation of China (No.51075237)the National Basic Research Program of China (No.2009CB724402)+3 种基金the Taishan Scholar Program of Shandong Provincethe Outstanding Young Scholar Science Foundation of Shandong (No.JQ200917)the National Natural Science Foundation of Shandong (No.ZR2010EZ002)National High Technology Research and Development Program (No.2009AA044303)
文摘MoS2/Zr composite films were deposited on the cemented carbide YT14 （WC＋14%TiC＋6%Co） by medium-frequency magnetron sputtered and coupled with multi-arc ion plated techniques.The influence of negative bias voltage on the composite film properties,including adhesion strength,micro-hardness,thickness and tribological properties were investigated.The results showed that proper negative bias voltage could significantly improve the mechanical and tribological properties of composite films.The effects of negative bias voltage on film properties were also put forward.The optimal negative bias voltage was -200 V under this experiment conditions.The obtained composite films were dense,the adhesion strength was about 60 N,the thickness was about 2.4 μm,and the micro-hardness was about 9.0 GPa.The friction coefficient and wear rate was 0.12 and 2.1×10-7 cm3/N·m respectively after 60 m sliding operation against hardened steel under a load of 20 N and a sliding speed of 200 rev·min-1.
基金Project(gf200901002)supported by the Open Research Fund of National Defense Key Disciplines Laboratory of Light Alloy Processing Science and Technology of Nanchang Hangkong University,China
文摘ZrO2/TiO2 composite photocatalytic film was produced on the pure titanium substrate using in-situ Zr（OH）4 colloidal particle by the micro-arc oxidation technique and characterized by scanning electron microscope （SEM）, energy dispersive X-ray （EDX）, X-ray diffraction （XRD） and ultraviolet-visible （UV-Vis） spectrophotometer. The composite film shows a lamellar and porous structure which consists of anatase, futile and ZrO2 phases. The optical absorption edge of film is shifted to longer wavelength when ZrO2 is introduced to TiO2. Furthermore, the photocatalytic reaction rate constants of degradation of rhodamine B solution with ZrO2/TiO2 composite film and pure TiO2 film under ultraviolet irradiation are measured as 0.0442 and 0.0186 h 1, respectively.
基金Project supported by Natural Science Basic Research Plan in Shaanxi Province of China(No.2018JM2021)Xi'an Science and Technology Plan Project(2016CXWL10,CXY1443WL21)Program of Education Department of Shaanxi Provincial Government(15JK2152)
文摘In this work, CaF_2:Ln^(3+)(Ln:Er,Er/Yb)/Nafion composite films were prepared using Nafion as modifications and matrices by dripping method. The composite films were characterized by Fourier transform infrared spectroscopy(FT-IR), X-ray diffraction(XRD) and scanning electron microscopy(SEM). Composite films are transparent and CaF_2:Ln^(3+)(Ln:Er,Er/Yb) nanoparticles are well dispersed in Nafion films.The thicknesses of CaF_2:Er^(3+)/Nafion and CaF_2:Er^(3+),Yb^(3+)/Nafion composite film are about 77 and 73 μm,respectively. The nanoparticles in composite film possess cubic phase. CaF_2:Er^(3+),Yb^(3+)/Nafion composite film has stronger characteristic emission of Er^(3+) around 1530 nm with full width at half-maximum(FWHM) of 73 nm and longer luminescence lifetimes of 22.04 μs(25.03%) and 100.77 μs(74.97%).
基金Project supported by the National Natural Science Foundation of China (Grant No 10474075)
文摘This paper reports that single-layer and graded Au-TiO2 granular composite films with Au atom content 15%- 66% were prepared by using reactive co-sputtering technique. The third-order optical nonlinearity of single-layer and graded composite films was investigated by using s- and p-polarized Z-scans in femtosecond time scale. The nonlinear absorption coefficient βeff of single-layer Au-TiO2 films is measured to be -2.3×10^3-0.76×10^3 cm/GW with Au atom content 15%-66%. The βeff value of the 10-layer Au-TiO2 graded film is enhanced to be -2.1×10^4cm/GW calculated from p-polarized Z-scans, which is about ten times the maximum βeff of single-layer films. Broadened response in the wavelength region 730-860 nm of the enhanced optical nonlinearity of graded Au-TiO2 composite films was also investigated.
