In this research, development of AI356-AI203 nanocomposite coatings has been investigated. AI356-AI203 composite powders were prepared by mechanical milling of AI356 powder and 5 vol.% micro and nanoscaled alumina par...In this research, development of AI356-AI203 nanocomposite coatings has been investigated. AI356-AI203 composite powders were prepared by mechanical milling of AI356 powder and 5 vol.% micro and nanoscaled alumina particles. The milled powders were used as feedstock to deposit composite coatings on A356-T6 aluminum alloy substrate using high velocity oxy-fuel （HVOF） process. X-ray diffractometry, optical and scanning electron microscopy, microhardness and wear tests were used to characterize the composite powders and coatings. The hardness of composite coatings containing micro and nanosized AI203 were 114.1 ± 5.9 HV and 138.4 ± 6.9 HV, respectively which were higher than those for substrate （79.2 ± 1.1 HV）. Nano and microcomposite coatings revealed low friction coefficients and wear rates, which were significantly lower than those obtained for AI356-T6 substrate. Addition of 5 vol.% micro and nanoscaled alumina particles improved the wear resistance by an average of 85% and 91%, respectively. This is mainly caused by the presence of AI203 in matrix and nanocrystalline structure of matrix. Scanning electron microscopy tests revealed different wear mechanisms on the surface of the wear test specimens.展开更多
文摘In this research, development of AI356-AI203 nanocomposite coatings has been investigated. AI356-AI203 composite powders were prepared by mechanical milling of AI356 powder and 5 vol.% micro and nanoscaled alumina particles. The milled powders were used as feedstock to deposit composite coatings on A356-T6 aluminum alloy substrate using high velocity oxy-fuel （HVOF） process. X-ray diffractometry, optical and scanning electron microscopy, microhardness and wear tests were used to characterize the composite powders and coatings. The hardness of composite coatings containing micro and nanosized AI203 were 114.1 ± 5.9 HV and 138.4 ± 6.9 HV, respectively which were higher than those for substrate （79.2 ± 1.1 HV）. Nano and microcomposite coatings revealed low friction coefficients and wear rates, which were significantly lower than those obtained for AI356-T6 substrate. Addition of 5 vol.% micro and nanoscaled alumina particles improved the wear resistance by an average of 85% and 91%, respectively. This is mainly caused by the presence of AI203 in matrix and nanocrystalline structure of matrix. Scanning electron microscopy tests revealed different wear mechanisms on the surface of the wear test specimens.