Ag TiO 2 thin films were prepared on glasses.The morphology and structure of Ag TiO 2 films were investigated by XRD, SEM and FT IR.The photocatalytic and hydrophilic properties of Ag TiO 2 thin films were also...Ag TiO 2 thin films were prepared on glasses.The morphology and structure of Ag TiO 2 films were investigated by XRD, SEM and FT IR.The photocatalytic and hydrophilic properties of Ag TiO 2 thin films were also evaluated by examining photocatalytic degradation dichlorophos under sunlight illumination and the change of contact angle respectively.The research results show that the Ag TiO 2 thin film is mainly composed of 20-100nm Ag and TiO 2 particles.The Ag TiO 2 thin films possess a super hydrophilic ability and higher photocatalytic activity than that of pure TiO 2 thin film.展开更多
The photo-induced hydrophilicity of SiO2 overlayer on TiO2 films prepared by sol-gel method was investigated by means of soak angle measurement, XPS, UV-VIS and FTIR spectra. The results show that, compared with the T...The photo-induced hydrophilicity of SiO2 overlayer on TiO2 films prepared by sol-gel method was investigated by means of soak angle measurement, XPS, UV-VIS and FTIR spectra. The results show that, compared with the TiO2 film without SiO2 overlayer, when the TiO2 film is thoroughly covered by SiO2 overlayer, the hydrophilicity and the sustained effect are enhanced. It is found that the significant growth of the OH- group occurs in the surface of SiO2 overlayer. The different mechanism of enhanced hydrophilicity between SiO2 overlayer on TiO2 films and TiO2/SiO2 mixing films was analyzed. The result suggests that the photo-generated electrons created in the interface between TiO2 and SiO2 tend to reduce the Ti（Ⅳ） cation to the Ti（Ⅲ） state, and the photogenerated holes transmit through the SiO2 layer to uppermost surface efficiently. Once the holes go up to the surface, they tend to make the surface hydrophilic. The stable hydrophilicity of SiO2 overlayer which adsorbs more stable OH groups, enhances the sustained effect, i.e. the super-hydrophilic state can be maintained for a long time in dark place.展开更多
The dynamic wetting of water spreading on TiO 2 and TiO 2 SiO 2 films prepared by sol gel method and subsequently treated by air plasma and UV irradiation was investigated. Water completely spread on TiO 2 surface wit...The dynamic wetting of water spreading on TiO 2 and TiO 2 SiO 2 films prepared by sol gel method and subsequently treated by air plasma and UV irradiation was investigated. Water completely spread on TiO 2 surface within 3 s and its dynamic contact angles can be expressed by a power law θ d= k(t+a) -n with the n value 0.98. Less than 50%(molar fraction) SiO 2 addition can accelerate the dynamic water spreading rate on the TiO 2 SiO 2 films and the optimum molar fraction of SiO 2 amount corresponding to as annealed, air plasma, and UV irradiation treatment process is 15%, 10% and 20%, respectively.展开更多
文摘Ag TiO 2 thin films were prepared on glasses.The morphology and structure of Ag TiO 2 films were investigated by XRD, SEM and FT IR.The photocatalytic and hydrophilic properties of Ag TiO 2 thin films were also evaluated by examining photocatalytic degradation dichlorophos under sunlight illumination and the change of contact angle respectively.The research results show that the Ag TiO 2 thin film is mainly composed of 20-100nm Ag and TiO 2 particles.The Ag TiO 2 thin films possess a super hydrophilic ability and higher photocatalytic activity than that of pure TiO 2 thin film.
文摘The photo-induced hydrophilicity of SiO2 overlayer on TiO2 films prepared by sol-gel method was investigated by means of soak angle measurement, XPS, UV-VIS and FTIR spectra. The results show that, compared with the TiO2 film without SiO2 overlayer, when the TiO2 film is thoroughly covered by SiO2 overlayer, the hydrophilicity and the sustained effect are enhanced. It is found that the significant growth of the OH- group occurs in the surface of SiO2 overlayer. The different mechanism of enhanced hydrophilicity between SiO2 overlayer on TiO2 films and TiO2/SiO2 mixing films was analyzed. The result suggests that the photo-generated electrons created in the interface between TiO2 and SiO2 tend to reduce the Ti（Ⅳ） cation to the Ti（Ⅲ） state, and the photogenerated holes transmit through the SiO2 layer to uppermost surface efficiently. Once the holes go up to the surface, they tend to make the surface hydrophilic. The stable hydrophilicity of SiO2 overlayer which adsorbs more stable OH groups, enhances the sustained effect, i.e. the super-hydrophilic state can be maintained for a long time in dark place.
文摘The dynamic wetting of water spreading on TiO 2 and TiO 2 SiO 2 films prepared by sol gel method and subsequently treated by air plasma and UV irradiation was investigated. Water completely spread on TiO 2 surface within 3 s and its dynamic contact angles can be expressed by a power law θ d= k(t+a) -n with the n value 0.98. Less than 50%(molar fraction) SiO 2 addition can accelerate the dynamic water spreading rate on the TiO 2 SiO 2 films and the optimum molar fraction of SiO 2 amount corresponding to as annealed, air plasma, and UV irradiation treatment process is 15%, 10% and 20%, respectively.
文摘利用溶胶 凝胶技术,控制钛酸四丁酯(TBOT)与硅酸乙酯(TEOS)的水解速度,使其共同水解成溶胶、凝胶,以乙醇为溶剂进行超临界干燥,经过一定温度热处理后,得到暗黄色透明的块体材料·进行了透射电镜观察和X衍射分析,表明锐钛矿结构的纳米TiO2均匀地分散于无定形SiO2基质中·FT IR光谱分析发现纳米TiO2与SiO2基质之间存在着Ti O Si键·在对罗丹明B水溶液的光催化降解中,此块体材料显示较好的光催化活性,在1h内催化降解86%的罗丹明B·此材料克服了粉状TiO2在实际水污染治理应用中的局限性,有着广泛的应用前景·