文摘Nano sized powders of TiO2 （titanium dioxide） and Nb2O5 （Niobium （V） oxide） were used to fabricate TiO2/Nb2O5 composites thin films by EPD （electrophoretic deposition） technique. The metal oxide powders, together with magnesium nitrate hexahydrate pellets, were suspended in propan-2-ol inside an EPD cell. The electrodes, placed 1.2 cm apart, were partially immersed in the suspension and a DC potential applied across them. Key EPD process parameters, which include applied DC electric field, deposition time and solid concentration in suspension, were optimized through visual inspection and from UV-Vis-NIR spectrophotometer spectra. The highest （55%） transmittance was obtained for films with deposition time of 90 s, powder concentration of 0.01 g/40 mL, and 35 V DC （direct current） voltage. XRD micrographs confirmed that TiO2 and Nb2O5 particles were presented in the composite film. SEM （scanning electron microscope） micrographs of the composite electrode thin films showed that porous films of high quality with well controlled morphology were deposited by using the EPD technique.
基金Supported by the National Natural Science Foundation of China under Grant Nos 11174137,11474215 and 21204058the Natural Science Foundation for the Youth of Jiangsu Province under Grant No BK20130284the Priority Academic Program Development of Jiangsu Higher Education Institutions
文摘Titanium dioxide （TiO2） loaded tungsten trioxide （WO3） composite films are prepared by an E-beam vapor system. Associated with the existence of a heterojunction at the interface of TiO2 and WO3, the prepared TiO2-WO3 composite film shows enhanced photocurrent density, four times than the pure WO3 film illuminated under xenon lamp, and higher incident-photon-to-current conversion e^ciency. By varying the initial TiO2 film thickness, such composite structures could be optimized to obtain the highest photocurrent density. We believe that thin TiO2 films improve the light response and increase the surface roughness of WO3 films. Furthermore, the existence of the heterojunction results in the e^cient charge carriers＇ separation, transfer process, and a lower recombination of electron-hole pairs, which is beneficial for the enhancement of photocurrent density.
文摘CuIn（S,Se）2 thin films were prepared by thermal crystallization of co-sputtered Cu-In alloy precursors in S/Se atmosphere. In-depth compositional uniformity is an important prereq- uisite for obtaining device-quality CuIn（S,Se）2 absorber thin films. In order to figure out the influence of heat treatments on in-depth composition uniformity of CuIn（S,Se）2 thin films, two kinds of reaction temperature profiles were investigated. One process is ＂one step profile＂, referring to formation of CuIn（S,Se）2 thin films just at elevated temperature （e.g. 500 ℃）. The other is ＂two step profile＂, which allows for slow diffusion of S and Se elements into the alloy precursors at a low temperature before the formation and re-crystallization of CuIn（S,Se）2 thin films at higher temperature （e.g. first 250 ℃ then 500 ℃）. X-ray diffrac- tion studies reveal that there is a discrepancy in the shape of （112） peak. Samples annealed with ＂one step profile＂ have splits on （112） peaks, while samples annealed with ＂two step profile＂ have relatively symmetrical （112） peaks. Grazing incident X-ray diffraction and en- ergy dispersive spectrum measurements of samples successively etched in bromine methanol show that CuIn（S,Se）2 thin films have better in-depth composition uniformity after ＂two step profile＂ annealing. The reaction mechanism during the two thermal processing was also investigated by X-ray diffraction and Raman spectra.
基金Sponsored by Hi-Tech Research and Development Program of China (2003AA305120)
文摘The Ni-P/TiO2 composite film on sintered NdFeB permanent magnet was investigated by X-ray diffraction （XRD）,environmental scanning electron microscopy （ESEM）,and energy dispersive X-ray spectrometer （EDX）. The corrosion resistance of Ni-P/TiO2 film coated on NdFeB magnet,in 0.5 mol/L NaCl solution,was studied by potentiodynamic polarization,salt spray test and electrochemical impedance spectroscopy （EIS） techniques. The self-corrosion current density （icorr） and the polarization resistance （Rp） of Ni-P/TiO2 film are 0.22 μA/cm2 （about 14% of that of Ni-P coating）,and 120 kΩ·cm2 （about 2 times of that of Ni-P coating）,respectively. The anti-salt spray time of Ni-P/TiO2 film is about 2.5 times of that of the Ni-P coating. The results indicate that Ni-P/TiO2 film has a better corrosion resistance than Ni-P coating,and the composite film increases the corrosion resistance of NdFeB magnet markedly.
