感应熔炼制备La0.8-xCexMg0.2 Ni 3.8(x=0,0.1,0.3,0.5),研究Ce替代部分La对La4MgNi19超晶格负极材料相结构及电化学性能的影响。研究表明,La4MgNi19合金相由LaNi5,(La,Mg)2Ni7,(La,Mg)5Ni19(3R-Ce5Co19)相组成。加入Ce后,(La,Mg)2Ni7...感应熔炼制备La0.8-xCexMg0.2 Ni 3.8(x=0,0.1,0.3,0.5),研究Ce替代部分La对La4MgNi19超晶格负极材料相结构及电化学性能的影响。研究表明,La4MgNi19合金相由LaNi5,(La,Mg)2Ni7,(La,Mg)5Ni19(3R-Ce5Co19)相组成。加入Ce后,(La,Mg)2Ni7相消失,出现2H-Pr 5Co 19结构的(La,Mg)5Ni19相,同时随着Ce替代量的增多,(La,Mg)5Ni19相含量增多,LaNi5相随之减少,Ce加入有利于形成A5B19相,特别是形成2H-Pr5Co19结构。电化学放电容量随着x值的增加呈现先增后减趋势,x=0.1时样品的电化学放电容量380.36 mAh/g最佳。合金电极活化次数、容量保持率和倍率放电性能随着Ce含量增加而增大。H在合金中的扩散速率是影响其倍率放电性能主要因素。展开更多
La-Mg-Ni-based hydrogen storage alloys with superlattice structures are the new generation anode material for nickel metal hydride(Ni-MH)batteries owing to the advantages of high capacity and exceptional activation pr...La-Mg-Ni-based hydrogen storage alloys with superlattice structures are the new generation anode material for nickel metal hydride(Ni-MH)batteries owing to the advantages of high capacity and exceptional activation properties.However,the cycling stability is not currently satisfactory enough which plagues its application.Herein,a strategy of partially substituting La with the Y element is proposed to boost the capacity durability of La-Mg-Ni-based alloys.Furthermore,phase structure regulation is implemented simultaneously to obtain the A5 B19-type alloy with good crystal stability specifically.It is found that Y promotes the phase formation of the Pr5 Co19-type phase after annealing at 985℃.The alloy containing Y contributes to the superior rate capability resulting from the promoted hydrogen diffusion rate.Notably,Y substitution enables strengthening the anti-pulverization ability of the alloy in terms of increasing the volume match between[A_(2)B_(4)]and[AB5]subunits,and effectively enhances the anti-corrosion ability of the alloy due to high electronegativity,realizing improved long-term cycling stability of the alloy from 74.2%to 78.5%after cycling 300 times.The work is expected to shed light on the composition and structure design of the La-Mg-Ni-based hydrogen storage alloy for Ni-MH batteries.展开更多
采用中间合金法在感应熔炼炉中制备La4MgNi19-xCox（x=02）合金,研究Co部分替代Ni对合金相结构和电化学性能的影响。XRD测试结果表明:合金主要由La4MgNi19(Ce5Co19+Pr5Co19)相和LaNi5相组成;x的增加有利于促进La4MgNi19相的形成,且晶胞...采用中间合金法在感应熔炼炉中制备La4MgNi19-xCox（x=02）合金,研究Co部分替代Ni对合金相结构和电化学性能的影响。XRD测试结果表明:合金主要由La4MgNi19(Ce5Co19+Pr5Co19)相和LaNi5相组成;x的增加有利于促进La4MgNi19相的形成,且晶胞体积随之增大。显微组织观察发现,合金为树枝晶结构,x的增加会使树枝晶变细。电化学测试表明:合金均具有良好的活化性能和高倍率放电性能(HRD600>92.57%);随着x的增加,合金的最大放电容量明显提高（从x=0时的359.23 m A·h/g增大到x=2的380.85 m A·h/g）,而循环寿命则先下降后逐渐提升。高倍率放电性能主要由合金电极的扩散系数控制,而循环稳定性的下降则是由于合金中La4MgNi19相的增加使膨胀率和晶间应力集中增大加速粉化所致。展开更多
The phase structure and electrochemical properties of La1.7＋xMg1.3-x（NiCoMn）9.3（x=0-0.4） alloys were investigated. The XRD analysis reveals that the alloys consist of LaNi5 phase and other phases, such as LaMg2Ni...The phase structure and electrochemical properties of La1.7＋xMg1.3-x（NiCoMn）9.3（x=0-0.4） alloys were investigated. The XRD analysis reveals that the alloys consist of LaNi5 phase and other phases, such as LaMg2Ni9 phase （PuNi3 structure） and La4MgNi19 phases （Ce5Co19＋Pr5Co19 structure, namely A5B19 type）. With the increase of the x value, the LaMg2Ni9 phase fades away and La4MgNi19 phases appear, while the abundance of LaNi5 phase firstly increases and then decreases. At the same time, the cell volume of LaNi5 phase and LaMg2Ni9 phase decreases. The electrochemical measurement shows that alloy electrodes could be activated in 4-5 cycles, and with the increase of the x value, the maximum discharge capacity gradually increases from 330.9 mA-h/g （x=0） to 366.8 mA-h/g （x=0.4）, but the high-rate dischargeability （HRD） and cyclic stability （S） decrease somewhat （x=0.4, HRD600=82.32%, S100=73.8%）. It is found that the HRD is mainly controlled by the electrocatalytic activity on the alloy electrode surface, and the decline of cyclic stability is due to the appearance of A5B19 type phase with larger hydrogen storage capacity, which leads to larger volume expansion and more intercrystalline stress and then easier pulverization during charging/discharging.展开更多
