To reveal how cerium stabilizes Cu/SAPO-34 at low-temperature hydrothermal aging,various amounts of cerium were introduced into Cu/SAPO-34 via impregnation method and treated at 70℃with RH 80%for 96 h.Cerium as Ce^(3...To reveal how cerium stabilizes Cu/SAPO-34 at low-temperature hydrothermal aging,various amounts of cerium were introduced into Cu/SAPO-34 via impregnation method and treated at 70℃with RH 80%for 96 h.Cerium as Ce^(3+)and CeO_(2)nanoparticle is located on the surface of Cu/SAPO-34,and Ce^(3+)plays a vital role on gradually decreasing surface acidity and blocking defect sites with an increase of Ce loading.After hydrothermal aging,Cu/SAPO-34 with high Ce loading shows the superior SCR activity comparable to fresh samples.It is proven that the surface acidity determines the stability of the structure during hydrothermal aging process,and lower surface acidity prevents the number of Cu(Ⅱ)ions from decreasing significantly.Furthermore,the structure's stability helps the recovery of Cu(Ⅱ)ions and renders an outstanding regene ration ability.Our finding paves the way for the design of new Cu/SAPO-34catalysts with good SCR activity and long-term stability in real application.展开更多
The elegant 2D multiquantum (MQ) MAS NMR has been applied to investigate the coordination of Al atoms in SAPO-34. The results show that the effects of the template and/or water on the coordination of Al atoms are sig...The elegant 2D multiquantum (MQ) MAS NMR has been applied to investigate the coordination of Al atoms in SAPO-34. The results show that the effects of the template and/or water on the coordination of Al atoms are significant, which lead to the formation of various Al species. Up to four kinds of Al species are distinctly resolved.展开更多
Based on the previous findings that the presence of hydroxyl groups on the outer surface is crucial for maintaining skeletal stability,we propose a strategy modified Cu/SAPO-34 using Pr ions in this study.Therefore,we...Based on the previous findings that the presence of hydroxyl groups on the outer surface is crucial for maintaining skeletal stability,we propose a strategy modified Cu/SAPO-34 using Pr ions in this study.Therefore,we conducted several measurements to investigate the effect of Pr ions on the lowtemperature hydrothermal stability of Cu/SAPO-34.We find that Pr exists only on the surface of Cu/SAPO-34 as ions and oxides,with Pr^(3+)ions playing a protective role in occupying surface acidic sites.The addition of small amounts of Pr leads to the re-dispersion of Cu,resulting in improved lowtemperature selective catalytic reduction(SCR)activity in the as-synthesized samples.Furthermore,it enhances the resistance to decomposition of the Si-(OH)-Al framework during low-temperature hydrothermal aging,thereby preserving the framework structure and allowing detached active Cu species to return to exchangeable positions,ultimately restoring SCR activity.However,as the Pr content increases,the enhanced acidity causes some structural damage,gradually weakening the protective effect.Our work demonstrates that Pr modification is a simple and effective solution to the issue of poor lowtemperature hydrothermal stability in Cu/SAPO-34,providing a promising way for the application of light rare earth elements.展开更多
This study was aimed to investigate the effects of hydrothermal aging, propene and SO<sub>2</sub> poisoning on the ammonia-selective catalytic reduction (NH<sub>3</sub>-SCR) performance of both...This study was aimed to investigate the effects of hydrothermal aging, propene and SO<sub>2</sub> poisoning on the ammonia-selective catalytic reduction (NH<sub>3</sub>-SCR) performance of both Cu-SAPO-34 and Cu-ZSM-5. The catalytic activities of fresh, aged and poisoned samples were tested in ammonia-selective catalytic reduction (NH<sub>3</sub>-SCR) of NO<sub>x</sub> conditions. The XRD, TG and N<sub>2</sub>-desorption results showed that the structures of the Cu-SAPO-34 and Cu-ZSM-5 remained intact after 750˚C hydrothermally aged, SO<sub>2</sub> and propene poisoned. After hydrothermal aging at 750˚C for 12 h, the NO reduction performance of Cu-ZSM-5 was significantly reduced at lower temperatures, while that of Cu-SAPO-34 was less affected. Moreover, Cu-SAPO-34 catalyst showed high NO conversion with SO<sub>2</sub> or propene compared to Cu-ZSM-5. However, Cu-ZSM-5 showed a larger drop in catalytic activity with SO<sub>2</sub> or propene compared to Cu-SAPO-34 catalyst. The H<sub>2</sub>-TPR results showed that Cu<sup>2 </sup> ions could be reduced to Cu<sup> </sup> and Cu<sup>0</sup> for Cu-ZSM-5, while no significant transformation of copper species was observed for Cu-SAPO-34. Meanwhile, the UV-vis DRS results showed that CuO species were formed in Cu-ZSM-5, while little changes were observed for the Cu-SAPO-34. Cu-SAPO-34 showed high sulfur and hydrocarbon poison resistance compared to Cu-ZSM-5. In summary, Cu-SAPO-34 with small-pore zeolite showed higher hydrothermal stability and better hydrocarbon and sulfur poison resistant than Cu-ZSM-5 with medium-pore.展开更多
基金the National Natural Science Foundation of China for Youths(21908207)National Key R&D Program of China(2021YFB3503200)+3 种基金the Key R&D project of Shandong Province(2021CXGC010703)China Postdoctoral Science Foundation(2020M670659)Shanxi Province Science Foundation for Youths(201901D211224)Scientific and Technological Innovation Programs of Higher Education Institutions in Shanxi(2019L0575)。
文摘To reveal how cerium stabilizes Cu/SAPO-34 at low-temperature hydrothermal aging,various amounts of cerium were introduced into Cu/SAPO-34 via impregnation method and treated at 70℃with RH 80%for 96 h.Cerium as Ce^(3+)and CeO_(2)nanoparticle is located on the surface of Cu/SAPO-34,and Ce^(3+)plays a vital role on gradually decreasing surface acidity and blocking defect sites with an increase of Ce loading.After hydrothermal aging,Cu/SAPO-34 with high Ce loading shows the superior SCR activity comparable to fresh samples.It is proven that the surface acidity determines the stability of the structure during hydrothermal aging process,and lower surface acidity prevents the number of Cu(Ⅱ)ions from decreasing significantly.Furthermore,the structure's stability helps the recovery of Cu(Ⅱ)ions and renders an outstanding regene ration ability.Our finding paves the way for the design of new Cu/SAPO-34catalysts with good SCR activity and long-term stability in real application.
