In order to improve the electrochemical cycle stability of the RE–Mg–Ni-based A2B7-type electrode alloys, a small amount of Si has been added into the alloys.The casting and annealing technologies were adopted to fa...In order to improve the electrochemical cycle stability of the RE–Mg–Ni-based A2B7-type electrode alloys, a small amount of Si has been added into the alloys.The casting and annealing technologies were adopted to fabricate the La0.8Mg0.2Ni3.3Co0.2Six(x = 0–0.2) electrode alloys. The impacts of the addition of Si and annealing treatment on the structures and electrochemical performances of the alloys were investigated systematically. The results obtained by XRD and SEM show that all the as-cast and annealed alloys are of a multiphase structure, involving two main phases(La, Mg)2Ni7and La Ni5 as well as a residual phase La Ni3. Both adding Si and the annealing treatment lead to an evident change in the phase abundance and cell parameters of(La, Mg)2Ni7and La Ni5 major phases of the alloy without altering its main phase component. Moreover, the annealing treatment has the composition of the alloy distributed more homogeneously overall and simultaneously causes the grain of the alloy to be coarsened obviously. The electrochemical measurements indicate that adding Si and the annealing treatment give a significant rise to the influence on the electrochemical performances of the alloys. In brief, the cycle stability of the as-cast and annealed alloys evidently increases with the rising of Si content, while their discharge capacities obviously decrease under the same circumstances. Furthermore, the electrochemical kineticproperties of the electrode alloys, including the high rate discharge ability, the limiting current density(IL), hydrogen diffusion coefficient(D), and the charge-transfer resistance, first augment and then decline with the rising of Si content. Similarly, it is found that the above-mentioned electrochemical properties first mount up and then go down with the rising annealing temperature.展开更多
The La-Mg-Ni-based A2B7-type La0.5Mg0.2Ni3.3Co0.2Six （x=0-0.2） electrode alloys were prepared by casting and annealing. The influences of the additional silicon and the annealing treatment on the structure and elect...The La-Mg-Ni-based A2B7-type La0.5Mg0.2Ni3.3Co0.2Six （x=0-0.2） electrode alloys were prepared by casting and annealing. The influences of the additional silicon and the annealing treatment on the structure and electrochemical performances of the alloys were investigated systemically. Both of the analyses of XRD and SEM reveal that the as-cast and annealed alloys are of a multiphase structure, involving two main phases （La, Mg）2Ni7 and LaNi5 as well as one minor phase LaNi3. The addition of Si and annealing treatment bring on an evident change in the phase abundances and cell parameters of （La, Mg）2Ni7 and LaNi5 phase for the alloy without altering its phase structure. The phase abundances decrease from 74.3% （x=0） to 57.8% （x=0.2） for the （La, Mg）2Ni7 phase, and those of LaNi5 phase increase from 20.2% （x^0） to 37.3% （x=0.2）. As for the electrochemical measurements, adding Si and performing annealing treatment have engendered obvious impacts. The cycle stability of the alloys is improved dramatically, being enhanced from 80.3% to 93.7% for the as-annealed （950 ℃） alloys with Si content increasing from 0 to 0.2. However, the discharge capacity is reduced by adding Si, from 399.4 to 345.3 mA.h/g as the Si content increases from 0 to 0.2. Furthermore, such addition makes the electrochemical kinetic properties of the alloy electrodes first increase and then decrease. Also, it is found that the overall electrochemical properties of the alloys first augment and then fall with the annealing temperature rising.展开更多
基金financially supported by the National Natural Science Foundation of China (Nos. 50961009 and 51161015)the National High Technology Research and Development Program of China (No. 2011AA03A408)the National High Technology Research and Development Program of China (Nos. 2011ZD10 and 2010ZD05)
文摘In order to improve the electrochemical cycle stability of the RE–Mg–Ni-based A2B7-type electrode alloys, a small amount of Si has been added into the alloys.The casting and annealing technologies were adopted to fabricate the La0.8Mg0.2Ni3.3Co0.2Six(x = 0–0.2) electrode alloys. The impacts of the addition of Si and annealing treatment on the structures and electrochemical performances of the alloys were investigated systematically. The results obtained by XRD and SEM show that all the as-cast and annealed alloys are of a multiphase structure, involving two main phases(La, Mg)2Ni7and La Ni5 as well as a residual phase La Ni3. Both adding Si and the annealing treatment lead to an evident change in the phase abundance and cell parameters of(La, Mg)2Ni7and La Ni5 major phases of the alloy without altering its main phase component. Moreover, the annealing treatment has the composition of the alloy distributed more homogeneously overall and simultaneously causes the grain of the alloy to be coarsened obviously. The electrochemical measurements indicate that adding Si and the annealing treatment give a significant rise to the influence on the electrochemical performances of the alloys. In brief, the cycle stability of the as-cast and annealed alloys evidently increases with the rising of Si content, while their discharge capacities obviously decrease under the same circumstances. Furthermore, the electrochemical kineticproperties of the electrode alloys, including the high rate discharge ability, the limiting current density(IL), hydrogen diffusion coefficient(D), and the charge-transfer resistance, first augment and then decline with the rising of Si content. Similarly, it is found that the above-mentioned electrochemical properties first mount up and then go down with the rising annealing temperature.
基金Projects(51371094,51161015)supported by the National Natural Science Foundations of ChinaProject(2011ZD10)supported by Natural Science Foundation of Inner Mongolia,China
文摘The La-Mg-Ni-based A2B7-type La0.5Mg0.2Ni3.3Co0.2Six （x=0-0.2） electrode alloys were prepared by casting and annealing. The influences of the additional silicon and the annealing treatment on the structure and electrochemical performances of the alloys were investigated systemically. Both of the analyses of XRD and SEM reveal that the as-cast and annealed alloys are of a multiphase structure, involving two main phases （La, Mg）2Ni7 and LaNi5 as well as one minor phase LaNi3. The addition of Si and annealing treatment bring on an evident change in the phase abundances and cell parameters of （La, Mg）2Ni7 and LaNi5 phase for the alloy without altering its phase structure. The phase abundances decrease from 74.3% （x=0） to 57.8% （x=0.2） for the （La, Mg）2Ni7 phase, and those of LaNi5 phase increase from 20.2% （x^0） to 37.3% （x=0.2）. As for the electrochemical measurements, adding Si and performing annealing treatment have engendered obvious impacts. The cycle stability of the alloys is improved dramatically, being enhanced from 80.3% to 93.7% for the as-annealed （950 ℃） alloys with Si content increasing from 0 to 0.2. However, the discharge capacity is reduced by adding Si, from 399.4 to 345.3 mA.h/g as the Si content increases from 0 to 0.2. Furthermore, such addition makes the electrochemical kinetic properties of the alloy electrodes first increase and then decrease. Also, it is found that the overall electrochemical properties of the alloys first augment and then fall with the annealing temperature rising.