La（1-x）MgxNi（1.75）Co（2.05）（x=0.07, 0.08, 0.10, 0.13, 0.15） alloys were prepared by high-frequency inductive method, and then their structure and electrochemical properties were investigated systematically. The...La（1-x）MgxNi（1.75）Co（2.05）（x=0.07, 0.08, 0.10, 0.13, 0.15） alloys were prepared by high-frequency inductive method, and then their structure and electrochemical properties were investigated systematically. The XRD analysis revealed that the alloys consisted of LaNi5 phase and La4MgNi（19）（Ce5Co（19） ＋ Pr5Co（19）） phase, and the introduction of Mg could promote the formation of La4MgNi（19） phase. The observation of microstructure showed that all the alloys processed dendritic structure, which was refined with the increase of x value. The electrochemical measurements showed that all the alloys could be activated within 2 cycles, and with increasing x, the maximum discharge capacity obviously increased from 254.00 m Ah/g（x=0.07） to 351.51 mAh/g（x=0.15）, but the cycling stability（S（80）） decreased somehow from 78.4% to 73.9%. Meanwhile, the appropriate addition of Mg could improve the high-rate discharge capacity（HRD） of the alloy electrodes, which was mainly controlled by the electrochemical reaction rate on the surface of the alloys.展开更多
基金the financial support by the National Nat-ural Science Foundation of China(Nos.52201282,52071281,52371239)the China Postdoctoral Science Foundation(No.2023M742945)+4 种基金Hebei Provincial Postdoctoral Science Foundation(No.B2023003023)the Science Research Project of Hebei Education Department(No.BJK2022033)the Natural Science Foundation of Hebei Province(No.C2022203003)the Inner Mongolia Science and Technology Major Project(No.2020ZD0012)the Baotou Science and Technology Planning Project(No.XM2022BT09).
文摘La-Mg-Ni-based hydrogen storage alloys with superlattice structures are the new generation anode material for nickel metal hydride(Ni-MH)batteries owing to the advantages of high capacity and exceptional activation properties.However,the cycling stability is not currently satisfactory enough which plagues its application.Herein,a strategy of partially substituting La with the Y element is proposed to boost the capacity durability of La-Mg-Ni-based alloys.Furthermore,phase structure regulation is implemented simultaneously to obtain the A5 B19-type alloy with good crystal stability specifically.It is found that Y promotes the phase formation of the Pr5 Co19-type phase after annealing at 985℃.The alloy containing Y contributes to the superior rate capability resulting from the promoted hydrogen diffusion rate.Notably,Y substitution enables strengthening the anti-pulverization ability of the alloy in terms of increasing the volume match between[A_(2)B_(4)]and[AB5]subunits,and effectively enhances the anti-corrosion ability of the alloy due to high electronegativity,realizing improved long-term cycling stability of the alloy from 74.2%to 78.5%after cycling 300 times.The work is expected to shed light on the composition and structure design of the La-Mg-Ni-based hydrogen storage alloy for Ni-MH batteries.
