An AZ41 magnesium alloy in the hot-rolled condition without further thermomechanical processing to modify its microstructure was investigated to establish its suitability for use within a superplastic forming process ...An AZ41 magnesium alloy in the hot-rolled condition without further thermomechanical processing to modify its microstructure was investigated to establish its suitability for use within a superplastic forming process and to establish optimum forming parameters.Formability was assessed using elevated temperature tensile testing and hot gas bulging,across a range of strain rates(1×10^(−1)−1×10^(−3)s^(−1))and temperatures(350−450℃).Circle grid analysis with GOM Aramis cameras was used to understand peak strains and material thinning in relation to industrial forming processes.Post forming EBSD and STEM analysis was conducted to understand the mechanisms responsible for the materials formability,with dynamic recrystallization being clearly evident.Peak elongation of 520%was achieved at 450℃ and 1×10^(−3)s^(−1);industrially relevant elongation was achieved at 1×10^(−2) s^(−1) at both 450℃(195%)and 400℃(170%).展开更多
A dynamic material model of Mg-4.51Al-1.19Zn-0.5Mn-0.5Ca(AZ41,mass fraction,%)magnesium alloy was put forward.The results show that the dynamic material model can characterize the deformation behavior and microstructu...A dynamic material model of Mg-4.51Al-1.19Zn-0.5Mn-0.5Ca(AZ41,mass fraction,%)magnesium alloy was put forward.The results show that the dynamic material model can characterize the deformation behavior and microstructure evolution and describe the relations among flow stress,strain,strain rates and deformation temperatures.Statistical analysis shows the validity of the proposed model.The model predicts that lower deformation temperature and higher strain rate cause the sharp strain hardening. Meanwhile,the flow stress curve turns into a steady state at high temperature and lower strain rate.The moderate temperature of 350 ℃and strain rate of 0.01 s-1 are appropriate to this alloy.展开更多
基金The authors would like to thank the WMG High Value Manufacturing Catapult Centre for funding this work.In addition,the characterisation facility is supported from the Higher Education Funding Council for England(HEFCE).
文摘An AZ41 magnesium alloy in the hot-rolled condition without further thermomechanical processing to modify its microstructure was investigated to establish its suitability for use within a superplastic forming process and to establish optimum forming parameters.Formability was assessed using elevated temperature tensile testing and hot gas bulging,across a range of strain rates(1×10^(−1)−1×10^(−3)s^(−1))and temperatures(350−450℃).Circle grid analysis with GOM Aramis cameras was used to understand peak strains and material thinning in relation to industrial forming processes.Post forming EBSD and STEM analysis was conducted to understand the mechanisms responsible for the materials formability,with dynamic recrystallization being clearly evident.Peak elongation of 520%was achieved at 450℃ and 1×10^(−3)s^(−1);industrially relevant elongation was achieved at 1×10^(−2) s^(−1) at both 450℃(195%)and 400℃(170%).
基金Project(Y2008F27)supported by the Natural Science Foundation of Shandong Province,China
文摘A dynamic material model of Mg-4.51Al-1.19Zn-0.5Mn-0.5Ca(AZ41,mass fraction,%)magnesium alloy was put forward.The results show that the dynamic material model can characterize the deformation behavior and microstructure evolution and describe the relations among flow stress,strain,strain rates and deformation temperatures.Statistical analysis shows the validity of the proposed model.The model predicts that lower deformation temperature and higher strain rate cause the sharp strain hardening. Meanwhile,the flow stress curve turns into a steady state at high temperature and lower strain rate.The moderate temperature of 350 ℃and strain rate of 0.01 s-1 are appropriate to this alloy.