基金We are grateful to the support of the National Natural Science Foundation of China and the Ministry of Science and Technology of China. We appreciate Dr. R. Fu (NHMFL Tallahassee) for his kind help regarding the MQ MAS NMR experiments.
文摘The elegant 2D multiquantum (MQ) MAS NMR has been applied to investigate the coordination of Al atoms in SAPO-34. The results show that the effects of the template and/or water on the coordination of Al atoms are significant, which lead to the formation of various Al species. Up to four kinds of Al species are distinctly resolved.
基金supported by the National Key R&D Program of China(2021YFB3503200)the Innovative Research Groups of the National Natural Science Foundation of China(51921004)+1 种基金Young Elite Scientists Sponsorship Program by CAST(2021QNRC001)the Key R&D project of Shandong Province(2021CXGC010703,2022CXGC020311)。
文摘Based on the previous findings that the presence of hydroxyl groups on the outer surface is crucial for maintaining skeletal stability,we propose a strategy modified Cu/SAPO-34 using Pr ions in this study.Therefore,we conducted several measurements to investigate the effect of Pr ions on the lowtemperature hydrothermal stability of Cu/SAPO-34.We find that Pr exists only on the surface of Cu/SAPO-34 as ions and oxides,with Pr^(3+)ions playing a protective role in occupying surface acidic sites.The addition of small amounts of Pr leads to the re-dispersion of Cu,resulting in improved lowtemperature selective catalytic reduction(SCR)activity in the as-synthesized samples.Furthermore,it enhances the resistance to decomposition of the Si-(OH)-Al framework during low-temperature hydrothermal aging,thereby preserving the framework structure and allowing detached active Cu species to return to exchangeable positions,ultimately restoring SCR activity.However,as the Pr content increases,the enhanced acidity causes some structural damage,gradually weakening the protective effect.Our work demonstrates that Pr modification is a simple and effective solution to the issue of poor lowtemperature hydrothermal stability in Cu/SAPO-34,providing a promising way for the application of light rare earth elements.
文摘This study was aimed to investigate the effects of hydrothermal aging, propene and SO<sub>2</sub> poisoning on the ammonia-selective catalytic reduction (NH<sub>3</sub>-SCR) performance of both Cu-SAPO-34 and Cu-ZSM-5. The catalytic activities of fresh, aged and poisoned samples were tested in ammonia-selective catalytic reduction (NH<sub>3</sub>-SCR) of NO<sub>x</sub> conditions. The XRD, TG and N<sub>2</sub>-desorption results showed that the structures of the Cu-SAPO-34 and Cu-ZSM-5 remained intact after 750˚C hydrothermally aged, SO<sub>2</sub> and propene poisoned. After hydrothermal aging at 750˚C for 12 h, the NO reduction performance of Cu-ZSM-5 was significantly reduced at lower temperatures, while that of Cu-SAPO-34 was less affected. Moreover, Cu-SAPO-34 catalyst showed high NO conversion with SO<sub>2</sub> or propene compared to Cu-ZSM-5. However, Cu-ZSM-5 showed a larger drop in catalytic activity with SO<sub>2</sub> or propene compared to Cu-SAPO-34 catalyst. The H<sub>2</sub>-TPR results showed that Cu<sup>2 </sup> ions could be reduced to Cu<sup> </sup> and Cu<sup>0</sup> for Cu-ZSM-5, while no significant transformation of copper species was observed for Cu-SAPO-34. Meanwhile, the UV-vis DRS results showed that CuO species were formed in Cu-ZSM-5, while little changes were observed for the Cu-SAPO-34. Cu-SAPO-34 showed high sulfur and hydrocarbon poison resistance compared to Cu-ZSM-5. In summary, Cu-SAPO-34 with small-pore zeolite showed higher hydrothermal stability and better hydrocarbon and sulfur poison resistant than Cu-ZSM-5 with medium-pore.