文摘采用中间合金法在感应熔炼炉中制备La4MgNi19-xCox（x=02）合金,研究Co部分替代Ni对合金相结构和电化学性能的影响。XRD测试结果表明:合金主要由La4MgNi19(Ce5Co19+Pr5Co19)相和LaNi5相组成;x的增加有利于促进La4MgNi19相的形成,且晶胞体积随之增大。显微组织观察发现,合金为树枝晶结构,x的增加会使树枝晶变细。电化学测试表明:合金均具有良好的活化性能和高倍率放电性能(HRD600>92.57%);随着x的增加,合金的最大放电容量明显提高（从x=0时的359.23 m A·h/g增大到x=2的380.85 m A·h/g）,而循环寿命则先下降后逐渐提升。高倍率放电性能主要由合金电极的扩散系数控制,而循环稳定性的下降则是由于合金中La4MgNi19相的增加使膨胀率和晶间应力集中增大加速粉化所致。
基金Project (2008CL068L) supported by the Natural Science Research Project of Higher Education of Jiangsu Province, ChinaProject (50901036) supported by the National Natural Science Foundation of China
文摘The phase structure and electrochemical properties of La1.7＋xMg1.3-x（NiCoMn）9.3（x=0-0.4） alloys were investigated. The XRD analysis reveals that the alloys consist of LaNi5 phase and other phases, such as LaMg2Ni9 phase （PuNi3 structure） and La4MgNi19 phases （Ce5Co19＋Pr5Co19 structure, namely A5B19 type）. With the increase of the x value, the LaMg2Ni9 phase fades away and La4MgNi19 phases appear, while the abundance of LaNi5 phase firstly increases and then decreases. At the same time, the cell volume of LaNi5 phase and LaMg2Ni9 phase decreases. The electrochemical measurement shows that alloy electrodes could be activated in 4-5 cycles, and with the increase of the x value, the maximum discharge capacity gradually increases from 330.9 mA-h/g （x=0） to 366.8 mA-h/g （x=0.4）, but the high-rate dischargeability （HRD） and cyclic stability （S） decrease somewhat （x=0.4, HRD600=82.32%, S100=73.8%）. It is found that the HRD is mainly controlled by the electrocatalytic activity on the alloy electrode surface, and the decline of cyclic stability is due to the appearance of A5B19 type phase with larger hydrogen storage capacity, which leads to larger volume expansion and more intercrystalline stress and then easier pulverization during charging/discharging.
基金Project supported by the National Natural Science Foundation of China(50901036)the Graduate Science and Technology Innovation Project of Jiangsu University of Science and Technology(YCX15S-18)Priority Academic Program Development of Jiangsu Higher Education Institutions
文摘La（1-x）MgxNi（1.75）Co（2.05）（x=0.07, 0.08, 0.10, 0.13, 0.15） alloys were prepared by high-frequency inductive method, and then their structure and electrochemical properties were investigated systematically. The XRD analysis revealed that the alloys consisted of LaNi5 phase and La4MgNi（19）（Ce5Co（19） ＋ Pr5Co（19）） phase, and the introduction of Mg could promote the formation of La4MgNi（19） phase. The observation of microstructure showed that all the alloys processed dendritic structure, which was refined with the increase of x value. The electrochemical measurements showed that all the alloys could be activated within 2 cycles, and with increasing x, the maximum discharge capacity obviously increased from 254.00 m Ah/g（x=0.07） to 351.51 mAh/g（x=0.15）, but the cycling stability（S（80）） decreased somehow from 78.4% to 73.9%. Meanwhile, the appropriate addition of Mg could improve the high-rate discharge capacity（HRD） of the alloy electrodes, which was mainly controlled by the electrochemical reaction rate on the surface of the alloys.