The mixed grain structure and mechanical property anisotropy of AZ40 magnesium alloy bar with a diameter of 160 mm manufactured by ＂multi-direction forging（MDF） ＋ extrusion ＋ online cooling＂ technique were inves...The mixed grain structure and mechanical property anisotropy of AZ40 magnesium alloy bar with a diameter of 160 mm manufactured by ＂multi-direction forging（MDF） ＋ extrusion ＋ online cooling＂ technique were investigated by optical microscopy（OM）, scanning electron microscopy（SEM）, X-ray diffraction macro-texture measurement and room temperature（RT） tensile test. The results show that mixed grain structure is caused by the micro-segregation of Al in semi-continuous casting ingot. Homogenization of（380 °C, 8 h） ＋（410 °C, 12 h） cannot totally eliminate such micro-segregation. During MDF and extrusion, the dendrite interiors with 3%-4% Al（mass fraction） transform to fine grain zones, yet the dendrite edges with about 6% Al transform to coarse grain zones. XRD macro-textures of the outer, R/2 and center show typical fiber texture characteristics and the intensity of [0001]//Ra D orientation in the outer（11.245） is about twice as big as those in the R/2（6.026） and center（6.979）. The as-extruded AZ40 magnesium alloy bar has high elongation（A） and moderate ultimate tensile strength（Rm） in both extrusion direction（ED） and radius direction（Ra D）, i.e., A of 19%-25% and Rm of 256-264 MPa; however, yield strength（Rp0.2） shows anisotropy and heterogeneity, i.e., 103 MPa in Ra D, 137 MPa in ED-C（the center） and 161 MPa in ED-O（the outer）, which are mainly caused by the texture.（155 °C, 7 h） ＋（170 °C, 24 h） aging has no influence on strength and elongation of AZ40 magnesium bar.展开更多
Hot compression tests on AZ40 magnesium alloy were conducted on a Gleeble 1500 d hot simulation testing machine in a deformation temperature range of 330 ℃-420 ℃ and a strain rate range of 0.002-2 s^-1. Hot deformat...Hot compression tests on AZ40 magnesium alloy were conducted on a Gleeble 1500 d hot simulation testing machine in a deformation temperature range of 330 ℃-420 ℃ and a strain rate range of 0.002-2 s^-1. Hot deformation behaviors were investigated on the basis of the analysis of the flow stressstrain curves, constitutive equation, and processing map. The stress exponent and apparent activation energy were calculated to be 5.821 and 173.96 k J/mol, respectively. Deformation twins and cracks located in grain boundaries were generated at 330 ℃ and 0.02 s^-1, which are associated with a high strain rate and a limited number of available slip systems. With increasing temperature and decreasing strain rate, the twins disappeared and the degree of dynamic recrystallization increased. The alloy was completely dynamically recrystallized at 420 ℃ and 0.002 s^-1, with a homogenous grain size of approximately 13.7 μm. The instability domains of the deformation behavior can be recognized by processing maps. By considering the processing maps and characterizing the microstructure, the optimum hot deformation parameters in this experiment were determined to be 420 ℃ and 0.002 s^-1.展开更多
基金Project(2013CB632202)supported by the National Basic Research Program of China
文摘The mixed grain structure and mechanical property anisotropy of AZ40 magnesium alloy bar with a diameter of 160 mm manufactured by ＂multi-direction forging（MDF） ＋ extrusion ＋ online cooling＂ technique were investigated by optical microscopy（OM）, scanning electron microscopy（SEM）, X-ray diffraction macro-texture measurement and room temperature（RT） tensile test. The results show that mixed grain structure is caused by the micro-segregation of Al in semi-continuous casting ingot. Homogenization of（380 °C, 8 h） ＋（410 °C, 12 h） cannot totally eliminate such micro-segregation. During MDF and extrusion, the dendrite interiors with 3%-4% Al（mass fraction） transform to fine grain zones, yet the dendrite edges with about 6% Al transform to coarse grain zones. XRD macro-textures of the outer, R/2 and center show typical fiber texture characteristics and the intensity of [0001]//Ra D orientation in the outer（11.245） is about twice as big as those in the R/2（6.026） and center（6.979）. The as-extruded AZ40 magnesium alloy bar has high elongation（A） and moderate ultimate tensile strength（Rm） in both extrusion direction（ED） and radius direction（Ra D）, i.e., A of 19%-25% and Rm of 256-264 MPa; however, yield strength（Rp0.2） shows anisotropy and heterogeneity, i.e., 103 MPa in Ra D, 137 MPa in ED-C（the center） and 161 MPa in ED-O（the outer）, which are mainly caused by the texture.（155 °C, 7 h） ＋（170 °C, 24 h） aging has no influence on strength and elongation of AZ40 magnesium bar.
基金Funded by the National Natural Science Foundation of China(No.51204020)the National Program on Key Basic Research Project(No 2013CB632202)the Qinghai Provincial Science and Technology Support Project(2014-GX-106A)
文摘Hot compression tests on AZ40 magnesium alloy were conducted on a Gleeble 1500 d hot simulation testing machine in a deformation temperature range of 330 ℃-420 ℃ and a strain rate range of 0.002-2 s^-1. Hot deformation behaviors were investigated on the basis of the analysis of the flow stressstrain curves, constitutive equation, and processing map. The stress exponent and apparent activation energy were calculated to be 5.821 and 173.96 k J/mol, respectively. Deformation twins and cracks located in grain boundaries were generated at 330 ℃ and 0.02 s^-1, which are associated with a high strain rate and a limited number of available slip systems. With increasing temperature and decreasing strain rate, the twins disappeared and the degree of dynamic recrystallization increased. The alloy was completely dynamically recrystallized at 420 ℃ and 0.002 s^-1, with a homogenous grain size of approximately 13.7 μm. The instability domains of the deformation behavior can be recognized by processing maps. By considering the processing maps and characterizing the microstructure, the optimum hot deformation parameters in this experiment were determined to be 420 ℃ and 0.002 s^-1.