The corrosion behavior of the acidophilic sulfur-oxidizing microorganism(ASOM)Acidithiobacillusthiooxidans(A.thiooxidans)on mortar was investigated for changes of medium and mortar,as well as for weight lossand surfac...The corrosion behavior of the acidophilic sulfur-oxidizing microorganism(ASOM)Acidithiobacillusthiooxidans(A.thiooxidans)on mortar was investigated for changes of medium and mortar,as well as for weight lossand surface morphology of mortar specimens.Weight loss analysis showed that mortar weight was reduced by(15.1±2.2)%after 56 d.Morphological surface analysis of mortar specimens showed weakly structured fibrous substances with2−100μm in size.The pH variations of the mortar surface and medium indicated that biogenic sulfuric acid had beenproduced by A.thiooxidans.The results prove that A.thiooxidans accelerated concrete corrosion and caused concretefailure.展开更多
Microbiologically-induced concrete corrosion(MICC)refers to chemical reactions between biologically produced sulphuric acid and with hydration products in the hardened concrete paste,resulting in an early reduction of...Microbiologically-induced concrete corrosion(MICC)refers to chemical reactions between biologically produced sulphuric acid and with hydration products in the hardened concrete paste,resulting in an early reduction of strength,deterioration,and very severe circumstances,structural failure.This paper explores the bactericidal characteristics of cementitious materials with surface coated with modified zeolite-polyurethane.The zeolite-polyurethane coating incorporated with silver was studied in environments inoculated with A.thiooxidans bacteria for 8 consecutive weeks.The antibacterial characteristics were evaluated in terms of pH,optical density(OD),sulphate production and bacteria count to determine the effectiveness of the zeolite-polyurethane coatings in environments inoculated with A.thiooxidans bacteria producing the sulphuric acid.The results revealed that the samples incorporated with silver modified zeolites generally showed antibacterial performance(regardless of the zeolite type)compared with unmodified polyurethane coating.This was evaluated by the lack of bacteria attachment and the deformed microcolonies on the sample surface,lag in pH reduction,increase in OD,and sulphate production.The silver zeolites gained their antibacterial performance from the release of silver ions(Ag^(+))when the sample comes into contact with aqueous solutions.This results in the inhibition of cell functions of the bacteria and subsequently causes cell damage.展开更多
基金Project(42476209)supported by the National Natural Science Foundation of ChinaProject(2023GXNSFBA026252)supported by the Youth Science Foundation of Guangxi Province,China+2 种基金Project(ZR2023MD024)supported by the Natural Science Foundation of Shandong Province,ChinaProject(JC22022104)supported by the Natural Science Foundation of Nantong,ChinaProject(2023VEA0007)supported by the Chinese Academy of Sciences President’s International Fellowship Initiative。
文摘The corrosion behavior of the acidophilic sulfur-oxidizing microorganism(ASOM)Acidithiobacillusthiooxidans(A.thiooxidans)on mortar was investigated for changes of medium and mortar,as well as for weight lossand surface morphology of mortar specimens.Weight loss analysis showed that mortar weight was reduced by(15.1±2.2)%after 56 d.Morphological surface analysis of mortar specimens showed weakly structured fibrous substances with2−100μm in size.The pH variations of the mortar surface and medium indicated that biogenic sulfuric acid had beenproduced by A.thiooxidans.The results prove that A.thiooxidans accelerated concrete corrosion and caused concretefailure.
基金Project(J130000.2524.04H87) supported by the Ministry of Higher Education of Malaysia and Universiti Teknologi Malaysia。
文摘Microbiologically-induced concrete corrosion(MICC)refers to chemical reactions between biologically produced sulphuric acid and with hydration products in the hardened concrete paste,resulting in an early reduction of strength,deterioration,and very severe circumstances,structural failure.This paper explores the bactericidal characteristics of cementitious materials with surface coated with modified zeolite-polyurethane.The zeolite-polyurethane coating incorporated with silver was studied in environments inoculated with A.thiooxidans bacteria for 8 consecutive weeks.The antibacterial characteristics were evaluated in terms of pH,optical density(OD),sulphate production and bacteria count to determine the effectiveness of the zeolite-polyurethane coatings in environments inoculated with A.thiooxidans bacteria producing the sulphuric acid.The results revealed that the samples incorporated with silver modified zeolites generally showed antibacterial performance(regardless of the zeolite type)compared with unmodified polyurethane coating.This was evaluated by the lack of bacteria attachment and the deformed microcolonies on the sample surface,lag in pH reduction,increase in OD,and sulphate production.The silver zeolites gained their antibacterial performance from the release of silver ions(Ag^(+))when the sample comes into contact with aqueous solutions.This results in the inhibition of cell functions of the bacteria and subsequently causes cell damage.