To investigate the influence of Al-Zn-Mg-Cu alloy with as-homogenized and as-rolled initial microstructures on the tensile flow behavior,isothermal tensile tests were conducted on a GLEEBLE-3500 isothermal simulator a...To investigate the influence of Al-Zn-Mg-Cu alloy with as-homogenized and as-rolled initial microstructures on the tensile flow behavior,isothermal tensile tests were conducted on a GLEEBLE-3500 isothermal simulator at temperatures of 380-440℃and strain rates of 0.05-1 s^(−1).The Johnson-Cook model,Hensel-Spittel model,strain-compensated Arrhenius model,and critical fracture strain model were established.Results show that through the evaluation of the models using the correlation coefficient(R)and the average absolute relative error,the strain-compensated Arrhenius model can represent the flow behavior of the alloy more accurately.Shear bands are more pronounced in the as-homogenized specimens,whereas dynamic recrystallization is predominantly observed in as-rolled specimens.Fracture morphology analysis reveals that a mixed fracture mechanism is prevalent in the as-homogenized specimen,whereas a ductile fracture mechanism is predominant in the as-rolled specimen.The processing maps indicate that the unstable region is reduced in the as-rolled specimens compared with that in the as-homogenized specimens.The optimal hot working windows for the as-homogenized and as-rolled specimens are determined as 410-440℃/0.14-1 s^(−1)and 380-400℃/0.05-0.29 s^(−1),respectively.展开更多
文摘To investigate the influence of Al-Zn-Mg-Cu alloy with as-homogenized and as-rolled initial microstructures on the tensile flow behavior,isothermal tensile tests were conducted on a GLEEBLE-3500 isothermal simulator at temperatures of 380-440℃and strain rates of 0.05-1 s^(−1).The Johnson-Cook model,Hensel-Spittel model,strain-compensated Arrhenius model,and critical fracture strain model were established.Results show that through the evaluation of the models using the correlation coefficient(R)and the average absolute relative error,the strain-compensated Arrhenius model can represent the flow behavior of the alloy more accurately.Shear bands are more pronounced in the as-homogenized specimens,whereas dynamic recrystallization is predominantly observed in as-rolled specimens.Fracture morphology analysis reveals that a mixed fracture mechanism is prevalent in the as-homogenized specimen,whereas a ductile fracture mechanism is predominant in the as-rolled specimen.The processing maps indicate that the unstable region is reduced in the as-rolled specimens compared with that in the as-homogenized specimens.The optimal hot working windows for the as-homogenized and as-rolled specimens are determined as 410-440℃/0.14-1 s^(−1)and 380-400℃/0.05-0.29 s^(−1),respectively.