基金Funded by the National Natural Science Foundation of China(No.61205062)the Scientific Research Foundation for Doctor of University(No.2019Y02)。
文摘A novel fiber optic sensor based on optical composite oxygen-sensitive film was developed for determination of 2,4-dichlorophenol(DCP).The optical composite oxygen-sensitive film consists of tris(2,2’-bipyridyl)dichloro ruthenium(II)hexahydrate(Ru(bpy)3Cl2)as the fluorescence indicator and iron(III)tetrasulfophthalocyanine(Fe(III)PcTs)as bionic enzyme.A lock-in amplifier was used for detecting the lifetime of the composite oxygen-sensitive film by measuring the phase delay of the sensor head.The different variables affecting the sensor performance were evaluated and optimized.Under the optimal conditions(i e,pH 6.0,25℃,Fe(III)PcTs concentration of 5.0×10^-5 mol/L),the linear detection range,detection limit and response time of the fiber optic sensor are 3.0×10^-7-9.0×10^-5 mol/L,4.8×10^-8 mol/L(S/N=3),and 220 s,respectively.The sensor displays high selectivity,good repeatability and stability,which have good potentials in analyzing DCP concentration in practical water samples.
文摘A NiP/TiO2 composite film on carbon steel was prepared by electroless plating and sol-gel composite process. An artificial neural network was applied to optimize the prepared condition of the composite film. Corrosion behavior of the NiP/TiO2 composite film was investigated by polarization resistance measurement, anode polarization, ESEM （environmental scanning electron microscopy） and EIS （electrochemical impedance spectroscopy） measurements. Results showed that the NiP/ TiO2 composite film has a good corrosion resistance in 0.5mol/L H2SO4 solution. The element valence of the composite film was characterized by XPS （X-ray photoelectron spectroscopy） spectrum, and an anticorrosion mechanism of the composite film was discussed.
基金supported by the National Science Funds for Creative Research Groups of China (No. 51421006)the National Major Projects of Water Pollution Control and Management Technology (No. 2017ZX07204003)+2 种基金the National Key Plan for Research and Development of China (2016YFC0502203)the Key Program of National Natural Science Foundation of China (No. 91647206)the Qing Lan Project of Jiangsu Province, and PAPD
文摘TiO2 films have received increasing attention for the removal of organic pollutants via photocatalysis. To develop a simple and effective method for improving the photodegradation efficiency of pollutants in surface water, we herein examined the preparation of a P25-TiO2 composite film on a cement substrate via a sol–gel method. In this case, Rhodamine B（Rh B）was employed as the target organic pollutant. The self-generated TiO2 film and the P25-TiO2 composite film were characterized by X-ray diffraction（XRD）, N2 adsorption/desorption measurements, scanning electron microscopy（SEM）, transmission electron microscopy（TEM）, and diffuse reflectance spectroscopy（DRS）. The photodegradation efficiencies of the two films were studied by Rh B removal in water under UV（ultraviolet） irradiation. Over 4 day exposure, the P25-TiO2 composite film exhibited higher photocatalytic performance than the self-generated TiO2 film. The photodegradation rate indicated that the efficiency of the P25-TiO2 composite film was enhanced by the addition of the rutile phase Degussa P25 powder. As such, cooperation between the anatase TiO2 and rutile P25 nanoparticles was beneficial for separation of the photo-induced electrons and holes. In addition, the influence of P25 doping on the P25-TiO2 composite films was evaluated. We found that up to a certain saturation point, increased doping enhanced the photodegradation ability of the composite film. Thus, we herein demonstrated that the doping of P25 powders is a simple but effective strategy to prepare a P25-TiO2 composite film on a cement substrate, and the resulting film exhibits excellent removal efficiency in the degradation of organic pollutants.
文摘The oxidation behaviors of Fe26Cr1Mo with and without the Ni La 2O 3 electrodeposited composite film have been investigated by thermogravimetric analysis (TGA) and a scanning electron microscope equipped with an energy dispersive analytical X ray system(SEM/EDAX). The experimental results show that the oxide scale growing on Fe26Cr1Mo exposed at 900 ℃ spalled severely during cooling, while after the stainless steel was coated with the Ni La 2O 3 electrodeposited composite film, its high temperature cyclic oxidation resistance was significantly improved. The reason is that a La 2O 3 modified NiO scale, which has a superior adhesion to the substrate, was formed on the Fe26Cr1Mo stainless steel coated with Ni La 2O 3 composite film.